Funcionalização de celulose e sílica através de modificação química de superfície

Detalhes bibliográficos
Autor(a) principal: Batista, Dina Patricia Jesus
Data de Publicação: 2015
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/10316/40239
Resumo: Dissertação de Mestrado Integrado em Engenharia Química apresentada à Faculdade de Ciências e Tecnologia da Universidade de Coimbra
id RCAP_87bb046c6799154849db891a8a24cfb8
oai_identifier_str oai:estudogeral.uc.pt:10316/40239
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Funcionalização de celulose e sílica através de modificação química de superfícieFuncionalizaçãoCeluloseSilicaExcertoSuperfícieFunctionalizationCelluloseSilicaGraftingSurfaceDissertação de Mestrado Integrado em Engenharia Química apresentada à Faculdade de Ciências e Tecnologia da Universidade de CoimbraEste estudo tem como objetivo a modificação de superfície de celulose e sílica hidrofílicas no sentido da introdução de novas funcionalidades pelo método de grafting. O processo compreende três etapas distintas: ativação, formação de iniciadores na superfície e polimerização da superfície do material. A etapa inicial de ativação é realizada pela reação entre o material a modificar e TDI, sendo que um dos grupos NCO do TDI se liga à estrutura da celulose ou da sílica e o outro permanece livre. A análise dos espetros de FTIR para ambos os materiais mostra a banda do NCO livre aos cerca de 2260 - 2270 cm-1, o que indica que a ativação da superfície foi alcançada com sucesso. No entanto, para a celulose foi preciso recorrer a um maior número de técnicas de caracterização de superfície para comprovar o sucesso da etapa. A medição do valor de ângulo de contato mostra que a superfície se torna mais hidrofóbica após a primeira etapa e a análise por TGA também indica diferenças na celulose que reage com TDI. A segunda fase do estudo consiste em induzir processos de polimerização na superfície do material ativado fazendo-o funcionar como um macroiniciador. Esta etapa é realizada pela reação do material ativado com hidroperóxido de tetra butilo (TBHP). Para a sílica, a banda correspondente à ligação carbamato que se forma é visível no espetro de FTIR aos 1732 cm-1. O mesmo não acontece no caso da celulose, em que a banda correspondente ao NCO livre diminui mas não se visualiza a banda da ligação carbamato. A segunda etapa do processo foi ainda executada fazendo reagir a amina 1,6-diaminohexano (HMDA) com o material ativado o que origina uma ligação ureia. Esta ligação é visível no espetro de FTIR para a sílica por volta dos 1680 cm-1, no entanto para a celulose a banda também não é percetível. Após a segunda etapa utilizando a sílica como macroiniciador fez-se a polimerização usando dois monómeros diferentes: acrilato de metilo e NIPAM. A polimerização da superfície da celulose foi realizada usando apenas o monómero acrilato de metilo. Por FTIR obtêm-se evidências de que ocorreu polimerização na superfície de ambos os materiais. Os objetivos deste estudo foram conseguidos, contribuindo para o desenvolvimento de técnicas de modificação química de superfície e para se puder substituir materiais de origem fóssil por materiais menos prejudiciais ao ambiente.This study aims surface modification to cellulose and silica hydrophilic for introduction of new functionalities by grafting method. The process consists of three distinct steps: activation, forming initiators and polymerization on the material surface. The initial activation step is carried out by reaction between the modifying material and TDI; and one of NCO groups of the TDI binds into the structure of the cellulose or silica and the other remains free. The analysis of the FTIR spectra for both materials shows the free NCO band at about 2260 - 2270 cm-1, indicating that activation of the surface was successfully achieved. However, for the cellulose it has been necessary to resort to a larger number of surface characterization techniques to demonstrate the success of the step. The measurement of contact angle value shows that the surface becomes hydrophobic after the first step and TGA analysis also shows differences in the cellulose that reacts with TDI. The second phase of the study is to induce polymerization processes on the surface of the activated material making it operate as a macroinitiator. This step is conducted by reaction of the material activated with tetra butyl hydroperoxide (TBHP). For silica, the band corresponding to the carbamate linkage is formed which is visible in the FTIR spectrum at 1732 cm-1. This does not apply in the case of the cellulose, in which the band corresponding to the free NCO decreases but it does not change the band on the connecting carbamate. The second step of the process was still carried out by reacting the amine 1,6 – diaminohexane (HMDA) with activated material which causes a urea bond. This link is visible in the FTIR spectrum for the silica at around 1680 cm-1 for cellulose however the band on the is not noticeable. After the second step using silica as macroinitiator the polymerizing was made using two different monomers: methyl acrylate and NIPAM. The polymerization of the cellulose surface was performed using only the monomer methyl acrylate. For FTIR obtains evidence that polymerization occurred on the surface of both materials. The objectives of this study were achieved, contributing to the development of chemical modification of surface techniques and if you can replace fossil materials for more environmentally friendly materials.2015-09-21info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesishttp://hdl.handle.net/10316/40239http://hdl.handle.net/10316/40239TID:201674939porBatista, Dina Patricia Jesusinfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2022-02-21T15:42:09Zoai:estudogeral.uc.pt:10316/40239Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T20:59:29.540562Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Funcionalização de celulose e sílica através de modificação química de superfície
title Funcionalização de celulose e sílica através de modificação química de superfície
spellingShingle Funcionalização de celulose e sílica através de modificação química de superfície
Batista, Dina Patricia Jesus
Funcionalização
Celulose
Silica
Excerto
Superfície
Functionalization
Cellulose
Silica
Grafting
Surface
title_short Funcionalização de celulose e sílica através de modificação química de superfície
title_full Funcionalização de celulose e sílica através de modificação química de superfície
title_fullStr Funcionalização de celulose e sílica através de modificação química de superfície
title_full_unstemmed Funcionalização de celulose e sílica através de modificação química de superfície
title_sort Funcionalização de celulose e sílica através de modificação química de superfície
author Batista, Dina Patricia Jesus
author_facet Batista, Dina Patricia Jesus
author_role author
dc.contributor.author.fl_str_mv Batista, Dina Patricia Jesus
dc.subject.por.fl_str_mv Funcionalização
Celulose
Silica
Excerto
Superfície
Functionalization
Cellulose
Silica
Grafting
Surface
topic Funcionalização
Celulose
Silica
Excerto
Superfície
Functionalization
Cellulose
Silica
Grafting
Surface
description Dissertação de Mestrado Integrado em Engenharia Química apresentada à Faculdade de Ciências e Tecnologia da Universidade de Coimbra
publishDate 2015
dc.date.none.fl_str_mv 2015-09-21
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/10316/40239
http://hdl.handle.net/10316/40239
TID:201674939
url http://hdl.handle.net/10316/40239
identifier_str_mv TID:201674939
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799133886181015552

Registros relacionados