Influência da geometria da junta na resistência à tração e à fadiga de juntas coladas híbridas em alumínio

Detalhes bibliográficos
Autor(a) principal: Oliveira, Vladimir Joukov Costa de
Data de Publicação: 2020
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/10316/93950
Resumo: Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
id RCAP_1dbfefa5914e123165622b5e5e05e2b4
oai_identifier_str oai:estudogeral.uc.pt:10316/93950
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Influência da geometria da junta na resistência à tração e à fadiga de juntas coladas híbridas em alumínioInfluence of the geometry of the joint on the tensile strength and fatigue strength of hybrid adhesive joints in aluminumLigações adesivasJunta colada mista scarf com degrausResistência à traçãoResistência à fadigaespessura do adesivoAdhesive bondsstepped scarf mixed jointTensile strengthFatigue strengthadhesive thicknessDissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e TecnologiaAs ligações adesivas podem ser utilizadas em várias aplicações estruturais, tais como no setor automóvel, no ferroviário e no aeronáutico. Estas proporcionam a capacidade de se obterem estruturas mais leves, de reduzir o custo de fabrico, colar materiais diferentes e de distribuírem melhor as tensões do que os métodos mais convencionais. Pelo facto de existirem ainda muitas indústrias que utilizam esses métodos convencionais e que precisam da utilização de materiais mais leves, é importante o estudo das ligações adesivas de modo a que seja viável a utilização destas ligações nessas áreas industriais. Para isso, nesta dissertação foi estudada a resistência à fadiga e a resistência à tração num novo tipo de junta, a junta colada mista scarf com degraus em contacto positivo.Nesta junta foram estudados dois parâmetros: a inclinação e a altura dos degraus. Realizaram-se quatro geometrias de junta diferentes, com inclinações de 15º e de 30º, e altura dos degraus de 0,50 mm e de 0,75 mm. O adesivo utilizado foi uma resina epóxi Araldite® 420 A/B e o material para os aderentes foi a liga de alumínio 5083-H111. As quatro geometrias foram submetidas a ensaios de tração. Nos ensaios de fadiga foram testadas apenas as juntas com altura de degrau de 0,75 mm e inclinações de 15º e 30º com. Analisou-se evolução da falha através de um equipamento de extensometria ótica que utiliza a técnica de correlação de imagem digital (DIC) e concluiu-se que esta tem origem na extremidade da junta e propaga-se até ao centro da junta.Foram também observadas as superfícies de rotura e as espessuras do adesivo. Quanto às superfícies de rotura, concluiu-se que não existe nenhuma relação entre a percentagem de rotura adesiva e a espessura do adesivo; nem entre a percentagem de rotura adesiva e o número de ciclos de vida na fadiga. Para a espessura foi observado que existe uma relação com os números de ciclos realizados à mesma tensão aplicada. Para espessuras baixas obtiveram-se melhores resultados de resistência à fadiga.No estudo da resistência à tração, concluiu-se que as juntas coladas mistas scarf com degraus apresentam melhores resultados em comparação com as juntas scarf; para a mesma inclinação houve um aumento de 29,4% de resistência à tração. Quando comparado com as juntas com três degraus, os resultados foram inferiores 54.7%. Nos ensaios de fadiga, as juntas estudadas obtiveram melhores resultados do que as existentes na literatura.Bonded joints can be used in several structural applications such as the automobile, railroad and aeronautics industry. They can provide the capacity to obtain lighter structures, to reduce the production costs, to bond different materials and to distribute better the tensions than the most conventional methods. Because there are many industries that continue to use conventional methods and need to use more lightweight materials, it is important to study the bonded joints in order to get better results and thus be able to use in more industries. For that, in this dissertation it was studied a new type of geometry, the stepped scarf mixed joint, and was studied the behavior to the tensile strength and fatigue strength.For this joint two parameters were studied: the angle and the height of the step. Four different geometries were made with angles of 15º and 30º, and with a height of 0,50 mm and 0,75 mm of the step. The adhesive utilized was an epoxy resin Araldite® 420 A/B and the material used on the adherent was an aluminium alloy 5083-H111.The four geometries were submitted to tensile tests. In the fatigue tests only the joints with a step height of 0,75 mm and angles of 15º and 30º were tested. The crack propagation was analysed through an equipment of optic extensometry that utilizes the technic of the digital image correlation (DIC) and it was concluded that the crack initiated at the end of the joint and evolved to the center. The fracture surface and the adhesive thickness was also analyzed. As to the fracture surface, it was concluded that there is no relation between the percentage of the adhesive fracture and the thickness of the adhesive, nor between the percentage of the adhesive fracture and the number of cycles in the fatigue tests. For the thickness it was observed a relation with the number of cycles for the same tension applied. The lower thicknesses obtained the better the result.In the study of the tensile strength, it was concluded that the stepped scarf mixed joint presents better results than the scarf joint. For the same angle it has 29,39% more tensile strength. When compared to the three step lap joints, the results were lower by 54,7%. In the fatigue tests, the joint studied obtained better results that the ones that are on the literature.2020-11-27info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesishttp://hdl.handle.net/10316/93950http://hdl.handle.net/10316/93950TID:202687392porOliveira, Vladimir Joukov Costa deinfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2022-05-25T10:24:08Zoai:estudogeral.uc.pt:10316/93950Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T21:12:48.122353Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Influência da geometria da junta na resistência à tração e à fadiga de juntas coladas híbridas em alumínio
Influence of the geometry of the joint on the tensile strength and fatigue strength of hybrid adhesive joints in aluminum
title Influência da geometria da junta na resistência à tração e à fadiga de juntas coladas híbridas em alumínio
spellingShingle Influência da geometria da junta na resistência à tração e à fadiga de juntas coladas híbridas em alumínio
Oliveira, Vladimir Joukov Costa de
Ligações adesivas
Junta colada mista scarf com degraus
Resistência à tração
Resistência à fadiga
espessura do adesivo
Adhesive bonds
stepped scarf mixed joint
Tensile strength
Fatigue strength
adhesive thickness
title_short Influência da geometria da junta na resistência à tração e à fadiga de juntas coladas híbridas em alumínio
title_full Influência da geometria da junta na resistência à tração e à fadiga de juntas coladas híbridas em alumínio
title_fullStr Influência da geometria da junta na resistência à tração e à fadiga de juntas coladas híbridas em alumínio
title_full_unstemmed Influência da geometria da junta na resistência à tração e à fadiga de juntas coladas híbridas em alumínio
title_sort Influência da geometria da junta na resistência à tração e à fadiga de juntas coladas híbridas em alumínio
author Oliveira, Vladimir Joukov Costa de
author_facet Oliveira, Vladimir Joukov Costa de
author_role author
dc.contributor.author.fl_str_mv Oliveira, Vladimir Joukov Costa de
dc.subject.por.fl_str_mv Ligações adesivas
Junta colada mista scarf com degraus
Resistência à tração
Resistência à fadiga
espessura do adesivo
Adhesive bonds
stepped scarf mixed joint
Tensile strength
Fatigue strength
adhesive thickness
topic Ligações adesivas
Junta colada mista scarf com degraus
Resistência à tração
Resistência à fadiga
espessura do adesivo
Adhesive bonds
stepped scarf mixed joint
Tensile strength
Fatigue strength
adhesive thickness
description Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
publishDate 2020
dc.date.none.fl_str_mv 2020-11-27
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/10316/93950
http://hdl.handle.net/10316/93950
TID:202687392
url http://hdl.handle.net/10316/93950
identifier_str_mv TID:202687392
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799134023211024384

Registros relacionados