Projeto, manufatura e validação mecânica de uma solução multimaterial (liga Ti6AI4V e CoCr) para implantes de anca

Detalhes bibliográficos
Autor(a) principal: Andrade, Carlos Jorge Cunha
Data de Publicação: 2023
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: https://hdl.handle.net/1822/85448
Resumo: Dissertação de mestrado integrado em Engenharia Mecânica
id RCAP_7231662b85207d73ca6c1f0c7a009ffc
oai_identifier_str oai:repositorium.sdum.uminho.pt:1822/85448
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Projeto, manufatura e validação mecânica de uma solução multimaterial (liga Ti6AI4V e CoCr) para implantes de ancaImplanteMultimaterialLigas de titânio e cobaltoTestes de corteLaser powder bed fusionImplantTitanium and cobalt alloysShear testsEngenharia e Tecnologia::Engenharia MecânicaDissertação de mestrado integrado em Engenharia MecânicaA necessidade de soluções para a mobilidade humana é uma constante no desenvolvimento científico. Os implantes de anca e os seus componentes continuam em constante evolução, pelo que a descoberta de soluções mais resistentes e mais duradouras, capazes de providenciar mais conforto para o paciente, são urgentes. A maioria das soluções existentes tem como base a utilização de componente monomaterial, seja ele metálico, cerâmico ou polimérico que dificilmente responde a todas as necessidades da aplicação e do paciente. Esta dissertação surge com o objetivo de solucionar os problemas existentes no componente acetabular do implante de anca, através de uma solução disruptiva capaz de combinar diferentes materiais, e suas diferentes propriedades intrínsecas, em distintas zonas de um mesmo componente. Esta solução é apenas possível recorrendo a uma tecnologia de manufatura inovadora: Multimaterial Laser Powder Bed Fusion. Neste estudo investigou-se a combinação de duas ligas metálicas: liga Ti6Al4V que apresenta uma excelente resistência mecânica bem como uma excelente biocompatibilidade, sendo por isso indicada para a integração óssea; liga CoCr que possui uma excelente resistência ao desgaste bem como propriedades antibacterianas, indicadas para o contacto constante e necessário da articulação da anca. Foram produzidas amostras monomaterial de CoCr e de Ti6Al4V (amostras controlo) e amostras multimaterial Ti6Al4V-CoCr. No fabrico das amostras multimaterial recorreram-se a estratégias de otimização da interface bem como a geometrias de interlocking mecânico entre ambos os materiais, ambicionando sucesso na produção de amostras com resistência mecânica. As amostras foram analisadas recorrendo à Microscopia Eletrónica de Varrimento para análise morfológica, observação de defeitos, sendo que as propriedades mecânicas foram determinadas através de ensaios de corte, com foco na análise da resistência da transição entre os materiais distintos. Os resultados obtidos indicam que esta combinação de materiais apresenta capacidade para ser adotada numa solução prostética, pelo que entre os grupos de amostras produzidos, a melhor alternativa garante uma resistência de 337,27 MPa comparativamente ao osso com 40,95 MPa. Estes resultados validam a/o capacidade/potencial da tecnologia Multimaterial Laser Powder Bed Fusion gerar soluções de engenharia baseadas num conceito multimaterial, o material adequado no local necessário.Achieving the solutions for better human mobility is a constant research endeavour. The hip joints are in the epicentre of human locomotion, which equates to an urgent need to obtain more appropriate, resistant, long lasting, and comfortable solutions for hip implants and their components. Most of the existing solutions use monomaterial components manufactured from either a metal or a ceramic or a polymer. These existing solutions hardly fulfil all the necessary requirements for the application and the patient. This thesis emerges with the objective to solve the existing problems in the acetabular component of the hip implant through a disruptive solution capable of combining different materials for various zones of the implant. This solution is only possible though the use of an innovative manufacturing technology: Multimaterial Laser Powder Bed Fusion. In this study, we focus on the use of a Titanium alloy (Ti6Al4V) and a Cobalt alloy (CoCr). The Ti6Al4V alloy imparts great mechanical properties and biocompatibility, which is a requirement for proper bone integration. On the other hand, the CoCr alloy possesses better wear resistance and antibacterial properties, advantageous for the inherent contact and friction required in the hip joint. Various monomaterial samples of CoCr and Ti6Al4V were produced (control specimens), along with multimaterial samples Ti6Al4V-CoCr. Different optimization strategies, as well as geometric interlocking structures between both materials at the interface, allowed the successful production of mechanically adequate testing samples. Scanning Electron Microscopy analysed the visual morphological quality and presence of defects and cracks, whereas the mechanical properties were determined by the shear tests. The shear tests were focused on the resistance of the transition between both materials. The results obtained indicate that this material combination of Ti6Al4V and CoCr is valid and adequate for a prosthetic solution. The best results obtained present a maximum shear stress value of 337,27 MPa, which is vastly superior to the maximum shear stress value of the human bone, 40,95 MPa. These results therefore validate the proposition presented in the beginning of this thesis, a multimaterial prosthesis is possible and adequate.Bartolomeu, FlávioSilva, Filipe SamuelUniversidade do MinhoAndrade, Carlos Jorge Cunha2023-06-132023-06-13T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfhttps://hdl.handle.net/1822/85448por203326261info:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-07-21T12:42:11Zoai:repositorium.sdum.uminho.pt:1822/85448Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T19:39:22.911474Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Projeto, manufatura e validação mecânica de uma solução multimaterial (liga Ti6AI4V e CoCr) para implantes de anca
title Projeto, manufatura e validação mecânica de uma solução multimaterial (liga Ti6AI4V e CoCr) para implantes de anca
spellingShingle Projeto, manufatura e validação mecânica de uma solução multimaterial (liga Ti6AI4V e CoCr) para implantes de anca
Andrade, Carlos Jorge Cunha
Implante
Multimaterial
Ligas de titânio e cobalto
Testes de corte
Laser powder bed fusion
Implant
Titanium and cobalt alloys
Shear tests
Engenharia e Tecnologia::Engenharia Mecânica
title_short Projeto, manufatura e validação mecânica de uma solução multimaterial (liga Ti6AI4V e CoCr) para implantes de anca
title_full Projeto, manufatura e validação mecânica de uma solução multimaterial (liga Ti6AI4V e CoCr) para implantes de anca
title_fullStr Projeto, manufatura e validação mecânica de uma solução multimaterial (liga Ti6AI4V e CoCr) para implantes de anca
title_full_unstemmed Projeto, manufatura e validação mecânica de uma solução multimaterial (liga Ti6AI4V e CoCr) para implantes de anca
title_sort Projeto, manufatura e validação mecânica de uma solução multimaterial (liga Ti6AI4V e CoCr) para implantes de anca
author Andrade, Carlos Jorge Cunha
author_facet Andrade, Carlos Jorge Cunha
author_role author
dc.contributor.none.fl_str_mv Bartolomeu, Flávio
Silva, Filipe Samuel
Universidade do Minho
dc.contributor.author.fl_str_mv Andrade, Carlos Jorge Cunha
dc.subject.por.fl_str_mv Implante
Multimaterial
Ligas de titânio e cobalto
Testes de corte
Laser powder bed fusion
Implant
Titanium and cobalt alloys
Shear tests
Engenharia e Tecnologia::Engenharia Mecânica
topic Implante
Multimaterial
Ligas de titânio e cobalto
Testes de corte
Laser powder bed fusion
Implant
Titanium and cobalt alloys
Shear tests
Engenharia e Tecnologia::Engenharia Mecânica
description Dissertação de mestrado integrado em Engenharia Mecânica
publishDate 2023
dc.date.none.fl_str_mv 2023-06-13
2023-06-13T00:00:00Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/1822/85448
url https://hdl.handle.net/1822/85448
dc.language.iso.fl_str_mv por
language por
dc.relation.none.fl_str_mv 203326261
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799132934466174976

Registros relacionados