Application of the response surface method to optimize alkali activated cements based on low-reactivity ladle furnace slag
Autor(a) principal: | |
---|---|
Data de Publicação: | 2020 |
Outros Autores: | , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
Texto Completo: | https://hdl.handle.net/10216/133481 |
Resumo: | Steel-making slags, resulting from basic oxygen furnaces or electric arc furnaces are heavily applied in the construction industry, as an aggregate for pavements or concrete. Although possessing a significant crystalline content, it is expected that, if properly milled, the reactivity of these slags can increase up to a point when they are viable to produce alkaline cements. The aim of this study was the application of a response surface method to design the experimental work required to optimise the composition of an alkaline cement based on ladle furnace slag, a specific type of steel slag (SG). Fly ash (FA) was also added, in a precursor role, and the activation was achieved with an alkaline solution prepared with sodium silicate (SS) and sodium hydroxide (SH). The factors/variables considered were the activator index X = SS/(SS + SH), the precursor index Y = SG/(SG + FA) and the SH concentration (Z). The output variables were the unconfined compression strength and the flexural strength, after 7 and 28 days curing. Results indicate that the activator index (X) was the most influential variable, followed by the precursor index (Y). Microstructural analysis of selected pastes was also performed, using scanning electron microscopy and energy dispersive spectroscopy. The ideal composition obtained for the alkaline cement was the mixture constituted by X = 0.75, Y = 0.5 and Z = 10 (activator: 75% SS and 25% SH; precursor: 50% SG and 50% FA; SH concentration = 10 molal). This mixture achieved 8.70 MPa of flexural strength and 44.25 MPa of compressive strength which is reasonable for the required application (soil stabilisation). |
id |
RCAP_242b4991f3493babc6a2c6c01d67a59b |
---|---|
oai_identifier_str |
oai:repositorio-aberto.up.pt:10216/133481 |
network_acronym_str |
RCAP |
network_name_str |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
repository_id_str |
7160 |
spelling |
Application of the response surface method to optimize alkali activated cements based on low-reactivity ladle furnace slagSteel-making slags, resulting from basic oxygen furnaces or electric arc furnaces are heavily applied in the construction industry, as an aggregate for pavements or concrete. Although possessing a significant crystalline content, it is expected that, if properly milled, the reactivity of these slags can increase up to a point when they are viable to produce alkaline cements. The aim of this study was the application of a response surface method to design the experimental work required to optimise the composition of an alkaline cement based on ladle furnace slag, a specific type of steel slag (SG). Fly ash (FA) was also added, in a precursor role, and the activation was achieved with an alkaline solution prepared with sodium silicate (SS) and sodium hydroxide (SH). The factors/variables considered were the activator index X = SS/(SS + SH), the precursor index Y = SG/(SG + FA) and the SH concentration (Z). The output variables were the unconfined compression strength and the flexural strength, after 7 and 28 days curing. Results indicate that the activator index (X) was the most influential variable, followed by the precursor index (Y). Microstructural analysis of selected pastes was also performed, using scanning electron microscopy and energy dispersive spectroscopy. The ideal composition obtained for the alkaline cement was the mixture constituted by X = 0.75, Y = 0.5 and Z = 10 (activator: 75% SS and 25% SH; precursor: 50% SG and 50% FA; SH concentration = 10 molal). This mixture achieved 8.70 MPa of flexural strength and 44.25 MPa of compressive strength which is reasonable for the required application (soil stabilisation).2020-12-202020-12-20T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/articleapplication/pdfhttps://hdl.handle.net/10216/133481eng0950-061810.1016/j.conbuildmat.2020.120271Claver PinheiroSara RiosA. Viana da FonsecaAna Fernandez-JimenezNuno Cristeloinfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-11-29T16:00:47Zoai:repositorio-aberto.up.pt:10216/133481Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-20T00:36:37.716134Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse |
dc.title.none.fl_str_mv |
Application of the response surface method to optimize alkali activated cements based on low-reactivity ladle furnace slag |
title |
Application of the response surface method to optimize alkali activated cements based on low-reactivity ladle furnace slag |
spellingShingle |
Application of the response surface method to optimize alkali activated cements based on low-reactivity ladle furnace slag Claver Pinheiro |
title_short |
Application of the response surface method to optimize alkali activated cements based on low-reactivity ladle furnace slag |
title_full |
Application of the response surface method to optimize alkali activated cements based on low-reactivity ladle furnace slag |
title_fullStr |
Application of the response surface method to optimize alkali activated cements based on low-reactivity ladle furnace slag |
title_full_unstemmed |
Application of the response surface method to optimize alkali activated cements based on low-reactivity ladle furnace slag |
title_sort |
Application of the response surface method to optimize alkali activated cements based on low-reactivity ladle furnace slag |
author |
Claver Pinheiro |
author_facet |
Claver Pinheiro Sara Rios A. Viana da Fonseca Ana Fernandez-Jimenez Nuno Cristelo |
author_role |
author |
author2 |
Sara Rios A. Viana da Fonseca Ana Fernandez-Jimenez Nuno Cristelo |
author2_role |
author author author author |
dc.contributor.author.fl_str_mv |
Claver Pinheiro Sara Rios A. Viana da Fonseca Ana Fernandez-Jimenez Nuno Cristelo |
description |
Steel-making slags, resulting from basic oxygen furnaces or electric arc furnaces are heavily applied in the construction industry, as an aggregate for pavements or concrete. Although possessing a significant crystalline content, it is expected that, if properly milled, the reactivity of these slags can increase up to a point when they are viable to produce alkaline cements. The aim of this study was the application of a response surface method to design the experimental work required to optimise the composition of an alkaline cement based on ladle furnace slag, a specific type of steel slag (SG). Fly ash (FA) was also added, in a precursor role, and the activation was achieved with an alkaline solution prepared with sodium silicate (SS) and sodium hydroxide (SH). The factors/variables considered were the activator index X = SS/(SS + SH), the precursor index Y = SG/(SG + FA) and the SH concentration (Z). The output variables were the unconfined compression strength and the flexural strength, after 7 and 28 days curing. Results indicate that the activator index (X) was the most influential variable, followed by the precursor index (Y). Microstructural analysis of selected pastes was also performed, using scanning electron microscopy and energy dispersive spectroscopy. The ideal composition obtained for the alkaline cement was the mixture constituted by X = 0.75, Y = 0.5 and Z = 10 (activator: 75% SS and 25% SH; precursor: 50% SG and 50% FA; SH concentration = 10 molal). This mixture achieved 8.70 MPa of flexural strength and 44.25 MPa of compressive strength which is reasonable for the required application (soil stabilisation). |
publishDate |
2020 |
dc.date.none.fl_str_mv |
2020-12-20 2020-12-20T00:00:00Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
https://hdl.handle.net/10216/133481 |
url |
https://hdl.handle.net/10216/133481 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
0950-0618 10.1016/j.conbuildmat.2020.120271 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.source.none.fl_str_mv |
reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação instacron:RCAAP |
instname_str |
Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação |
instacron_str |
RCAAP |
institution |
RCAAP |
reponame_str |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
collection |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
repository.name.fl_str_mv |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação |
repository.mail.fl_str_mv |
|
_version_ |
1799136274436587520 |