Corrosion resistance of diamond-like carbon coated rotary endodontic instruments - pilot study

Detalhes bibliográficos
Autor(a) principal: Caetano, Diogo Alexandre Santos
Data de Publicação: 2018
Tipo de documento: Dissertação
Idioma: eng
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/10316/81789
Resumo: Trabalho Final do Mestrado Integrado em Medicina Dentária apresentado à Faculdade de Medicina
id RCAP_e4105cdc70bfcdecebdc1363b947acbd
oai_identifier_str oai:estudogeral.uc.pt:10316/81789
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Corrosion resistance of diamond-like carbon coated rotary endodontic instruments - pilot studyResistência à corrosão de limas endodônticas mecanizadas revestidas com diamond-like carbon - estudo pilotofadiga cíclicalimas endodônticas mecanizadasníquel-titânioresistência à corrosãorevestimento DLCcorrosion resistancecyclic fatigueDLC coatingengine-driven endodontic filesnickel-titaniumTrabalho Final do Mestrado Integrado em Medicina Dentária apresentado à Faculdade de MedicinaObjetivo: Este estudo pretende avaliar se um revestimento de diamond-like carbon em limas endodônticas mecanizadas de Níquel-Titânio (Hyflex CM, Hyflex EDM and Reciproc Blue) tem um efeito protetor da superfície contra corrosão por contacto com hipoclorito de sódio (NaOCl).Materiais e métodos: Um total de 12 limas foram divididas em 6 grupos: 2 limas Hyflex CM, 2 Hyflex EDM, 2 Reciproc Blue, 2 Hyflex CM com revestimento DLC, 2 Hyflex EDM com revestimento DLC e 2 Reciproc Blue com revestimento DLC. Uma lima de cada grupo foi sujeita a dois protocolos de imersão em NaOCl com análise de superfície através de microscopia eletrónica de varrimento realizada após o primeiro e previamente ao segundo protocolo. A segunda lima do grupo foi mantida tal como fornecida pelo fabricante. No primeiro protocolo de imersão, cada lima foi dinamicamente imersa durante 5 minutos em 4 ml de hipoclorito a 6% e a uma temperatura de 37ºC. De seguida, a lima foi retirada e dinamicamente imersa em água destilada durante 1 minuto, com secagem posterior. Após a análise de superfície, as limas foram sujeitas ao segundo protocolo de imersão, no qual foram imersas em hipoclorito a 6% e retiradas imediatamente a seguir. Posteriormente, foram colocadas num suporte sem qualquer manipulação durante 1 hora, após a qual foram lavadas com água destilada e posterior secagem. Todas as limas foram novamente analisadas através de microscopia eletrónica de varrimento. Adicionalmente, duas limas (Hyflex EDM com e sem revestimento DLC) foram sujeitas a fadiga cíclica num dispositivo especificamente desenvolvido para o efeito.Resultados: A lima Hyflex CM mostrou uma textura de superfície uniforme com marcas de maquinação visíveis, tendo essa textura sido mantida após o revestimento de superfície com DLC. Após o segundo protocolo de imersão, a lima deste sistema com revestimento mostrou perda de DLC na superfície de corte da mesma. Relativamente ao sistema Hyflex EDM, a distinção mais notável foi uma suavização do relevo na porção interna da hélice das limas após o revestimento. A análise de superfície do sistema Reciproc Blue mostrou uma textura de superfície uniforme com máquinas de maquinação, tendo também o relevo da superfície sido mantido após a adição do revestimento de DLC, tendo este também demostrado sinais de resistência aos protocolos de imersão em hipoclorito visto não se ter verificado perdas de material em nenhuma das observações. O teste de resistência à fadiga cíclica revelou sinais de desgaste na aresta de corte da lima do sistema Hyflex EDM sem revestimento e perda significativa de material de revestimento na porção interna da hélice da lima revestida, ainda que a aresta de corte permanecesse mais integra (também esta com perda de material de revestimento).Conclusões: Os resultados do presente estudo sugerem que não se verifica uma diferença apreciável entre limas revestidas e não revestidas com diamond-like carbon no que concerne à resistência à corrosão decorrente do contacto destes instrumentos com hipoclorito de sódio.Aim: The purpose of this study was to determine if a diamond-like carbon (DLC) coating in NiTi alloy engine-driven endodontic files (Hyflex CM, Hyflex EDM and Reciproc Blue) can protect the surface against sodium hypochlorite (NaOCl) driven corrosion.Materials and Methods: A total of 12 files were split in six groups: 2 Hyflex CM files (size 25, .06 taper, 25 mm), 2 Hyflex EDM files (size 25/~ OneFile, 25mm), 2 Reciproc Blue files, 2 Hyflex CM (size 25, .06 taper, 25 mm) files with DLC coating, 2 Hyflex EDM files (size 25/~ OneFile, 25mm) with DLC coating and 2 Reciproc Blue files with DLC coating. One file from each group was subject to two NaOCl immersion protocols, with surface analysis performed in between through scanning electron microscopy (SEM), and the other was left untouched as received by the company. In the first experimental NaOCl protocol, files were dynamically immersed for 5 minutes in 4 ml of 6% sodium hypochlorite solution at 37 ºC. Subsequently, files were immediately submitted to dynamic immersion in distilled water for 1 minute and air dried. Following SEM, in a second immersion protocol, the previously immersed files were briefly immersed in 4 ml of 6% sodium hypochlorite solution, immediately removed, and left untouched for 1 hour, after which all files were rinsed with distilled water and air dried. All files were observed in SEM. Additionally, two files (Hyflex EDM with and without DLC coating) were submitted to cyclic fatigue in a specifically developed device.Results: Uncoated Hyflex CM file showed a uniform texture with machining grooves, preserved after coating, and loss of DLC coating material on the cutting edge of the instrument after the second immersion protocol, while with the Hyflex EDM system the main noticeable change was in the coated EDM file which revealed a less pronounced texture, with the pits, pores and voids in the inner section of the coil having a smoother relief. Surface analysis of uncoated Reciproc Blue revealed a uniform texture with machining grooves, also preserved by DLC coating, and no signs of failure to resist the immersion protocol in both observations. Cyclic fatigue resistance testing showed signs of wear on the cutting edge of the Hyflex EDM uncoated instrument and extensive loss of coating on the inner section of the coil of the DLC coated file with the edge appearing to be better preserved in the latter.Conclusions: Our findings suggest there’s no difference concerning sodium hypochlorite driven corrosion resistance among files with diamond-like carbon coating or in its original surface.2018-07-23info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesishttp://hdl.handle.net/10316/81789http://hdl.handle.net/10316/81789TID:202049949engCaetano, Diogo Alexandre Santosinfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2019-09-17T14:45:21Zoai:estudogeral.uc.pt:10316/81789Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T21:03:49.341363Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Corrosion resistance of diamond-like carbon coated rotary endodontic instruments - pilot study
Resistência à corrosão de limas endodônticas mecanizadas revestidas com diamond-like carbon - estudo piloto
title Corrosion resistance of diamond-like carbon coated rotary endodontic instruments - pilot study
spellingShingle Corrosion resistance of diamond-like carbon coated rotary endodontic instruments - pilot study
Caetano, Diogo Alexandre Santos
fadiga cíclica
limas endodônticas mecanizadas
níquel-titânio
resistência à corrosão
revestimento DLC
corrosion resistance
cyclic fatigue
DLC coating
engine-driven endodontic files
nickel-titanium
title_short Corrosion resistance of diamond-like carbon coated rotary endodontic instruments - pilot study
title_full Corrosion resistance of diamond-like carbon coated rotary endodontic instruments - pilot study
title_fullStr Corrosion resistance of diamond-like carbon coated rotary endodontic instruments - pilot study
title_full_unstemmed Corrosion resistance of diamond-like carbon coated rotary endodontic instruments - pilot study
title_sort Corrosion resistance of diamond-like carbon coated rotary endodontic instruments - pilot study
author Caetano, Diogo Alexandre Santos
author_facet Caetano, Diogo Alexandre Santos
author_role author
dc.contributor.author.fl_str_mv Caetano, Diogo Alexandre Santos
dc.subject.por.fl_str_mv fadiga cíclica
limas endodônticas mecanizadas
níquel-titânio
resistência à corrosão
revestimento DLC
corrosion resistance
cyclic fatigue
DLC coating
engine-driven endodontic files
nickel-titanium
topic fadiga cíclica
limas endodônticas mecanizadas
níquel-titânio
resistência à corrosão
revestimento DLC
corrosion resistance
cyclic fatigue
DLC coating
engine-driven endodontic files
nickel-titanium
description Trabalho Final do Mestrado Integrado em Medicina Dentária apresentado à Faculdade de Medicina
publishDate 2018
dc.date.none.fl_str_mv 2018-07-23
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/10316/81789
http://hdl.handle.net/10316/81789
TID:202049949
url http://hdl.handle.net/10316/81789
identifier_str_mv TID:202049949
dc.language.iso.fl_str_mv eng
language eng
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799133931508858880

Registros relacionados