Efeito do pó de vidro na mitigação da reação álcali-sílica de compósitos cimentícios de alto desempenho
Autor(a) principal: | |
---|---|
Data de Publicação: | 2019 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFSCAR |
Texto Completo: | https://repositorio.ufscar.br/handle/ufscar/12137 |
Resumo: | For some years researches has been adressing the replacement of part of the cement used in concrete and mortars with alternative materials such as ground glass powder. This alternative reduces 〖CO〗_2, emissions since it’s used a smaller portion of concrete. In order for this substitution to be considered viable and applicable on the market, several factors and possible problems that this incorporation may result should be examined. One of the problems that can compromise the durability of concrete is the Alkali-Aggregate Reaction. This reaction causes expansion and fissure of concrete elements, by the chemical reaction between the reactive aggregate, alkaline concrete ions and hydroxyl ions, in the presence of moisture. So, this work aims to evaluate the effect of the incorporation of ground glass powder into cementied composites in the Alkali-Aggregate Reaction. Cementious composites were made with CPV cement, active silica, additives, sand with a maximum dimension of 1.2 mm, water (water/cement ratio of 0.18) and incorporation of glass powder in the contents of 0%,10%,20%,30% and 50% in volumetric replacement to cement. Tests were performed to characterize cementitious composites, axial compression resistance, capillarity water absorption, tensile strength by diametric compression, tensile strength in flexion, static elasticity module and dynamic. Expansion tests were performed in mortar bars by the accelerated method in order to evaluate the mitigation of expansions. The results show that the incorporation of glass powder did not interfere in the workability of the mixture in the fresh state, and reduced the air content incorporated into the mixture. There was an improvement in the mechanical and physical properties of cementitious composites from 28 days, such as a decrease in water absorption by capillarity and resistance to axial compression, obtaining the highest value for composite with 30% of glass powder in 129.03 MPa and high elasticity modules, in order of 45 to 50 GPa, characteristics of high performance concrete. Concerning the results found for cementitious composites with incorporation of glass powder, they reached values close to those of the reference material. Already for the specific tests of Alkali-Silica Reaction, it is noted that the contents of 10 and 20% of glass powder incorporation increased expansions in the mortar bars studied and the contents of 30 and 50% decreased to expansions, reaching dimensional variations close to 0%. Therefore, the behavior in the face of the Alkali-Silica Reaction varied according to the glass powder content of the mixtures. It was found that 30 and 50% of incorporation are the optimal substitution levels in relation to the alkali-silica reaction. |
id |
SCAR_87bad5d64a3009b540afa1833710bff8 |
---|---|
oai_identifier_str |
oai:repositorio.ufscar.br:ufscar/12137 |
network_acronym_str |
SCAR |
network_name_str |
Repositório Institucional da UFSCAR |
repository_id_str |
4322 |
spelling |
Freitas, Taís Oliveira GonçalvesFerreira, Fernanda Giannotti da Silvahttp://lattes.cnpq.br/0329487394818763http://lattes.cnpq.br/892477243434879543f154cc-b403-4f9e-8424-101f8938a78e2020-01-09T13:18:09Z2020-01-09T13:18:09Z2019-11-06FREITAS, Taís Oliveira Gonçalves. Efeito do pó de vidro na mitigação da reação álcali-sílica de compósitos cimentícios de alto desempenho. 2019. Dissertação (Mestrado em Engenharia Civil) – Universidade Federal de São Carlos, São Carlos, 2019. Disponível em: https://repositorio.ufscar.br/handle/ufscar/12137.https://repositorio.ufscar.br/handle/ufscar/12137For some years researches has been adressing the replacement of part of the cement used in concrete and mortars with alternative materials such as ground glass powder. This alternative reduces 〖CO〗_2, emissions since it’s used a smaller portion of concrete. In order for this substitution to be considered viable and applicable on the market, several factors and possible problems that this incorporation may result should be examined. One of the problems that can compromise the durability of concrete is the Alkali-Aggregate Reaction. This reaction causes expansion and fissure of concrete elements, by the chemical reaction between the reactive aggregate, alkaline concrete ions and hydroxyl ions, in the presence of moisture. So, this work aims to evaluate the effect of the incorporation of ground glass powder into cementied composites in the Alkali-Aggregate Reaction. Cementious composites were made with CPV cement, active silica, additives, sand with a maximum dimension of 1.2 mm, water (water/cement ratio of 0.18) and incorporation of glass powder in the contents of 0%,10%,20%,30% and 50% in volumetric replacement to cement. Tests were performed to characterize cementitious composites, axial compression resistance, capillarity water absorption, tensile strength by diametric compression, tensile strength in flexion, static elasticity module and dynamic. Expansion tests were performed in mortar bars by the accelerated method in order to evaluate the mitigation of expansions. The results show that the incorporation of glass powder did not interfere in the workability of the mixture in the fresh state, and reduced the air content incorporated into the mixture. There was an improvement in the mechanical and physical properties of cementitious composites from 28 days, such as a decrease in water absorption by capillarity and resistance to axial compression, obtaining the highest value for composite with 30% of glass powder in 129.03 MPa and high elasticity modules, in order of 45 to 50 GPa, characteristics of high performance concrete. Concerning the results found for cementitious composites with incorporation of glass powder, they reached values close to those of the reference material. Already for the specific tests of Alkali-Silica Reaction, it is noted that the contents of 10 and 20% of glass powder incorporation increased expansions in the mortar bars studied and the contents of 30 and 50% decreased to expansions, reaching dimensional variations close to 0%. Therefore, the behavior in the face of the Alkali-Silica Reaction varied according to the glass powder content of the mixtures. It was found that 30 and 50% of incorporation are the optimal substitution levels in relation to the alkali-silica reaction.Há alguns anos pesquisas vem abordando a substituição de parte do cimento utilizado em concretos e argamassas por materiais alternativos como o pó de vidro moído. Essa alternativa reduz a emissão de 〖CO〗_2, já que é utilizada uma parcela menor de cimento. Para que essa substituição seja considerada viável e aplicável no mercado, deve-se analisar diversos fatores e possíveis problemas que esta incorporação pode acarretar. Um dos problemas que pode comprometer a durabilidade do concreto é a reação álcali-agregado. Essa reação causa expansão e fissuração dos elementos de concreto, pela reação química entre o agregado reativo, íons alcalinos do concreto e íons hidroxila, na presença de umidade. Assim, este trabalho tem o objetivo de avaliar o efeito da incorporação de pó de vidro moído em compósitos cimentícios na reação álcali-agregado. Foram confeccionados compósitos cimentícios com cimento CPV, sílica ativa, aditivos, areia com dimensão máxima de 1,2 mm, água (relação água/cimento de 0,18) e incorporação de pó de vidro nos teores de 0%,10%,20%,30% e 50% em substituição volumétrica ao cimento. Foram realizados ensaios para a caracterização dos compósitos cimentícios, resistência à compressão axial, absorção de água por capilaridade, resistência à tração por compressão diametral, resistência à tração na flexão, módulo de elasticidade estático e dinâmico. Foram realizados ensaios de expansão em barras de argamassa pelo método acelerado com o objetivo de avaliar a mitigação das expansões. Os resultados mostram que a incorporação de pó de vidro não interferiu na trabalhabilidade da mistura, além de ter reduzido o teor de ar incorporado na mistura. Observou-se uma melhoria de propriedades físicas e mecânicas dos compósitos cimentícios a partir dos 28 dias, como por exemplo, uma diminuição na absorção de água por capilaridade. Avaliando a resistência à compressão axial, obteve-se o maior valor para o compósito com incorporação de 30% de pó de vidro em 129,03 MPa e módulos de elasticidade altos, na ordem de 45 a 50 GPa, características do concreto de alto desempenho. Em relação aos resultados encontrados para os compósitos cimentícios com incorporação de pó de vidro, estes alcançaram valores próximos aos do material de referência. Já para os ensaios específicos de reação álcali-sílica, nota-se que os teores de 10 e 20% de incorporação de pó de vidro aumentaram as expansões nas barras de argamassa estudadas e os teores de 30 e 50% diminuíram as expansões, chegando a variações dimensionais próximas de 0%. Portanto, o comportamento frente à reação álcali-sílica variou de acordo com o teor de pó de vidro das misturas. Foi possível constatar que 30 e 50% de incorporação são os teores ótimos de substituição em relação à reação álcali-sílica.Não recebi financiamentoporUniversidade Federal de São CarlosCâmpus São CarlosPrograma de Pós-Graduação em Engenharia Civil - PPGECivUFSCarAttribution-NonCommercial-NoDerivs 3.0 Brazilhttp://creativecommons.org/licenses/by-nc-nd/3.0/br/info:eu-repo/semantics/openAccessCompósito cimentícioPó de vidroMitigaçãoReação álcali-silicaCement compositeAlkali-silica reactionGlass powderMitigationENGENHARIAS::ENGENHARIA CIVIL::CONSTRUCAO CIVILEfeito do pó de vidro na mitigação da reação álcali-sílica de compósitos cimentícios de alto desempenhoEffect of glass powder on the mitigation of alkali-silica reaction of high performance cementitious composites.info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis600600f87ab993-25ae-46c4-9870-968e4b38f539reponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINALTexto de dissertação final - Taís Oliveira G. Freitas.pdfTexto de dissertação final - Taís Oliveira G. Freitas.pdfDissertação de mestradoapplication/pdf3560943https://repositorio.ufscar.br/bitstream/ufscar/12137/1/Texto%20de%20disserta%c3%a7%c3%a3o%20final%20-%20Ta%c3%ads%20Oliveira%20G.%20Freitas.pdf928b4c0808920c2bf6a59da11ecaac89MD51Carta de aprovação - Professora Fernanda.pdfCarta de aprovação - Professora Fernanda.pdfCarta comprovante da orientadoraapplication/pdf313098https://repositorio.ufscar.br/bitstream/ufscar/12137/2/Carta%20de%20aprova%c3%a7%c3%a3o%20-%20Professora%20Fernanda.pdf3d12b39469af327f7907b9619c879746MD52CC-LICENSElicense_rdflicense_rdfapplication/rdf+xml; charset=utf-8811https://repositorio.ufscar.br/bitstream/ufscar/12137/3/license_rdfe39d27027a6cc9cb039ad269a5db8e34MD53TEXTTexto de dissertação final - Taís Oliveira G. Freitas.pdf.txtTexto de dissertação final - Taís Oliveira G. Freitas.pdf.txtExtracted texttext/plain242923https://repositorio.ufscar.br/bitstream/ufscar/12137/4/Texto%20de%20disserta%c3%a7%c3%a3o%20final%20-%20Ta%c3%ads%20Oliveira%20G.%20Freitas.pdf.txt95a27511f90a5ad97db5c6588b20a0c7MD54Carta de aprovação - Professora Fernanda.pdf.txtCarta de aprovação - Professora Fernanda.pdf.txtExtracted texttext/plain1289https://repositorio.ufscar.br/bitstream/ufscar/12137/6/Carta%20de%20aprova%c3%a7%c3%a3o%20-%20Professora%20Fernanda.pdf.txt09dfdfb88c72580c766199f7bba1384dMD56THUMBNAILTexto de dissertação final - Taís Oliveira G. Freitas.pdf.jpgTexto de dissertação final - Taís Oliveira G. Freitas.pdf.jpgIM Thumbnailimage/jpeg6852https://repositorio.ufscar.br/bitstream/ufscar/12137/5/Texto%20de%20disserta%c3%a7%c3%a3o%20final%20-%20Ta%c3%ads%20Oliveira%20G.%20Freitas.pdf.jpgf7e8df2158d9f9d8c02ca429c6e7e882MD55Carta de aprovação - Professora Fernanda.pdf.jpgCarta de aprovação - Professora Fernanda.pdf.jpgIM Thumbnailimage/jpeg12929https://repositorio.ufscar.br/bitstream/ufscar/12137/7/Carta%20de%20aprova%c3%a7%c3%a3o%20-%20Professora%20Fernanda.pdf.jpg9cd32b1ba8898f8bbc83f00a780001baMD57ufscar/121372023-09-18 18:31:48.054oai:repositorio.ufscar.br:ufscar/12137Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222023-09-18T18:31:48Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.por.fl_str_mv |
Efeito do pó de vidro na mitigação da reação álcali-sílica de compósitos cimentícios de alto desempenho |
dc.title.alternative.eng.fl_str_mv |
Effect of glass powder on the mitigation of alkali-silica reaction of high performance cementitious composites. |
title |
Efeito do pó de vidro na mitigação da reação álcali-sílica de compósitos cimentícios de alto desempenho |
spellingShingle |
Efeito do pó de vidro na mitigação da reação álcali-sílica de compósitos cimentícios de alto desempenho Freitas, Taís Oliveira Gonçalves Compósito cimentício Pó de vidro Mitigação Reação álcali-silica Cement composite Alkali-silica reaction Glass powder Mitigation ENGENHARIAS::ENGENHARIA CIVIL::CONSTRUCAO CIVIL |
title_short |
Efeito do pó de vidro na mitigação da reação álcali-sílica de compósitos cimentícios de alto desempenho |
title_full |
Efeito do pó de vidro na mitigação da reação álcali-sílica de compósitos cimentícios de alto desempenho |
title_fullStr |
Efeito do pó de vidro na mitigação da reação álcali-sílica de compósitos cimentícios de alto desempenho |
title_full_unstemmed |
Efeito do pó de vidro na mitigação da reação álcali-sílica de compósitos cimentícios de alto desempenho |
title_sort |
Efeito do pó de vidro na mitigação da reação álcali-sílica de compósitos cimentícios de alto desempenho |
author |
Freitas, Taís Oliveira Gonçalves |
author_facet |
Freitas, Taís Oliveira Gonçalves |
author_role |
author |
dc.contributor.authorlattes.por.fl_str_mv |
http://lattes.cnpq.br/8924772434348795 |
dc.contributor.author.fl_str_mv |
Freitas, Taís Oliveira Gonçalves |
dc.contributor.advisor1.fl_str_mv |
Ferreira, Fernanda Giannotti da Silva |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/0329487394818763 |
dc.contributor.authorID.fl_str_mv |
43f154cc-b403-4f9e-8424-101f8938a78e |
contributor_str_mv |
Ferreira, Fernanda Giannotti da Silva |
dc.subject.por.fl_str_mv |
Compósito cimentício Pó de vidro Mitigação Reação álcali-silica |
topic |
Compósito cimentício Pó de vidro Mitigação Reação álcali-silica Cement composite Alkali-silica reaction Glass powder Mitigation ENGENHARIAS::ENGENHARIA CIVIL::CONSTRUCAO CIVIL |
dc.subject.eng.fl_str_mv |
Cement composite Alkali-silica reaction Glass powder Mitigation |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS::ENGENHARIA CIVIL::CONSTRUCAO CIVIL |
description |
For some years researches has been adressing the replacement of part of the cement used in concrete and mortars with alternative materials such as ground glass powder. This alternative reduces 〖CO〗_2, emissions since it’s used a smaller portion of concrete. In order for this substitution to be considered viable and applicable on the market, several factors and possible problems that this incorporation may result should be examined. One of the problems that can compromise the durability of concrete is the Alkali-Aggregate Reaction. This reaction causes expansion and fissure of concrete elements, by the chemical reaction between the reactive aggregate, alkaline concrete ions and hydroxyl ions, in the presence of moisture. So, this work aims to evaluate the effect of the incorporation of ground glass powder into cementied composites in the Alkali-Aggregate Reaction. Cementious composites were made with CPV cement, active silica, additives, sand with a maximum dimension of 1.2 mm, water (water/cement ratio of 0.18) and incorporation of glass powder in the contents of 0%,10%,20%,30% and 50% in volumetric replacement to cement. Tests were performed to characterize cementitious composites, axial compression resistance, capillarity water absorption, tensile strength by diametric compression, tensile strength in flexion, static elasticity module and dynamic. Expansion tests were performed in mortar bars by the accelerated method in order to evaluate the mitigation of expansions. The results show that the incorporation of glass powder did not interfere in the workability of the mixture in the fresh state, and reduced the air content incorporated into the mixture. There was an improvement in the mechanical and physical properties of cementitious composites from 28 days, such as a decrease in water absorption by capillarity and resistance to axial compression, obtaining the highest value for composite with 30% of glass powder in 129.03 MPa and high elasticity modules, in order of 45 to 50 GPa, characteristics of high performance concrete. Concerning the results found for cementitious composites with incorporation of glass powder, they reached values close to those of the reference material. Already for the specific tests of Alkali-Silica Reaction, it is noted that the contents of 10 and 20% of glass powder incorporation increased expansions in the mortar bars studied and the contents of 30 and 50% decreased to expansions, reaching dimensional variations close to 0%. Therefore, the behavior in the face of the Alkali-Silica Reaction varied according to the glass powder content of the mixtures. It was found that 30 and 50% of incorporation are the optimal substitution levels in relation to the alkali-silica reaction. |
publishDate |
2019 |
dc.date.issued.fl_str_mv |
2019-11-06 |
dc.date.accessioned.fl_str_mv |
2020-01-09T13:18:09Z |
dc.date.available.fl_str_mv |
2020-01-09T13:18:09Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
FREITAS, Taís Oliveira Gonçalves. Efeito do pó de vidro na mitigação da reação álcali-sílica de compósitos cimentícios de alto desempenho. 2019. Dissertação (Mestrado em Engenharia Civil) – Universidade Federal de São Carlos, São Carlos, 2019. Disponível em: https://repositorio.ufscar.br/handle/ufscar/12137. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufscar.br/handle/ufscar/12137 |
identifier_str_mv |
FREITAS, Taís Oliveira Gonçalves. Efeito do pó de vidro na mitigação da reação álcali-sílica de compósitos cimentícios de alto desempenho. 2019. Dissertação (Mestrado em Engenharia Civil) – Universidade Federal de São Carlos, São Carlos, 2019. Disponível em: https://repositorio.ufscar.br/handle/ufscar/12137. |
url |
https://repositorio.ufscar.br/handle/ufscar/12137 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.confidence.fl_str_mv |
600 600 |
dc.relation.authority.fl_str_mv |
f87ab993-25ae-46c4-9870-968e4b38f539 |
dc.rights.driver.fl_str_mv |
Attribution-NonCommercial-NoDerivs 3.0 Brazil http://creativecommons.org/licenses/by-nc-nd/3.0/br/ info:eu-repo/semantics/openAccess |
rights_invalid_str_mv |
Attribution-NonCommercial-NoDerivs 3.0 Brazil http://creativecommons.org/licenses/by-nc-nd/3.0/br/ |
eu_rights_str_mv |
openAccess |
dc.publisher.none.fl_str_mv |
Universidade Federal de São Carlos Câmpus São Carlos |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Engenharia Civil - PPGECiv |
dc.publisher.initials.fl_str_mv |
UFSCar |
publisher.none.fl_str_mv |
Universidade Federal de São Carlos Câmpus São Carlos |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFSCAR instname:Universidade Federal de São Carlos (UFSCAR) instacron:UFSCAR |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
UFSCAR |
institution |
UFSCAR |
reponame_str |
Repositório Institucional da UFSCAR |
collection |
Repositório Institucional da UFSCAR |
bitstream.url.fl_str_mv |
https://repositorio.ufscar.br/bitstream/ufscar/12137/1/Texto%20de%20disserta%c3%a7%c3%a3o%20final%20-%20Ta%c3%ads%20Oliveira%20G.%20Freitas.pdf https://repositorio.ufscar.br/bitstream/ufscar/12137/2/Carta%20de%20aprova%c3%a7%c3%a3o%20-%20Professora%20Fernanda.pdf https://repositorio.ufscar.br/bitstream/ufscar/12137/3/license_rdf https://repositorio.ufscar.br/bitstream/ufscar/12137/4/Texto%20de%20disserta%c3%a7%c3%a3o%20final%20-%20Ta%c3%ads%20Oliveira%20G.%20Freitas.pdf.txt https://repositorio.ufscar.br/bitstream/ufscar/12137/6/Carta%20de%20aprova%c3%a7%c3%a3o%20-%20Professora%20Fernanda.pdf.txt https://repositorio.ufscar.br/bitstream/ufscar/12137/5/Texto%20de%20disserta%c3%a7%c3%a3o%20final%20-%20Ta%c3%ads%20Oliveira%20G.%20Freitas.pdf.jpg https://repositorio.ufscar.br/bitstream/ufscar/12137/7/Carta%20de%20aprova%c3%a7%c3%a3o%20-%20Professora%20Fernanda.pdf.jpg |
bitstream.checksum.fl_str_mv |
928b4c0808920c2bf6a59da11ecaac89 3d12b39469af327f7907b9619c879746 e39d27027a6cc9cb039ad269a5db8e34 95a27511f90a5ad97db5c6588b20a0c7 09dfdfb88c72580c766199f7bba1384d f7e8df2158d9f9d8c02ca429c6e7e882 9cd32b1ba8898f8bbc83f00a780001ba |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
|
_version_ |
1802136367837216768 |