Reverse shape selectivity in the adsorption of hexane and xylene isomers in MOF UiO-66

• Autor(a) principal: Silva, José A.C.
• Data de Publicação: 2011
• Outros Autores: Rodrigues, Alírio, Bárcia, Patrick da Silva, Guimarães, Daniela, Mendes, Patricia, Chevreau, Hubert, Serre, Christian, Guillerm, Vincent
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
• Texto Completo: http://hdl.handle.net/10198/6370
• topic: MOFs; Hexane isomers; Adsorption

An adsorption study of hexane and xylene isomers mixtures was addressed in a rigid zirconium terephthalate UiO-66 (UiO for University of Oslo) with octahedral and tetrahedral cavities of free diameter close to 1.1 nm and 0.8 nm, respectively. Multicomponent equimolar breakthrough experiments show that the adsorption hierarchy of structural isomers in UiO-66 is opposite to the one observed in conventional adsorbents. For hexane isomers, it was found that the amount adsorbed increases with the degree of branching, being 2,2-dimethylbutane (22DMB) and 2,3-dimethylbutane (23DMB) the more retained molecules. Regarding the xylene isomers, the results show that the adsorption of the bulkier ortho-xylene(oX) is favoured compared to its homologues. The structural similarity between MOF UiO-66 and zeolite MCM-22 suggests that the reverse shape selectivity observed in the adsorption of hexane and xylene isomers might be attributed to the rotational freedom of the molecules inside the small cavities.