Efeito do tempo de imersão em ambiente salino na resposta à fadiga de laminados vidro/epóxido

Detalhes bibliográficos
Autor(a) principal: Aguiar, David Manuel de Campos
Data de Publicação: 2021
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/10316/98187
Resumo: Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
id RCAP_7813c955707f187d4b2591fc061713e3
oai_identifier_str oai:estudogeral.uc.pt:10316/98187
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Efeito do tempo de imersão em ambiente salino na resposta à fadiga de laminados vidro/epóxidoEffect of immersion time in a saline environment in response to the fatigue of glass/epoxide laminatesFadiga de compósitos laminadosvidro/epóxidoFadiga em água do marAbsorção de águaMecanismos de falhaLaminated composite fatigueGlass/epoxyFatigue in seawaterWater absorptionMechanical failureDissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e TecnologiaNos dias que correm, o aumento da utilização dos materiais compósitos reforçados é cada vez mais notório em diversos ramos da engenharia, como o da aeronáutica, aeroespacial, indústria automóvel, indústria naval, construção civil e muitos outros. Este aumento tem cada vez maior tendência a aumentar, devido à necessidade que a engenharia sente na utilização de componentes mais leves em determinadas situações, mas garantindo propriedades mecânicas semelhantes às dos aços e das ligas de alumínio. No entanto, este tipo de material é suscetível a determinados ambientes e a determinados tipos de carga, acabando por provocar degradação da sua estrutura.O principal objetivo deste estudo é avaliar o efeito que o tempo de imersão em água do mar provoca na resposta à fadiga de laminados vidro/epóxido. Para a realização dos ensaios experimentais foram utilizados provetes retangulares com um furo central. Foram comparados os valores obtidos para provetes com e sem pré-tensão sujeitos a diferentes tempos de imersão.Foram efetuadas medições das massas ao longo de 900 dias, para avaliar a percentagem de água absorvida pelo material. Foram realizados ensaios de tração para avaliar o efeito do tempo de imersão nas propriedades mecânicas. Foram também realizados ensaios para avaliar o efeito do tempo de imersão na variação da resistência à fadiga para carregamentos uniaxiais de tração com R=0,1. Os ensaios à fadiga foram acompanhados pelo software VIC-3D, que tem por base o método de Correlação Digital de Imagem (DIC), com o objetivo de acompanhar e analisar as deformações que ocorreram na região do furo central.Após 900 dias de imersão em água do mar, verificou-se uma redução na resistência à tração. Através dos ensaios de fadiga foi notório que para um tempo de imersão de 900 dias, ocorreu uma redução de vida significativa do material, quando comparados com os resultados obtidos para os 229 dias e 0 dias de imersão. Para provetes com pré-tensão, os resultados obtidos nos ensaios de fadiga para provetes com 229 dias quando comparados com os obtidos para provetes com 900 dias, não foram conclusivos. Apenas os provetes com uma pré-tensão de 50% apresentaram uma redução média de vida. Pelo contrário, tanto para uma pré-tensão de 25% como para 75%, verificou-se um aumento médio de vida. Através das imagens fornecidas pelo método DIC, foi possível acompanhar o campo de deformações na zona do furo e prever com alguma precisão, o local de iniciação de rotura das amostras.In the current world, an increase in the use of reinforced composite materials is noticeable in various branches of engineering, such as aeronautical, aerospace, automobile, naval, civil, and many others. This increase will only tend to grow due to the necessity in using lighter components in certain situations, while guaranteeing similar mechanical properties to those of steel and aluminum alloys. However, this type of material is susceptible to certain environments and loads, which may provoke its rupture. The main objective of this study is to evaluate the effect that immersion time in seawater has in response to fatigue of glass/epoxy laminates. To perform the necessary experiments, perforated rectangular samples were used, with the hole in the center. The results were then compared between samples with and without prestress subject to different immersion times. Mass was measured several times over a period of 900 days to evaluate the percentage of water absorbed by the material. Tensile tests were conducted to evaluate the effect of immersion time on the mechanical properties. Tests were also conducted to evaluate the effect of immersion time on the variation of fatigue strength for uniaxial loading with R=0,1. The fatigue tests were accompanied by the VIC-3D software, which uses the Digital Image Correlation (DIC) method, to analyze the strain that occurs in the hollowed central region. After 900 days immersed in seawater, a reduction in tensile strength was verified. A significant reduction of the material’s life was verified for samples immersed 900 days, when compared to the results obtained for samples immersed 229 days and 0 days. For prestressed samples, the results obtained for samples immersed 229 and 900 days were non-conclusive. Only the samples with 50% prestress presented a reduction of life. For samples with 25% and 75% prestress, an increase was verified. Through the images supplied by the DIC method, it was possible to accompany the strain field in the perforated area, and predict, with certain accuracy, the location where rupture of the samples would commence.2021-11-25info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesishttp://hdl.handle.net/10316/98187http://hdl.handle.net/10316/98187TID:202921557porAguiar, David Manuel de Camposinfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2022-05-25T10:10:20Zoai:estudogeral.uc.pt:10316/98187Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T21:16:04.945825Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Efeito do tempo de imersão em ambiente salino na resposta à fadiga de laminados vidro/epóxido
Effect of immersion time in a saline environment in response to the fatigue of glass/epoxide laminates
title Efeito do tempo de imersão em ambiente salino na resposta à fadiga de laminados vidro/epóxido
spellingShingle Efeito do tempo de imersão em ambiente salino na resposta à fadiga de laminados vidro/epóxido
Aguiar, David Manuel de Campos
Fadiga de compósitos laminados
vidro/epóxido
Fadiga em água do mar
Absorção de água
Mecanismos de falha
Laminated composite fatigue
Glass/epoxy
Fatigue in seawater
Water absorption
Mechanical failure
title_short Efeito do tempo de imersão em ambiente salino na resposta à fadiga de laminados vidro/epóxido
title_full Efeito do tempo de imersão em ambiente salino na resposta à fadiga de laminados vidro/epóxido
title_fullStr Efeito do tempo de imersão em ambiente salino na resposta à fadiga de laminados vidro/epóxido
title_full_unstemmed Efeito do tempo de imersão em ambiente salino na resposta à fadiga de laminados vidro/epóxido
title_sort Efeito do tempo de imersão em ambiente salino na resposta à fadiga de laminados vidro/epóxido
author Aguiar, David Manuel de Campos
author_facet Aguiar, David Manuel de Campos
author_role author
dc.contributor.author.fl_str_mv Aguiar, David Manuel de Campos
dc.subject.por.fl_str_mv Fadiga de compósitos laminados
vidro/epóxido
Fadiga em água do mar
Absorção de água
Mecanismos de falha
Laminated composite fatigue
Glass/epoxy
Fatigue in seawater
Water absorption
Mechanical failure
topic Fadiga de compósitos laminados
vidro/epóxido
Fadiga em água do mar
Absorção de água
Mecanismos de falha
Laminated composite fatigue
Glass/epoxy
Fatigue in seawater
Water absorption
Mechanical failure
description Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
publishDate 2021
dc.date.none.fl_str_mv 2021-11-25
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/10316/98187
http://hdl.handle.net/10316/98187
TID:202921557
url http://hdl.handle.net/10316/98187
identifier_str_mv TID:202921557
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799134056776990720

Registros relacionados