Heat-treatment (Annealing) Effect on the Mechanical and Electrochemical Performance of a Synthesized AlCrFeMnNiV Equi-atomic High Entropy Alloy (HEA) via Arc-melting and Casting Technologies

Detalhes bibliográficos
Autor(a) principal: Kanyane,L. R.
Data de Publicação: 2022
Outros Autores: Malatji,N., Popoola,A. P. I.
Tipo de documento: Artigo
Idioma: eng
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042022000500337
Resumo: Abstract In this work, an equi-atomic AlCrFeMnNiV HEA was synthesized by means of arc-melting and casting processes. The casted alloy ingots were heat-treated (annealed) at temperatures of 400, 600 and 800 ºC, for 2 h. The effect of the heat-treatment temperature on the HEA microstructural evolution, compressive strength and corrosion behavior was investigated. Heat-treatment temperatures of 400 and 600 ºC resulted in increased micro-hardness properties that, at 800 ºC, were drastically reduced, although a good combination between strength and ductility was observed. HEA showed an extreme decrease in the current density (J (A/cm2)), after the heat-treatment, with a lower potential (V). The heat-treated HEA demonstrated a good corrosion rate in acidic conditions, as compared to that of nickel (Ni) based, titanium (Ti) alloys and stainless steel (SS) super alloys.
id RCAP_8e70e17ea4ecfc0f49d4f37d9f2f9683
oai_identifier_str oai:scielo:S0872-19042022000500337
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Heat-treatment (Annealing) Effect on the Mechanical and Electrochemical Performance of a Synthesized AlCrFeMnNiV Equi-atomic High Entropy Alloy (HEA) via Arc-melting and Casting TechnologiesHEAAlCrFeMnNiVarc-meltingcastingheat-treatment (annealing)compression and corrosionAbstract In this work, an equi-atomic AlCrFeMnNiV HEA was synthesized by means of arc-melting and casting processes. The casted alloy ingots were heat-treated (annealed) at temperatures of 400, 600 and 800 ºC, for 2 h. The effect of the heat-treatment temperature on the HEA microstructural evolution, compressive strength and corrosion behavior was investigated. Heat-treatment temperatures of 400 and 600 ºC resulted in increased micro-hardness properties that, at 800 ºC, were drastically reduced, although a good combination between strength and ductility was observed. HEA showed an extreme decrease in the current density (J (A/cm2)), after the heat-treatment, with a lower potential (V). The heat-treated HEA demonstrated a good corrosion rate in acidic conditions, as compared to that of nickel (Ni) based, titanium (Ti) alloys and stainless steel (SS) super alloys.Sociedade Portuguesa de Electroquímica2022-10-01info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/articletext/htmlhttp://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042022000500337Portugaliae Electrochimica Acta v.40 n.5 2022reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAPenghttp://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042022000500337Kanyane,L. R.Malatji,N.Popoola,A. P. I.info:eu-repo/semantics/openAccess2024-02-06T17:07:38Zoai:scielo:S0872-19042022000500337Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-20T02:20:29.503396Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Heat-treatment (Annealing) Effect on the Mechanical and Electrochemical Performance of a Synthesized AlCrFeMnNiV Equi-atomic High Entropy Alloy (HEA) via Arc-melting and Casting Technologies
title Heat-treatment (Annealing) Effect on the Mechanical and Electrochemical Performance of a Synthesized AlCrFeMnNiV Equi-atomic High Entropy Alloy (HEA) via Arc-melting and Casting Technologies
spellingShingle Heat-treatment (Annealing) Effect on the Mechanical and Electrochemical Performance of a Synthesized AlCrFeMnNiV Equi-atomic High Entropy Alloy (HEA) via Arc-melting and Casting Technologies
Kanyane,L. R.
HEA
AlCrFeMnNiV
arc-melting
casting
heat-treatment (annealing)
compression and corrosion
title_short Heat-treatment (Annealing) Effect on the Mechanical and Electrochemical Performance of a Synthesized AlCrFeMnNiV Equi-atomic High Entropy Alloy (HEA) via Arc-melting and Casting Technologies
title_full Heat-treatment (Annealing) Effect on the Mechanical and Electrochemical Performance of a Synthesized AlCrFeMnNiV Equi-atomic High Entropy Alloy (HEA) via Arc-melting and Casting Technologies
title_fullStr Heat-treatment (Annealing) Effect on the Mechanical and Electrochemical Performance of a Synthesized AlCrFeMnNiV Equi-atomic High Entropy Alloy (HEA) via Arc-melting and Casting Technologies
title_full_unstemmed Heat-treatment (Annealing) Effect on the Mechanical and Electrochemical Performance of a Synthesized AlCrFeMnNiV Equi-atomic High Entropy Alloy (HEA) via Arc-melting and Casting Technologies
title_sort Heat-treatment (Annealing) Effect on the Mechanical and Electrochemical Performance of a Synthesized AlCrFeMnNiV Equi-atomic High Entropy Alloy (HEA) via Arc-melting and Casting Technologies
author Kanyane,L. R.
author_facet Kanyane,L. R.
Malatji,N.
Popoola,A. P. I.
author_role author
author2 Malatji,N.
Popoola,A. P. I.
author2_role author
author
dc.contributor.author.fl_str_mv Kanyane,L. R.
Malatji,N.
Popoola,A. P. I.
dc.subject.por.fl_str_mv HEA
AlCrFeMnNiV
arc-melting
casting
heat-treatment (annealing)
compression and corrosion
topic HEA
AlCrFeMnNiV
arc-melting
casting
heat-treatment (annealing)
compression and corrosion
description Abstract In this work, an equi-atomic AlCrFeMnNiV HEA was synthesized by means of arc-melting and casting processes. The casted alloy ingots were heat-treated (annealed) at temperatures of 400, 600 and 800 ºC, for 2 h. The effect of the heat-treatment temperature on the HEA microstructural evolution, compressive strength and corrosion behavior was investigated. Heat-treatment temperatures of 400 and 600 ºC resulted in increased micro-hardness properties that, at 800 ºC, were drastically reduced, although a good combination between strength and ductility was observed. HEA showed an extreme decrease in the current density (J (A/cm2)), after the heat-treatment, with a lower potential (V). The heat-treated HEA demonstrated a good corrosion rate in acidic conditions, as compared to that of nickel (Ni) based, titanium (Ti) alloys and stainless steel (SS) super alloys.
publishDate 2022
dc.date.none.fl_str_mv 2022-10-01
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/article
format article
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042022000500337
url http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042022000500337
dc.language.iso.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042022000500337
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv text/html
dc.publisher.none.fl_str_mv Sociedade Portuguesa de Electroquímica
publisher.none.fl_str_mv Sociedade Portuguesa de Electroquímica
dc.source.none.fl_str_mv Portugaliae Electrochimica Acta v.40 n.5 2022
reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799137292487491584

Registros relacionados