Desenvolvimento e caracterização de um banho não-cianetado para a eletrodeposição de ligas de Cu-Sn-Zn: caracterização dos eletrodepósitos
Autor(a) principal: | |
---|---|
Data de Publicação: | 2014 |
Tipo de documento: | Tese |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFSCAR |
Texto Completo: | https://repositorio.ufscar.br/handle/ufscar/6304 |
Resumo: | The electrodeposition of Cu-Sn-Zn ternary alloys onto AISI 1010 steel from an acid bath with EDTA or NTA salts was investigated, with various proportions of the metal ions in the baths. The concentration of these metals in the baths was determined by factorial design of mixtures with pseudocomponents. From potentiometric titration of these baths were determined regression equations, which led to studies of variance analysis and of surface response. These studies allowed to a pH of stabilization of the Cu-Sn-Zn electrodeposition baths. The Cu-Sn-Zn voltammetric profile showed five cathodic regions: c1, c1 , c2, c3 and c4 (depending on bath composition), and the conditional potentials for the Cu2+, Sn2+ and Zn2+ complexes indicated that these regions were associated, respectively, with reduction of [CuY]2- complex to Cu; [Sn(H2O)6]2+ complex to Sn; [SnY]2- complex to Sn; H2O to H2; and [ZnY]2- complex to Zn. In the presence of NTA, [Cu(NTA)2]4- and [SnNTA]-, [Sn(NTA)2]4-; H2O and [ZnNTA]- and [Zn(NTA)2]4-, respectively, in the regions c1, c2, c3 and c4. Cu-Sn-Zn electrodeposits produced at Ed 1.70 V with qd 3.0 C cm−2 were characterized by EDS, SEM, XRD and confocal optical microscopy (COM) analysis. EDS indicated that a transition potential exists wherein a transition from Cu-Sn binary alloy to Cu-Sn-Zn ternary alloy occurred and, also, that Cu-Sn-Zn co-deposition was normal, preferential or anomalous depending on the bath composition. Moreover, this analyze showed that Zn reduction was facilitated in the presence of NTA. SEM of electrodeposits showed that they were formed by globular and/or irregular crystallites, and, in general, by clusters of crystallites of different sizes dispersed on this layer, depending on the bath composition. COM analysis showed that electrodeposit produced from NTA was more roughness than with EDTA. XRD pattern indicated that the Cu-Sn-Zn electrodeposits, depending on the composition of the baths, presented low crystallinity or crystalline structure with mixture of SnO, η- Cu6Sn5 and Cu5Zn8 phases or pure Sn, η-Cu6Sn5 and Cu5Zn8 phases. Multivariate analysis allows extracting the maximum relevant chemical information from the data. |
id |
SCAR_481990c64841cbe33dd3fcab2b36f181 |
---|---|
oai_identifier_str |
oai:repositorio.ufscar.br:ufscar/6304 |
network_acronym_str |
SCAR |
network_name_str |
Repositório Institucional da UFSCAR |
repository_id_str |
4322 |
spelling |
Carvalho, Marcos Fernandes deCarlos, Ivani Aparecidahttp://genos.cnpq.br:12010/dwlattes/owa/prc_imp_cv_int?f_cod=K4780131E6http://lattes.cnpq.br/0922916090536806da5b2f31-65c1-46aa-baf1-e2f30ec81a402016-06-02T20:34:52Z2014-08-012016-06-02T20:34:52Z2014-05-16CARVALHO, Marcos Fernandes de. Development and characterization of a non-cianyde bath for Cu- Sn-Zn alloys electrodeposition. Characterization of the Cu-Sn-Zn electrodeposits. 2014. 1 f. Tese (Doutorado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2014.https://repositorio.ufscar.br/handle/ufscar/6304The electrodeposition of Cu-Sn-Zn ternary alloys onto AISI 1010 steel from an acid bath with EDTA or NTA salts was investigated, with various proportions of the metal ions in the baths. The concentration of these metals in the baths was determined by factorial design of mixtures with pseudocomponents. From potentiometric titration of these baths were determined regression equations, which led to studies of variance analysis and of surface response. These studies allowed to a pH of stabilization of the Cu-Sn-Zn electrodeposition baths. The Cu-Sn-Zn voltammetric profile showed five cathodic regions: c1, c1 , c2, c3 and c4 (depending on bath composition), and the conditional potentials for the Cu2+, Sn2+ and Zn2+ complexes indicated that these regions were associated, respectively, with reduction of [CuY]2- complex to Cu; [Sn(H2O)6]2+ complex to Sn; [SnY]2- complex to Sn; H2O to H2; and [ZnY]2- complex to Zn. In the presence of NTA, [Cu(NTA)2]4- and [SnNTA]-, [Sn(NTA)2]4-; H2O and [ZnNTA]- and [Zn(NTA)2]4-, respectively, in the regions c1, c2, c3 and c4. Cu-Sn-Zn electrodeposits produced at Ed 1.70 V with qd 3.0 C cm−2 were characterized by EDS, SEM, XRD and confocal optical microscopy (COM) analysis. EDS indicated that a transition potential exists wherein a transition from Cu-Sn binary alloy to Cu-Sn-Zn ternary alloy occurred and, also, that Cu-Sn-Zn co-deposition was normal, preferential or anomalous depending on the bath composition. Moreover, this analyze showed that Zn reduction was facilitated in the presence of NTA. SEM of electrodeposits showed that they were formed by globular and/or irregular crystallites, and, in general, by clusters of crystallites of different sizes dispersed on this layer, depending on the bath composition. COM analysis showed that electrodeposit produced from NTA was more roughness than with EDTA. XRD pattern indicated that the Cu-Sn-Zn electrodeposits, depending on the composition of the baths, presented low crystallinity or crystalline structure with mixture of SnO, η- Cu6Sn5 and Cu5Zn8 phases or pure Sn, η-Cu6Sn5 and Cu5Zn8 phases. Multivariate analysis allows extracting the maximum relevant chemical information from the data.A eletrodeposição da liga ternária Cu-Sn-Zn sobre aço 1010 a partir de um banho ácido com os sais de EDTA ou NTA foi investigada, com varias proporções dos íons metálicos nos banhos. A concentração desses metais nos banhos foi determinada através da montagem de um planejamento fatorial de misturas com pseudocomponentes. Dos resultados obtidos por titulação potenciométrica foram determinadas equações de regressão, as quais permitiram estudos da análise de variância e das superfícies de resposta. Destes estudos, foi determinado o pH ótimo para os estudos dos banhos de Cu-Sn-Zn. Efeitos da utilização do EDTA ou NTA nos banhos de eletrodeposição de Cu, Sn, Zn e Cu-Sn-Zn, sem ES também foram avaliados. Curvas voltamétricas de eletrodeposição mostraram que a composição do banho e a presença de EDTA ou NTA afetaram a cinética e a termodinâmica do processo de redução. O mecanismo de redução na presença de EDTA ocorreu, em geral, pela redução de [CuY]2-, seguido por [Sn(H2O)6]2+, [SnY]2- e [ZnY]2-. Já na presença de NTA, a redução iniciou-se pelos complexos [Cu(NTA)2]4- e [SnNTA]-, seguidos por [Sn(NTA)2]4-, [ZnNTA]- e [Zn(NTA)2]4-. Caracterização dos eletrodepósitos por EDX mostrou que, na presença de NTA a redução dos íons Zn(II) foi mais facilitada e, também, que existe um potencial de eletrodeposição onde ocorre a transição das ligas Cu-Sn para as ligas Cu-Sn-Zn, o qual depende do complexante utilizado e da composição do banho. Análises de DRX mostraram que, em geral, a mistura das fases Sn, Cu5Zn8 e η-Cu6Sn5 indicaram a formação da liga Cu-Sn-Zn. Análise morfológica mostrou que os eletrodepósitos de Cu-Sn-Zn foram formados por cristalitos globulares e/ou irregulares de diferentes tamanhos, com aglomerados de cristalitos dispersos e/ou dendríticos, dependendo da composição do banho. Análise de rugosidade média mostrou que os eletrodepósitos obtidos a partir dos banhos contendo NTA foram mais rugosos. Análise multivariada relacionou a composição do banho com a composição química dos eletrodepósitos de Cu-Sn-Zn, fornecendo a relação entre tais parâmetros.Universidade Federal de Minas Geraisapplication/pdfporUniversidade Federal de São CarlosPrograma de Pós-Graduação em Química - PPGQUFSCarBREletrodeposiçãoLigas Cu-Sn-ZnPlanejamento fatorial de misturasMicroestruturaRaios X - difraçãoAnálise multivariadaCIENCIAS EXATAS E DA TERRA::QUIMICADesenvolvimento e caracterização de um banho não-cianetado para a eletrodeposição de ligas de Cu-Sn-Zn: caracterização dos eletrodepósitosDevelopment and characterization of a non-cianyde bath for Cu- Sn-Zn alloys electrodeposition: characterization of the Cu-Sn-Zn electrodepositsinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesis-1-16ab22b71-dd06-4945-bc9e-1a23f05da42einfo:eu-repo/semantics/embargoedAccessreponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINALTeseMFC.pdfTeseMFC.pdfapplication/pdf36016280https://repositorio.ufscar.br/bitstream/ufscar/6304/1/TeseMFC.pdf03051c46f677b648dd152a6d8107857aMD51TEXTTeseMFC.pdf.txtTeseMFC.pdf.txtExtracted texttext/plain659187https://repositorio.ufscar.br/bitstream/ufscar/6304/2/TeseMFC.pdf.txtae963f121a1d3b87214c6fb8e8af788fMD52THUMBNAILTeseMFC.pdf.jpgTeseMFC.pdf.jpgIM Thumbnailimage/jpeg10625https://repositorio.ufscar.br/bitstream/ufscar/6304/3/TeseMFC.pdf.jpg63f5214186bf3c8f74c1cf553e637a06MD53ufscar/63042023-09-18 18:32:00.308oai:repositorio.ufscar.br:ufscar/6304Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222023-09-18T18:32Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.por.fl_str_mv |
Desenvolvimento e caracterização de um banho não-cianetado para a eletrodeposição de ligas de Cu-Sn-Zn: caracterização dos eletrodepósitos |
dc.title.alternative.eng.fl_str_mv |
Development and characterization of a non-cianyde bath for Cu- Sn-Zn alloys electrodeposition: characterization of the Cu-Sn-Zn electrodeposits |
title |
Desenvolvimento e caracterização de um banho não-cianetado para a eletrodeposição de ligas de Cu-Sn-Zn: caracterização dos eletrodepósitos |
spellingShingle |
Desenvolvimento e caracterização de um banho não-cianetado para a eletrodeposição de ligas de Cu-Sn-Zn: caracterização dos eletrodepósitos Carvalho, Marcos Fernandes de Eletrodeposição Ligas Cu-Sn-Zn Planejamento fatorial de misturas Microestrutura Raios X - difração Análise multivariada CIENCIAS EXATAS E DA TERRA::QUIMICA |
title_short |
Desenvolvimento e caracterização de um banho não-cianetado para a eletrodeposição de ligas de Cu-Sn-Zn: caracterização dos eletrodepósitos |
title_full |
Desenvolvimento e caracterização de um banho não-cianetado para a eletrodeposição de ligas de Cu-Sn-Zn: caracterização dos eletrodepósitos |
title_fullStr |
Desenvolvimento e caracterização de um banho não-cianetado para a eletrodeposição de ligas de Cu-Sn-Zn: caracterização dos eletrodepósitos |
title_full_unstemmed |
Desenvolvimento e caracterização de um banho não-cianetado para a eletrodeposição de ligas de Cu-Sn-Zn: caracterização dos eletrodepósitos |
title_sort |
Desenvolvimento e caracterização de um banho não-cianetado para a eletrodeposição de ligas de Cu-Sn-Zn: caracterização dos eletrodepósitos |
author |
Carvalho, Marcos Fernandes de |
author_facet |
Carvalho, Marcos Fernandes de |
author_role |
author |
dc.contributor.authorlattes.por.fl_str_mv |
http://lattes.cnpq.br/0922916090536806 |
dc.contributor.author.fl_str_mv |
Carvalho, Marcos Fernandes de |
dc.contributor.advisor1.fl_str_mv |
Carlos, Ivani Aparecida |
dc.contributor.advisor1Lattes.fl_str_mv |
http://genos.cnpq.br:12010/dwlattes/owa/prc_imp_cv_int?f_cod=K4780131E6 |
dc.contributor.authorID.fl_str_mv |
da5b2f31-65c1-46aa-baf1-e2f30ec81a40 |
contributor_str_mv |
Carlos, Ivani Aparecida |
dc.subject.por.fl_str_mv |
Eletrodeposição Ligas Cu-Sn-Zn Planejamento fatorial de misturas Microestrutura Raios X - difração Análise multivariada |
topic |
Eletrodeposição Ligas Cu-Sn-Zn Planejamento fatorial de misturas Microestrutura Raios X - difração Análise multivariada CIENCIAS EXATAS E DA TERRA::QUIMICA |
dc.subject.cnpq.fl_str_mv |
CIENCIAS EXATAS E DA TERRA::QUIMICA |
description |
The electrodeposition of Cu-Sn-Zn ternary alloys onto AISI 1010 steel from an acid bath with EDTA or NTA salts was investigated, with various proportions of the metal ions in the baths. The concentration of these metals in the baths was determined by factorial design of mixtures with pseudocomponents. From potentiometric titration of these baths were determined regression equations, which led to studies of variance analysis and of surface response. These studies allowed to a pH of stabilization of the Cu-Sn-Zn electrodeposition baths. The Cu-Sn-Zn voltammetric profile showed five cathodic regions: c1, c1 , c2, c3 and c4 (depending on bath composition), and the conditional potentials for the Cu2+, Sn2+ and Zn2+ complexes indicated that these regions were associated, respectively, with reduction of [CuY]2- complex to Cu; [Sn(H2O)6]2+ complex to Sn; [SnY]2- complex to Sn; H2O to H2; and [ZnY]2- complex to Zn. In the presence of NTA, [Cu(NTA)2]4- and [SnNTA]-, [Sn(NTA)2]4-; H2O and [ZnNTA]- and [Zn(NTA)2]4-, respectively, in the regions c1, c2, c3 and c4. Cu-Sn-Zn electrodeposits produced at Ed 1.70 V with qd 3.0 C cm−2 were characterized by EDS, SEM, XRD and confocal optical microscopy (COM) analysis. EDS indicated that a transition potential exists wherein a transition from Cu-Sn binary alloy to Cu-Sn-Zn ternary alloy occurred and, also, that Cu-Sn-Zn co-deposition was normal, preferential or anomalous depending on the bath composition. Moreover, this analyze showed that Zn reduction was facilitated in the presence of NTA. SEM of electrodeposits showed that they were formed by globular and/or irregular crystallites, and, in general, by clusters of crystallites of different sizes dispersed on this layer, depending on the bath composition. COM analysis showed that electrodeposit produced from NTA was more roughness than with EDTA. XRD pattern indicated that the Cu-Sn-Zn electrodeposits, depending on the composition of the baths, presented low crystallinity or crystalline structure with mixture of SnO, η- Cu6Sn5 and Cu5Zn8 phases or pure Sn, η-Cu6Sn5 and Cu5Zn8 phases. Multivariate analysis allows extracting the maximum relevant chemical information from the data. |
publishDate |
2014 |
dc.date.available.fl_str_mv |
2014-08-01 2016-06-02T20:34:52Z |
dc.date.issued.fl_str_mv |
2014-05-16 |
dc.date.accessioned.fl_str_mv |
2016-06-02T20:34:52Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/doctoralThesis |
format |
doctoralThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
CARVALHO, Marcos Fernandes de. Development and characterization of a non-cianyde bath for Cu- Sn-Zn alloys electrodeposition. Characterization of the Cu-Sn-Zn electrodeposits. 2014. 1 f. Tese (Doutorado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2014. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufscar.br/handle/ufscar/6304 |
identifier_str_mv |
CARVALHO, Marcos Fernandes de. Development and characterization of a non-cianyde bath for Cu- Sn-Zn alloys electrodeposition. Characterization of the Cu-Sn-Zn electrodeposits. 2014. 1 f. Tese (Doutorado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2014. |
url |
https://repositorio.ufscar.br/handle/ufscar/6304 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.confidence.fl_str_mv |
-1 -1 |
dc.relation.authority.fl_str_mv |
6ab22b71-dd06-4945-bc9e-1a23f05da42e |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/embargoedAccess |
eu_rights_str_mv |
embargoedAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal de São Carlos |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Química - PPGQ |
dc.publisher.initials.fl_str_mv |
UFSCar |
dc.publisher.country.fl_str_mv |
BR |
publisher.none.fl_str_mv |
Universidade Federal de São Carlos |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFSCAR instname:Universidade Federal de São Carlos (UFSCAR) instacron:UFSCAR |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
UFSCAR |
institution |
UFSCAR |
reponame_str |
Repositório Institucional da UFSCAR |
collection |
Repositório Institucional da UFSCAR |
bitstream.url.fl_str_mv |
https://repositorio.ufscar.br/bitstream/ufscar/6304/1/TeseMFC.pdf https://repositorio.ufscar.br/bitstream/ufscar/6304/2/TeseMFC.pdf.txt https://repositorio.ufscar.br/bitstream/ufscar/6304/3/TeseMFC.pdf.jpg |
bitstream.checksum.fl_str_mv |
03051c46f677b648dd152a6d8107857a ae963f121a1d3b87214c6fb8e8af788f 63f5214186bf3c8f74c1cf553e637a06 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
|
_version_ |
1813715550418763776 |