Novas aproximações para o fabrico por via aditiva de componentes multimaterial

Detalhes bibliográficos
Autor(a) principal: Alves, Bernardo da Silva
Data de Publicação: 2018
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/10316/86012
Resumo: Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
id RCAP_bb08b01a20b1315cfdac62d54e37b0de
oai_identifier_str oai:estudogeral.uc.pt:10316/86012
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Novas aproximações para o fabrico por via aditiva de componentes multimaterialAdditive manufacturing of multimaterial components: a new approachMoagem de Alta EnergiaWC-CoSoldadura a frioFusão Seletiva por LaserEscoabilidadeHigh Energy Ball MillingHardmetalH13Selective Laser MeltingFlowabilityDissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e TecnologiaInovar não é apenas criar algo novo, é também apresentar alterações e novos pontos de vista àquilo que já existe. A utilização do processo de Moagem de Alta Energia como método de preparação de mistura de dois tipos de pós para uso no fabrico aditivo, permite recorrer à possibilidade de criar um gradiente composicional, que permita a coexistência de dois materiais distintos sem necessidade de usar processos de ligação como a brasagem.A produção de ferramentas de corte, constituídas na sua grande maioria por carboneto de tungsténio designado vulgarmente por metal duro obriga a um suporte normalmente em aço ferramenta brasado. Criar uma interface entre o carboneto de tungsténio e o aço ferramenta (H13) por um processo único - processo aditivo-, é obrigatório para atingir o objetivo. A síntese mecânica permite a distribuição homogénea dos materiais, garantindo também uma diminuição dos defeitos durante o processo de Fusão Seletiva por Laser (SLM). Após seleção dos parâmetros adequados para o Processo de Moagem de Alta Energia (moinho de bolas planetário), várias misturas com teores diferentes de cada material em jogo foram sujeitas ao processo de moagem. Como a escoabilidade dos pós é um parâmetro fundamental para o SLM particular atenção foi dada a esta característica. Contrariamente ao previsto, para determinadas quantidades de pó, os parâmetros de moagem induziram a dissociação de WC. Com objetivo de inibir a dissociação do WC pelo efeito do H13 martensítico na destruição do Co existente como aditivo do WC foi adicionado Ni. Contudo, a presença de Ni tornou o comportamento da mistura aleatório, pois para teores similares de Ni ocorria ora soldadura entre os diversos pós, ora tinha um comportamento de acordo com o previsto. Em consequência, com o intuito de analisar em detalhe as consequências desta ocorrência há a necessidade de compreender este comportamento. Para tal foram processadas estas misturas não por SLM, mas por prensagem uniaxial, seguida de sinterização. Em consequência, poder-se-á concluir que para os teores de WC+Co e H13 estudados há sempre aplicação na pulverotecnologia - processos aditivos (para misturas de baixo teor em H13 e sem níquel) e processo replicativos (para misturas de maiores teores de H13 e Níquel).Innovating isn’t simply the act of creating something new, but also to bring change and different points of view. That said, taking a new approach of the High Energy Ball Milling process by viewing it as a preparation method for Additive Manufacturing creates the possibility to form a compositional gradient, allowing two inherently different materials to coexist, without the need of conventional processes such as brazing. The production of cutting tools, the big majority being made of Tungsten Carbide, also known as Hard Metal, obligates the junction with a steel tool usually through the process of brazing. Therefore, The production of an interface between Hardmetal and H13 Tool Steel using a single method – Additive Manufacturing – is the main goal. The Mechanical Alloying process allows for a homogeneous distribution of the elements, lessening the defects of the Selective Laser Melting process. After studying the most adequate parameters for the High Energy Ball Milling Process, several sets of mixtures with different %wt of each material were subdued to the process. Afterwards, their flowability was assessed, since it is an extremely important characteristic to the SLM process. However, unlike it was predicted, some of the different mixtures with the selected ball milling parameters led to mechanisms of dissociation during milling turning WC into W+C due to the high friction within the chamber. Aiming to lessen the effects of dissociation, Ni was added to the mixture, since it has similar properties to Co as a binder. The addition on Ni proved unsuccessful, due to its aleatory behavior: it produced usable powder for SLM as well as agglomerated powder, strengthening too much the effects of cold welding. With these unexpected results, the SLM process is put aside due to poor conditions of the powder, and, in order to understand the causes of this behavior, the samples were uniaxially pressed, sintered and analysed in order to determine their density and hardness. These samples, after sintering, showed values of density and hardness within the norm. In conclusion, the several grades of WC+Co and H13 used always have an application within pulverotechnology: either through additive manufacturing (for low grades of H13) and through replicative processes (for higher grades of H13 and Ni).2018-10-02info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesishttp://hdl.handle.net/10316/86012http://hdl.handle.net/10316/86012TID:202203387porAlves, Bernardo da Silvainfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2021-05-25T08:24:12Zoai:estudogeral.uc.pt:10316/86012Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T21:07:15.394070Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Novas aproximações para o fabrico por via aditiva de componentes multimaterial
Additive manufacturing of multimaterial components: a new approach
title Novas aproximações para o fabrico por via aditiva de componentes multimaterial
spellingShingle Novas aproximações para o fabrico por via aditiva de componentes multimaterial
Alves, Bernardo da Silva
Moagem de Alta Energia
WC-Co
Soldadura a frio
Fusão Seletiva por Laser
Escoabilidade
High Energy Ball Milling
Hardmetal
H13
Selective Laser Melting
Flowability
title_short Novas aproximações para o fabrico por via aditiva de componentes multimaterial
title_full Novas aproximações para o fabrico por via aditiva de componentes multimaterial
title_fullStr Novas aproximações para o fabrico por via aditiva de componentes multimaterial
title_full_unstemmed Novas aproximações para o fabrico por via aditiva de componentes multimaterial
title_sort Novas aproximações para o fabrico por via aditiva de componentes multimaterial
author Alves, Bernardo da Silva
author_facet Alves, Bernardo da Silva
author_role author
dc.contributor.author.fl_str_mv Alves, Bernardo da Silva
dc.subject.por.fl_str_mv Moagem de Alta Energia
WC-Co
Soldadura a frio
Fusão Seletiva por Laser
Escoabilidade
High Energy Ball Milling
Hardmetal
H13
Selective Laser Melting
Flowability
topic Moagem de Alta Energia
WC-Co
Soldadura a frio
Fusão Seletiva por Laser
Escoabilidade
High Energy Ball Milling
Hardmetal
H13
Selective Laser Melting
Flowability
description Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
publishDate 2018
dc.date.none.fl_str_mv 2018-10-02
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/10316/86012
http://hdl.handle.net/10316/86012
TID:202203387
url http://hdl.handle.net/10316/86012
identifier_str_mv TID:202203387
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799133964131106816

Registros relacionados