Deteção de defeitos em materiais compósitos usando tecnologia de ultrassons

Detalhes bibliográficos
Autor(a) principal: Coelho, Bruno Miguel Alves
Data de Publicação: 2020
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/1822/65770
Resumo: Dissertação de mestrado integrado em Engenharia de Polímeros
id RCAP_d3670a606ebc7cab65e6ecbfab426641
oai_identifier_str oai:repositorium.sdum.uminho.pt:1822/65770
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Deteção de defeitos em materiais compósitos usando tecnologia de ultrassonsDefeitosEnsaios não destrutivosMateriais compósitosUltrassonsVARIComposite materialsDefectsNon-destructive testingUltrasoundEngenharia e Tecnologia::Engenharia dos MateriaisDissertação de mestrado integrado em Engenharia de PolímerosA utilização de materiais compósitos em aplicações estruturais comporta alguns desafios, pois a sua natureza heterogénea, resulta em mecanismos de dano complexos, sendo alguns tipos de defeito de difícil deteção a olho nu. O uso de técnicas de Ensaios Não Destrutivos (END) neste tipo de materiais é de extrema importância, uma vez que, permite a deteção de defeitos de outro modo impercetíveis. Este trabalho tem como objetivo principal o uso da técnica de análise não destrutiva de ultrassons (UT) no estudo, avaliação e caracterização de defeitos em materiais compósitos de matriz polimérica. Para o efeito foi utilizado o equipamento Prisma da Sonatest do tipo A-Scan com sonda Phased Array. Tendo em conta a pretensão referida, numa primeira fase, foram produzidos diferentes laminados com defeitos impostos como furos e inclusões, recorrendo ao processo de produção por infusão de resina assistida a vácuo (VARI). No caso das furações, os resultados experimentais obtidos evidenciam uma pequena tendência para a diminuição da extensão da região delaminada com o aumento do diâmetro da broca. Por outro lado, o estudo efetuado sobre as inclusões mostra que, quanto menores forem as suas dimensões, maior é a facilidade dos ultrassons em “contorná-las”, tornando-se a superfície oposta do laminado menos esbatida. Numa segunda fase, e utilizando o mesmo processo de produção, foram fabricados provetes de diferentes laminados sem defeitos, para análise UT de dois tipos de defeitos específicos: danos mecânicos e juntas adesivas. Os danos mecânicos foram induzidos por ação de diferentes solicitações mecânicas controladas como impacto e flexão, e caracterizados quanto à sua estrutura. As juntas adesivas (colagens entre laminados), por sua vez, foram avaliadas quanto à sua qualidade, tendo sido também submetidas a tensões mecânicas controladas, nomeadamente tração, de forma a causar danos nas juntas. Em relação aos resultados obtidos a partir da análise UT de laminados submetidos a solicitações de impacto de baixa energia e flexão, conclui-se que estas solicitações provocam um dano de formato cónico, verificando-se um fenómeno de crescimento das delaminações ao longo da espessura, à medida que a distância à superfície solicitada aumenta. Por último, constata-se que o dano induzido nas juntas origina uma descontinuidade no material, resultando em falhas no sinal de UT quer na interface substrato superior/adesivo quer no fundo do adesivo.The use of composite materials in structural applications poses some challenges, as their heterogeneous nature results in complex damage mechanisms, with some types of defects difficult to detect with the naked eye. The use of Non-Destructive Testing (NDT) techniques in this type of material is extremely important, since it allows the detection of defects that are otherwise imperceptible. This work has as main objective the use of the non-destructive ultrasound analysis (UT) technique in the study, evaluation and characterization of defects in polymeric matrix composite materials. For this purpose, Sonatest Prisma A-Scan equipment with Phased Array probe was used. In view of the above claim, in the first stage different laminates with defects imposed, such as, holes and inclusions, were produced using the vacuum assisted resin infusion (VARI) production process. In the case of defects produced by drilling, the experimental results obtained show a small tendency to decrease the extension of the delaminated region with the increase of the diameter of the drill. On the other hand, the study carried out on the inclusions shows that the smaller the dimensions, the greater the ease of ultrasound in “surrounding them” making the opposite surface of the laminate less blurred. In a second phase, and using the same production process, specimens of different defect-free laminates were fabricated for UT analysis of two specific types of defects: mechanical damage and adhesive joints. Mechanical damage was induced by the action of different controlled mechanical stresses, such as, impact and bending, and characterized by its structure. Adhesive joints (glue between laminates), in turn, were evaluated for their quality, and were also subjected to controlled tensile stress, to cause damage to the joints. Regarding the results obtained from the UT analysis of laminates subjected to low energy impact and bending, it is concluded that these stresses cause damage of a conical shape, indicating a phenomenon of growth of delamination along the thickness, as that the distance to the requested surface increases. Finally, it appears that the damage induced in the joints causes a discontinuity in the material, resulting in flaws in the UT signal both at the upper substrate/adhesive interface and at the bottom of the adhesive.Nunes, J. P.Malheiro, Joana Mafalda MouraUniversidade do MinhoCoelho, Bruno Miguel Alves20202020-01-01T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfhttp://hdl.handle.net/1822/65770por202485960info:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-07-21T12:14:27Zoai:repositorium.sdum.uminho.pt:1822/65770Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T19:06:46.174786Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Deteção de defeitos em materiais compósitos usando tecnologia de ultrassons
title Deteção de defeitos em materiais compósitos usando tecnologia de ultrassons
spellingShingle Deteção de defeitos em materiais compósitos usando tecnologia de ultrassons
Coelho, Bruno Miguel Alves
Defeitos
Ensaios não destrutivos
Materiais compósitos
Ultrassons
VARI
Composite materials
Defects
Non-destructive testing
Ultrasound
Engenharia e Tecnologia::Engenharia dos Materiais
title_short Deteção de defeitos em materiais compósitos usando tecnologia de ultrassons
title_full Deteção de defeitos em materiais compósitos usando tecnologia de ultrassons
title_fullStr Deteção de defeitos em materiais compósitos usando tecnologia de ultrassons
title_full_unstemmed Deteção de defeitos em materiais compósitos usando tecnologia de ultrassons
title_sort Deteção de defeitos em materiais compósitos usando tecnologia de ultrassons
author Coelho, Bruno Miguel Alves
author_facet Coelho, Bruno Miguel Alves
author_role author
dc.contributor.none.fl_str_mv Nunes, J. P.
Malheiro, Joana Mafalda Moura
Universidade do Minho
dc.contributor.author.fl_str_mv Coelho, Bruno Miguel Alves
dc.subject.por.fl_str_mv Defeitos
Ensaios não destrutivos
Materiais compósitos
Ultrassons
VARI
Composite materials
Defects
Non-destructive testing
Ultrasound
Engenharia e Tecnologia::Engenharia dos Materiais
topic Defeitos
Ensaios não destrutivos
Materiais compósitos
Ultrassons
VARI
Composite materials
Defects
Non-destructive testing
Ultrasound
Engenharia e Tecnologia::Engenharia dos Materiais
description Dissertação de mestrado integrado em Engenharia de Polímeros
publishDate 2020
dc.date.none.fl_str_mv 2020
2020-01-01T00:00:00Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/1822/65770
url http://hdl.handle.net/1822/65770
dc.language.iso.fl_str_mv por
language por
dc.relation.none.fl_str_mv 202485960
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799132483785064448

Registros relacionados