Propriedades Elétricas versus a Solicitação Mecânica de Componentes Processados por Fabrico Aditivo

Detalhes bibliográficos
Autor(a) principal: Marinho, Andrea de Amorim
Data de Publicação: 2022
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/10316/103106
Resumo: Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
id RCAP_d7f319f01f85c84d4db711bfe52dce19
oai_identifier_str oai:estudogeral.uc.pt:10316/103106
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Propriedades Elétricas versus a Solicitação Mecânica de Componentes Processados por Fabrico AditivoElectric Properties versus Mechanical Stress of Components Processed by Additive ManufacturingFabrico AditivoCompósitos CondutoresPropriedades ElétricasÂngulo de ImpressãoEnsaio DinâmicoAdditive ManufacturingConductive CompositesElectric PropertiesPrinting AngleDynamic TestDissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e TecnologiaO uso de materiais compósitos em todas as áreas de desenvolvimento tem sido cada vez mais abundante devido às inúmeras características que se podem obter através da mistura de diferentes tipos de materiais. Os polímeros, por norma, não são condutores elétricos. No entanto, compósitos de matriz polimérica com reforço de material condutor podem suprir este problema. Estes materiais abrem novas possibilidades na produção de componentes elétricos inovadores e úteis em várias áreas.O processamento por fabrico aditivo oferece inúmeras vantagens, como liberdade no design, complexidade e personalização da geometria dos componentes elétricos, bem como nos parâmetros de impressão. Contudo, as propriedades dos materiais termoplásticos sob forma de filamentos podem sofrer alterações durante o processamento.Atualmente, existem no mercado vários filamentos de materiais compósitos diferentes. Neste trabalho foram estudados dois filamentos comerciais, o FilaFlex®, um compósito constituído por poliuretana termoplástica (TPU) e “lampblack”, e o Koltron G1®, um compósito constituído por poli(diflureto de vinilo) (PVDF) e grafeno. O objetivo deste trabalho foi analisar a possível alteração das propriedades elétricas dos materiais compósitos após o processamento por fabrico aditivo, com a variação do ângulo de enchimento (+45º/-45º e 0º) e durante ensaios mecânicos. A caracterização dos materiais englobou as vertentes química, térmica, elétrica (ensaios estático, dinâmico e cíclico) dos filamentos comerciais e dos provetes impressos. A análise da variação das propriedades elétricas dos materiais (ensaio estático) permitiu concluir que existe uma perda destas propriedades nos dois materiais após a impressão. Os filamentos de FilaFlex® e Koltron G1® apresentam condutividade elétrica de 33 e 30 S.mm-1, respetivamente e os provetes impressos de FilaFlex® e Koltron G1® apresentam condutividade elétrica de 11 e 15 S.mm-1, respetivamente. Através dos ensaios dinâmicos, realizados tanto nas amostras de filamento como nos provetes impressos, foi possível constatar que o material FilaFlex®, quando sujeito a tração, tem uma maior estabilidade elétrica e menor resistência elétrica em comparação com o material Koltron G1®. Nos ensaios cíclicos, foi possível observar que a resistência elétrica de ambos os materiais tende a decrescer durante o ensaio. Esta caracterização permitiu ainda observar que existe um padrão de resposta da resistência elétrica do material FilaFlex® em função da deformação do material.The use of composite materials has been increasingly growing due to the diverse characteristics and properties that can be obtained by mixing different types of materials. Polymers, as a rule, are not electrical conductors. However, polymer matrix composites reinforced with conductive material can overcome this problem. These materials open up new possibilities in the production of innovative and useful electrical components for application in several areas.Additive manufacturing processing offers numerous advantages such as freedom in design, complexity and customization of electrical component geometry as well as printing parameters. However, the properties of thermoplastic materials in the form of filaments may change during processing.Currently, there are several filaments of different composite materials on the market. In this work, two new commercial filaments were studied, FilaFlex®, a composite made of thermoplastic polyurethane (TPU) and “lampblack”, and Koltron G1®, a composite made of poly(vinyl difluoride) (PVDF) and graphene.The objective of this work was to analyse the possible change in the electrical properties of composite materials after processing by additive manufacturing, with the variation of the filling angle (+45º/-45º and 0º) and during mechanical tests. The characterization of the materials included the chemical, thermal, electrical properties (during static, dynamic and cyclic tests) of commercial filaments and printed specimens.The analysis of the variation of the electrical properties of the materials (static test) allowed to conclude that there is a loss of these properties in the two materials after printing. FilaFlex® and Koltron G1® filaments present electrical conductivity of 33 and 30 S.mm-1, respectively, and the printed specimens of FilaFlex® and Koltron G1® present electrical conductivity of 11 and 15 S.mm-1, respectively.Through dynamic tests, performed both on the filament samples and on the printed specimens, it was possible to verify that the FilaFlex® material, when subjected to traction, has greater electrical stability and lower electrical resistance compared to the Koltron G1® material.In the cyclic tests, it was possible to observe the electrical resistance of both materials tends to decrease during the test. This characterization also allowed us to observe that there is a response pattern of the electrical resistance of the FilaFlex® material as a function of the material's deformation.2022-07-132023-07-13T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesishttp://hdl.handle.net/10316/103106http://hdl.handle.net/10316/103106TID:203078519porMarinho, Andrea de Amoriminfo:eu-repo/semantics/embargoedAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-10-27T11:09:41Zoai:estudogeral.uc.pt:10316/103106Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T21:19:59.798750Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Propriedades Elétricas versus a Solicitação Mecânica de Componentes Processados por Fabrico Aditivo
Electric Properties versus Mechanical Stress of Components Processed by Additive Manufacturing
title Propriedades Elétricas versus a Solicitação Mecânica de Componentes Processados por Fabrico Aditivo
spellingShingle Propriedades Elétricas versus a Solicitação Mecânica de Componentes Processados por Fabrico Aditivo
Marinho, Andrea de Amorim
Fabrico Aditivo
Compósitos Condutores
Propriedades Elétricas
Ângulo de Impressão
Ensaio Dinâmico
Additive Manufacturing
Conductive Composites
Electric Properties
Printing Angle
Dynamic Test
title_short Propriedades Elétricas versus a Solicitação Mecânica de Componentes Processados por Fabrico Aditivo
title_full Propriedades Elétricas versus a Solicitação Mecânica de Componentes Processados por Fabrico Aditivo
title_fullStr Propriedades Elétricas versus a Solicitação Mecânica de Componentes Processados por Fabrico Aditivo
title_full_unstemmed Propriedades Elétricas versus a Solicitação Mecânica de Componentes Processados por Fabrico Aditivo
title_sort Propriedades Elétricas versus a Solicitação Mecânica de Componentes Processados por Fabrico Aditivo
author Marinho, Andrea de Amorim
author_facet Marinho, Andrea de Amorim
author_role author
dc.contributor.author.fl_str_mv Marinho, Andrea de Amorim
dc.subject.por.fl_str_mv Fabrico Aditivo
Compósitos Condutores
Propriedades Elétricas
Ângulo de Impressão
Ensaio Dinâmico
Additive Manufacturing
Conductive Composites
Electric Properties
Printing Angle
Dynamic Test
topic Fabrico Aditivo
Compósitos Condutores
Propriedades Elétricas
Ângulo de Impressão
Ensaio Dinâmico
Additive Manufacturing
Conductive Composites
Electric Properties
Printing Angle
Dynamic Test
description Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
publishDate 2022
dc.date.none.fl_str_mv 2022-07-13
2023-07-13T00:00:00Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/10316/103106
http://hdl.handle.net/10316/103106
TID:203078519
url http://hdl.handle.net/10316/103106
identifier_str_mv TID:203078519
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/embargoedAccess
eu_rights_str_mv embargoedAccess
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799134093456179200

Registros relacionados