Influence of method and period of storage on the microtensile bond strength of indirect composite resin restorations to dentine
Autor(a) principal: | |
---|---|
Data de Publicação: | 2008 |
Outros Autores: | , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Brazilian Oral Research |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242008000400012 |
Resumo: | This study evaluated the influence of the method and period of storage on the adhesive bond strength of indirect composite resin to bovine dentin. Ninety bovine incisors were stored in three different solutions: 0.2% thymol, 10% formalin, and 0.2% sodium azide, during 3 periods of storage: 7 days, 30 days and 6 months, resulting in 9 groups (n = 10). The roots were cut off and the buccal surface was ground with #600-grit silicon carbide paper. The surface was conditioned with 37% phosphoric acid for 15 s and a composite resin restoration (TPH Spectrum) was fixed using a one-bottle adhesive system (Adper Single Bond) and a dual-cured resinous cement (Rely X ARC) under a load of 500 g for 5 minutes. The samples were serially cut perpendicular to the bonded interface to obtain slices of 1.2 mm in thickness. Each slab was trimmed with a cylindrical diamond bur resulting in an hourglass shape with a cross-sectional area of approximately 1 mm². The microtensile bond strength (μTBS) testing was performed in a testing machine (EMIC 2000 DL) at a 0.5 mm/minute crosshead-speed until failure. After fracture, the specimens were examined under SEM to analyze the mode of fracture. μTBS Means were expressed in MPa and the data were analyzed by two-way ANOVA (3X3) and the Tukey test (α = 0.05). The storage times of 7 and 30 days produced no significant difference irrespective of the solution type. The formalin and thymol solutions, however, did have a negative influence on bond strength when the teeth were stored for 6 months. |
id |
SBPQO-1_0ae142044d940a34e94a4c15d4c73d84 |
---|---|
oai_identifier_str |
oai:scielo:S1806-83242008000400012 |
network_acronym_str |
SBPQO-1 |
network_name_str |
Brazilian Oral Research |
repository_id_str |
|
spelling |
Influence of method and period of storage on the microtensile bond strength of indirect composite resin restorations to dentineComposite resinsTensile strengthThymolFormaldehydeSodium azideDentinThis study evaluated the influence of the method and period of storage on the adhesive bond strength of indirect composite resin to bovine dentin. Ninety bovine incisors were stored in three different solutions: 0.2% thymol, 10% formalin, and 0.2% sodium azide, during 3 periods of storage: 7 days, 30 days and 6 months, resulting in 9 groups (n = 10). The roots were cut off and the buccal surface was ground with #600-grit silicon carbide paper. The surface was conditioned with 37% phosphoric acid for 15 s and a composite resin restoration (TPH Spectrum) was fixed using a one-bottle adhesive system (Adper Single Bond) and a dual-cured resinous cement (Rely X ARC) under a load of 500 g for 5 minutes. The samples were serially cut perpendicular to the bonded interface to obtain slices of 1.2 mm in thickness. Each slab was trimmed with a cylindrical diamond bur resulting in an hourglass shape with a cross-sectional area of approximately 1 mm². The microtensile bond strength (μTBS) testing was performed in a testing machine (EMIC 2000 DL) at a 0.5 mm/minute crosshead-speed until failure. After fracture, the specimens were examined under SEM to analyze the mode of fracture. μTBS Means were expressed in MPa and the data were analyzed by two-way ANOVA (3X3) and the Tukey test (α = 0.05). The storage times of 7 and 30 days produced no significant difference irrespective of the solution type. The formalin and thymol solutions, however, did have a negative influence on bond strength when the teeth were stored for 6 months.Sociedade Brasileira de Pesquisa Odontológica - SBPqO2008-12-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242008000400012Brazilian Oral Research v.22 n.4 2008reponame:Brazilian Oral Researchinstname:Sociedade Brasileira de Pesquisa Odontológica (SBPqO)instacron:SBPQO10.1590/S1806-83242008000400012info:eu-repo/semantics/openAccessSantana,Fernanda RibeiroPereira,Janaína CarlaPereira,Cristina AlvesFernandes Neto,Alfredo JúlioSoares,Carlos Joséeng2009-10-20T00:00:00Zoai:scielo:S1806-83242008000400012Revistahttps://www.scielo.br/j/bor/https://old.scielo.br/oai/scielo-oai.phppob@edu.usp.br||bor@sbpqo.org.br1807-31071806-8324opendoar:2009-10-20T00:00Brazilian Oral Research - Sociedade Brasileira de Pesquisa Odontológica (SBPqO)false |
dc.title.none.fl_str_mv |
Influence of method and period of storage on the microtensile bond strength of indirect composite resin restorations to dentine |
title |
Influence of method and period of storage on the microtensile bond strength of indirect composite resin restorations to dentine |
spellingShingle |
Influence of method and period of storage on the microtensile bond strength of indirect composite resin restorations to dentine Santana,Fernanda Ribeiro Composite resins Tensile strength Thymol Formaldehyde Sodium azide Dentin |
title_short |
Influence of method and period of storage on the microtensile bond strength of indirect composite resin restorations to dentine |
title_full |
Influence of method and period of storage on the microtensile bond strength of indirect composite resin restorations to dentine |
title_fullStr |
Influence of method and period of storage on the microtensile bond strength of indirect composite resin restorations to dentine |
title_full_unstemmed |
Influence of method and period of storage on the microtensile bond strength of indirect composite resin restorations to dentine |
title_sort |
Influence of method and period of storage on the microtensile bond strength of indirect composite resin restorations to dentine |
author |
Santana,Fernanda Ribeiro |
author_facet |
Santana,Fernanda Ribeiro Pereira,Janaína Carla Pereira,Cristina Alves Fernandes Neto,Alfredo Júlio Soares,Carlos José |
author_role |
author |
author2 |
Pereira,Janaína Carla Pereira,Cristina Alves Fernandes Neto,Alfredo Júlio Soares,Carlos José |
author2_role |
author author author author |
dc.contributor.author.fl_str_mv |
Santana,Fernanda Ribeiro Pereira,Janaína Carla Pereira,Cristina Alves Fernandes Neto,Alfredo Júlio Soares,Carlos José |
dc.subject.por.fl_str_mv |
Composite resins Tensile strength Thymol Formaldehyde Sodium azide Dentin |
topic |
Composite resins Tensile strength Thymol Formaldehyde Sodium azide Dentin |
description |
This study evaluated the influence of the method and period of storage on the adhesive bond strength of indirect composite resin to bovine dentin. Ninety bovine incisors were stored in three different solutions: 0.2% thymol, 10% formalin, and 0.2% sodium azide, during 3 periods of storage: 7 days, 30 days and 6 months, resulting in 9 groups (n = 10). The roots were cut off and the buccal surface was ground with #600-grit silicon carbide paper. The surface was conditioned with 37% phosphoric acid for 15 s and a composite resin restoration (TPH Spectrum) was fixed using a one-bottle adhesive system (Adper Single Bond) and a dual-cured resinous cement (Rely X ARC) under a load of 500 g for 5 minutes. The samples were serially cut perpendicular to the bonded interface to obtain slices of 1.2 mm in thickness. Each slab was trimmed with a cylindrical diamond bur resulting in an hourglass shape with a cross-sectional area of approximately 1 mm². The microtensile bond strength (μTBS) testing was performed in a testing machine (EMIC 2000 DL) at a 0.5 mm/minute crosshead-speed until failure. After fracture, the specimens were examined under SEM to analyze the mode of fracture. μTBS Means were expressed in MPa and the data were analyzed by two-way ANOVA (3X3) and the Tukey test (α = 0.05). The storage times of 7 and 30 days produced no significant difference irrespective of the solution type. The formalin and thymol solutions, however, did have a negative influence on bond strength when the teeth were stored for 6 months. |
publishDate |
2008 |
dc.date.none.fl_str_mv |
2008-12-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242008000400012 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242008000400012 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/S1806-83242008000400012 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
Sociedade Brasileira de Pesquisa Odontológica - SBPqO |
publisher.none.fl_str_mv |
Sociedade Brasileira de Pesquisa Odontológica - SBPqO |
dc.source.none.fl_str_mv |
Brazilian Oral Research v.22 n.4 2008 reponame:Brazilian Oral Research instname:Sociedade Brasileira de Pesquisa Odontológica (SBPqO) instacron:SBPQO |
instname_str |
Sociedade Brasileira de Pesquisa Odontológica (SBPqO) |
instacron_str |
SBPQO |
institution |
SBPQO |
reponame_str |
Brazilian Oral Research |
collection |
Brazilian Oral Research |
repository.name.fl_str_mv |
Brazilian Oral Research - Sociedade Brasileira de Pesquisa Odontológica (SBPqO) |
repository.mail.fl_str_mv |
pob@edu.usp.br||bor@sbpqo.org.br |
_version_ |
1750318321311416320 |