Avaliação da nanoinfiltração de um sistema adesivo universal experimental e de sistemas adesivos universais comerciais

Detalhes bibliográficos
Autor(a) principal: Cunha, Mariana Mascarenhas Pyrrait Trincão
Data de Publicação: 2019
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/10400.26/31079
Resumo: Dissertação para obtenção do grau de Mestre no Instituto Universitário Egas Moniz
id RCAP_b94ed683f44e158d1b3eb5e346616424
oai_identifier_str oai:comum.rcaap.pt:10400.26/31079
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Avaliação da nanoinfiltração de um sistema adesivo universal experimental e de sistemas adesivos universais comerciaisAdesivos universaisAdesãoDentinaNanoinfiltraçãoDissertação para obtenção do grau de Mestre no Instituto Universitário Egas MonizObjetivo: Avaliar a nanoinfiltração da interface adesiva por SEM-EDS de sistemas adesivos universais com Bis-GMA e de um sistema adesivo sem Bis-GMA. Materiais e Métodos: 15 molares humanos hígidos armazenados de acordo com a norma ISO 11405 foram distribuídos aleatoriamente em 3 grupos (n=5), Grupo SBU, Scotchbond Universal Adhesive, adesivo com bis-GMA; Grupo FBU, Futurabond U, adesivo com bis-GMA; Grupo AUA, Ambar Universal APS, sem bis-GMA. Os dentes foram seccionados num micrótomo de tecidos duros de modo a expor a dentina superficial, sendo em seguida submetidos a um polimento com um disco de CSi 600 grit. Foi aplicado o sistema adesivo selecionado para cada grupo segundo as instruções dos fabricantes, construídos blocos de resina composta com 6 a 8 mm de altura e armazenados durante 24 horas numa estufa a 37ºC em água destilada. As amostras foram seccionadas de forma a obter fatias de 0,7mm e para cada grupo foram selecionadas 10 fatias. As fatias foram armazenadas numa estufa, em água destilada, a 37ºC durante 1 mês. Após o período de incubação, as amostras foram imersas numa solução aquosa de nitrato de prata amoniacal a 37ºC durante 24 horas em recipientes protegidos da luz e seguidamente imersas numa solução fotográfica reveladora durante 8 horas sob luz fluorescente. As amostras foram novamente imersas numa solução reveladora de pH 7,3 durante 12h a 4ºC, sendo em seguida lavadas com cacodilato de sódio durante 1 hora. Posteriormente as amostras foram desidratadas em imersões de graus ascendentes de etanol. De seguida foram colocadas numa diluição de 1:1 de etanol com hexametildisilazano durante 10 minutos e secas por imersão em hexametildisilazano durante 10 minutos. Depois de secas, foram embebidas em resina epóxi autopolimerizável, polidas com discos de CSi com abrasão decrescente e suspensões diamantadas de 3 e 1 μm. Por fim as amostras foram colocadas no ultrassom num banho de 100% etanol durante 10 minutos, secas e desmineralizadas em 0,5% de ácido fosfórico durante 1 minuto e sujeitas a testes de nanoinfiltração por SEM-EDS. Resultados: O grupo FBU foi o que apresentou o grau de nanoinfiltração mais elevado, ao invés do grupo AUA que foi o que obteve menor quantidade nanoinfiltração, no entanto, não foram encontradas diferenças significativas entre os adesivos estudados. Conclusão: Os 3 adesivos não apresentam diferenças estatisticamente significativas entre si.Objective: To evaluate the adhesive interphase nanoleakage by SEM-EDS of universal adhesive systems with bis-GMA and a universal adhesive system without bis-GMA. Materials and Methods: 15 sound human molars stored according to ISO 11405 were randomly assigned to 3 groups (n = 5), SBU Group, Scotchbond Universal Adhesive, bis- GMA adhesive; FBU Group, Futurabond U, bis-GMA adhesive; AUA group, Ambar Universal APS, without bis-GMA. The teeth were sectioned in a hard tissue microtome to expose the superficial dentin, then polished with a 600 grit CSi disc. The adhesive system selected for each group was applied according to the manufacturers' instructions, 6 to 8 mm high composite resin blocks were made and stored for 24 hours in a 37ºC oven in distilled water. The samples were sectioned to obtain 0.7mm slices and for each group 10 slices were selected. The slices were stored in an oven in distilled water at 37ºC for 1 month. After the incubation period, the samples were immersed in an aqueous ammonia silver nitrate solution at 37°C for 24 hours in light-protected containers and then immersed in a developing photographic solution for 8 hours under fluorescent light. The samples were again immersed in a pH 7.3 developer solution for 12h at 4°C, then washed with sodium cacodylate for 1 hour. The samples were subsequently dehydrated in upward grade immersions of ethanol. They were then placed in a 1: 1 dilution of ethanol with hexamethyldisilazane for 10 minutes and dried by immersion in hexamethyldisilazane for 10 minutes. After drying, they were soaked in self-curing epoxy resin, polished with decreasing abrasion CSi discs and 3 and 1 μm diamond suspensions. Finally, the samples were sonicated in a 100% ethanol bath for 10 minutes, dried and demineralized in 0.5% phosphoric acid for 1 minute and subjected to SEM-EDS nanoleakage tests. Results: The FBU group presented the highest degree of nanoleakage, as opposed to the AUA group which had the lowest amount of nanoleakage. However, no significant differences were found between the adhesives studied. Conclusion: The 3 adhesives do not present statistically significant differences among themselves.Polido, Mário CruzRepositório ComumCunha, Mariana Mascarenhas Pyrrait Trincão2022-12-31T01:30:23Z2019-122019-12-01T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfhttp://hdl.handle.net/10400.26/31079URNTID:202364372porinfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-01-05T02:30:25Zoai:comum.rcaap.pt:10400.26/31079Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T15:09:51.698234Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Avaliação da nanoinfiltração de um sistema adesivo universal experimental e de sistemas adesivos universais comerciais
title Avaliação da nanoinfiltração de um sistema adesivo universal experimental e de sistemas adesivos universais comerciais
spellingShingle Avaliação da nanoinfiltração de um sistema adesivo universal experimental e de sistemas adesivos universais comerciais
Cunha, Mariana Mascarenhas Pyrrait Trincão
Adesivos universais
Adesão
Dentina
Nanoinfiltração
title_short Avaliação da nanoinfiltração de um sistema adesivo universal experimental e de sistemas adesivos universais comerciais
title_full Avaliação da nanoinfiltração de um sistema adesivo universal experimental e de sistemas adesivos universais comerciais
title_fullStr Avaliação da nanoinfiltração de um sistema adesivo universal experimental e de sistemas adesivos universais comerciais
title_full_unstemmed Avaliação da nanoinfiltração de um sistema adesivo universal experimental e de sistemas adesivos universais comerciais
title_sort Avaliação da nanoinfiltração de um sistema adesivo universal experimental e de sistemas adesivos universais comerciais
author Cunha, Mariana Mascarenhas Pyrrait Trincão
author_facet Cunha, Mariana Mascarenhas Pyrrait Trincão
author_role author
dc.contributor.none.fl_str_mv Polido, Mário Cruz
Repositório Comum
dc.contributor.author.fl_str_mv Cunha, Mariana Mascarenhas Pyrrait Trincão
dc.subject.por.fl_str_mv Adesivos universais
Adesão
Dentina
Nanoinfiltração
topic Adesivos universais
Adesão
Dentina
Nanoinfiltração
description Dissertação para obtenção do grau de Mestre no Instituto Universitário Egas Moniz
publishDate 2019
dc.date.none.fl_str_mv 2019-12
2019-12-01T00:00:00Z
2022-12-31T01:30:23Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/10400.26/31079
URN
TID:202364372
url http://hdl.handle.net/10400.26/31079
identifier_str_mv URN
TID:202364372
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799129967871655936

Registros relacionados