Rotura diferida em soldadura laser de materiais dissimilares

Detalhes bibliográficos
Autor(a) principal: Nogueira, Leandro Filipe de Jesus
Data de Publicação: 2021
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/10316/97996
Resumo: Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
id RCAP_91a062f0e63bc35a4565a313caa0dc79
oai_identifier_str oai:estudogeral.uc.pt:10316/97996
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Rotura diferida em soldadura laser de materiais dissimilaresDelayed cracking in dissimilar metal laser weldingSoldadura dissimilarFissuração a frioRecobrimentoZona termicamente afetadaHidrogénio difusívelDissimilar metal weldCold crackingOverlap zoneThermal affected zoneDiffusible hydrogenDissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e TecnologiaO interesse pela soldadura laser de metais dissimilares, para a produção de componentes de transmissão, tem vindo a aumentar no seio da indústria automóvel, uma vez que permite aliar excelentes propriedades e requisitos de projeto a custos reduzidos. As juntas dissimilares, apesar de atenderem a requisitos de projeto complexos, apresentam problemas de soldabilidade, relacionados com as diferenças nas propriedades físicas, químicas e mecânicas dos metais envolvidos na ligação.No fabrico das caixas de velocidades, é utilizada a ligação por soldadura para acoplar a coroa à caixa diferencial. A coroa é fabricada em aço 27MnCr5 sujeito a um tratamento térmico super profundo de carbonitruração. A caixa diferencial é maquinada em ferro fundido dúctil, FCS 600-3. O material de adição utilizado é uma liga de crómio-níquel, NiCr20Mn3Nb.Este estudo tem como objetivo otimizar o processo de soldadura laser das caixas diferenciais, bem como avaliar o fluxo de hidrogénio difusível no aço, antes de este ser soldado. O cordão de soldadura estudado apresenta uma geometria circular, havendo uma zona de sobreposição, designada por zona do recobrimento. Esta zona foi identificada como crítica e de elevada contribuição para o fenómeno da fissuração a frio, pelo que foi realizado um plano de ensaios recorrendo à soldadura de várias amostras e testando diferentes parametrizações do sistema de alimentação do material de adição. As amostras foram inspecionadas através de ultrassons e, posteriormente, recorrendo à análise destrutiva.Relativamente ao fluxo de hidrogénio difusível no aço, este foi medido durante o tratamento térmico de revenido com a finalidade de avaliar se o hidrogénio se difunde para o exterior do material durante o revenido, como é que essa difusão reage ao aumento da temperatura e se a duração de 3h de revenido é suficiente para reduzir o nível de hidrogénio abaixo do nível considerado crítico para evitar a fissuração a frio.Com a realização desta investigação foi possível concluir que a zona do recobrimento é propícia ao surgimento de defeitos de soldadura, nomeadamente fissuras. Conclui-se ainda que grandes quantidades de hidrogénio são absorvidas pelo aço durante o tratamento térmico de carbonitruração, que depois é libertado durante o revenido. Contudo, ao fim de 3h de revenido o fluxo de hidrogénio é superior a 1000 pL/s, que ainda assim, é prejudicial e favorece a fissuração a frio.The interest in laser welding of dissimilar metals, to produce transmission components, has been increasing within the automotive industry, since it allows to combine excellent properties and design requirements at reduced costs. Dissimilar joints, despite meeting complex design requirements, presents weldability problems related to differences between physical, chemical and mechanical properties of the metals involved in welded joint.In the manufacture of gearboxes, welding is used to attach the crown to the differential housing. The crown is made of 27MnCr5 steel subject to a carbonitriding heat treatment. The differential case is machined in cast iron, FCS 600-3. The filler material used is a chromium-nickel alloy, NiCr20Mn3Nb.This study aims to optimize the laser welding process of the differential boxes, as well as to evaluate the flux of diffusible hydrogen in steel before welding. The welding bead studied presents a circular geometry with an overlap zone. This area was identified as critical with a high contribution to the phenomenon of cold cracking, so a test plan was carried out using the welding of several samples and testing different parameterizations of the feeding system of the filler material. The samples were inspected by ultrasound and subsequently using destructive analysis.The diffusible hydrogen flux in steel was measured during tempering for the purpose of assessing whether hydrogen diffuses to the outside of the material during heat treatment, how this diffusion reacts to the temperature increase and whether the duration of 3h of tempering is sufficient to reduce the level of hydrogen below the level considered critical to avoid cold cracking.With this investigation, it was possible to conclude that the overlap zone is prone to the appearance of welding defects, more precisely, cold cracks. It is also concluded that large amounts of hydrogen are absorbed by steel during the heat treatment of carbonitriding and that it is then released during tempering. However, after 3 hours of tempering the hydrogen flux is greater than 1000 pL/s, which is prone to cold cracking.2021-12-09info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesishttp://hdl.handle.net/10316/97996http://hdl.handle.net/10316/97996TID:202921824porNogueira, Leandro Filipe de Jesusinfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2022-05-25T03:49:52Zoai:estudogeral.uc.pt:10316/97996Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T21:15:55.885102Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Rotura diferida em soldadura laser de materiais dissimilares
Delayed cracking in dissimilar metal laser welding
title Rotura diferida em soldadura laser de materiais dissimilares
spellingShingle Rotura diferida em soldadura laser de materiais dissimilares
Nogueira, Leandro Filipe de Jesus
Soldadura dissimilar
Fissuração a frio
Recobrimento
Zona termicamente afetada
Hidrogénio difusível
Dissimilar metal weld
Cold cracking
Overlap zone
Thermal affected zone
Diffusible hydrogen
title_short Rotura diferida em soldadura laser de materiais dissimilares
title_full Rotura diferida em soldadura laser de materiais dissimilares
title_fullStr Rotura diferida em soldadura laser de materiais dissimilares
title_full_unstemmed Rotura diferida em soldadura laser de materiais dissimilares
title_sort Rotura diferida em soldadura laser de materiais dissimilares
author Nogueira, Leandro Filipe de Jesus
author_facet Nogueira, Leandro Filipe de Jesus
author_role author
dc.contributor.author.fl_str_mv Nogueira, Leandro Filipe de Jesus
dc.subject.por.fl_str_mv Soldadura dissimilar
Fissuração a frio
Recobrimento
Zona termicamente afetada
Hidrogénio difusível
Dissimilar metal weld
Cold cracking
Overlap zone
Thermal affected zone
Diffusible hydrogen
topic Soldadura dissimilar
Fissuração a frio
Recobrimento
Zona termicamente afetada
Hidrogénio difusível
Dissimilar metal weld
Cold cracking
Overlap zone
Thermal affected zone
Diffusible hydrogen
description Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
publishDate 2021
dc.date.none.fl_str_mv 2021-12-09
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/10316/97996
http://hdl.handle.net/10316/97996
TID:202921824
url http://hdl.handle.net/10316/97996
identifier_str_mv TID:202921824
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799134055861583872

Registros relacionados