Síntese assistida por microondas de LiMn2O4, caracterização e testes como catodo para dispositivos de armazenamento de energia
Autor(a) principal: | |
---|---|
Data de Publicação: | 2011 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFSCAR |
Texto Completo: | https://repositorio.ufscar.br/handle/ufscar/6492 |
Resumo: | Lithium manganese oxide - LiMn2O4 - was produced by a microwaveassited solid state reaction. Solid mixtures containing LiOH.H2O and -MnO2 (synthesized electrolytically) underwent microwave irradiation for 3, 4 and 5 min. The obtained material was characterized by X-ray diffraction (XRD), scanning electron microscopy and cyclic voltammetry. Conductivity measurements and charge / discharge tests were carried out with the mixture: 85% LiMn2O4 / 10% carbon black / 5% PVDF. XRD analyses showed that LiMn2O4 was obtained in a single phase of cubic structure belonging to the space group Fd3m in only 3 min of microwave irradiation. This short time for the LiMn2O4 synthesis represents an energy saving greater than 90% when compared with the time employed in the traditional method of synthesis. SEM micrographs showed morphological changes and particle size increase when the microwave irradiation time was increased. The mixture (85% LiMn2O4 / 10% carbon black / 5% PVDF) presented electronic conductivity similar to that of a semiconductor (σ ~ 10-1 S m-1), which is adequate for using as cathode in lithium ion battery. Charge and discharge tests showed good electrochemical stability for all the oxides synthesized at different times, evidenced by a small decrease (12 to 17%) of their specific capacities during 30 cycles of charge and discharge. The oxide produced at 3 min of microwave irradiation presented the highest charge supply (77 93 mA h g-1) at an elevated discharge rate (C/1), besides a highly uniform morphology and the lowest particle size (~1 μm). |
id |
SCAR_59c00de569ca22c7bc44da96b0a07fd1 |
---|---|
oai_identifier_str |
oai:repositorio.ufscar.br:ufscar/6492 |
network_acronym_str |
SCAR |
network_name_str |
Repositório Institucional da UFSCAR |
repository_id_str |
4322 |
spelling |
Silva, João Pedro daBiaggio, Sonia Reginahttp://lattes.cnpq.br/0418215244233120http://lattes.cnpq.br/2087603202355409035a501b-eea1-463b-bdb3-6ade62a465792016-06-02T20:36:31Z2011-05-202016-06-02T20:36:31Z2011-03-02SILVA, João Pedro da. Microwave-assisted sinthesys of LiMn2O4, characterization and testing as cathode for energy storage devices. 2011. 98 f. Dissertação (Mestrado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2011.https://repositorio.ufscar.br/handle/ufscar/6492Lithium manganese oxide - LiMn2O4 - was produced by a microwaveassited solid state reaction. Solid mixtures containing LiOH.H2O and -MnO2 (synthesized electrolytically) underwent microwave irradiation for 3, 4 and 5 min. The obtained material was characterized by X-ray diffraction (XRD), scanning electron microscopy and cyclic voltammetry. Conductivity measurements and charge / discharge tests were carried out with the mixture: 85% LiMn2O4 / 10% carbon black / 5% PVDF. XRD analyses showed that LiMn2O4 was obtained in a single phase of cubic structure belonging to the space group Fd3m in only 3 min of microwave irradiation. This short time for the LiMn2O4 synthesis represents an energy saving greater than 90% when compared with the time employed in the traditional method of synthesis. SEM micrographs showed morphological changes and particle size increase when the microwave irradiation time was increased. The mixture (85% LiMn2O4 / 10% carbon black / 5% PVDF) presented electronic conductivity similar to that of a semiconductor (σ ~ 10-1 S m-1), which is adequate for using as cathode in lithium ion battery. Charge and discharge tests showed good electrochemical stability for all the oxides synthesized at different times, evidenced by a small decrease (12 to 17%) of their specific capacities during 30 cycles of charge and discharge. The oxide produced at 3 min of microwave irradiation presented the highest charge supply (77 93 mA h g-1) at an elevated discharge rate (C/1), besides a highly uniform morphology and the lowest particle size (~1 μm).Óxido de manganês litiado - LiMn2O4 - foi produzido por uma rota de síntese diferenciada, a síntese de estado sólido assistida por microondas. Misturas sólidas contendo LiOH.H2O e -MnO2, sintetizado eletroliticamente, foram irradiadas por microondas durante 3, 4 e 5 min. O material obtido foi caracterizado por difratometria de raios-X (DRX), microscopia eletrônica de varredura (MEV) e voltametria cíclica. Também foram realizadas medidas de condutividade e testes de carga e descarga com a mistura: 85% LiMn2O4 / 10% negro de acetileno / 5% PVDF. As análises de DRX indicaram que LiMn2O4 foi obtido com estrutura cúbica pertencente ao grupo espacial Fd3m em apenas 3 min de irradiação de microondas. O reduzido tempo de síntese do espinélio representa uma economia energética superior a 90%, quando comparado com o tempo empregado no método tradicional de síntese. As micrografias de MEV mostraram alterações de morfologia, bem como aumento no tamanho de partícula conforme é aumentado o tempo de irradiação por microondas. A condutividade eletrônica da mistura (85% LiMn2O4 / 10% negro de acetileno / 5% PVDF) é da ordem daquela de um material semicondutor (σ ~ 10-1 S m-1), adequada para sua utilização como catodo em bateria de íons lítio. Os testes de carga e descarga mostraram que os óxidos obtidos a diferentes tempos apresentam boa estabilidade eletroquímica, com queda de capacidade específica durante 30 ciclos de carga e descarga variando de 12 a 17%. Entretanto, o LiMn2O4 produzido a 3 min por irradiação de microondas apresentou o maior fornecimento de carga (77 93 mA h g-1) quando os óxidos foram testados a uma elevada taxa de descarga (C/1). Além disso, este material destacou-se por apresentar uniformidade morfológica e o menor tamanho de partícula (~1 μm).Universidade Federal de Sao Carlosapplication/pdfporUniversidade Federal de São CarlosPrograma de Pós-Graduação em Química - PPGQUFSCarBREletroquímicaBaterias de íons-lítioEnergia - armazenamentoEspinélioCIENCIAS EXATAS E DA TERRA::QUIMICASíntese assistida por microondas de LiMn2O4, caracterização e testes como catodo para dispositivos de armazenamento de energiaMicrowave-assisted sinthesys of LiMn2O4, characterization and testing as cathode for energy storage devicesinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-1-10d9aad8b-4ef3-404d-a51d-c4786a32370cinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINAL3616.pdfapplication/pdf4536970https://repositorio.ufscar.br/bitstream/ufscar/6492/1/3616.pdfa09a48e60e18c8e6da33bf6a6d467ff4MD51THUMBNAIL3616.pdf.jpg3616.pdf.jpgIM Thumbnailimage/jpeg9179https://repositorio.ufscar.br/bitstream/ufscar/6492/2/3616.pdf.jpg0fe812287c3f7b8195231bff182334e3MD52ufscar/64922023-09-18 18:31:41.067oai:repositorio.ufscar.br:ufscar/6492Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222023-09-18T18:31:41Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.por.fl_str_mv |
Síntese assistida por microondas de LiMn2O4, caracterização e testes como catodo para dispositivos de armazenamento de energia |
dc.title.alternative.eng.fl_str_mv |
Microwave-assisted sinthesys of LiMn2O4, characterization and testing as cathode for energy storage devices |
title |
Síntese assistida por microondas de LiMn2O4, caracterização e testes como catodo para dispositivos de armazenamento de energia |
spellingShingle |
Síntese assistida por microondas de LiMn2O4, caracterização e testes como catodo para dispositivos de armazenamento de energia Silva, João Pedro da Eletroquímica Baterias de íons-lítio Energia - armazenamento Espinélio CIENCIAS EXATAS E DA TERRA::QUIMICA |
title_short |
Síntese assistida por microondas de LiMn2O4, caracterização e testes como catodo para dispositivos de armazenamento de energia |
title_full |
Síntese assistida por microondas de LiMn2O4, caracterização e testes como catodo para dispositivos de armazenamento de energia |
title_fullStr |
Síntese assistida por microondas de LiMn2O4, caracterização e testes como catodo para dispositivos de armazenamento de energia |
title_full_unstemmed |
Síntese assistida por microondas de LiMn2O4, caracterização e testes como catodo para dispositivos de armazenamento de energia |
title_sort |
Síntese assistida por microondas de LiMn2O4, caracterização e testes como catodo para dispositivos de armazenamento de energia |
author |
Silva, João Pedro da |
author_facet |
Silva, João Pedro da |
author_role |
author |
dc.contributor.authorlattes.por.fl_str_mv |
http://lattes.cnpq.br/2087603202355409 |
dc.contributor.author.fl_str_mv |
Silva, João Pedro da |
dc.contributor.advisor1.fl_str_mv |
Biaggio, Sonia Regina |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/0418215244233120 |
dc.contributor.authorID.fl_str_mv |
035a501b-eea1-463b-bdb3-6ade62a46579 |
contributor_str_mv |
Biaggio, Sonia Regina |
dc.subject.por.fl_str_mv |
Eletroquímica Baterias de íons-lítio Energia - armazenamento Espinélio |
topic |
Eletroquímica Baterias de íons-lítio Energia - armazenamento Espinélio CIENCIAS EXATAS E DA TERRA::QUIMICA |
dc.subject.cnpq.fl_str_mv |
CIENCIAS EXATAS E DA TERRA::QUIMICA |
description |
Lithium manganese oxide - LiMn2O4 - was produced by a microwaveassited solid state reaction. Solid mixtures containing LiOH.H2O and -MnO2 (synthesized electrolytically) underwent microwave irradiation for 3, 4 and 5 min. The obtained material was characterized by X-ray diffraction (XRD), scanning electron microscopy and cyclic voltammetry. Conductivity measurements and charge / discharge tests were carried out with the mixture: 85% LiMn2O4 / 10% carbon black / 5% PVDF. XRD analyses showed that LiMn2O4 was obtained in a single phase of cubic structure belonging to the space group Fd3m in only 3 min of microwave irradiation. This short time for the LiMn2O4 synthesis represents an energy saving greater than 90% when compared with the time employed in the traditional method of synthesis. SEM micrographs showed morphological changes and particle size increase when the microwave irradiation time was increased. The mixture (85% LiMn2O4 / 10% carbon black / 5% PVDF) presented electronic conductivity similar to that of a semiconductor (σ ~ 10-1 S m-1), which is adequate for using as cathode in lithium ion battery. Charge and discharge tests showed good electrochemical stability for all the oxides synthesized at different times, evidenced by a small decrease (12 to 17%) of their specific capacities during 30 cycles of charge and discharge. The oxide produced at 3 min of microwave irradiation presented the highest charge supply (77 93 mA h g-1) at an elevated discharge rate (C/1), besides a highly uniform morphology and the lowest particle size (~1 μm). |
publishDate |
2011 |
dc.date.available.fl_str_mv |
2011-05-20 2016-06-02T20:36:31Z |
dc.date.issued.fl_str_mv |
2011-03-02 |
dc.date.accessioned.fl_str_mv |
2016-06-02T20:36:31Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
SILVA, João Pedro da. Microwave-assisted sinthesys of LiMn2O4, characterization and testing as cathode for energy storage devices. 2011. 98 f. Dissertação (Mestrado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2011. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufscar.br/handle/ufscar/6492 |
identifier_str_mv |
SILVA, João Pedro da. Microwave-assisted sinthesys of LiMn2O4, characterization and testing as cathode for energy storage devices. 2011. 98 f. Dissertação (Mestrado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2011. |
url |
https://repositorio.ufscar.br/handle/ufscar/6492 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.confidence.fl_str_mv |
-1 -1 |
dc.relation.authority.fl_str_mv |
0d9aad8b-4ef3-404d-a51d-c4786a32370c |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal de São Carlos |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Química - PPGQ |
dc.publisher.initials.fl_str_mv |
UFSCar |
dc.publisher.country.fl_str_mv |
BR |
publisher.none.fl_str_mv |
Universidade Federal de São Carlos |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFSCAR instname:Universidade Federal de São Carlos (UFSCAR) instacron:UFSCAR |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
UFSCAR |
institution |
UFSCAR |
reponame_str |
Repositório Institucional da UFSCAR |
collection |
Repositório Institucional da UFSCAR |
bitstream.url.fl_str_mv |
https://repositorio.ufscar.br/bitstream/ufscar/6492/1/3616.pdf https://repositorio.ufscar.br/bitstream/ufscar/6492/2/3616.pdf.jpg |
bitstream.checksum.fl_str_mv |
a09a48e60e18c8e6da33bf6a6d467ff4 0fe812287c3f7b8195231bff182334e3 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
|
_version_ |
1802136295296729088 |