Structural characterization of lead metaniobate thin films deposited by pulsed laser ablation

• Autor(a) principal: Cardoso, Fátima
• Data de Publicação: 2006
• Outros Autores: Almeida, B. G., Caldelas, Pedro, Mendes, Jorge A.
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
• Texto Completo: https://hdl.handle.net/1822/85653
• topic: lead metaniobate; thin films; laser ablation; structural properties; Ciências Naturais::Ciências Físicas

The ferroelectric polymorph of lead metaniobate (PbNb2O6) presents an orthorhombic structure that is metastable at room temperature. This phase is obtained by quenching from high temperature. The fabrication of lead niobate thin films with this orthorhombic form has been reported to be difficult due to the presence of phases with the rhombohedric form or other non-stoichimetric phases. In this work, lead niobate thin films have been prepared by laser ablation, at different oxygen pressures and with different substrate temperatures. Their structure was studied by X-ray diffraction and their surface was examined by scanning electron microscopy (SEM). The results show that for low deposition temperatures the films presented a rhombohedric-PbNb2O6 structural phase. As Tdep increases the films started to develop an orthorhombic- PbNb2O6 structure that appeared at 400ºC and remains up to 600ºC. For lower oxygen pressure during deposition, a mixture of this phase and other orthorhombic lead deficient phases are present in the films. On the other hand, by increasing the oxygen pressure the lead deficient phases are strongly reduced and the films present only the orthorhombic- PbNb2O6 structure.