Desenvolvimento de nanocompósitos híbridos de epóxi/NTCPM/cargas minerais e avaliação das propriedades mecânicas, elétricas e térmicas

Detalhes bibliográficos
Autor(a) principal: Backes, Eduardo Henrique
Data de Publicação: 2016
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSCAR
Texto Completo: https://repositorio.ufscar.br/handle/ufscar/8537
Resumo: In the present work epoxy/ MWCNT/ mineral fillers nanocomposites were obtained using ultrasonication and calendering. The effect of addition of mineral filler (calcium carbonate, montmorillonite and sepiolite) in electrical, mechanical and thermal properties of epoxy/ MWCNT were analyzed. Two different CNT were studied, with different aspect ration and purity, however only Nanocyl CNT’s presented improvement in the nanocomposites electrical properties and for that reason was employed for hybrid epoxy/ MWCNT/ mineral nanocomposites production. The electrical percolation threshold was determined as 0.04 wt% and for 0.3 wt% the electrical conductivity reached 1.29X10-2 S/m. The addition of calcium carbonate and montmorillonite improved electrical conductivity for epoxy nanocomposites produced with 0.05 wt% CNT and the same behavior was observed for epoxy/ MWCNT / sepiolite nanocomposites at 0.1 wt% CNT. The epoxy/ MWCNT nanocomposite at 0.05% CNT when produzed via calendering presented improvement in the electrical conductivity compared to the same nanocomposite produced via ultrasonication. For epoxy/ MWCNT at 0.05 wt% of CNT, the addition of calcium carbonate in the nanocomposite led to an electrical conductivity 1 decade higher than the epoxy/ 0.05 wt% CNT nanocomposite produced via calendering. The mineral fillers also modified thermal and mechanical behavior of the nanocomposites, and improvements in flexural modulus, thermal stability and Tg were observed.
id SCAR_1ef7745642f0b7573d65c98a58525a73
oai_identifier_str oai:repositorio.ufscar.br:ufscar/8537
network_acronym_str SCAR
network_name_str Repositório Institucional da UFSCAR
repository_id_str 4322
spelling Backes, Eduardo HenriquePessan, Luiz Antoniohttp://lattes.cnpq.br/8276650236213537Passador, Fabio Robertohttp://lattes.cnpq.br/0152213852695153http://lattes.cnpq.br/6407713491620749d33279f5-cecc-4c5b-84a9-82137495a9fe2017-03-02T12:49:51Z2017-03-02T12:49:51Z2016-07-11BACKES, Eduardo Henrique. Desenvolvimento de nanocompósitos híbridos de epóxi/NTCPM/cargas minerais e avaliação das propriedades mecânicas, elétricas e térmicas. 2016. Dissertação (Mestrado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2016. Disponível em: https://repositorio.ufscar.br/handle/ufscar/8537.https://repositorio.ufscar.br/handle/ufscar/8537In the present work epoxy/ MWCNT/ mineral fillers nanocomposites were obtained using ultrasonication and calendering. The effect of addition of mineral filler (calcium carbonate, montmorillonite and sepiolite) in electrical, mechanical and thermal properties of epoxy/ MWCNT were analyzed. Two different CNT were studied, with different aspect ration and purity, however only Nanocyl CNT’s presented improvement in the nanocomposites electrical properties and for that reason was employed for hybrid epoxy/ MWCNT/ mineral nanocomposites production. The electrical percolation threshold was determined as 0.04 wt% and for 0.3 wt% the electrical conductivity reached 1.29X10-2 S/m. The addition of calcium carbonate and montmorillonite improved electrical conductivity for epoxy nanocomposites produced with 0.05 wt% CNT and the same behavior was observed for epoxy/ MWCNT / sepiolite nanocomposites at 0.1 wt% CNT. The epoxy/ MWCNT nanocomposite at 0.05% CNT when produzed via calendering presented improvement in the electrical conductivity compared to the same nanocomposite produced via ultrasonication. For epoxy/ MWCNT at 0.05 wt% of CNT, the addition of calcium carbonate in the nanocomposite led to an electrical conductivity 1 decade higher than the epoxy/ 0.05 wt% CNT nanocomposite produced via calendering. The mineral fillers also modified thermal and mechanical behavior of the nanocomposites, and improvements in flexural modulus, thermal stability and Tg were observed.Neste trabalho produziu-se nanocompósitos híbridos de resina epóxi/ NTCPM/ cargas minerais utilizando-se sonicação de alta energia e calandragem, e estudou-se a influência da adição de diferentes cargas minerais (carbonato de cálcio, montmorilonita e sepiolita) nas propriedades elétricas, térmicas e mecânicas de nanocompósitos epóxi/NTCPM. Neste trabalho foram utilizados dois diferentes tipos de nanotubos de carbono, com razões de aspecto e purezas diferentes, e verificou-se que somente um deles apresentou melhoria nas propriedades elétricas dos nanocompósitos epóxi/NTCPM, o qual foi empregado na produção de nanocompósitos híbridos epóxi/ NTCPM/ cargas minerais. A percolação elétrica dos nanotubos de carbono foi determinada em aproximadamente 0,04% em massa, e para um teor de 0,3% em massa de nanotubos de carbono, a condutividade elétrica atingiu 1,29X10-2 S/m. Nos nanocompósitos processados via sonicação de alta energia, observou-se elevação da condutividade elétrica com a adição de montmorilonita sódica e carbonato de cálcio para os teores de 0,05% em massa de NTCPM e com a adição de sepiolita somente para o teor de 0,1% em massa de NTCPM. Nos nanocompósitos processados via calandragem, o nanocompósito de resina epóxi/ 0,05% NTCPM apresentou condutividade elétrica duas vezes superior ao mesmo nanocompósito processado via sonicação de alta energia e a adição de carbonato de cálcio elevou a condutividade elétrica do nanocompósito de resina epóxi/ 0,05% NTCPM/ carbonato de cálcio em uma ordem de grandeza quando comparado ao nanocompósito epóxi/ 0,05% NTCPM processado via calandragem. A adição de NTCPM e cargas minerais também modificou os comportamentos mecânico e térmico dos nanocompósitos, elevando-se o módulo elástico em flexão, resistência térmica e Tg.Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)FAPESP: 2014/16299-8porUniversidade Federal de São CarlosCâmpus São CarlosPrograma de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEMUFSCarEpóxiNanotubos de carbonoNanocompósitos epóxi/NTCPMPropriedades elétricasEpoxyCarbon nanotubesEpoxy/MWCNT nanocompositesElectrical propertiesENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICADesenvolvimento de nanocompósitos híbridos de epóxi/NTCPM/cargas minerais e avaliação das propriedades mecânicas, elétricas e térmicasinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisOnline60060027e170ed-63e5-4ae6-96cf-f7ccb26a3076info:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINALDissEHB.pdfDissEHB.pdfapplication/pdf15859692https://repositorio.ufscar.br/bitstream/ufscar/8537/1/DissEHB.pdfc4538902f4ec95de542bf12edadd5749MD51LICENSElicense.txtlicense.txttext/plain; charset=utf-81957https://repositorio.ufscar.br/bitstream/ufscar/8537/2/license.txtae0398b6f8b235e40ad82cba6c50031dMD52TEXTDissEHB.pdf.txtDissEHB.pdf.txtExtracted texttext/plain231562https://repositorio.ufscar.br/bitstream/ufscar/8537/3/DissEHB.pdf.txtf4dd4d6ec5ac5eb3a03fa657f3e117fcMD53THUMBNAILDissEHB.pdf.jpgDissEHB.pdf.jpgIM Thumbnailimage/jpeg6579https://repositorio.ufscar.br/bitstream/ufscar/8537/4/DissEHB.pdf.jpg13924768e8b845b693f419f50a9d5e97MD54ufscar/85372023-09-18 18:31:07.799oai:repositorio.ufscar.br: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Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222023-09-18T18:31:07Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false
dc.title.por.fl_str_mv Desenvolvimento de nanocompósitos híbridos de epóxi/NTCPM/cargas minerais e avaliação das propriedades mecânicas, elétricas e térmicas
title Desenvolvimento de nanocompósitos híbridos de epóxi/NTCPM/cargas minerais e avaliação das propriedades mecânicas, elétricas e térmicas
spellingShingle Desenvolvimento de nanocompósitos híbridos de epóxi/NTCPM/cargas minerais e avaliação das propriedades mecânicas, elétricas e térmicas
Backes, Eduardo Henrique
Epóxi
Nanotubos de carbono
Nanocompósitos epóxi/NTCPM
Propriedades elétricas
Epoxy
Carbon nanotubes
Epoxy/MWCNT nanocomposites
Electrical properties
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
title_short Desenvolvimento de nanocompósitos híbridos de epóxi/NTCPM/cargas minerais e avaliação das propriedades mecânicas, elétricas e térmicas
title_full Desenvolvimento de nanocompósitos híbridos de epóxi/NTCPM/cargas minerais e avaliação das propriedades mecânicas, elétricas e térmicas
title_fullStr Desenvolvimento de nanocompósitos híbridos de epóxi/NTCPM/cargas minerais e avaliação das propriedades mecânicas, elétricas e térmicas
title_full_unstemmed Desenvolvimento de nanocompósitos híbridos de epóxi/NTCPM/cargas minerais e avaliação das propriedades mecânicas, elétricas e térmicas
title_sort Desenvolvimento de nanocompósitos híbridos de epóxi/NTCPM/cargas minerais e avaliação das propriedades mecânicas, elétricas e térmicas
author Backes, Eduardo Henrique
author_facet Backes, Eduardo Henrique
author_role author
dc.contributor.authorlattes.por.fl_str_mv http://lattes.cnpq.br/6407713491620749
dc.contributor.author.fl_str_mv Backes, Eduardo Henrique
dc.contributor.advisor1.fl_str_mv Pessan, Luiz Antonio
dc.contributor.advisor1Lattes.fl_str_mv http://lattes.cnpq.br/8276650236213537
dc.contributor.advisor-co1.fl_str_mv Passador, Fabio Roberto
dc.contributor.advisor-co1Lattes.fl_str_mv http://lattes.cnpq.br/0152213852695153
dc.contributor.authorID.fl_str_mv d33279f5-cecc-4c5b-84a9-82137495a9fe
contributor_str_mv Pessan, Luiz Antonio
Passador, Fabio Roberto
dc.subject.por.fl_str_mv Epóxi
Nanotubos de carbono
Nanocompósitos epóxi/NTCPM
Propriedades elétricas
topic Epóxi
Nanotubos de carbono
Nanocompósitos epóxi/NTCPM
Propriedades elétricas
Epoxy
Carbon nanotubes
Epoxy/MWCNT nanocomposites
Electrical properties
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
dc.subject.eng.fl_str_mv Epoxy
Carbon nanotubes
Epoxy/MWCNT nanocomposites
Electrical properties
dc.subject.cnpq.fl_str_mv ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
description In the present work epoxy/ MWCNT/ mineral fillers nanocomposites were obtained using ultrasonication and calendering. The effect of addition of mineral filler (calcium carbonate, montmorillonite and sepiolite) in electrical, mechanical and thermal properties of epoxy/ MWCNT were analyzed. Two different CNT were studied, with different aspect ration and purity, however only Nanocyl CNT’s presented improvement in the nanocomposites electrical properties and for that reason was employed for hybrid epoxy/ MWCNT/ mineral nanocomposites production. The electrical percolation threshold was determined as 0.04 wt% and for 0.3 wt% the electrical conductivity reached 1.29X10-2 S/m. The addition of calcium carbonate and montmorillonite improved electrical conductivity for epoxy nanocomposites produced with 0.05 wt% CNT and the same behavior was observed for epoxy/ MWCNT / sepiolite nanocomposites at 0.1 wt% CNT. The epoxy/ MWCNT nanocomposite at 0.05% CNT when produzed via calendering presented improvement in the electrical conductivity compared to the same nanocomposite produced via ultrasonication. For epoxy/ MWCNT at 0.05 wt% of CNT, the addition of calcium carbonate in the nanocomposite led to an electrical conductivity 1 decade higher than the epoxy/ 0.05 wt% CNT nanocomposite produced via calendering. The mineral fillers also modified thermal and mechanical behavior of the nanocomposites, and improvements in flexural modulus, thermal stability and Tg were observed.
publishDate 2016
dc.date.issued.fl_str_mv 2016-07-11
dc.date.accessioned.fl_str_mv 2017-03-02T12:49:51Z
dc.date.available.fl_str_mv 2017-03-02T12:49:51Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.citation.fl_str_mv BACKES, Eduardo Henrique. Desenvolvimento de nanocompósitos híbridos de epóxi/NTCPM/cargas minerais e avaliação das propriedades mecânicas, elétricas e térmicas. 2016. Dissertação (Mestrado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2016. Disponível em: https://repositorio.ufscar.br/handle/ufscar/8537.
dc.identifier.uri.fl_str_mv https://repositorio.ufscar.br/handle/ufscar/8537
identifier_str_mv BACKES, Eduardo Henrique. Desenvolvimento de nanocompósitos híbridos de epóxi/NTCPM/cargas minerais e avaliação das propriedades mecânicas, elétricas e térmicas. 2016. Dissertação (Mestrado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2016. Disponível em: https://repositorio.ufscar.br/handle/ufscar/8537.
url https://repositorio.ufscar.br/handle/ufscar/8537
dc.language.iso.fl_str_mv por
language por
dc.relation.confidence.fl_str_mv 600
600
dc.relation.authority.fl_str_mv 27e170ed-63e5-4ae6-96cf-f7ccb26a3076
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.publisher.none.fl_str_mv Universidade Federal de São Carlos
Câmpus São Carlos
dc.publisher.program.fl_str_mv Programa de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEM
dc.publisher.initials.fl_str_mv UFSCar
publisher.none.fl_str_mv Universidade Federal de São Carlos
Câmpus São Carlos
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSCAR
instname:Universidade Federal de São Carlos (UFSCAR)
instacron:UFSCAR
instname_str Universidade Federal de São Carlos (UFSCAR)
instacron_str UFSCAR
institution UFSCAR
reponame_str Repositório Institucional da UFSCAR
collection Repositório Institucional da UFSCAR
bitstream.url.fl_str_mv https://repositorio.ufscar.br/bitstream/ufscar/8537/1/DissEHB.pdf
https://repositorio.ufscar.br/bitstream/ufscar/8537/2/license.txt
https://repositorio.ufscar.br/bitstream/ufscar/8537/3/DissEHB.pdf.txt
https://repositorio.ufscar.br/bitstream/ufscar/8537/4/DissEHB.pdf.jpg
bitstream.checksum.fl_str_mv c4538902f4ec95de542bf12edadd5749
ae0398b6f8b235e40ad82cba6c50031d
f4dd4d6ec5ac5eb3a03fa657f3e117fc
13924768e8b845b693f419f50a9d5e97
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
MD5
MD5
repository.name.fl_str_mv Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)
repository.mail.fl_str_mv
_version_ 1802136321021444096

Registros relacionados