Avaliação experimental do efeito de adições na autorregeneração de argamassas de cimento
Autor(a) principal: | |
---|---|
Data de Publicação: | 2019 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
Texto Completo: | http://hdl.handle.net/10400.26/25912 |
Resumo: | Mestrado em Engenharia Civil Área de Especialização: Construção Dissertação |
id |
RCAP_b61bf383ba9db2b2fa3bb37dfe014971 |
---|---|
oai_identifier_str |
oai:comum.rcaap.pt:10400.26/25912 |
network_acronym_str |
RCAP |
network_name_str |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
repository_id_str |
7160 |
spelling |
Avaliação experimental do efeito de adições na autorregeneração de argamassas de cimentoAutorregeneraçãoargamassacimentofíler calcáriocinza volanteself-healingmortarcementlimestone fillerfly ashMestrado em Engenharia Civil Área de Especialização: Construção DissertaçãoA pertinência do tema da autorregeneração está no crescente interesse, em medidas preventivas, associadas à durabilidade dos revestimentos dos edifícios. Idealmente, um revestimento com capacidade autorregenerante terá um maior tempo de vida útil, minimizando os inconvenientes e dispendiosas intervenções que estes requerem. Posto isto, na presente dissertação, é feita uma avaliação experimental do efeito de adições na autorregeneração de argamassas cimentícias, nomeadamente a cinza volante e o fíler calcário. A campanha laboratorial incidiu na produção de 5 tipo de argamassa: de cimento (como referência), com substituição parcial de cimento por fíler calcário (com 15% e 30%) e com substituição de cimento por cinza volante (com 15% e 30%). Para cada tipo de argamassa sujeitou-se metade dos provetes a um dano, ou seja, aplicou-se uma carga à compressão, de cerca de 60% da carga de rotura (carga máxima sem que ocorra a desintegração do provete), com o intuito de avaliar o seu desenvolvimento em termos de eventual autorregeneração ao fim de 120 dias. Foi feito um conjunto de ensaios aos 28 e aos 120 dias, tanto no estado fresco como no estado endurecido. No estado fresco ensaiou-se a consistência por espalhamento, massa volúmica aparente e o teor de ar. No estado endurecido determinou-se a resistência à compressão, a resistência à tração por flexão, a porosidade aberta e calcularam-se as massas volúmicas. Fez-se, também, o ensaio da absorção de água de capilaridade, obtendo-se o coeficiente de capilaridade e o valor assintótico. Para além dos ensaios ditos tradicionais fez-se, também, uma monitorização da velocidade de propagação dos ultrassons (a cada 15 dias) com o intuito de observar um possível desenvolvimento da estrutura interna das argamassas, associado à autorregeneração e, calculando também, o módulo de elasticidade dinâmico. Os resultados decorrentes dos ensaios laboratoriais não permitiram concluir que o dano provocado tenha sido efetivo, no entanto, foi possível observar que, na maioria dos ensaios, os provetes danificados não conseguiram atingir os mesmos resultados obtidos para os provetes não danificados. Não obstante, foi possível observar que a substituição parcial de cimento por 15% de fíler calcário e por 30% de cinza volante apresenta diversas vantagens das quais se destacam, um melhor arranjo do esqueleto sólido da argamassa acompanhado por um menor teor de ar na mistura (no estado fresco). Ao mesmo tempo, obtém-se menores porosidades, velocidades de absorção capilar e absorção total de água por capilaridade.The relevance of the self-healing theme lies in the growing interest in preventive measures associated with the durability of building coatings. Ideally, a self-healing coating will have a longer shelf life, minimizing the drawbacks and costly interventions that these require. Thus, in the present dissertation, an experimental evaluation of the effect of additions on the self-healing of cement mortars, namely fly ash, and the limestone filler is studied. The laboratory campaign focused on the production of 5 types of mortar: cement (as a reference), partial replacement of cement by limestone filler (15% and 30%) and replacement of cement by fly ash (15% and 30%). For each type of mortar, half of the test pieces were subjected to a damage, i.e. a compressive load of about 60% of the breaking load (maximum load without disintegration of the test piece) was applied, in order to evaluate its development in terms of possible self-healing after 120 days. A set of tests were performed at 28 and 120 days, both fresh and in the hardened state. In the fresh state the consistency, bulk density and air content were tested. In the hardened state, the compressive strength, the flexural tensile strength, the open porosity was determined, and the densities were calculated. The capillary water absorption test was also performed, obtaining the capillary coefficient and the asymptotic value. In addition to the traditional tests, ultrasonic propagation velocity was monitored (every 15 days) in order to observe a possible development of the internal structure, associated with self-healing, and the dynamic elasticity was calculated. The results of the laboratory tests did not allow to conclude that the damage caused was effective, however, it was possible to observe that, in most of the tests, the damaged specimens were not able to reach the same results obtained for the undamaged specimens. Nevertheless, it was possible to observe that the partial substitution of cement by 15% of limestone filler and by 30% of fly ash has several advantages, of which a better arrangement of the solid skeleton of the mortar accompanied by a lower content of air in the mixture (in the fresh state). At the same time, lower porosities, capillary absorption rates and total water absorption by capillarity are obtained.Instituto Politécnico de Setúbal. Escola Superior de Tecnologia do BarreiroPereira, CristianaRodrigues, Maria PaulinaRepositório ComumOliveira, Melissa Orlanda Vivas de2019-01-28T11:39:53Z2019-012019-01-01T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfhttp://hdl.handle.net/10400.26/25912TID:202164004porinfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-11-21T09:54:47Zoai:comum.rcaap.pt:10400.26/25912Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T23:10:36.952953Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse |
dc.title.none.fl_str_mv |
Avaliação experimental do efeito de adições na autorregeneração de argamassas de cimento |
title |
Avaliação experimental do efeito de adições na autorregeneração de argamassas de cimento |
spellingShingle |
Avaliação experimental do efeito de adições na autorregeneração de argamassas de cimento Oliveira, Melissa Orlanda Vivas de Autorregeneração argamassa cimento fíler calcário cinza volante self-healing mortar cement limestone filler fly ash |
title_short |
Avaliação experimental do efeito de adições na autorregeneração de argamassas de cimento |
title_full |
Avaliação experimental do efeito de adições na autorregeneração de argamassas de cimento |
title_fullStr |
Avaliação experimental do efeito de adições na autorregeneração de argamassas de cimento |
title_full_unstemmed |
Avaliação experimental do efeito de adições na autorregeneração de argamassas de cimento |
title_sort |
Avaliação experimental do efeito de adições na autorregeneração de argamassas de cimento |
author |
Oliveira, Melissa Orlanda Vivas de |
author_facet |
Oliveira, Melissa Orlanda Vivas de |
author_role |
author |
dc.contributor.none.fl_str_mv |
Pereira, Cristiana Rodrigues, Maria Paulina Repositório Comum |
dc.contributor.author.fl_str_mv |
Oliveira, Melissa Orlanda Vivas de |
dc.subject.por.fl_str_mv |
Autorregeneração argamassa cimento fíler calcário cinza volante self-healing mortar cement limestone filler fly ash |
topic |
Autorregeneração argamassa cimento fíler calcário cinza volante self-healing mortar cement limestone filler fly ash |
description |
Mestrado em Engenharia Civil Área de Especialização: Construção Dissertação |
publishDate |
2019 |
dc.date.none.fl_str_mv |
2019-01-28T11:39:53Z 2019-01 2019-01-01T00:00:00Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://hdl.handle.net/10400.26/25912 TID:202164004 |
url |
http://hdl.handle.net/10400.26/25912 |
identifier_str_mv |
TID:202164004 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Instituto Politécnico de Setúbal. Escola Superior de Tecnologia do Barreiro |
publisher.none.fl_str_mv |
Instituto Politécnico de Setúbal. Escola Superior de Tecnologia do Barreiro |
dc.source.none.fl_str_mv |
reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação instacron:RCAAP |
instname_str |
Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação |
instacron_str |
RCAAP |
institution |
RCAAP |
reponame_str |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
collection |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
repository.name.fl_str_mv |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação |
repository.mail.fl_str_mv |
|
_version_ |
1817550674690310144 |