Estudo do comportamento tribológico de materiais compósitos à base de titânio reforçado com partículas cerâmicas para aplicação em implantes articulares

Detalhes bibliográficos
Autor(a) principal: Barbosa, Virgínia Leonor Mendes
Data de Publicação: 2015
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/1822/39618
Resumo: Dissertação de mestrado integrado em Engenharia Biomédica
id RCAP_ef440a21117d02777866f7f89fae67df
oai_identifier_str oai:repositorium.sdum.uminho.pt:1822/39618
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Estudo do comportamento tribológico de materiais compósitos à base de titânio reforçado com partículas cerâmicas para aplicação em implantes articularesStudy of the tribological behaviour of composite materials based on titanium reinforced with ceramic particles for joint implants aplicationBiotribologia,Próteses articularesCompósitosAtritoDesgasteBiotribologyArticular prosthesesCompositesFrictionWearEngenharia e Tecnologia::Engenharia MecânicaDissertação de mestrado integrado em Engenharia BiomédicaA necessidade de materiais com propriedades semelhantes às das articulações humanas leva ao surgimento de novas alternativas no que diz respeito a materiais para próteses. O grande problema dos materiais existentes prende-se com o facto de apresentarem diferentes mas persistentes fraquezas. A oferta de materiais é variada e, como tal, cada um apresenta os seus prós e contras. Os principais problemas centram-se na propensão para a fratura, desgaste e consequentes partículas de desgaste que podem causar complicações oncológicas, sendo que todos estes aspetos devem ser contornados. O presente trabalho teve como principal objetivo a caracterização tribológica de materiais metálicos e compósitos de matriz metálica reforçados com partículas cerâmicas de alumina de diferente geometria e condição superficial recorrendo à avaliação das suas propriedades de atrito e de desgaste, tendo este estudo sido complementado com a realização de testes de dureza Vickers. Os materiais considerados foram processados no âmbito do projeto de investigação em que o presente estudo se enquadra e os testes tribológicos de deslizamento linear alternativo foram realizados num tribómetro com a configuração esfera-placa à temperatura de 37 ⁰C ± 1 ⁰C. Como contra corpo foi utilizada uma esfera de alumina e o deslizamento decorreu na presença de uma solução salina (PBS). A frequência de oscilação foi de 1 Hz e, a carga normal aplicada variou, tendo assumindo os valores de 3, 9, 15 e 25 N. Procedeu-se à quantificação do coeficiente de atrito e do coeficiente de desgaste para todos os testes, bem como à análise dos mecanismos de desgaste através de microscopia eletrónica de varrimento. Feita a análise dos resultados obtidos, concluiu-se que dos compósitos testados apenas um, correspondente ao reforço com partículas não revestidas e de forma irregular, apresentou valores de resistência ao desgaste superiores ao material de referência (liga Ti6Al4V) nos testes sujeitos a 3 N. Assim, de um modo geral, a adição à liga Ti6Al4V de partículas de reforço de alumina no estado superficial e forma tal como foram consideradas no presente estudo, não trouxe melhorias em termos de comportamento tribológico do compósito, tanto a nível de atrito como de desgaste. Este resultado foi atribuído à má adesão entre as partículas cerâmicas e o material da liga metálica da matriz. Contudo, a melhoria da resistência ao desgaste dos compósitos para uma condição particular de processamento e de teste, desperta interesse pela continuação da investigação iniciada no presente estudo em torno deste tipo de materiais.The need for materials with similar properties to the human joints leads to the emergence of new alternatives to materials for prostheses. The biggest problem with materials that already exist is related with the fact that they have different but persistent weaknesses. The material offer is varied and all of them have its pros and cons. Most serious issues are related to the propensity to fracture, wear and its consequents particles that can cause oncological complications, these are all issues to overcome. The aim goal of this study consisted in the tribological characterization of metallic and composite materials based on a metallic matrix reinforced with ceramic particles by assessment of its friction and wear properties, this study has been completed with Vickers hardness tests. The materials considered were processed under the investigation project where the current study fits and the tribological tests with reciprocating sliding were performed in a tribometer with a ball on plate configuration, under a physiological temperature 37 ⁰C ± 1 ⁰C. As a counter body, an alumina ball was used and the sliding occured in the presence of a saline solution (PBS). Reciprocating motion frequency was 1 Hz and applied normal loads varying between 3, 9, 15 and 25 N were used. The next procedure was to quantify the friction coefficient and wear coefficient for all tests and the analysis of wear mechanisms through scanning electron microscopy. After the analysis of the obtained results was realized, it was concluded for all composites tested, that only one, which corresponds to the reinforcement with uncoated particles and irregular shape, presents wear resistance values higher than reference material (Ti6Al4V) on tests subjected to 3 N. Thus, in general, the addition to titanium matrix with ceramic reinforcement particles with superficial and shape states, just like has been considered on present study does not bring improvement in terms of composite tribological behaviour, which includes friction and wear. This result was attributed to poor adhesion of the ceramic particles and metallic matrix. However, the improvement of composite wear resistance for a particular processing and test condition, arouses interest for the continuation of research initiated in the present study surrounding this type of material.Fundação para a Ciência e Tecnologia (FCT) - Projetos EXCL/EMS-TEC/0460/2012 e UID/EEA/04436/2013Gomes, J. R.Flores, PauloUniversidade do MinhoBarbosa, Virgínia Leonor Mendes20152015-01-01T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfhttp://hdl.handle.net/1822/39618porinfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-07-21T12:05:35Zoai:repositorium.sdum.uminho.pt:1822/39618Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T18:56:02.555484Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Estudo do comportamento tribológico de materiais compósitos à base de titânio reforçado com partículas cerâmicas para aplicação em implantes articulares
Study of the tribological behaviour of composite materials based on titanium reinforced with ceramic particles for joint implants aplication
title Estudo do comportamento tribológico de materiais compósitos à base de titânio reforçado com partículas cerâmicas para aplicação em implantes articulares
spellingShingle Estudo do comportamento tribológico de materiais compósitos à base de titânio reforçado com partículas cerâmicas para aplicação em implantes articulares
Barbosa, Virgínia Leonor Mendes
Biotribologia,
Próteses articulares
Compósitos
Atrito
Desgaste
Biotribology
Articular prostheses
Composites
Friction
Wear
Engenharia e Tecnologia::Engenharia Mecânica
title_short Estudo do comportamento tribológico de materiais compósitos à base de titânio reforçado com partículas cerâmicas para aplicação em implantes articulares
title_full Estudo do comportamento tribológico de materiais compósitos à base de titânio reforçado com partículas cerâmicas para aplicação em implantes articulares
title_fullStr Estudo do comportamento tribológico de materiais compósitos à base de titânio reforçado com partículas cerâmicas para aplicação em implantes articulares
title_full_unstemmed Estudo do comportamento tribológico de materiais compósitos à base de titânio reforçado com partículas cerâmicas para aplicação em implantes articulares
title_sort Estudo do comportamento tribológico de materiais compósitos à base de titânio reforçado com partículas cerâmicas para aplicação em implantes articulares
author Barbosa, Virgínia Leonor Mendes
author_facet Barbosa, Virgínia Leonor Mendes
author_role author
dc.contributor.none.fl_str_mv Gomes, J. R.
Flores, Paulo
Universidade do Minho
dc.contributor.author.fl_str_mv Barbosa, Virgínia Leonor Mendes
dc.subject.por.fl_str_mv Biotribologia,
Próteses articulares
Compósitos
Atrito
Desgaste
Biotribology
Articular prostheses
Composites
Friction
Wear
Engenharia e Tecnologia::Engenharia Mecânica
topic Biotribologia,
Próteses articulares
Compósitos
Atrito
Desgaste
Biotribology
Articular prostheses
Composites
Friction
Wear
Engenharia e Tecnologia::Engenharia Mecânica
description Dissertação de mestrado integrado em Engenharia Biomédica
publishDate 2015
dc.date.none.fl_str_mv 2015
2015-01-01T00:00:00Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/1822/39618
url http://hdl.handle.net/1822/39618
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799132347070676992

Registros relacionados