Durabilidade de compósitos de matriz termoplástica - termoendurecível reforçada com fibras sintéticas e naturais

Detalhes bibliográficos
Autor(a) principal: Leite, Fernando Luís Pinheiro Pires
Data de Publicação: 2017
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: https://hdl.handle.net/1822/48258
Resumo: Dissertação de mestrado integrado em Engenharia de Polímeros
id RCAP_8f6e39f0485a614a5e374109a7707997
oai_identifier_str oai:repositorium.sdum.uminho.pt:1822/48258
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Durabilidade de compósitos de matriz termoplástica - termoendurecível reforçada com fibras sintéticas e naturaisDurabilidadeFibras naturaisFibras sintéticasFTIRTinuvin PDurabilityNatural fibersSsynthetic fibersEngenharia e Tecnologia::Outras Engenharias e TecnologiasDissertação de mestrado integrado em Engenharia de PolímerosO objetivo da presente dissertação é investigar a durabilidade de compósitos de matriz polimérica termoplástica e termoendurecível reforçados com fibras naturais e sintéticas em ambientes corrosivos. Para a produção de compósitos foram escolhidos o PP como matriz termoplástica e uma resina epóxido como matriz termoendurecível que se reforçaram com fibras natural de juta e sintética de vidro. Para melhorar a adesão entre fibra e matriz e a durabilidade dos compósitos, submeteu-se a fibra natural a tratamentos superficiais, nomeadamente, a um tratamento alcalino e a um revestimento com verniz protetor de madeira. A resina epóxida foi ainda aditivada com um absorvedor UV (Tinuvin P). Os compósitos foram produzidos por moldação por compressão e posteriormente sujeitos a ensaios de corrosão e durabilidade em ambientes alcalinos, ricos em cloretos, condições gelo/degelo e ensaios acelerados de envelhecimento por ultravioletas (QUV). Após exposição durante 30 dias nesses ambientes os compósitos foram sujeitos a ensaios de espectrofotometria com emissão ótica, microscopia ótica, espectroscopia de infravermelho de transformação de Fourier (FTIR), análise térmica simultânea (STA) e de tração para se avaliarem, respetivamente, as mudanças causadas na sua cor, na estrutura organizativa, e/ou na estrutura química por efeitos dos diferentes tratamentos superficiais a que as fibras foram sujeitas e/ou da aditivação das matrizes e/ou ainda alterações causadas nas suas características de degradação (perda de massa) com a temperatura e mecânicas. Observou-se que, após sujeição aos ensaios de durabilidade, os compósitos de resina epóxido reforçada com fibras de vidros apresentaram geralmente melhores propriedades mecânicas que os de PP reforçado com fibras de juta. Enquanto a aditivação do epóxido com Tinuvin P melhorou os resultados de durabilidade e degradação nos compósitos reforçados com fibra de vidro, o mesmo não aconteceu no caso dos compósitos reforçados com fibras de juta que viram diminuída a durabilidade e aumentada a sua degradação com a temperatura. Este absorvedor de ultravioletas (Tinuvin P) também mostrou diminuir a perda de massa em alguns compósitos sujeitos a ensaios de envelhecimento acelerado (QUV) e não influenciar a temperatura máxima de degradação da resina epóxido. Os tratamentos superficiais usados nas fibras de juta aumentaram a durabilidade e diminuíram a descoloração nos compósitos com matriz de PP mas, pelo contrário, afetaram negativamente essas propriedades nos compósitos de matriz termoendurecível.The objective of this dissertation is to investigate the durability of thermoplastic and thermosetting polymer matrix composites reinforced with natural and synthetic fibers in corrosive environments. For the production of composites PP was chosen as a thermoplastic matrix and an epoxy resin as a thermosetting matrix that were reinforced with natural jute and synthetic glass fibers. To improve adhesion between fiber and matrix and the durability of the composites, natural fibers were subjected to surface treatments, namely, an alkaline treatment and a coating with protective wood varnish. The epoxy resin was further supplemented with a UV absorber (Tinuvin P). The composites were produced by compression molding and subsequently subjected to corrosion and durability tests in alkaline environments, rich in chlorides, freeze / thaw conditions and accelerated ultraviolet aging (QUV) tests. After exposure for 30 days in these environments the composites were subjected to spectrophotometry tests with optical emission, optical microscopy, Fourier transform infrared spectroscopy (FTIR), simultaneous thermal analysis (STA) and tensile tests to evaluate, respectively, the changes caused by their color, organizational structure and / or chemical structure by the effects of the different surface treatments to which the fibers were subjected and / or the additives of the matrices and / or changes caused in their degradation characteristics (loss of mass) with temperature and mechanical. It was found that, following subjection to the durability tests, glass fiber reinforced epoxy resin composites generally had better mechanical properties than those of jute fiber reinforced PP. While the epoxide with Tinuvin P improved the durability and degradation results in glass fiber reinforced composites, this was not the case for composites reinforced with jute fibers which decreased durability and increased degradation with temperature. This ultraviolet absorber (Tinuvin P) also showed to decrease the mass loss in some composites subject to accelerated aging tests (QUV) and did not influence the maximum degradation temperature of the epoxy resin. The surface treatments used in jute fibers increased durability and decreased discoloration in the PP matrix composites but, on the contrary, negatively affected these properties in the thermosetting matrix composites.Nunes, J. P.Fangueiro, RaúlUniversidade do MinhoLeite, Fernando Luís Pinheiro Pires20172017-01-01T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfhttps://hdl.handle.net/1822/48258por201777916info:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-09-30T01:31:28Zoai:repositorium.sdum.uminho.pt:1822/48258Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T19:49:34.651338Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Durabilidade de compósitos de matriz termoplástica - termoendurecível reforçada com fibras sintéticas e naturais
title Durabilidade de compósitos de matriz termoplástica - termoendurecível reforçada com fibras sintéticas e naturais
spellingShingle Durabilidade de compósitos de matriz termoplástica - termoendurecível reforçada com fibras sintéticas e naturais
Leite, Fernando Luís Pinheiro Pires
Durabilidade
Fibras naturais
Fibras sintéticas
FTIR
Tinuvin P
Durability
Natural fibers
Ssynthetic fibers
Engenharia e Tecnologia::Outras Engenharias e Tecnologias
title_short Durabilidade de compósitos de matriz termoplástica - termoendurecível reforçada com fibras sintéticas e naturais
title_full Durabilidade de compósitos de matriz termoplástica - termoendurecível reforçada com fibras sintéticas e naturais
title_fullStr Durabilidade de compósitos de matriz termoplástica - termoendurecível reforçada com fibras sintéticas e naturais
title_full_unstemmed Durabilidade de compósitos de matriz termoplástica - termoendurecível reforçada com fibras sintéticas e naturais
title_sort Durabilidade de compósitos de matriz termoplástica - termoendurecível reforçada com fibras sintéticas e naturais
author Leite, Fernando Luís Pinheiro Pires
author_facet Leite, Fernando Luís Pinheiro Pires
author_role author
dc.contributor.none.fl_str_mv Nunes, J. P.
Fangueiro, Raúl
Universidade do Minho
dc.contributor.author.fl_str_mv Leite, Fernando Luís Pinheiro Pires
dc.subject.por.fl_str_mv Durabilidade
Fibras naturais
Fibras sintéticas
FTIR
Tinuvin P
Durability
Natural fibers
Ssynthetic fibers
Engenharia e Tecnologia::Outras Engenharias e Tecnologias
topic Durabilidade
Fibras naturais
Fibras sintéticas
FTIR
Tinuvin P
Durability
Natural fibers
Ssynthetic fibers
Engenharia e Tecnologia::Outras Engenharias e Tecnologias
description Dissertação de mestrado integrado em Engenharia de Polímeros
publishDate 2017
dc.date.none.fl_str_mv 2017
2017-01-01T00:00:00Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/1822/48258
url https://hdl.handle.net/1822/48258
dc.language.iso.fl_str_mv por
language por
dc.relation.none.fl_str_mv 201777916
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799133077504524288

Registros relacionados