Estudo da plastificação de poli(ácido láctico) via extrusão reactiva utilizando álcoois ramificados e oligómeros de ácido láctico

Detalhes bibliográficos
Autor(a) principal: Sangarote, Sérgio Ambrósio
Data de Publicação: 2016
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/10316/81661
Resumo: Dissertação de Mestrado Integrado em Engenharia Química apresentada à Faculdade de Ciências e Tecnologia da Universidade de Coimbra.
id RCAP_3f75196331976cfae136c7b2b2c12509
oai_identifier_str oai:estudogeral.uc.pt:10316/81661
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Estudo da plastificação de poli(ácido láctico) via extrusão reactiva utilizando álcoois ramificados e oligómeros de ácido lácticoPlasticization of poly lactic acid via reactive extrusion using branched alcohols and lactic acid oligomersPLAPlastificaçãoExtrusão reativaÁlcool ramificadoOLA-HEMAPLAplasticizationreactive extrusionbranched alcoholOLA-HEMADissertação de Mestrado Integrado em Engenharia Química apresentada à Faculdade de Ciências e Tecnologia da Universidade de Coimbra.Este trabalho teve como principal objetivo o estudo da plastificação do poli(ácido láctico) (PLA) com recurso à extrusão reativa (REx), utilizando três plastificantes diferentes: álcool ramificado (AR), diéster derivado do AR e oligómeros de ácido láctico funcionalizados com ligações duplas (OLA-HEMA de 1000 e 5000 g/mol) na presença de peróxido de dicumilo (DCP). O AR está disponível comercialmente, ao passo que o diéster e o OLA-HEMA foram sintetizados com sucesso no decorrer do trabalho. Os plastificantes foram depois usados em diferentes concentrações (4, 10 e 20 % m/m), tendo sido utilizados dois métodos de mistura das formulações: (i) dissolução dos componentes da mistura (PLA, DCP, plastificante) em clorofórmio, seguido de evaporação para a obtenção de um filme e (ii) mistura física dos componentes sem uso de solvente. De seguida as misturas foram submetidas à REx numa extrusora laboratorial de fuso simples com objetivo de enxertar os plastificantes nas cadeias do PLA. O PLA plastificado foi recolhido na forma de fios com cerca de 1.4 mm de diâmetro. Para alguns testes de caracterização, nomeadamente, análise dinâmica termomecânica (DMTA) e ensaios de tração, foi necessário obter provetes pelo que o fio extrudido foi sujeito a um processamento adicional (prensagem a quente).A partir da avaliação preliminar efetuada às misturas extrudidas, constatou-se que o efeito plastificante nos materiais misturados fisicamente e plastificados com OLA-HEMA de menor peso molecular (˜1000 g/mol) não foi significativo, razão pela qual foram abandonados e o estudo passou a dar atenção aos materiais resultantes da REx a partir das misturas obtidas por dissolução dos componentes em clorofórmio, seguido de evaporação, e em cujas misturas foram usados como plastificantes o AR, diéster e OLA-HEMA de 5000 g/mol.Da avaliação efectuada, os resultados de análise termogravimétrica (TGA) revelaram maior estabilidade térmica (359 °C) para os materiais plastificados com 10 % (m/m) de diéster em comparação com PLA puro (311 °C). No entanto, é de salientar que nenhum dos outros plastificantes levou a um decréscimo acentuado da estabilidade térmica. A calorimetria diferencial de varrimento (DSC) revelou uma redução da Tg em 12 ºC e 13 ºC, para o PLA plastificado (na forma de fio) com 4 e 20 % (m/m) de diéster e OLA-HEMA, respetivamente. Os resultados de DMTA revelaram que as misturas não apresentaram nenhuma separação de fase relacionada com imiscibilidade do sistema PLA-plastificante, tendo-se verificado que todos os materiais plastificados tinham um módulo elástico (E’) inferior ao apresentado para o PLA puro. Esta diminuição é mais evidente para a formulação com 10 % (m/m) de diéster (E’PLA/Ester-10=1415 MPa vs E’PLA puro=2524 MPa). Os ensaios de tração revelaram aumento da elongação em até 6 e 52 vezes para amostras em provetes (PLA/AR-10) e fios (PLA/OLA-10), respetivamente em relação ao PLA puro. O PLA plastificado com OLA-HEMA apresentou boa estabilidade química face ao ácido acético e etanol nos testes de migração.This work aimed to study the plasticization of poly(lactic acid) (PLA) by means of reactive extrusion (REx) using three different plasticizers: a branched alcohol (BA), a BA based diester and lactic acid oligomers functionalized with double bonds (OLA-HEMA, 1000 and 5000 g/mol) in the presence of dicumyl peroxide (DCP). The BA is commercially available, whereas the diester and OLA-HEMA were successfully synthesized in this work. Plasticizers were then used in different concentrations (4, 10 to 20 % wt.) and two blending methods were used: (i) dissolution of the components of the mixture (PLA, DCP, plasticizer) in chloroform, followed by evaporation to obtain a film and (ii) physical mixture of the components without solvent. Then the mixtures were subjected to REx on a laboratory single-screw extruder in order to graft the plasticizers onto PLA chains. The plasticized blends were collected in the form of strands with 1.4 mm in diameter. For some characterization tests, namely, dynamic thermomechanical analysis (DMTA) and tensile tests, it was necessary to obtain test pieces (e.g., dog-bone-shape) and in such cases the extruded strand was subjected to additional processing (hot melt pressing).From the preliminary studies performed on the extruded blends, it was found that the plasticization effect of the materiasl mixed physically and where lower molecular weight OLA-HEMA (˜1000 g/mol) was used as plasticizer was not significant and because of that, the work developed during the study focused essentially on the REx of the mixtures obtained by dissolving the components in chloroform, followed by evaporation, and mixtures in which the BA, diester and OLA-HEMA (5000 g/mol) were used as plasticizers .The results of thermogravimetric analysis (TGA) showed that the blends comprising 10 % (wt.) of the diester had better thermal stability (359 °C) than neat PLA (311 °C). However, it is noteworthy that none of the other plasticizers led to a significant decrease in thermal stability. The differential scanning calorimetry (DSC) showed a reduction of Tg by 12 °C and 13 °C for plasticized PLA (in the form of strands) with 4 and 20 % (wt) of diester and OLA-HEMA, respectively. The DMTA results revealed that the blends showed no phase separation related to the immiscibility of the PLA-plasticizer system, and it was found that all the plasticized materials had an elastic modulus (E’) lower than that of neat PLA. This decrease is more evident for formulation with 10 % (wt.) of the diester (E’PLA/Ester-10=1415 MPa vs E’neat PLA=2524 MPa). Tensile tests showed increased elongation up to 6 and 52 times for samples on dog-bone-shaped samples (PLA/AR-10) and strands (PLA/OLA-10), respectively, compared to neat PLA. The plasticized PLA with OLA-HEMA showed good chemical stability against acetic acid and ethanol in the migration tests.2016-09-12info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesishttp://hdl.handle.net/10316/81661http://hdl.handle.net/10316/81661TID:202057321porSangarote, Sérgio Ambrósioinfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2022-01-06T09:05:51Zoai:estudogeral.uc.pt:10316/81661Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T21:03:44.002661Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Estudo da plastificação de poli(ácido láctico) via extrusão reactiva utilizando álcoois ramificados e oligómeros de ácido láctico
Plasticization of poly lactic acid via reactive extrusion using branched alcohols and lactic acid oligomers
title Estudo da plastificação de poli(ácido láctico) via extrusão reactiva utilizando álcoois ramificados e oligómeros de ácido láctico
spellingShingle Estudo da plastificação de poli(ácido láctico) via extrusão reactiva utilizando álcoois ramificados e oligómeros de ácido láctico
Sangarote, Sérgio Ambrósio
PLA
Plastificação
Extrusão reativa
Álcool ramificado
OLA-HEMA
PLA
plasticization
reactive extrusion
branched alcohol
OLA-HEMA
title_short Estudo da plastificação de poli(ácido láctico) via extrusão reactiva utilizando álcoois ramificados e oligómeros de ácido láctico
title_full Estudo da plastificação de poli(ácido láctico) via extrusão reactiva utilizando álcoois ramificados e oligómeros de ácido láctico
title_fullStr Estudo da plastificação de poli(ácido láctico) via extrusão reactiva utilizando álcoois ramificados e oligómeros de ácido láctico
title_full_unstemmed Estudo da plastificação de poli(ácido láctico) via extrusão reactiva utilizando álcoois ramificados e oligómeros de ácido láctico
title_sort Estudo da plastificação de poli(ácido láctico) via extrusão reactiva utilizando álcoois ramificados e oligómeros de ácido láctico
author Sangarote, Sérgio Ambrósio
author_facet Sangarote, Sérgio Ambrósio
author_role author
dc.contributor.author.fl_str_mv Sangarote, Sérgio Ambrósio
dc.subject.por.fl_str_mv PLA
Plastificação
Extrusão reativa
Álcool ramificado
OLA-HEMA
PLA
plasticization
reactive extrusion
branched alcohol
OLA-HEMA
topic PLA
Plastificação
Extrusão reativa
Álcool ramificado
OLA-HEMA
PLA
plasticization
reactive extrusion
branched alcohol
OLA-HEMA
description Dissertação de Mestrado Integrado em Engenharia Química apresentada à Faculdade de Ciências e Tecnologia da Universidade de Coimbra.
publishDate 2016
dc.date.none.fl_str_mv 2016-09-12
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/10316/81661
http://hdl.handle.net/10316/81661
TID:202057321
url http://hdl.handle.net/10316/81661
identifier_str_mv TID:202057321
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799133930566189056

Registros relacionados