One-year aging effects on microtensile bond strengths of composite and repairs with different surface treatments
Autor(a) principal: | |
---|---|
Data de Publicação: | 2017 |
Outros Autores: | , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Brazilian Oral Research |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242017000100204 |
Resumo: | Abstract The present study aimed to evaluate effects of different surface treatments and aging of composite cylinders on bond strength of composite resin repair. Thirty-two composite cylinders were produced and divided into four groups according to type of surface treatment and storage time of composite cylinder and repair. Cylinder surface of control group (Gcontrol) received no treatment before composite repair. Other groups were sandblasted with aluminum oxide (GAl2O3), followed by silane (GAl2O3sil) or adhesive (GAl2O3ad). Composite cylinders were stored in artificial saliva for either 24 hours or 1 year. Repairs were performed and stored in artificial saliva for 24 hours or 1 year and repair strength was evaluated using microtensile bond strength test. Data were submitted to Student’s t test, two-way ANOVA, and post hoc test for storage time and treatment (α = 0.05). Gcontrol group showed lower values of aging of composite cylinder and storage time of repair (24 hours or 1 year for both) compared with other groups (p < 0.05). GAl2O3ad and GAl2O3sil groups did not exhibit decreased microtensile bond strength with aged repairs (1 year; p > 0.05). Polymer degradation was significant for composite cylinders during the first year of storage in Gcontrol, GAl2O3, and GAl2O3ad groups (p < 0.05). In GAl2O3sil group, storage time of composite cylinders was not significant (p > 0.05). Aging of composite resin influenced bond strength of restoration repair for up to 1 year. Sandblasting with Al2O3, followed by application of silane layer, produced high bond strength after composite or repair aging. |
id |
SBPQO-1_18817fa52609b7b22b0f3ea458094804 |
---|---|
oai_identifier_str |
oai:scielo:S1806-83242017000100204 |
network_acronym_str |
SBPQO-1 |
network_name_str |
Brazilian Oral Research |
repository_id_str |
|
spelling |
One-year aging effects on microtensile bond strengths of composite and repairs with different surface treatmentsComposite ResinsDental Restoration FailureDental Restoration RepairDental BondingAbstract The present study aimed to evaluate effects of different surface treatments and aging of composite cylinders on bond strength of composite resin repair. Thirty-two composite cylinders were produced and divided into four groups according to type of surface treatment and storage time of composite cylinder and repair. Cylinder surface of control group (Gcontrol) received no treatment before composite repair. Other groups were sandblasted with aluminum oxide (GAl2O3), followed by silane (GAl2O3sil) or adhesive (GAl2O3ad). Composite cylinders were stored in artificial saliva for either 24 hours or 1 year. Repairs were performed and stored in artificial saliva for 24 hours or 1 year and repair strength was evaluated using microtensile bond strength test. Data were submitted to Student’s t test, two-way ANOVA, and post hoc test for storage time and treatment (α = 0.05). Gcontrol group showed lower values of aging of composite cylinder and storage time of repair (24 hours or 1 year for both) compared with other groups (p < 0.05). GAl2O3ad and GAl2O3sil groups did not exhibit decreased microtensile bond strength with aged repairs (1 year; p > 0.05). Polymer degradation was significant for composite cylinders during the first year of storage in Gcontrol, GAl2O3, and GAl2O3ad groups (p < 0.05). In GAl2O3sil group, storage time of composite cylinders was not significant (p > 0.05). Aging of composite resin influenced bond strength of restoration repair for up to 1 year. Sandblasting with Al2O3, followed by application of silane layer, produced high bond strength after composite or repair aging.Sociedade Brasileira de Pesquisa Odontológica - SBPqO2017-01-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242017000100204Brazilian Oral Research v.31 2017reponame:Brazilian Oral Researchinstname:Sociedade Brasileira de Pesquisa Odontológica (SBPqO)instacron:SBPQO10.1590/1807-3107bor-2017.vol31.0004info:eu-repo/semantics/openAccessSOUZA,Marcela Oliveira deLEITUNE,Vicente Castelo BrancoRODRIGUES,Stéfani BeckerSAMUEL,Susana Maria WernerCOLLARES,Fabrício Mezzomoeng2017-01-02T00:00:00Zoai:scielo:S1806-83242017000100204Revistahttps://www.scielo.br/j/bor/https://old.scielo.br/oai/scielo-oai.phppob@edu.usp.br||bor@sbpqo.org.br1807-31071806-8324opendoar:2017-01-02T00:00Brazilian Oral Research - Sociedade Brasileira de Pesquisa Odontológica (SBPqO)false |
dc.title.none.fl_str_mv |
One-year aging effects on microtensile bond strengths of composite and repairs with different surface treatments |
title |
One-year aging effects on microtensile bond strengths of composite and repairs with different surface treatments |
spellingShingle |
One-year aging effects on microtensile bond strengths of composite and repairs with different surface treatments SOUZA,Marcela Oliveira de Composite Resins Dental Restoration Failure Dental Restoration Repair Dental Bonding |
title_short |
One-year aging effects on microtensile bond strengths of composite and repairs with different surface treatments |
title_full |
One-year aging effects on microtensile bond strengths of composite and repairs with different surface treatments |
title_fullStr |
One-year aging effects on microtensile bond strengths of composite and repairs with different surface treatments |
title_full_unstemmed |
One-year aging effects on microtensile bond strengths of composite and repairs with different surface treatments |
title_sort |
One-year aging effects on microtensile bond strengths of composite and repairs with different surface treatments |
author |
SOUZA,Marcela Oliveira de |
author_facet |
SOUZA,Marcela Oliveira de LEITUNE,Vicente Castelo Branco RODRIGUES,Stéfani Becker SAMUEL,Susana Maria Werner COLLARES,Fabrício Mezzomo |
author_role |
author |
author2 |
LEITUNE,Vicente Castelo Branco RODRIGUES,Stéfani Becker SAMUEL,Susana Maria Werner COLLARES,Fabrício Mezzomo |
author2_role |
author author author author |
dc.contributor.author.fl_str_mv |
SOUZA,Marcela Oliveira de LEITUNE,Vicente Castelo Branco RODRIGUES,Stéfani Becker SAMUEL,Susana Maria Werner COLLARES,Fabrício Mezzomo |
dc.subject.por.fl_str_mv |
Composite Resins Dental Restoration Failure Dental Restoration Repair Dental Bonding |
topic |
Composite Resins Dental Restoration Failure Dental Restoration Repair Dental Bonding |
description |
Abstract The present study aimed to evaluate effects of different surface treatments and aging of composite cylinders on bond strength of composite resin repair. Thirty-two composite cylinders were produced and divided into four groups according to type of surface treatment and storage time of composite cylinder and repair. Cylinder surface of control group (Gcontrol) received no treatment before composite repair. Other groups were sandblasted with aluminum oxide (GAl2O3), followed by silane (GAl2O3sil) or adhesive (GAl2O3ad). Composite cylinders were stored in artificial saliva for either 24 hours or 1 year. Repairs were performed and stored in artificial saliva for 24 hours or 1 year and repair strength was evaluated using microtensile bond strength test. Data were submitted to Student’s t test, two-way ANOVA, and post hoc test for storage time and treatment (α = 0.05). Gcontrol group showed lower values of aging of composite cylinder and storage time of repair (24 hours or 1 year for both) compared with other groups (p < 0.05). GAl2O3ad and GAl2O3sil groups did not exhibit decreased microtensile bond strength with aged repairs (1 year; p > 0.05). Polymer degradation was significant for composite cylinders during the first year of storage in Gcontrol, GAl2O3, and GAl2O3ad groups (p < 0.05). In GAl2O3sil group, storage time of composite cylinders was not significant (p > 0.05). Aging of composite resin influenced bond strength of restoration repair for up to 1 year. Sandblasting with Al2O3, followed by application of silane layer, produced high bond strength after composite or repair aging. |
publishDate |
2017 |
dc.date.none.fl_str_mv |
2017-01-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242017000100204 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242017000100204 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/1807-3107bor-2017.vol31.0004 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
Sociedade Brasileira de Pesquisa Odontológica - SBPqO |
publisher.none.fl_str_mv |
Sociedade Brasileira de Pesquisa Odontológica - SBPqO |
dc.source.none.fl_str_mv |
Brazilian Oral Research v.31 2017 reponame:Brazilian Oral Research instname:Sociedade Brasileira de Pesquisa Odontológica (SBPqO) instacron:SBPQO |
instname_str |
Sociedade Brasileira de Pesquisa Odontológica (SBPqO) |
instacron_str |
SBPQO |
institution |
SBPQO |
reponame_str |
Brazilian Oral Research |
collection |
Brazilian Oral Research |
repository.name.fl_str_mv |
Brazilian Oral Research - Sociedade Brasileira de Pesquisa Odontológica (SBPqO) |
repository.mail.fl_str_mv |
pob@edu.usp.br||bor@sbpqo.org.br |
_version_ |
1750318325215264768 |