Caracterização química microestrutural e mecânica de ligações Ti6Al4V-Ti6Al4V processadas por brasagem

Detalhes bibliográficos
Autor(a) principal: Gomes, Luís Mendes
Data de Publicação: 2015
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/1822/39552
Resumo: Dissertação de mestrado integrado em Engenharia de Materiais
id RCAP_dd97134a36bdba3c9edaf8b9ad0e3d07
oai_identifier_str oai:repositorium.sdum.uminho.pt:1822/39552
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Caracterização química microestrutural e mecânica de ligações Ti6Al4V-Ti6Al4V processadas por brasagemMicrostructural and mechanical characterization of Ti6Al4V-Ti6Al4V brazed jointsEngenharia e Tecnologia::Engenharia MecânicaDissertação de mestrado integrado em Engenharia de MateriaisEste trabalho consistiu na caracterização química microestrutural e mecânica de ligações Ti6Al4V/Ti6Al4V processadas por brasagem, com o auxílio de 3 ligas de brasagem comercialmente disponíveis (Cusil, Ticuni e Tini67) e a uma outra desenvolvida nesta investigação. Nas ligações processadas com a liga Cusil (72Ag-28Cu, % ponderal), a 820 °C, a temperatura de brasagem não alterou a microestrutura do material de base. Entre a liga Ti6Al4V e a liga de brasagem formaram-se duas camadas de reação essencialmente compostas por intermetálicos Ti-Cu; no centro da zona de ligação formou-se uma solução sólida de prata, que é sabido limitar a temperatura máxima de serviço destas ligações a sensivelmente 300 °C. Do processamento com as ligas Ticuni (Ti-15Cu-15Ni, % ponderal) e Tini67 (Ti-33Ni, % ponderal) a 1000 °C e 1080 °C, respetivamente, resultou a formação de interfaces com estrutura lamelar, difíceis de distinguir do material de base. O processamento de ligações com estas duas ligas de brasagem provocou alteração da microestrutura do material de base, de equiaxial para Widmanstätten. Esta modificação é considerada nefasta, visto provocar uma perda geral do excelente balanço de propriedades mecânicas, que a estrutura equiaxial confere à liga Ti6Al4V. Destes resultados, concluiu-se que nenhuma das ligas de brasagem comerciais testadas é inteiramente adequada, para a vasta gama de aplicações em que as ligações Ti6Al4V/Ti6Al4V podem ser empregues. Nesse sentido, desenvolveu-se uma nova liga de brasagem, com uma estrutura do tipo multicamada, por deposição de filmes Ag/Cu numa folha de Ti. Numa primeira abordagem o substrato foi revestido por eletrodeposição, processo que viria a ser considerado inviável, devido à dificuldade em produzir filmes com espessuras adequadas e controladas. Em alternativa, recorreuse à técnica de pulverização catódica (PVD), através da qual foi produzida uma nova liga de brasagem, designada 86Ag-14Cu/Ti/86Ag-14Cu. O processamento com a liga 86Ag-14Cu/Ti/86Ag-14Cu a 900 e a 950 °C, não provocou alterações significativas na microestrutura da liga Ti6Al4V. As interfaces resultantes encontravamse isentas de soluções sólidas baseadas em prata. Entre o material de base e o Ti da zona central formaram-se 3 camadas de reação, compostas por intermetálicos Ti-Ag. A dureza da região que engloba estas camadas, não exclui a possibilidade destas ligações poderem apresentar resistência mecânica superior à das processadas com a liga Cusil.This work mainly focused on the microstructural, chemical and mechanical characterization of Ti6Al4V/Ti6Al4V brazed joints, processed using three commercially available brazing fillers (Cusil, Ticuni and Tini67) and one other developed during this work. Parent metal microstructure did not suffer significant changes when processing with Cusil brazing alloy (72Ag-28Cu, weight %) at 820 °C. On the interface between Ti6Al4V and the molten filler, two reaction layers developed, mainly composed of Ti-Cu intermetallics. At the joint centre an Ag based solid solution remained, which is known to restrict the service temperature of these joints to a maximum of 300 °C. When processing with Ticuni (Ti-15Cu-15Ni, weight %) and Tini67 (Ti- 33Ni, weight %) brazing fillers, at 1000 and 1080 °C, respectively, transition from equiaxied to Widmanstätten microstructure was observed, on both the joint region and the parent metal. This change is considered to be detrimental, as, in general terms, the lamellar morphology is known to hold lower mechanical properties. From these results, it was concluded that none of the commercial brazing fillers tested is entirely suitable, for the vast range of applications where Ti6Al4V/Ti6Al4V joints can be applied. Thereafter, a new multi-layered filler metal was developed, by deposition of Ag/Cu films on a Ti substrate. On a first approach, the substrate was coated by electroplating, a process that would later be dismissed, due to difficulties on producing layers with adequate and controlled thickness. Alternatively, Ag/Cu layers were produced by magnetron sputtering (PVD), a technique through which a new brazing filler was developed, named 86-Ag-14Cu/Ti/86Ag-14Cu. When processing at 900 and 950 °C with the 86-Ag-14Cu/Ti/86Ag-14Cu filler, no significant changes were observed on the parent metal microstructure. No Ag based solid solutions were detected on the brazed joint. At the Ti/Ti6Al4V interface, 3 reaction layers were found, mainly composed of Ti-Ag intermetallic compounds. The hardness of these regions doesn’t exclude the possibility of these joints having better mechanical properties, than those processed with Cusil brazing filler.Guedes, A.Universidade do MinhoGomes, Luís Mendes20152015-01-01T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfhttp://hdl.handle.net/1822/39552porinfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-07-21T12:49:01Zoai:repositorium.sdum.uminho.pt:1822/39552Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T19:47:25.423639Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Caracterização química microestrutural e mecânica de ligações Ti6Al4V-Ti6Al4V processadas por brasagem
Microstructural and mechanical characterization of Ti6Al4V-Ti6Al4V brazed joints
title Caracterização química microestrutural e mecânica de ligações Ti6Al4V-Ti6Al4V processadas por brasagem
spellingShingle Caracterização química microestrutural e mecânica de ligações Ti6Al4V-Ti6Al4V processadas por brasagem
Gomes, Luís Mendes
Engenharia e Tecnologia::Engenharia Mecânica
title_short Caracterização química microestrutural e mecânica de ligações Ti6Al4V-Ti6Al4V processadas por brasagem
title_full Caracterização química microestrutural e mecânica de ligações Ti6Al4V-Ti6Al4V processadas por brasagem
title_fullStr Caracterização química microestrutural e mecânica de ligações Ti6Al4V-Ti6Al4V processadas por brasagem
title_full_unstemmed Caracterização química microestrutural e mecânica de ligações Ti6Al4V-Ti6Al4V processadas por brasagem
title_sort Caracterização química microestrutural e mecânica de ligações Ti6Al4V-Ti6Al4V processadas por brasagem
author Gomes, Luís Mendes
author_facet Gomes, Luís Mendes
author_role author
dc.contributor.none.fl_str_mv Guedes, A.
Universidade do Minho
dc.contributor.author.fl_str_mv Gomes, Luís Mendes
dc.subject.por.fl_str_mv Engenharia e Tecnologia::Engenharia Mecânica
topic Engenharia e Tecnologia::Engenharia Mecânica
description Dissertação de mestrado integrado em Engenharia de Materiais
publishDate 2015
dc.date.none.fl_str_mv 2015
2015-01-01T00:00:00Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/1822/39552
url http://hdl.handle.net/1822/39552
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799133047007739904

Registros relacionados