Estudo dos efeitos da substituição de Feldspato por Filito em massas de porcelanato
Autor(a) principal: | |
---|---|
Data de Publicação: | 2018 |
Tipo de documento: | Tese |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFSCAR |
Texto Completo: | https://repositorio.ufscar.br/handle/ufscar/10829 |
Resumo: | Porcelain stoneware tiles, porcelanatos, present excellent technical and aesthetic characteristics. In Europe, the bodies used in the manufacture of porcelain and porcelanatos are based on the classic triaxial ceramic, clay, quartz and feldspar, and the latter plays the role of flux. Bodies of this type have been thoroughly studied. In Brazil, for various reasons, virtually all the industries that produce glazed porcelain stoneware tiles replaced feldspar by the phyllites. Although this practice, the replacement of feldspar by phyllites, has already occurred for some decades, the implications of this substitution have not been properly studied. The general objective of this work was to identify and seek explanations for the differences in behavior during firing caused by the substitution of feldspar by phyllite in the bodies used in the manufacture of glazed porcelain stoneware tiles. For this, the raw materials alone, feldspar and phyllites, as well as bodies containing the same content of these raw materials, were evaluated comparatively. Based on the results produced by several characterization techniques, among them the gresification curves and the chemical composition of the vitreous phases after the firing, the following conclusions were reached: 1) the behavior of the raw materials, feldspar and phyllites during firing are quite different; 2) different phyllites exhibit significantly different behavior during firing; 3) the differences in behavior between the phyllites is mainly due to the variation of the sericite content (muscovite fine-grained mica); 4) the behavior of pure raw materials is transferred to the masses which contain them.; 5) although the minerals responsible for forming the liquid phase during firing are significantly different, a mixture of feldspar, albite and orthoclase, and sericite, the chemical compositions of the vitreous phases formed are similar; 6) the volume of liquid phase during sintering seems to be one of the main variable responsible for the observed differences in the behaviour during firing. |
id |
SCAR_9f21704adb85192a3c2a54b7a2c07f24 |
---|---|
oai_identifier_str |
oai:repositorio.ufscar.br:ufscar/10829 |
network_acronym_str |
SCAR |
network_name_str |
Repositório Institucional da UFSCAR |
repository_id_str |
4322 |
spelling |
Sanchez, Miguel Yesid HernandezBoschi, Anselmo Ortegahttp://lattes.cnpq.br/3259846931278607Dondi, Michelehttp://lattes.cnpq.br/4617859135105539http://lattes.cnpq.br/063242405361990409fb3d0f-965a-4856-babb-db3319de169a2019-01-10T19:10:48Z2019-01-10T19:10:48Z2018-11-21SANCHEZ, Miguel Yesid Hernandez. Estudo dos efeitos da substituição de Feldspato por Filito em massas de porcelanato. 2018. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2018. Disponível em: https://repositorio.ufscar.br/handle/ufscar/10829.https://repositorio.ufscar.br/handle/ufscar/10829Porcelain stoneware tiles, porcelanatos, present excellent technical and aesthetic characteristics. In Europe, the bodies used in the manufacture of porcelain and porcelanatos are based on the classic triaxial ceramic, clay, quartz and feldspar, and the latter plays the role of flux. Bodies of this type have been thoroughly studied. In Brazil, for various reasons, virtually all the industries that produce glazed porcelain stoneware tiles replaced feldspar by the phyllites. Although this practice, the replacement of feldspar by phyllites, has already occurred for some decades, the implications of this substitution have not been properly studied. The general objective of this work was to identify and seek explanations for the differences in behavior during firing caused by the substitution of feldspar by phyllite in the bodies used in the manufacture of glazed porcelain stoneware tiles. For this, the raw materials alone, feldspar and phyllites, as well as bodies containing the same content of these raw materials, were evaluated comparatively. Based on the results produced by several characterization techniques, among them the gresification curves and the chemical composition of the vitreous phases after the firing, the following conclusions were reached: 1) the behavior of the raw materials, feldspar and phyllites during firing are quite different; 2) different phyllites exhibit significantly different behavior during firing; 3) the differences in behavior between the phyllites is mainly due to the variation of the sericite content (muscovite fine-grained mica); 4) the behavior of pure raw materials is transferred to the masses which contain them.; 5) although the minerals responsible for forming the liquid phase during firing are significantly different, a mixture of feldspar, albite and orthoclase, and sericite, the chemical compositions of the vitreous phases formed are similar; 6) the volume of liquid phase during sintering seems to be one of the main variable responsible for the observed differences in the behaviour during firing.El porcelanato como revestimiento cerámico se destaca en el mercado mundial actual, ya que presenta excelentes características técnicas y estéticas. En Europa, las pastas utilizadas en la fabricación de porcelanas y porcelanatos se basan en el clásico triaxial cerámico, arcilla, cuarzo y feldespato, este último desempeña el papel de fundente. Estas tipologías de pastas porcelánicas fueron estudiadas exhaustivamente. En el Brasil, por diversos motivos, prácticamente todas las industrias productoras de porcelanatos esmaltados sustituyeron feldespato por filito. Aunque la práctica de sustituir feldespato por filito, ocurre hace varias décadas, no se tiene registro de ningún tratado que haya estudiado sistemáticamente sus implicaciones. El objetivo general del presente estudio fue identificar y buscar las explicaciones de las diferencias de comportamiento durante la quema producido por la sustitución de feldespato por filito en pastas utilizadas en la manufactura de porcelanatos esmaltados. Para tal fin, se evaluaron comparativamente las materias primas, feldespato e filitos, así como las pastas porcelânicas que contienen estos fundentes a una misma concentración. Los resultados encontrados por distintas técnicas de caracterización, entre ellas las curvas de gresificación y composición química de las fases vítreas después de la quema, se concluye que: 1) el comportamiento de las materias primas, feldespato e filitos durante la quema son bastante diferentes; 2) diferentes filitos presentan comportamientos significativamente diferentes durante la quema; 3) las diferencias de comportamiento entre filitos es principalmente debido a la variación de concentración de la sericita (mica moscovita de granulación fina); 4) el comportamiento de las materias primas puras es transferido a las pastas que las contienen; 5) aunque los minerales responsables por la formación de la fase líquida durante la quema sean significativamente diferentes, una mezcla de feldespatos, albita e ortoclasa, y sericita, las composiciones químicas de las fases vítreas formadas son muy similares; 6) la variación de volumen de la fase líquida durante la quema parece ser una de las principales variables responsables por las diferencias observadas.O porcelanato como revestimento cerâmico se destaca no mercado mundial atual apresentando excelentes características técnicas e estéticas. Na Europa, as massas utilizadas na fabricação de porcelanas e porcelanatos baseiam-se no clássico triaxial cerâmico, argila, quartzo e feldspato, sendo que este último desempenha a função de fundente. Massas desse tipo foram exaustivamente estudadas. No Brasil, por motivos diversos, praticamente todas as indústrias que produzem porcelanatos esmaltados substituíram o feldspato pelo filito. Muito embora essa prática, a substituição do feldspato pelo filito, já ocorra há algumas décadas, não se tem notícia de nenhum estudo que tenha sistematicamente estudado suas implicações. O objetivo geral deste trabalho foi identificar e buscar explicações para as diferenças de comportamento durante a queima decorrentes da substituição do feldspato pelo filito nas massas empregadas na fabricação de porcelanatos esmaltados. Para isso avaliou-se comparativamente as matérias-primas sozinhas, feldspato e filitos, assim como massas contendo o mesmo teor das mesmas. Com os resultados produzidos por várias técnicas de caracterização, dentre elas as curvas de gresificação e a composição química das fases vítreas após a queima, chegou-se às seguintes conclusões: 1) o comportamento das matérias-primas, feldspato e filitos, durante a queima são bastante diferentes; 2) diferentes filitos apresentam comportamentos significativamente distintos durante a queima; 3) as diferenças de comportamento entre os filitos é majoritariamente decorrente da variação do teor de sericita (mica muscovita de granulação fina); 4) o comportamento das matérias-primas puras, sozinhas, é transferido para as massas que as contém; 5) muito embora os minerais responsáveis pela formação da fase líquida durante a queima sejam significativamente diferentes, uma mistura de feldspatos, albita e ortoclásio, e sericita, as composições químicas das fases vítreas formadas são similares; 6) a variação do volume de fase líquida durante a queima parece ser uma das principais variáveis responsáveis pelas diferenças observadas.Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)CAPES: Código do Financiamento 001porUniversidade Federal de São CarlosCâmpus São CarlosPrograma de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEMUFSCarPorcelanatoFilito cerâmicoSericitaFluxo viscosoGresificaçãoPorcelain tilePhylliteSericiteViscous flowGresificationPorcelanatoFilito cerámicoSericitaFlujo viscosoGresificaciónENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOSENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICAEstudo dos efeitos da substituição de Feldspato por Filito em massas de porcelanatoEffects of substituting Feldspar by brazilian Phyllite in glazed porcelain bodiesEstudio de los efectos de la sustitución de Feldespato por Filito en pastas de porcelanatoinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisOnlinedef1d9c8-353a-4dec-a3b5-c49b68749aedinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINALMiguel Yesid Hernandez Sanchez - Tese.pdfMiguel Yesid Hernandez Sanchez - Tese.pdfapplication/pdf3731787https://repositorio.ufscar.br/bitstream/ufscar/10829/1/Miguel%20Yesid%20Hernandez%20Sanchez%20-%20Tese.pdffc6a5593a2daae5c04c4d9d33ee0bedcMD51LICENSElicense.txtlicense.txttext/plain; charset=utf-81957https://repositorio.ufscar.br/bitstream/ufscar/10829/3/license.txtae0398b6f8b235e40ad82cba6c50031dMD53TEXTMiguel Yesid Hernandez Sanchez - Tese.pdf.txtMiguel Yesid Hernandez Sanchez - Tese.pdf.txtExtracted texttext/plain214038https://repositorio.ufscar.br/bitstream/ufscar/10829/4/Miguel%20Yesid%20Hernandez%20Sanchez%20-%20Tese.pdf.txt9d7486210c5f2a35a4be9f57c5aa9fb6MD54THUMBNAILMiguel Yesid Hernandez Sanchez - Tese.pdf.jpgMiguel Yesid Hernandez Sanchez - Tese.pdf.jpgIM Thumbnailimage/jpeg6532https://repositorio.ufscar.br/bitstream/ufscar/10829/5/Miguel%20Yesid%20Hernandez%20Sanchez%20-%20Tese.pdf.jpgb9d4d1244ab45b1255041178f285b4edMD55ufscar/108292023-09-18 18:31:18.95oai:repositorio.ufscar.br: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Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222023-09-18T18:31:18Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.por.fl_str_mv |
Estudo dos efeitos da substituição de Feldspato por Filito em massas de porcelanato |
dc.title.alternative.eng.fl_str_mv |
Effects of substituting Feldspar by brazilian Phyllite in glazed porcelain bodies |
dc.title.alternative.spa.fl_str_mv |
Estudio de los efectos de la sustitución de Feldespato por Filito en pastas de porcelanato |
title |
Estudo dos efeitos da substituição de Feldspato por Filito em massas de porcelanato |
spellingShingle |
Estudo dos efeitos da substituição de Feldspato por Filito em massas de porcelanato Sanchez, Miguel Yesid Hernandez Porcelanato Filito cerâmico Sericita Fluxo viscoso Gresificação Porcelain tile Phyllite Sericite Viscous flow Gresification Porcelanato Filito cerámico Sericita Flujo viscoso Gresificación ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
title_short |
Estudo dos efeitos da substituição de Feldspato por Filito em massas de porcelanato |
title_full |
Estudo dos efeitos da substituição de Feldspato por Filito em massas de porcelanato |
title_fullStr |
Estudo dos efeitos da substituição de Feldspato por Filito em massas de porcelanato |
title_full_unstemmed |
Estudo dos efeitos da substituição de Feldspato por Filito em massas de porcelanato |
title_sort |
Estudo dos efeitos da substituição de Feldspato por Filito em massas de porcelanato |
author |
Sanchez, Miguel Yesid Hernandez |
author_facet |
Sanchez, Miguel Yesid Hernandez |
author_role |
author |
dc.contributor.authorlattes.por.fl_str_mv |
http://lattes.cnpq.br/0632424053619904 |
dc.contributor.author.fl_str_mv |
Sanchez, Miguel Yesid Hernandez |
dc.contributor.advisor1.fl_str_mv |
Boschi, Anselmo Ortega |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/3259846931278607 |
dc.contributor.advisor-co1.fl_str_mv |
Dondi, Michele |
dc.contributor.advisor-co1Lattes.fl_str_mv |
http://lattes.cnpq.br/4617859135105539 |
dc.contributor.authorID.fl_str_mv |
09fb3d0f-965a-4856-babb-db3319de169a |
contributor_str_mv |
Boschi, Anselmo Ortega Dondi, Michele |
dc.subject.por.fl_str_mv |
Porcelanato Filito cerâmico Sericita Fluxo viscoso Gresificação |
topic |
Porcelanato Filito cerâmico Sericita Fluxo viscoso Gresificação Porcelain tile Phyllite Sericite Viscous flow Gresification Porcelanato Filito cerámico Sericita Flujo viscoso Gresificación ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
dc.subject.eng.fl_str_mv |
Porcelain tile Phyllite Sericite Viscous flow Gresification |
dc.subject.spa.fl_str_mv |
Porcelanato Filito cerámico Sericita Flujo viscoso Gresificación |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
description |
Porcelain stoneware tiles, porcelanatos, present excellent technical and aesthetic characteristics. In Europe, the bodies used in the manufacture of porcelain and porcelanatos are based on the classic triaxial ceramic, clay, quartz and feldspar, and the latter plays the role of flux. Bodies of this type have been thoroughly studied. In Brazil, for various reasons, virtually all the industries that produce glazed porcelain stoneware tiles replaced feldspar by the phyllites. Although this practice, the replacement of feldspar by phyllites, has already occurred for some decades, the implications of this substitution have not been properly studied. The general objective of this work was to identify and seek explanations for the differences in behavior during firing caused by the substitution of feldspar by phyllite in the bodies used in the manufacture of glazed porcelain stoneware tiles. For this, the raw materials alone, feldspar and phyllites, as well as bodies containing the same content of these raw materials, were evaluated comparatively. Based on the results produced by several characterization techniques, among them the gresification curves and the chemical composition of the vitreous phases after the firing, the following conclusions were reached: 1) the behavior of the raw materials, feldspar and phyllites during firing are quite different; 2) different phyllites exhibit significantly different behavior during firing; 3) the differences in behavior between the phyllites is mainly due to the variation of the sericite content (muscovite fine-grained mica); 4) the behavior of pure raw materials is transferred to the masses which contain them.; 5) although the minerals responsible for forming the liquid phase during firing are significantly different, a mixture of feldspar, albite and orthoclase, and sericite, the chemical compositions of the vitreous phases formed are similar; 6) the volume of liquid phase during sintering seems to be one of the main variable responsible for the observed differences in the behaviour during firing. |
publishDate |
2018 |
dc.date.issued.fl_str_mv |
2018-11-21 |
dc.date.accessioned.fl_str_mv |
2019-01-10T19:10:48Z |
dc.date.available.fl_str_mv |
2019-01-10T19:10:48Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/doctoralThesis |
format |
doctoralThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
SANCHEZ, Miguel Yesid Hernandez. Estudo dos efeitos da substituição de Feldspato por Filito em massas de porcelanato. 2018. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2018. Disponível em: https://repositorio.ufscar.br/handle/ufscar/10829. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufscar.br/handle/ufscar/10829 |
identifier_str_mv |
SANCHEZ, Miguel Yesid Hernandez. Estudo dos efeitos da substituição de Feldspato por Filito em massas de porcelanato. 2018. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2018. Disponível em: https://repositorio.ufscar.br/handle/ufscar/10829. |
url |
https://repositorio.ufscar.br/handle/ufscar/10829 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.authority.fl_str_mv |
def1d9c8-353a-4dec-a3b5-c49b68749aed |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.publisher.none.fl_str_mv |
Universidade Federal de São Carlos Câmpus São Carlos |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEM |
dc.publisher.initials.fl_str_mv |
UFSCar |
publisher.none.fl_str_mv |
Universidade Federal de São Carlos Câmpus São Carlos |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFSCAR instname:Universidade Federal de São Carlos (UFSCAR) instacron:UFSCAR |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
UFSCAR |
institution |
UFSCAR |
reponame_str |
Repositório Institucional da UFSCAR |
collection |
Repositório Institucional da UFSCAR |
bitstream.url.fl_str_mv |
https://repositorio.ufscar.br/bitstream/ufscar/10829/1/Miguel%20Yesid%20Hernandez%20Sanchez%20-%20Tese.pdf https://repositorio.ufscar.br/bitstream/ufscar/10829/3/license.txt https://repositorio.ufscar.br/bitstream/ufscar/10829/4/Miguel%20Yesid%20Hernandez%20Sanchez%20-%20Tese.pdf.txt https://repositorio.ufscar.br/bitstream/ufscar/10829/5/Miguel%20Yesid%20Hernandez%20Sanchez%20-%20Tese.pdf.jpg |
bitstream.checksum.fl_str_mv |
fc6a5593a2daae5c04c4d9d33ee0bedc ae0398b6f8b235e40ad82cba6c50031d 9d7486210c5f2a35a4be9f57c5aa9fb6 b9d4d1244ab45b1255041178f285b4ed |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
|
_version_ |
1813715598360707072 |