Estudo da corrosividade de materiais metálicos em ambientes de envelhecimento acelerado

Detalhes bibliográficos
Autor(a) principal: Ferreira, Frederico Miguel Metelo
Data de Publicação: 2018
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/10451/36865
Resumo: Tese de mestrado em Química Tecnológica, Universidade de Lisboa, Faculdade de Ciências, 2018
id RCAP_f879f8316bdf0367b49e084741104085
oai_identifier_str oai:repositorio.ul.pt:10451/36865
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Estudo da corrosividade de materiais metálicos em ambientes de envelhecimento aceleradoAçoCobreZincoAlumínioEnsaios de envelhecimento aceleradoVelocidade de corrosãoSEMXRDTeses de mestrado - 2018Domínio/Área Científica::Ciências Naturais::Ciências QuímicasTese de mestrado em Química Tecnológica, Universidade de Lisboa, Faculdade de Ciências, 2018A corrosão é, segundo a definição da IUPAC, uma reação interfacial irreversível de um material com o seu meio ambiente que resulta no consumo do material ou na dissolução de um componente do meio ambiente no seio do material. À corrosão/degradação estão associados prejuízos económicos e riscos que põem em causa a segurança de infraestruturas de aplicação doméstica e industrial. É assim da maior importância o estudo e a proteção dos materiais contra o fenómeno da corrosão. O presente trabalho, teve como objetivo determinar as velocidades de corrosão dos materiais aço, cobre, zinco e alumínio, bem como os produtos de corrosão que se formaram após exposição desses materiais a ambientes de envelhecimento acelerado com diferentes contaminantes, permitindo desta forma conhecer, comparativamente, a sua corrosividade e selecionar os ensaios mais adequados para avaliação da proteção anticorrosiva de diferentes estruturas metálicas usadas para diferentes fins. A avaliação da velocidade de corrosão nos diferentes ambientes foi efetuada com base no método gravimétrico, tendo sido selecionados seis ensaios de envelhecimento acelerado com base em metodologias normativas internacionais (normas ISO), tendo em conta a sua extensa aplicação industrial. A caracterização dos produtos de corrosão formados realizou-se recorrendo a técnicas de microscopia eletrónica de varrimento (SEM) e de difração de raios-X (XRD) nos quatro ensaios considerados mais relevantes. Na análise da velocidade de corrosão, o ensaio que conduziu a valores mais altos foi o de exposição ao SO2. O ensaio que conduziu a valores mais baixos de velocidade de corrosão para todos os materiais foi o de exposição cíclica à radiação ultravioleta (UV)/condensação. A comparação das velocidades de corrosão nos ensaios de envelhecimento acelerado com as da exposição natural em duas estações com ambientes diferentes (urbano no Lumiar/Lisboa e marítimo/industrial em Sines) permitiu verificar que globalmente o ensaio de exposição ao SO2 é o ensaio que mais se assemelha ao ambiente destas estações. A análise por SEM/EDS revelou a presença de produtos de corrosão com morfologias muito distintas, principalmente para o aço e o zinco. No caso do alumínio, os produtos de corrosão formam uma camada uniforme fraturada na superfície dos provetes. No entanto, após o ensaio de exposição ao nevoeiro salino neutro, SO2 e NO2 parece existir corrosão localizada, provavelmente corrosão por picadas. Os resultados da interpretação dos difratogramas de XRD, com exceção do verificado nos resultados da Estação do Lumiar/Lisboa para o cobre e alumínio, revelam que os produtos de corrosão formados nos ensaios de envelhecimento acelerado diferem na composição química dos formados após os ensaios de envelhecimento natural.Corrosion is, according to the IUPAC definition, an irreversible interfacial reaction of a material with its environment which results in the consumption of the material or in the dissolution of a component of the environment into the material. Corrosion/degradation is associated with economic losses and risks that threaten the safety of domestic and industrial infrastructures. In this sense, it is of the utmost importance to study and protect materials against corrosion. The aim of this work was to determine the corrosion rate of steel, copper, zinc and aluminum and the corrosion products that were formed after exposure to accelerated aging environments with different contaminants. This will ultimately allow the knowledge of the corrosiveness for each material by comparison with the others and, thus, to select the most appropriate tests to evaluate the anticorrosive protection of different material structures used for different purposes. The evaluation of the corrosion rate in the different environments was based on the gravimetric method, and six accelerated aging tests were selected based on international standardized methodologies (ISO standards), taking into account their extensive industrial application. The characterization of the corrosion products was performed by using scanning electron microscopy (SEM) and X-ray diffraction (XRD) techniques in the four tests which were considered the most relevant. In the analysis of the corrosion rate, the test leading to the highest rate for all materials was the exposure to SO2. The test leading to the lowest corrosion rate for all materials was the cyclic exposure to UV radiation/condensation. The comparison of the corrosion rates in the accelerated aging tests, with those resulting from natural exposure in two outdoor exposure test sites (urban in Lumiar/Lisboa and marine/industrial in Sines) showed that globally the SO2 exposure test is the most similar to the atmospheres of these test sites. SEM/EDS analysis showed the presence of corrosion products with very distinct morphologies, especially in the case of steel and zinc. In the case of aluminum, the corrosion products form a fractured uniform layer on the sample surface. However, after the salt spray, SO2 and NO2 exposure test it seems to exist localized corrosion, probably pitting corrosion. The results from the interpretation of XRD diffractograms, with the exception of the results observed in the Lumiar/Lisboa site for copper and aluminum, revealed that the products formed in the accelerated tests differ in chemical composition from those formed after the natural exposure tests.Diamantino, Teresa CunhaMartins, Filomena,1960-Repositório da Universidade de LisboaFerreira, Frederico Miguel Metelo2019-02-05T16:10:42Z201820182018-01-01T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfhttp://hdl.handle.net/10451/36865TID:202193918porinfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-11-08T16:33:41Zoai:repositorio.ul.pt:10451/36865Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T21:51:01.788382Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Estudo da corrosividade de materiais metálicos em ambientes de envelhecimento acelerado
title Estudo da corrosividade de materiais metálicos em ambientes de envelhecimento acelerado
spellingShingle Estudo da corrosividade de materiais metálicos em ambientes de envelhecimento acelerado
Ferreira, Frederico Miguel Metelo
Aço
Cobre
Zinco
Alumínio
Ensaios de envelhecimento acelerado
Velocidade de corrosão
SEM
XRD
Teses de mestrado - 2018
Domínio/Área Científica::Ciências Naturais::Ciências Químicas
title_short Estudo da corrosividade de materiais metálicos em ambientes de envelhecimento acelerado
title_full Estudo da corrosividade de materiais metálicos em ambientes de envelhecimento acelerado
title_fullStr Estudo da corrosividade de materiais metálicos em ambientes de envelhecimento acelerado
title_full_unstemmed Estudo da corrosividade de materiais metálicos em ambientes de envelhecimento acelerado
title_sort Estudo da corrosividade de materiais metálicos em ambientes de envelhecimento acelerado
author Ferreira, Frederico Miguel Metelo
author_facet Ferreira, Frederico Miguel Metelo
author_role author
dc.contributor.none.fl_str_mv Diamantino, Teresa Cunha
Martins, Filomena,1960-
Repositório da Universidade de Lisboa
dc.contributor.author.fl_str_mv Ferreira, Frederico Miguel Metelo
dc.subject.por.fl_str_mv Aço
Cobre
Zinco
Alumínio
Ensaios de envelhecimento acelerado
Velocidade de corrosão
SEM
XRD
Teses de mestrado - 2018
Domínio/Área Científica::Ciências Naturais::Ciências Químicas
topic Aço
Cobre
Zinco
Alumínio
Ensaios de envelhecimento acelerado
Velocidade de corrosão
SEM
XRD
Teses de mestrado - 2018
Domínio/Área Científica::Ciências Naturais::Ciências Químicas
description Tese de mestrado em Química Tecnológica, Universidade de Lisboa, Faculdade de Ciências, 2018
publishDate 2018
dc.date.none.fl_str_mv 2018
2018
2018-01-01T00:00:00Z
2019-02-05T16:10:42Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/10451/36865
TID:202193918
url http://hdl.handle.net/10451/36865
identifier_str_mv TID:202193918
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799134445699072000

Registros relacionados