Reologia de misturas cimentícias com incorporação de superplastificante
Autor(a) principal: | |
---|---|
Data de Publicação: | 2013 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
Texto Completo: | http://hdl.handle.net/1822/30693 |
Resumo: | Dissertação de mestrado integrado em Engenharia Civil (área de especialização em Perfil de Construções) |
id |
RCAP_ebea6e4dc84bf1fa68d34ee48fe3b03a |
---|---|
oai_identifier_str |
oai:repositorium.sdum.uminho.pt:1822/30693 |
network_acronym_str |
RCAP |
network_name_str |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
repository_id_str |
7160 |
spelling |
Reologia de misturas cimentícias com incorporação de superplastificanteRheology of cementitious mixtures incorporating superplasticizer691.32666.94Engenharia e Tecnologia::Engenharia CivilDissertação de mestrado integrado em Engenharia Civil (área de especialização em Perfil de Construções)Na atualidade encontram-se, cada vez mais, edifícios com especificações e caraterísticas exigentes, sendo por isso, necessário a satisfação das mesmas. Uma das especificações é a diminuição da razão Água/Ligante que proporciona um melhor desempenho em betões, no estado endurecido. Mas, o que, por um lado, é favorável, torna-se num problema, pois faz diminuir consideravelmente a sua trabalhabilidade, afetando substancialmente a colocação em obra. Por isso são utilizados adjuvantes que permitem reduzir a razão Água/Ligante mantendo níveis adequados de trabalhabilidade e fluidez. No decorrer da dissertação será realizado um estudo em pastas cimentícias, com o objetivo de contribuir para o esclarecimento de várias questões relacionadas com a adição de superplastificantes no que diz respeito à reologia no estado fresco. As principais questões levantadas foram: A quantidade de superplastificante deve ser referida ao conteúdo total de ligante ou apenas ao do cimento? Será a ação do superplastificante mais eficaz em matrizes de cimentos ou em matrizes cimentícias contendo adições minerais? Como se processa a perda de trabalhabilidade ao longo do tempo das misturas cimentícias com superplastificante? Será a presença das adições minerais vantajosas relativamente a este aspeto? Qual o efeito da temperatura na reologia das misturas cimentícias? Neste contexto, é necessário compreender e estudar a ação do superplastificante e a sua compatibilidade com a matriz cimentícia, assim como com as adições minerais, que cada vez mais são utilizadas na produção de betões, tal como as cinzas volantes e o fíler calcário. Para tal foi realizada uma campanha experimental, que permitiu esclarecer as várias questões levantadas. A campanha experimental foi composta por vária fazes, submetendo as pastas a várias temperaturas com o intuito de tenter perceber o seu comportamento. Para tal, foram realizados os ensaios de Conde de Marsh, Mini-abaixamento e Viscosímetro de Brookfield Da campanha efetuada foi possível obter algumas conclusões, assim como levantar ainda mais questões sobre o tema abordado. Uma das principais conclusões retiradas foi, que a percentagem de superplastificante a utilizar deverá ser um compromisso entre os dois constituintes do ligante.At present, there are more and more buildings with demanding specifications and characteristics, so it is necessary to satisfy these needs. One of the specifications is the decrease of the water/binder ratio which provides a better concrete performance, in its hardened state. What, on one hand, is favorable becomes a problem, as it considerably lowers the workability, substantially affecting its placement on-site. Therefore, admixtures are used to reduce the water/binder ratio, maintaining adequate levels of workability and fluidity. Throughout this dissertation, the study of cement pastes was conducted, aiming to contribute to the clarification of several issues related to the addition of superplasticizers with respect to the rheology in its fresh state. The main issues raised were: Should the amount of superplasticizer be referred to the total content of the binder or merely the cement? Will the action of superplasticizer be most effective in cement matrices or in cementitious matrices containing mineral additions? How is the workability loss over time of the cementitious mixtures superplasticizer processed? Is the presence of mineral additions advantageous with regard to this aspect? What is the effect of temperature on the rheology of cementitious mixes? In this context, it is necessary to understand and study the action of the superplasticizer and its compatibility with the cementitious matrix, as well as mineral additions, such as fly ash and limestone fillers, which are increasingly used in the production of concrete. To this end, an experimental campaign was carried out, explaining the various issues previously mentioned. The experimental campaign was made up of various stages, subjecting the pastes to various temperatures in order to better understand their behavior. For this, the Marsh cone test, Mini-cone test and Brookfield viscometer tests were performed. Based on the experimentation, a few conclusions were drawn, as well as further questions about the topic. One of the main conclusions drawn was that the percentage of superplasticizer to be used should be a compromise between the two components of the binder.Camões, AiresUniversidade do MinhoMendes, Carla Sofia Fernandes20132013-01-01T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfhttp://hdl.handle.net/1822/30693por201186675info:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-07-21T12:39:49Zoai:repositorium.sdum.uminho.pt:1822/30693Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T19:36:29.873681Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse |
dc.title.none.fl_str_mv |
Reologia de misturas cimentícias com incorporação de superplastificante Rheology of cementitious mixtures incorporating superplasticizer |
title |
Reologia de misturas cimentícias com incorporação de superplastificante |
spellingShingle |
Reologia de misturas cimentícias com incorporação de superplastificante Mendes, Carla Sofia Fernandes 691.32 666.94 Engenharia e Tecnologia::Engenharia Civil |
title_short |
Reologia de misturas cimentícias com incorporação de superplastificante |
title_full |
Reologia de misturas cimentícias com incorporação de superplastificante |
title_fullStr |
Reologia de misturas cimentícias com incorporação de superplastificante |
title_full_unstemmed |
Reologia de misturas cimentícias com incorporação de superplastificante |
title_sort |
Reologia de misturas cimentícias com incorporação de superplastificante |
author |
Mendes, Carla Sofia Fernandes |
author_facet |
Mendes, Carla Sofia Fernandes |
author_role |
author |
dc.contributor.none.fl_str_mv |
Camões, Aires Universidade do Minho |
dc.contributor.author.fl_str_mv |
Mendes, Carla Sofia Fernandes |
dc.subject.por.fl_str_mv |
691.32 666.94 Engenharia e Tecnologia::Engenharia Civil |
topic |
691.32 666.94 Engenharia e Tecnologia::Engenharia Civil |
description |
Dissertação de mestrado integrado em Engenharia Civil (área de especialização em Perfil de Construções) |
publishDate |
2013 |
dc.date.none.fl_str_mv |
2013 2013-01-01T00:00:00Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://hdl.handle.net/1822/30693 |
url |
http://hdl.handle.net/1822/30693 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.none.fl_str_mv |
201186675 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.source.none.fl_str_mv |
reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação instacron:RCAAP |
instname_str |
Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação |
instacron_str |
RCAAP |
institution |
RCAAP |
reponame_str |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
collection |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
repository.name.fl_str_mv |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação |
repository.mail.fl_str_mv |
|
_version_ |
1799132895263064064 |