Perovskite-like LaNiO3-δ as oxygen electrode material for solid oxide electrolysis cells

• Autor(a) principal: Yaremchenko, Aleksey
• Data de Publicação: 2019
• Outros Autores: Arias-Serrano, Blanca I., Zakharchuk, Kiryl, Frade, Jorge R.
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
• Texto Completo: http://hdl.handle.net/10773/29079

Perovskite-like LaNiO3-δ was evaluated as potential oxygen electrode material for solid oxide electrolysis cells. Compared to the Ruddlesden-Popper Lan+1NinO3n+1 (n = 1,2,3) counterparts, LaNiO3-δ exhibits higher p-type metallic-like conductivity under oxidizing conditions (450 S×cm-1 at 800°C for highly porous ceramics) together with a moderate thermal expansion coefficient (13.7 ppm×K-1 in air at 25-800°C) compatible with common solid electrolytes. The measured electrode polarization resistance (Rη) in contact with YSZ, CGO and LSGM solid electrolytes was 1.4, 0.77 and 0.22 Ω×cm2 at 800°C, and 208, 123 and 7.1 Ω×cm2 at 600°C, respectively, under zero-current conditions in air. Surface modification of via PrOx infiltration resulted in lower values of Rη (0.024 Ω×cm2 at 800°C and 0.76 Ω×cm2 at 600°C) and low anodic overpotentials (20 mV at 800°C and 500 mA×cm-2) in contact with LSGM.