Influence of ethanol-wet dentin, adhesive mode of application, and aging on bond strength of universal adhesive
Autor(a) principal: | |
---|---|
Data de Publicação: | 2018 |
Outros Autores: | , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Brazilian Oral Research |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242018000100279 |
Resumo: | Abstract The aim of this study was to evaluate the effect of ethanol on the bond longevity of a universal adhesive system to bovine dentin, under different modes of adhesive application and artificial aging. Bovine dentin was exposed, and the smear layer was standardized by sandpaper polishing. Specimens were randomly divided into 2 groups: ethanol (E) and non-ethanol (N). Groups were subdivided according to adhesive mode of application into etch-and-rinse (Er) and self-etching (S). Resin blocks were built onto the treated surface, and the specimens were stored in deionized water at 37°C for 48 h. Half of the specimens (n = 10) were subjected to thermomechanical aging (A for aged and Na for non-aged). Resin/dentin beams were obtained and subjected to microtensile test in a universal testing machine. Data were analyzed using a three-way ANOVA and Tukey’s tests (α = 5%). There was interaction among the three factors (p=0.0003). The use of ethanol resulted in higher values, except for the Er and Na groups (E_Er_Na = N_Er_Na). The mode of application was similar, except for the N and A groups (N_S_A > N_Er_A). For the A groups, the values were lower, except in the cases using ethanol, in which the results were not affected. The study concluded that the use of ethanol resulted in higher microtensile bond strength values, even after aging. The mode of adhesive application did not influence the results. |
id |
SBPQO-1_abdb44a441e74b897d3f9c11cd67902c |
---|---|
oai_identifier_str |
oai:scielo:S1806-83242018000100279 |
network_acronym_str |
SBPQO-1 |
network_name_str |
Brazilian Oral Research |
repository_id_str |
|
spelling |
Influence of ethanol-wet dentin, adhesive mode of application, and aging on bond strength of universal adhesiveAgingDental BondingDentinEthanolAbstract The aim of this study was to evaluate the effect of ethanol on the bond longevity of a universal adhesive system to bovine dentin, under different modes of adhesive application and artificial aging. Bovine dentin was exposed, and the smear layer was standardized by sandpaper polishing. Specimens were randomly divided into 2 groups: ethanol (E) and non-ethanol (N). Groups were subdivided according to adhesive mode of application into etch-and-rinse (Er) and self-etching (S). Resin blocks were built onto the treated surface, and the specimens were stored in deionized water at 37°C for 48 h. Half of the specimens (n = 10) were subjected to thermomechanical aging (A for aged and Na for non-aged). Resin/dentin beams were obtained and subjected to microtensile test in a universal testing machine. Data were analyzed using a three-way ANOVA and Tukey’s tests (α = 5%). There was interaction among the three factors (p=0.0003). The use of ethanol resulted in higher values, except for the Er and Na groups (E_Er_Na = N_Er_Na). The mode of application was similar, except for the N and A groups (N_S_A > N_Er_A). For the A groups, the values were lower, except in the cases using ethanol, in which the results were not affected. The study concluded that the use of ethanol resulted in higher microtensile bond strength values, even after aging. The mode of adhesive application did not influence the results.Sociedade Brasileira de Pesquisa Odontológica - SBPqO2018-01-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242018000100279Brazilian Oral Research v.32 2018reponame:Brazilian Oral Researchinstname:Sociedade Brasileira de Pesquisa Odontológica (SBPqO)instacron:SBPQO10.1590/1807-3107bor-2018.vol32.0102info:eu-repo/semantics/openAccessSOUZA,Mauricio Yugo deDI NICOLÓ,RebecaBRESCIANI,Eduardoeng2018-10-08T00:00:00Zoai:scielo:S1806-83242018000100279Revistahttps://www.scielo.br/j/bor/https://old.scielo.br/oai/scielo-oai.phppob@edu.usp.br||bor@sbpqo.org.br1807-31071806-8324opendoar:2018-10-08T00:00Brazilian Oral Research - Sociedade Brasileira de Pesquisa Odontológica (SBPqO)false |
dc.title.none.fl_str_mv |
Influence of ethanol-wet dentin, adhesive mode of application, and aging on bond strength of universal adhesive |
title |
Influence of ethanol-wet dentin, adhesive mode of application, and aging on bond strength of universal adhesive |
spellingShingle |
Influence of ethanol-wet dentin, adhesive mode of application, and aging on bond strength of universal adhesive SOUZA,Mauricio Yugo de Aging Dental Bonding Dentin Ethanol |
title_short |
Influence of ethanol-wet dentin, adhesive mode of application, and aging on bond strength of universal adhesive |
title_full |
Influence of ethanol-wet dentin, adhesive mode of application, and aging on bond strength of universal adhesive |
title_fullStr |
Influence of ethanol-wet dentin, adhesive mode of application, and aging on bond strength of universal adhesive |
title_full_unstemmed |
Influence of ethanol-wet dentin, adhesive mode of application, and aging on bond strength of universal adhesive |
title_sort |
Influence of ethanol-wet dentin, adhesive mode of application, and aging on bond strength of universal adhesive |
author |
SOUZA,Mauricio Yugo de |
author_facet |
SOUZA,Mauricio Yugo de DI NICOLÓ,Rebeca BRESCIANI,Eduardo |
author_role |
author |
author2 |
DI NICOLÓ,Rebeca BRESCIANI,Eduardo |
author2_role |
author author |
dc.contributor.author.fl_str_mv |
SOUZA,Mauricio Yugo de DI NICOLÓ,Rebeca BRESCIANI,Eduardo |
dc.subject.por.fl_str_mv |
Aging Dental Bonding Dentin Ethanol |
topic |
Aging Dental Bonding Dentin Ethanol |
description |
Abstract The aim of this study was to evaluate the effect of ethanol on the bond longevity of a universal adhesive system to bovine dentin, under different modes of adhesive application and artificial aging. Bovine dentin was exposed, and the smear layer was standardized by sandpaper polishing. Specimens were randomly divided into 2 groups: ethanol (E) and non-ethanol (N). Groups were subdivided according to adhesive mode of application into etch-and-rinse (Er) and self-etching (S). Resin blocks were built onto the treated surface, and the specimens were stored in deionized water at 37°C for 48 h. Half of the specimens (n = 10) were subjected to thermomechanical aging (A for aged and Na for non-aged). Resin/dentin beams were obtained and subjected to microtensile test in a universal testing machine. Data were analyzed using a three-way ANOVA and Tukey’s tests (α = 5%). There was interaction among the three factors (p=0.0003). The use of ethanol resulted in higher values, except for the Er and Na groups (E_Er_Na = N_Er_Na). The mode of application was similar, except for the N and A groups (N_S_A > N_Er_A). For the A groups, the values were lower, except in the cases using ethanol, in which the results were not affected. The study concluded that the use of ethanol resulted in higher microtensile bond strength values, even after aging. The mode of adhesive application did not influence the results. |
publishDate |
2018 |
dc.date.none.fl_str_mv |
2018-01-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242018000100279 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242018000100279 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/1807-3107bor-2018.vol32.0102 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
Sociedade Brasileira de Pesquisa Odontológica - SBPqO |
publisher.none.fl_str_mv |
Sociedade Brasileira de Pesquisa Odontológica - SBPqO |
dc.source.none.fl_str_mv |
Brazilian Oral Research v.32 2018 reponame:Brazilian Oral Research instname:Sociedade Brasileira de Pesquisa Odontológica (SBPqO) instacron:SBPQO |
instname_str |
Sociedade Brasileira de Pesquisa Odontológica (SBPqO) |
instacron_str |
SBPQO |
institution |
SBPQO |
reponame_str |
Brazilian Oral Research |
collection |
Brazilian Oral Research |
repository.name.fl_str_mv |
Brazilian Oral Research - Sociedade Brasileira de Pesquisa Odontológica (SBPqO) |
repository.mail.fl_str_mv |
pob@edu.usp.br||bor@sbpqo.org.br |
_version_ |
1750318326113894400 |