Characterization of Hybrid Sol-gel Coatings Applied over Tinplate

Detalhes bibliográficos
Autor(a) principal: Álvarez,D.
Data de Publicação: 2013
Outros Autores: Collazo,A., Pérez,C.
Tipo de documento: Artigo
Idioma: eng
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042013000500003
Resumo: The present work studies the behavior of hybrid sol-gel films based on tetraethyl orthosilicate (TEOS) and vinyltrimethylsiloxane (VTMS) precursors applied over commercial tinplate. In previous works VTMS films obtained by the sol-gel technology were tested to verify their good corrosion performance over short immersion times in a citric acid/sodium citrate buffer solution. However, at longer exposure times the high porosity inherent to organic sol-gel films allows the aggressive media to reach the metallic substrate and start the corrosion process. In order to overcome these limitations, hybrid organic-inorganic sol-gel coatings were obtained using the dip- coating method. This work also studies the influence of the ageing time of the hybrid sol-gel in the formation of a uniform and continuous film. The obtained layers were characterized using a Scanning Electron Microscopy (SEM) and mechanical profilometry. The corrosion performance in organic acid media was tested using polarization curves and Electrochemical Impedance Spectroscopy (EIS) with a 0.1M citric/citrate buffer solution as electrolyte. The results obtained suggest that a minimum ageing time of 10 days is needed to obtain uniform films. The electrochemical measurements indicate a clear improvement on the barrier properties on the hybrid sol-gel compared to the organic ones. A major decrease in the impedance values after 24 hours of immersion indicates that it is necessary to improve the long-term barrier properties to achieve an industrial application.
id RCAP_ee5d1e5c10b6c2d9ef23d12813d6c239
oai_identifier_str oai:scielo:S0872-19042013000500003
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Characterization of Hybrid Sol-gel Coatings Applied over TinplateSol-geltinplatecitric/citrateEISequivalent circuitThe present work studies the behavior of hybrid sol-gel films based on tetraethyl orthosilicate (TEOS) and vinyltrimethylsiloxane (VTMS) precursors applied over commercial tinplate. In previous works VTMS films obtained by the sol-gel technology were tested to verify their good corrosion performance over short immersion times in a citric acid/sodium citrate buffer solution. However, at longer exposure times the high porosity inherent to organic sol-gel films allows the aggressive media to reach the metallic substrate and start the corrosion process. In order to overcome these limitations, hybrid organic-inorganic sol-gel coatings were obtained using the dip- coating method. This work also studies the influence of the ageing time of the hybrid sol-gel in the formation of a uniform and continuous film. The obtained layers were characterized using a Scanning Electron Microscopy (SEM) and mechanical profilometry. The corrosion performance in organic acid media was tested using polarization curves and Electrochemical Impedance Spectroscopy (EIS) with a 0.1M citric/citrate buffer solution as electrolyte. The results obtained suggest that a minimum ageing time of 10 days is needed to obtain uniform films. The electrochemical measurements indicate a clear improvement on the barrier properties on the hybrid sol-gel compared to the organic ones. A major decrease in the impedance values after 24 hours of immersion indicates that it is necessary to improve the long-term barrier properties to achieve an industrial application.Sociedade Portuguesa de Electroquímica2013-10-01info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/articletext/htmlhttp://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042013000500003Portugaliae Electrochimica Acta v.31 n.5 2013reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAPenghttp://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042013000500003Álvarez,D.Collazo,A.Pérez,C.info:eu-repo/semantics/openAccess2024-02-06T17:07:14Zoai:scielo:S0872-19042013000500003Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-20T02:20:14.523936Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Characterization of Hybrid Sol-gel Coatings Applied over Tinplate
title Characterization of Hybrid Sol-gel Coatings Applied over Tinplate
spellingShingle Characterization of Hybrid Sol-gel Coatings Applied over Tinplate
Álvarez,D.
Sol-gel
tinplate
citric/citrate
EIS
equivalent circuit
title_short Characterization of Hybrid Sol-gel Coatings Applied over Tinplate
title_full Characterization of Hybrid Sol-gel Coatings Applied over Tinplate
title_fullStr Characterization of Hybrid Sol-gel Coatings Applied over Tinplate
title_full_unstemmed Characterization of Hybrid Sol-gel Coatings Applied over Tinplate
title_sort Characterization of Hybrid Sol-gel Coatings Applied over Tinplate
author Álvarez,D.
author_facet Álvarez,D.
Collazo,A.
Pérez,C.
author_role author
author2 Collazo,A.
Pérez,C.
author2_role author
author
dc.contributor.author.fl_str_mv Álvarez,D.
Collazo,A.
Pérez,C.
dc.subject.por.fl_str_mv Sol-gel
tinplate
citric/citrate
EIS
equivalent circuit
topic Sol-gel
tinplate
citric/citrate
EIS
equivalent circuit
description The present work studies the behavior of hybrid sol-gel films based on tetraethyl orthosilicate (TEOS) and vinyltrimethylsiloxane (VTMS) precursors applied over commercial tinplate. In previous works VTMS films obtained by the sol-gel technology were tested to verify their good corrosion performance over short immersion times in a citric acid/sodium citrate buffer solution. However, at longer exposure times the high porosity inherent to organic sol-gel films allows the aggressive media to reach the metallic substrate and start the corrosion process. In order to overcome these limitations, hybrid organic-inorganic sol-gel coatings were obtained using the dip- coating method. This work also studies the influence of the ageing time of the hybrid sol-gel in the formation of a uniform and continuous film. The obtained layers were characterized using a Scanning Electron Microscopy (SEM) and mechanical profilometry. The corrosion performance in organic acid media was tested using polarization curves and Electrochemical Impedance Spectroscopy (EIS) with a 0.1M citric/citrate buffer solution as electrolyte. The results obtained suggest that a minimum ageing time of 10 days is needed to obtain uniform films. The electrochemical measurements indicate a clear improvement on the barrier properties on the hybrid sol-gel compared to the organic ones. A major decrease in the impedance values after 24 hours of immersion indicates that it is necessary to improve the long-term barrier properties to achieve an industrial application.
publishDate 2013
dc.date.none.fl_str_mv 2013-10-01
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/article
format article
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042013000500003
url http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042013000500003
dc.language.iso.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042013000500003
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv text/html
dc.publisher.none.fl_str_mv Sociedade Portuguesa de Electroquímica
publisher.none.fl_str_mv Sociedade Portuguesa de Electroquímica
dc.source.none.fl_str_mv Portugaliae Electrochimica Acta v.31 n.5 2013
reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799137291010048000