Monitoring the early stiffness development in epoxy adhesives for structural strengthening

• Autor(a) principal: Granja, José Luís Duarte
• Data de Publicação: 2015
• Outros Autores: Fernandes, Pedro Miguel Gomes, Benedetti, Andrea, Azenha, Miguel, Sena-Cruz, José
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
• Texto Completo: http://hdl.handle.net/1822/38153
• topic: Epoxy/epoxides; Non-destructive testing; Cure/hardening; Elastic modulus; Cyclic tensile test; Epoxylepoxides; A. Epoxy/epoxides; C. Non-destructive testing; D. Cure/hardening; D. Elastic modulus; Engenharia e Tecnologia::Engenharia Civil; Science & Technology

The present work aimed to assess the early-age evolution of E-modulus of epoxy adhesives used for Fibre-Reinforced Polymer (FRP) strengthening applications. The study involved adapting an existing technique devised for continuous monitoring of concrete stiffness since casting, called EMM-ARM (Elasticity Modulus Monitoring through Ambient Response Method) for evaluation of epoxy stiffness. Furthermore, monotonic tensile tests according to ISO standards and cyclic tensile tests were carried out at several ages. A comparison between the obtained results was performed in order to better understand the performance of the several techniques in the assessment of stiffness of epoxy resins. When compared to the other methodologies, the method for calculation of E-modulus recommended by ISO standard led to lower values, since in the considered strain interval, the adhesive had a non-linear stress-strain relationship. The EMM-ARM technique revealed its capability in clearly identifying the hardening kinetics of epoxy adhesives, measuring the material stiffness growth during the entire curing period. At very early ages the values of Young's modulus obtained with quasi-static tests were lower than the values collected by EMM-ARM, due to the fact that epoxy resin exhibited a significant visco-elastic behaviour.