Influence of surrounding wall thickness on the fatigue resistance of molars restored with ceramic inlay
Autor(a) principal: | |
---|---|
Data de Publicação: | 2014 |
Outros Autores: | , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Brazilian Oral Research |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242014000100229 |
Resumo: | The purpose of this study was to evaluate the influence of buccal and lingual wall thickness on the fatigue resistance of molars restored with CAD/CAM ceramic inlays. Forty human third molars were selected and divided into 4 groups, according to the remaining surrounding wall thickness chosen for inlay preparation (n = 10): G1, 2.0 mm; G2, 1.5 mm; G3, 1.0 mm; G4, 0.5 mm. All inlays were made from feldspathic ceramic blocks by a CAD/CAM system, and cemented adhesively. After 1 week stored in distilled water at 37 °C, the specimens were subjected to fatigue testing under the following protocol: 5Hz; pre-load of 200 N for 5,000 cycles, followed by increasing loads of 400, 600, 800, 1000, 1200 and 1400 N for 30,000 cycles each. The specimens were cycled until failure or completion of 185,000 cycles. The survival rate of the groups was compared using the Kaplan-Meier survival curves (p > 0.05). All specimens withstood the fatigue protocol (185,000 cycles), representing a 100% survival rate. The Kaplan-Meier survival curves showed no difference between groups. It can be concluded that the remaining tooth wall thickness did not influence the fatigue resistance of molars restored with CAD/CAM ceramic inlays. |
id |
SBPQO-1_169ad66225c9da4cc8d2cd5a0fff95f4 |
---|---|
oai_identifier_str |
oai:scielo:S1806-83242014000100229 |
network_acronym_str |
SBPQO-1 |
network_name_str |
Brazilian Oral Research |
repository_id_str |
|
spelling |
Influence of surrounding wall thickness on the fatigue resistance of molars restored with ceramic inlayStressMechanicalCeramicsInlaysThe purpose of this study was to evaluate the influence of buccal and lingual wall thickness on the fatigue resistance of molars restored with CAD/CAM ceramic inlays. Forty human third molars were selected and divided into 4 groups, according to the remaining surrounding wall thickness chosen for inlay preparation (n = 10): G1, 2.0 mm; G2, 1.5 mm; G3, 1.0 mm; G4, 0.5 mm. All inlays were made from feldspathic ceramic blocks by a CAD/CAM system, and cemented adhesively. After 1 week stored in distilled water at 37 °C, the specimens were subjected to fatigue testing under the following protocol: 5Hz; pre-load of 200 N for 5,000 cycles, followed by increasing loads of 400, 600, 800, 1000, 1200 and 1400 N for 30,000 cycles each. The specimens were cycled until failure or completion of 185,000 cycles. The survival rate of the groups was compared using the Kaplan-Meier survival curves (p > 0.05). All specimens withstood the fatigue protocol (185,000 cycles), representing a 100% survival rate. The Kaplan-Meier survival curves showed no difference between groups. It can be concluded that the remaining tooth wall thickness did not influence the fatigue resistance of molars restored with CAD/CAM ceramic inlays.Sociedade Brasileira de Pesquisa Odontológica - SBPqO2014-01-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242014000100229Brazilian Oral Research v.28 n.1 2014reponame:Brazilian Oral Researchinstname:Sociedade Brasileira de Pesquisa Odontológica (SBPqO)instacron:SBPQO10.1590/1807-3107BOR-2014.vol28.0011info:eu-repo/semantics/openAccessShibata,ShizumaGondo,RenataAraújo,ÉlitoRoesler,Carlos Rodrigo De MelloBaratieri,Luiz Narcisoeng2018-09-17T00:00:00Zoai:scielo:S1806-83242014000100229Revistahttps://www.scielo.br/j/bor/https://old.scielo.br/oai/scielo-oai.phppob@edu.usp.br||bor@sbpqo.org.br1807-31071806-8324opendoar:2018-09-17T00:00Brazilian Oral Research - Sociedade Brasileira de Pesquisa Odontológica (SBPqO)false |
dc.title.none.fl_str_mv |
Influence of surrounding wall thickness on the fatigue resistance of molars restored with ceramic inlay |
title |
Influence of surrounding wall thickness on the fatigue resistance of molars restored with ceramic inlay |
spellingShingle |
Influence of surrounding wall thickness on the fatigue resistance of molars restored with ceramic inlay Shibata,Shizuma Stress Mechanical Ceramics Inlays |
title_short |
Influence of surrounding wall thickness on the fatigue resistance of molars restored with ceramic inlay |
title_full |
Influence of surrounding wall thickness on the fatigue resistance of molars restored with ceramic inlay |
title_fullStr |
Influence of surrounding wall thickness on the fatigue resistance of molars restored with ceramic inlay |
title_full_unstemmed |
Influence of surrounding wall thickness on the fatigue resistance of molars restored with ceramic inlay |
title_sort |
Influence of surrounding wall thickness on the fatigue resistance of molars restored with ceramic inlay |
author |
Shibata,Shizuma |
author_facet |
Shibata,Shizuma Gondo,Renata Araújo,Élito Roesler,Carlos Rodrigo De Mello Baratieri,Luiz Narciso |
author_role |
author |
author2 |
Gondo,Renata Araújo,Élito Roesler,Carlos Rodrigo De Mello Baratieri,Luiz Narciso |
author2_role |
author author author author |
dc.contributor.author.fl_str_mv |
Shibata,Shizuma Gondo,Renata Araújo,Élito Roesler,Carlos Rodrigo De Mello Baratieri,Luiz Narciso |
dc.subject.por.fl_str_mv |
Stress Mechanical Ceramics Inlays |
topic |
Stress Mechanical Ceramics Inlays |
description |
The purpose of this study was to evaluate the influence of buccal and lingual wall thickness on the fatigue resistance of molars restored with CAD/CAM ceramic inlays. Forty human third molars were selected and divided into 4 groups, according to the remaining surrounding wall thickness chosen for inlay preparation (n = 10): G1, 2.0 mm; G2, 1.5 mm; G3, 1.0 mm; G4, 0.5 mm. All inlays were made from feldspathic ceramic blocks by a CAD/CAM system, and cemented adhesively. After 1 week stored in distilled water at 37 °C, the specimens were subjected to fatigue testing under the following protocol: 5Hz; pre-load of 200 N for 5,000 cycles, followed by increasing loads of 400, 600, 800, 1000, 1200 and 1400 N for 30,000 cycles each. The specimens were cycled until failure or completion of 185,000 cycles. The survival rate of the groups was compared using the Kaplan-Meier survival curves (p > 0.05). All specimens withstood the fatigue protocol (185,000 cycles), representing a 100% survival rate. The Kaplan-Meier survival curves showed no difference between groups. It can be concluded that the remaining tooth wall thickness did not influence the fatigue resistance of molars restored with CAD/CAM ceramic inlays. |
publishDate |
2014 |
dc.date.none.fl_str_mv |
2014-01-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242014000100229 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242014000100229 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/1807-3107BOR-2014.vol28.0011 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
Sociedade Brasileira de Pesquisa Odontológica - SBPqO |
publisher.none.fl_str_mv |
Sociedade Brasileira de Pesquisa Odontológica - SBPqO |
dc.source.none.fl_str_mv |
Brazilian Oral Research v.28 n.1 2014 reponame:Brazilian Oral Research instname:Sociedade Brasileira de Pesquisa Odontológica (SBPqO) instacron:SBPQO |
instname_str |
Sociedade Brasileira de Pesquisa Odontológica (SBPqO) |
instacron_str |
SBPQO |
institution |
SBPQO |
reponame_str |
Brazilian Oral Research |
collection |
Brazilian Oral Research |
repository.name.fl_str_mv |
Brazilian Oral Research - Sociedade Brasileira de Pesquisa Odontológica (SBPqO) |
repository.mail.fl_str_mv |
pob@edu.usp.br||bor@sbpqo.org.br |
_version_ |
1750318323792347136 |