Effect of neutralization and cross-linking on the thermal degradation of chitosan electrospun membranes

• Autor(a) principal: Correia, D. M.
• Data de Publicação: 2014
• Outros Autores: Gámiz- González, M. A., Botelho, G., Vidaurre, A., Gomez Ribelles, J. L., Lanceros-Mendez, S., Sencadas, V.
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
• Texto Completo: http://hdl.handle.net/11110/635
• topic: Chitosan; Electrospun membranes; Thermal degradation kinetics; Activation energy; Cross-linking

Thermal degradation of as electrospun chitosan membranes and samples subsequently treated with ethanol and cross-linked with glutaraldehyde (GA) have been studied by thermogravimetry (TG) coupled with an infrared spectrometer (FTIR). The influence of the electrospinning process and cross-linking in the electrospun chitosan thermal stability was evaluated. Up to three degradation steps were observed in the TG data, corresponding to water dehydration reaction at temperatures below 100 ºC, loss of side groups formed between the amine groups of chitosan and trifluoroacetic acid between 150 – 270 ºC and chitosan thermal degradation that starts around 250 ºC and goes up to 400 ºC. The Kissinger model was employed to evaluate the activation energies of the electrospun membranes during isothermal experiments and revealed that thermal degradation activation energy increases for the samples processed by electrospinning and subsequent neutralization and cross-linking treatments with respect to the neat chitosan powder.