Microhardness and flexural strength of two 3D-printed denture base resins

Detalhes bibliográficos
Autor(a) principal: Neves,Cristina Bettencourt
Data de Publicação: 2022
Outros Autores: Chasqueira,Ana Filipa, Rebelo,Patrícia, Fonseca,Mariana, Portugal,Jaime, Bettencourt,Ana
Tipo de documento: Artigo
Idioma: eng
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://scielo.pt/scielo.php?script=sci_arttext&pid=S1646-28902022000400198
Resumo: Abstract Objectives: To evaluate the microhardness and flexural strength of printed and conventionally produced denture base acrylic resins. Methods: A total of 32 parallelepiped specimens (64×10×3.3 mm) were manufactured using two light-cured resins suitable for 3D printing (V-Print Dentbase and Denture 3D+) and two heat-cured resins for conventional production (Probase Hot and Villacryl Rapid) (n=8). After 24-h storage in water, Knoop microhardness (98.12 mN load for 30 s) and three-point flexural strength (1 kN load cell, at a crosshead speed of 5 mm/min and 50 mm between rods) were determined. Microhardness data were analyzed with one-way ANOVA followed by Tukey post-hoc tests. Flexural strength data were submitted to the Kruskal-Wallis test. A significance level of 5% was considered (α=0.05). Results: The resins showed statistically significant (p<0.001) differences regarding microhardness (V-Print Dentbase < Denture 3D+ < Probase Hot < Villacryl Rapid). No statistically significant (p=0.527) differences were found in flexural strength between the four resins. Conclusions: The printed resins had lower microhardness values than conventional resins, but all resins showed similar flexural strength.
id RCAP_4e238077a542fa0d5c20943a61231bad
oai_identifier_str oai:scielo:S1646-28902022000400198
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Microhardness and flexural strength of two 3D-printed denture base resins3D-printingCAD-CAMDenture base resinFlexural strengthHardnessAbstract Objectives: To evaluate the microhardness and flexural strength of printed and conventionally produced denture base acrylic resins. Methods: A total of 32 parallelepiped specimens (64×10×3.3 mm) were manufactured using two light-cured resins suitable for 3D printing (V-Print Dentbase and Denture 3D+) and two heat-cured resins for conventional production (Probase Hot and Villacryl Rapid) (n=8). After 24-h storage in water, Knoop microhardness (98.12 mN load for 30 s) and three-point flexural strength (1 kN load cell, at a crosshead speed of 5 mm/min and 50 mm between rods) were determined. Microhardness data were analyzed with one-way ANOVA followed by Tukey post-hoc tests. Flexural strength data were submitted to the Kruskal-Wallis test. A significance level of 5% was considered (α=0.05). Results: The resins showed statistically significant (p<0.001) differences regarding microhardness (V-Print Dentbase < Denture 3D+ < Probase Hot < Villacryl Rapid). No statistically significant (p=0.527) differences were found in flexural strength between the four resins. Conclusions: The printed resins had lower microhardness values than conventional resins, but all resins showed similar flexural strength.Sociedade Portuguesa de Estomatologia e Medicina Dentária2022-12-01info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/articletext/htmlhttp://scielo.pt/scielo.php?script=sci_arttext&pid=S1646-28902022000400198Revista Portuguesa de Estomatologia, Medicina Dentária e Cirurgia Maxilofacial v.63 n.4 2022reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAPenghttp://scielo.pt/scielo.php?script=sci_arttext&pid=S1646-28902022000400198Neves,Cristina BettencourtChasqueira,Ana FilipaRebelo,PatríciaFonseca,MarianaPortugal,JaimeBettencourt,Anainfo:eu-repo/semantics/openAccess2024-02-06T17:21:12Zoai:scielo:S1646-28902022000400198Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-20T02:28:18.792630Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Microhardness and flexural strength of two 3D-printed denture base resins
title Microhardness and flexural strength of two 3D-printed denture base resins
spellingShingle Microhardness and flexural strength of two 3D-printed denture base resins
Neves,Cristina Bettencourt
3D-printing
CAD-CAM
Denture base resin
Flexural strength
Hardness
title_short Microhardness and flexural strength of two 3D-printed denture base resins
title_full Microhardness and flexural strength of two 3D-printed denture base resins
title_fullStr Microhardness and flexural strength of two 3D-printed denture base resins
title_full_unstemmed Microhardness and flexural strength of two 3D-printed denture base resins
title_sort Microhardness and flexural strength of two 3D-printed denture base resins
author Neves,Cristina Bettencourt
author_facet Neves,Cristina Bettencourt
Chasqueira,Ana Filipa
Rebelo,Patrícia
Fonseca,Mariana
Portugal,Jaime
Bettencourt,Ana
author_role author
author2 Chasqueira,Ana Filipa
Rebelo,Patrícia
Fonseca,Mariana
Portugal,Jaime
Bettencourt,Ana
author2_role author
author
author
author
author
dc.contributor.author.fl_str_mv Neves,Cristina Bettencourt
Chasqueira,Ana Filipa
Rebelo,Patrícia
Fonseca,Mariana
Portugal,Jaime
Bettencourt,Ana
dc.subject.por.fl_str_mv 3D-printing
CAD-CAM
Denture base resin
Flexural strength
Hardness
topic 3D-printing
CAD-CAM
Denture base resin
Flexural strength
Hardness
description Abstract Objectives: To evaluate the microhardness and flexural strength of printed and conventionally produced denture base acrylic resins. Methods: A total of 32 parallelepiped specimens (64×10×3.3 mm) were manufactured using two light-cured resins suitable for 3D printing (V-Print Dentbase and Denture 3D+) and two heat-cured resins for conventional production (Probase Hot and Villacryl Rapid) (n=8). After 24-h storage in water, Knoop microhardness (98.12 mN load for 30 s) and three-point flexural strength (1 kN load cell, at a crosshead speed of 5 mm/min and 50 mm between rods) were determined. Microhardness data were analyzed with one-way ANOVA followed by Tukey post-hoc tests. Flexural strength data were submitted to the Kruskal-Wallis test. A significance level of 5% was considered (α=0.05). Results: The resins showed statistically significant (p<0.001) differences regarding microhardness (V-Print Dentbase < Denture 3D+ < Probase Hot < Villacryl Rapid). No statistically significant (p=0.527) differences were found in flexural strength between the four resins. Conclusions: The printed resins had lower microhardness values than conventional resins, but all resins showed similar flexural strength.
publishDate 2022
dc.date.none.fl_str_mv 2022-12-01
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/article
format article
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://scielo.pt/scielo.php?script=sci_arttext&pid=S1646-28902022000400198
url http://scielo.pt/scielo.php?script=sci_arttext&pid=S1646-28902022000400198
dc.language.iso.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv http://scielo.pt/scielo.php?script=sci_arttext&pid=S1646-28902022000400198
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv text/html
dc.publisher.none.fl_str_mv Sociedade Portuguesa de Estomatologia e Medicina Dentária
publisher.none.fl_str_mv Sociedade Portuguesa de Estomatologia e Medicina Dentária
dc.source.none.fl_str_mv Revista Portuguesa de Estomatologia, Medicina Dentária e Cirurgia Maxilofacial v.63 n.4 2022
reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799137353067921408