Effect of curing conditions on compressive strength behavior on alkali-activated ceramic wastes
Autor(a) principal: | |
---|---|
Data de Publicação: | 2021 |
Outros Autores: | , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
Texto Completo: | http://hdl.handle.net/1822/70790 |
Resumo: | The industrial sector is responsible for the generation of a large amount of solid waste, of which some is partially recycled, but the majority is deposited in landfills or landfills causing various negative impacts on the environment. Alkaline cements are attracting growing interest for their potential to allow the industry to operate within the constraints imposed on CO2 emissions. The objective of this research was to know the effect of different curing conditions on the compressive strength behavior of alkaline activated ceramic residues. As a result, it was determined that an alkali-activated matrix is significantly influenced when cured at a temperature of 70 ° C, reaching, at 90 days of age, a compressive strength of up to 39.3 MPa in contrast to 27.08 MPa. when curing was carried out in environmental conditions of 20 ° C (± 0.5 ° C) and 60% (± 5%) of relative humidity (RH). This work was complemented with a microstructural analysis that included Scanning Electron Microscopy (SEM) and X-ray Energy Dispersion Analyzer (EDX). |
id |
RCAP_15330a5d97968a6cb250544f2b90cea9 |
---|---|
oai_identifier_str |
oai:repositorium.sdum.uminho.pt:1822/70790 |
network_acronym_str |
RCAP |
network_name_str |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
repository_id_str |
7160 |
spelling |
Effect of curing conditions on compressive strength behavior on alkali-activated ceramic wastesEfecto de las condiciones de curado en el comportamiento de resistencia a la compresión en residuos cerámicos activados alcalinamenteEfeito das condições de cura no comportamento da resistência à compressão em resíduos de cerâmica ativados por álcaliAlkali activationCeramic wasteCompressive strengthResiduos cerámicosActivación de álcalisResistencia a la compresiónAtivação alcalinaForça compressivaThe industrial sector is responsible for the generation of a large amount of solid waste, of which some is partially recycled, but the majority is deposited in landfills or landfills causing various negative impacts on the environment. Alkaline cements are attracting growing interest for their potential to allow the industry to operate within the constraints imposed on CO2 emissions. The objective of this research was to know the effect of different curing conditions on the compressive strength behavior of alkaline activated ceramic residues. As a result, it was determined that an alkali-activated matrix is significantly influenced when cured at a temperature of 70 ° C, reaching, at 90 days of age, a compressive strength of up to 39.3 MPa in contrast to 27.08 MPa. when curing was carried out in environmental conditions of 20 ° C (± 0.5 ° C) and 60% (± 5%) of relative humidity (RH). This work was complemented with a microstructural analysis that included Scanning Electron Microscopy (SEM) and X-ray Energy Dispersion Analyzer (EDX).El sector industrial es responsable de la generación de una gran cantidad de residuos sólidos, de los cuales algunos son parcialmente reciclados, pero la mayoría son depositados en vertederos o rellenos sanitarios provocando diversos impactos negativos en el medio ambiente. Los cementos alcalinos están atrayendo un interés creciente por su potencial para permitir que la industria opere dentro de las limitaciones impuestas a las emisiones de CO2. La presente investigación tuvo como objetivo conocer el efecto de diferentes condiciones de curado sobre el comportamiento de resistencia a compresión de los residuos cerámicos activados alcalinamente. Como resultado se determinó que una matriz álcali-activada es significativamente influenciada cuando se cura con una temperatura de 70°C alcanzando, a los 90 días de edad, una resistencia a la compresión de hasta 39,3 MPa en contraste con 27,08 MPa cuando el curado se realizó en condiciones ambientales de 20°C (± 0,5 ° C) y 60% (± 5%) de humedad relativa (RH). Este trabajo se complementó con un análisis microestructural que incluyó Microscopía electrónica de barrido (SEM) y Analizador de dispersión de energía de rayos X (EDX).O setor industrial é responsável pela geração de grande quantidade de resíduos sólidos, alguns deles parcialmente reciclados, mas a maior parte é depositada em aterros ou aterros sanitários causando diversos impactos negativos ao meio ambiente. Os cimentos alcalinos estão atraindo cada vez mais interesse por seu potencial de permitir que a indústria opere dentro das restrições impostas às emissões de CO2. O objetivo desta pesquisa foi conhecer o efeito de diferentes condições de cura no comportamento da resistência à compressão de resíduos cerâmicos alcalinos ativados. Como resultado, determinou-se que uma matriz alcalina ativada é significativamente influenciada quando curada a uma temperatura de 70 ° C, atingindo, aos 90 dias de idade, uma resistência à compressão de até 39,3 MPa em contraste com 27,08 MPa. quando a cura foi realizada em condições ambientais de 20 ° C (± 0,5 ° C) e 60% (± 5%) de umidade relativa (UR). Este trabalho foi complementado com uma análise microestrutural que incluiu Microscopia Eletrônica de Varredura (MEV) e Analisador de Dispersão de Energia de Raios-X (EDX).Casa Editora del PoloUniversidade do MinhoVaca, Norma Yolanda GaiborLeitão, DinisMiranda, Tiago F. S.Cunha, Vitor M. C. F.Cristelo, Nuno2021-032021-03-01T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/articleapplication/pdfhttp://hdl.handle.net/1822/70790engGaibor N. Y., Leitão D., Miranda T., Cunha V. M. C. F., Cristelo N. Effect of curing conditions on compressive strength behavior on alkali-activated ceramic wastes, Polo del Conocimiento, Vol. Vol. 6, n.º3, pp. 977-990, doi:10.23857/pc.v6i3.2416, 20212550-682X10.23857/pc.v6i3.2416https://polodelconocimiento.com/ojs/index.php/es/article/view/2416info:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-07-21T12:21:10Zoai:repositorium.sdum.uminho.pt:1822/70790Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T19:14:22.699848Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse |
dc.title.none.fl_str_mv |
Effect of curing conditions on compressive strength behavior on alkali-activated ceramic wastes Efecto de las condiciones de curado en el comportamiento de resistencia a la compresión en residuos cerámicos activados alcalinamente Efeito das condições de cura no comportamento da resistência à compressão em resíduos de cerâmica ativados por álcali |
title |
Effect of curing conditions on compressive strength behavior on alkali-activated ceramic wastes |
spellingShingle |
Effect of curing conditions on compressive strength behavior on alkali-activated ceramic wastes Vaca, Norma Yolanda Gaibor Alkali activation Ceramic waste Compressive strength Residuos cerámicos Activación de álcalis Resistencia a la compresión Ativação alcalina Força compressiva |
title_short |
Effect of curing conditions on compressive strength behavior on alkali-activated ceramic wastes |
title_full |
Effect of curing conditions on compressive strength behavior on alkali-activated ceramic wastes |
title_fullStr |
Effect of curing conditions on compressive strength behavior on alkali-activated ceramic wastes |
title_full_unstemmed |
Effect of curing conditions on compressive strength behavior on alkali-activated ceramic wastes |
title_sort |
Effect of curing conditions on compressive strength behavior on alkali-activated ceramic wastes |
author |
Vaca, Norma Yolanda Gaibor |
author_facet |
Vaca, Norma Yolanda Gaibor Leitão, Dinis Miranda, Tiago F. S. Cunha, Vitor M. C. F. Cristelo, Nuno |
author_role |
author |
author2 |
Leitão, Dinis Miranda, Tiago F. S. Cunha, Vitor M. C. F. Cristelo, Nuno |
author2_role |
author author author author |
dc.contributor.none.fl_str_mv |
Universidade do Minho |
dc.contributor.author.fl_str_mv |
Vaca, Norma Yolanda Gaibor Leitão, Dinis Miranda, Tiago F. S. Cunha, Vitor M. C. F. Cristelo, Nuno |
dc.subject.por.fl_str_mv |
Alkali activation Ceramic waste Compressive strength Residuos cerámicos Activación de álcalis Resistencia a la compresión Ativação alcalina Força compressiva |
topic |
Alkali activation Ceramic waste Compressive strength Residuos cerámicos Activación de álcalis Resistencia a la compresión Ativação alcalina Força compressiva |
description |
The industrial sector is responsible for the generation of a large amount of solid waste, of which some is partially recycled, but the majority is deposited in landfills or landfills causing various negative impacts on the environment. Alkaline cements are attracting growing interest for their potential to allow the industry to operate within the constraints imposed on CO2 emissions. The objective of this research was to know the effect of different curing conditions on the compressive strength behavior of alkaline activated ceramic residues. As a result, it was determined that an alkali-activated matrix is significantly influenced when cured at a temperature of 70 ° C, reaching, at 90 days of age, a compressive strength of up to 39.3 MPa in contrast to 27.08 MPa. when curing was carried out in environmental conditions of 20 ° C (± 0.5 ° C) and 60% (± 5%) of relative humidity (RH). This work was complemented with a microstructural analysis that included Scanning Electron Microscopy (SEM) and X-ray Energy Dispersion Analyzer (EDX). |
publishDate |
2021 |
dc.date.none.fl_str_mv |
2021-03 2021-03-01T00:00:00Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://hdl.handle.net/1822/70790 |
url |
http://hdl.handle.net/1822/70790 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
Gaibor N. Y., Leitão D., Miranda T., Cunha V. M. C. F., Cristelo N. Effect of curing conditions on compressive strength behavior on alkali-activated ceramic wastes, Polo del Conocimiento, Vol. Vol. 6, n.º3, pp. 977-990, doi:10.23857/pc.v6i3.2416, 2021 2550-682X 10.23857/pc.v6i3.2416 https://polodelconocimiento.com/ojs/index.php/es/article/view/2416 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Casa Editora del Polo |
publisher.none.fl_str_mv |
Casa Editora del Polo |
dc.source.none.fl_str_mv |
reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação instacron:RCAAP |
instname_str |
Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação |
instacron_str |
RCAAP |
institution |
RCAAP |
reponame_str |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
collection |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
repository.name.fl_str_mv |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação |
repository.mail.fl_str_mv |
|
_version_ |
1799132585620668416 |