Zircônia CO-dopada por compensação de cargas nos sistemas (ZrO2)1-(x+y)(InO1,5)x(MOz)y com MOz = TaO2,5, NbO2,5, MoO3 ou WO3, como revestimento para barreira térmica
Autor(a) principal: | |
---|---|
Data de Publicação: | 2016 |
Tipo de documento: | Tese |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFSCAR |
Texto Completo: | https://repositorio.ufscar.br/handle/ufscar/8318 |
Resumo: | InO1.5-stabilized zirconia (InSZ) is a potential hot corrosion resistant thermal barrier coating (TBC). However, the thermal instability prevents real applications of InSZ-based TBC. This thesis investigates the hypothesis of co-doping using the charge compensation to improve the phase stability of InSZ. Four co-doping systems were synthesized by coprecipitation and studied: (ZrO2)1-(x+y)(InO1.5)x(MOz)y with MOz = TaO2.5, NbO2.5, MoO3, or WO3. After synthesis, 9 mol% of InO1.5 plus the charge-compensating oxides was sufficient to stabilize the tetragonal phase. Specific surface area up to 106.1 m2.g-1 and crystallite size ~11 nm were achieved using ethanol washing followed by azeotropic distillation as dehydration technique in the precipitates. In these powders, initial thermal stability analysis indicated instability of the tetragonal phase, with extension of the t→m transformation less detrimental in the InMoSZ system. Further increase in the concentration of InO1.5:MoO3 results in monophasic samples with retention of cubic phase in the InMoSZ. Cubic InMoSZ exhibited hardness and thermal expansion coefficient of 13.5% and 9% higher than those of InSZ, respectively. However, thermal treatments at T ≥ 1200 °C showed that the InMoSZ is also passive to destabilization of the high temperature cubic polymorph. Although the cubic InMoSZ was the most promising system found in this thesis, the stability results do not support its application as TBC for temperatures ≥ 1000 ºC. A deep evaluation of the phase transformations between 1000 to 1200 °C indicated that the instability of the proposed systems is due to a progressive c→t→m destabilization of the polymorphs. This c→t→m transformation is directly associated with the reduction of the InO1.5 stabilizer in solid solution by volatilization as In2O during heat treatment. At temperatures ≤ 800 ºC, the c→t phase transformation do not occurs, then, InSZ-based TBC is stable in these conditions. |
id |
SCAR_ab6f3c44500e36330feea87536a3e94c |
---|---|
oai_identifier_str |
oai:repositorio.ufscar.br:ufscar/8318 |
network_acronym_str |
SCAR |
network_name_str |
Repositório Institucional da UFSCAR |
repository_id_str |
4322 |
spelling |
Piva, Roger HonoratoMorelli, Márcio Raymundohttp://lattes.cnpq.br/0172837599844991http://lattes.cnpq.br/05153217271445239f374a6e-5dbb-4af9-86a3-872317c0ff8b2016-11-08T19:10:21Z2016-11-08T19:10:21Z2016-09-30PIVA, Roger Honorato. Zircônia CO-dopada por compensação de cargas nos sistemas (ZrO2)1-(x+y)(InO1,5)x(MOz)y com MOz = TaO2,5, NbO2,5, MoO3 ou WO3, como revestimento para barreira térmica. 2016. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2016. Disponível em: https://repositorio.ufscar.br/handle/ufscar/8318.https://repositorio.ufscar.br/handle/ufscar/8318InO1.5-stabilized zirconia (InSZ) is a potential hot corrosion resistant thermal barrier coating (TBC). However, the thermal instability prevents real applications of InSZ-based TBC. This thesis investigates the hypothesis of co-doping using the charge compensation to improve the phase stability of InSZ. Four co-doping systems were synthesized by coprecipitation and studied: (ZrO2)1-(x+y)(InO1.5)x(MOz)y with MOz = TaO2.5, NbO2.5, MoO3, or WO3. After synthesis, 9 mol% of InO1.5 plus the charge-compensating oxides was sufficient to stabilize the tetragonal phase. Specific surface area up to 106.1 m2.g-1 and crystallite size ~11 nm were achieved using ethanol washing followed by azeotropic distillation as dehydration technique in the precipitates. In these powders, initial thermal stability analysis indicated instability of the tetragonal phase, with extension of the t→m transformation less detrimental in the InMoSZ system. Further increase in the concentration of InO1.5:MoO3 results in monophasic samples with retention of cubic phase in the InMoSZ. Cubic InMoSZ exhibited hardness and thermal expansion coefficient of 13.5% and 9% higher than those of InSZ, respectively. However, thermal treatments at T ≥ 1200 °C showed that the InMoSZ is also passive to destabilization of the high temperature cubic polymorph. Although the cubic InMoSZ was the most promising system found in this thesis, the stability results do not support its application as TBC for temperatures ≥ 1000 ºC. A deep evaluation of the phase transformations between 1000 to 1200 °C indicated that the instability of the proposed systems is due to a progressive c→t→m destabilization of the polymorphs. This c→t→m transformation is directly associated with the reduction of the InO1.5 stabilizer in solid solution by volatilization as In2O during heat treatment. At temperatures ≤ 800 ºC, the c→t phase transformation do not occurs, then, InSZ-based TBC is stable in these conditions.A zircônia estabilizada com InO1,5 (InSZ) é um material com potencial aplicação como revestimentos para barreira térmica (TBC) resistentes à corrosão. Contudo, a instabilidade de fases impede aplicações industriais da InSZ. Esta tese investiga a ação da co-dopagem por compensação de cargas como uma estratégia para aumentar a estabilidade de fases da InSZ. Quatro sistemas de co-dopagem foram sintetizados por co-precipitação e estudados: (ZrO2)1-(x+y)(InO1,5)x(MOz)y com MOz = TaO2,5, NbO2,5, MoO3 ou WO3. Após a síntese, 9 %mol de InO1,5 somado a concentração de óxidos compensadores de carga foi suficiente para estabilização da fase tetragonal. Área superficial específica de até 106,1 m2.g‒1 e tamanho de cristalitos de ~11 nm foram obtidos utilizando a lavagem com etanol seguida por destilação azeotrópica como técnica de desidratação dos precipitados. Para estes pós, testes de estabilidade térmica indicaram instabilidade da fase tetragonal, com extensão de transformação t→m menos detrimental no sistema InMoSZ. Aumentando gradativamente a concentração de InO1,5-MoO3 na InMoSZ resulta em amostras monofásicas com retenção da fase cúbica. A InMoSZ cúbica exibiu dureza e coeficiente de expansão térmica até 13,5% e 9% superiores aos valores da InSZ, respectivamente. No entanto, tratamentos em temperaturas ≥ 1200 ºC indicaram que a InMoSZ é também suscetível a desestabilização da fase cúbica. Embora a InMoSZ cúbica tenha sido o sistema mais promissor obtido nesta tese, os resultados de estabilidade indicam que sua aplicação como TBC não é possível em temperaturas ≥ 1000 ºC. Uma avaliação detalhada das fases formadas após os tratamentos entre 1000 a 1200 ºC demonstrou que a instabilidade dos sistemas estudados é decorrente de uma transformação progressiva tipo c→t→m. A origem da transformação c→t→m é associada a redução da concentração do estabilizador InO1,5 em solução sólida por volatilização como In2O durante os testes de estabilidade térmica. Em temperaturas ≤ 800 ºC, a transformação c→m não ocorre, neste caso, TBCs baseadas em InSZ são estáveis termicamente para aplicações industriais.Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)porUniversidade Federal de São CarlosCâmpus São CarlosPrograma de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEMUFSCarTBCZircônia estabilizadaCo-dopagemEstabilidade de fasesstabilized zirconiaco-dopingphase stabilityENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICAZircônia CO-dopada por compensação de cargas nos sistemas (ZrO2)1-(x+y)(InO1,5)x(MOz)y com MOz = TaO2,5, NbO2,5, MoO3 ou WO3, como revestimento para barreira térmicainfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisOnline600600054faa10-e587-4736-bbba-5c3147983b48info:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINALTeseRHP.pdfTeseRHP.pdfapplication/pdf8778601https://repositorio.ufscar.br/bitstream/ufscar/8318/1/TeseRHP.pdfeb4553a13387041c0fd36d153b524c3cMD51LICENSElicense.txtlicense.txttext/plain; charset=utf-81957https://repositorio.ufscar.br/bitstream/ufscar/8318/2/license.txtae0398b6f8b235e40ad82cba6c50031dMD52TEXTTeseRHP.pdf.txtTeseRHP.pdf.txtExtracted texttext/plain333773https://repositorio.ufscar.br/bitstream/ufscar/8318/3/TeseRHP.pdf.txt95a940379a30671b6126cdf253e68eeeMD53THUMBNAILTeseRHP.pdf.jpgTeseRHP.pdf.jpgIM Thumbnailimage/jpeg6768https://repositorio.ufscar.br/bitstream/ufscar/8318/4/TeseRHP.pdf.jpg4973dc5cf503409b623c700b3a6c5112MD54ufscar/83182023-09-18 18:31:04.199oai:repositorio.ufscar.br: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Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222023-09-18T18:31:04Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.por.fl_str_mv |
Zircônia CO-dopada por compensação de cargas nos sistemas (ZrO2)1-(x+y)(InO1,5)x(MOz)y com MOz = TaO2,5, NbO2,5, MoO3 ou WO3, como revestimento para barreira térmica |
title |
Zircônia CO-dopada por compensação de cargas nos sistemas (ZrO2)1-(x+y)(InO1,5)x(MOz)y com MOz = TaO2,5, NbO2,5, MoO3 ou WO3, como revestimento para barreira térmica |
spellingShingle |
Zircônia CO-dopada por compensação de cargas nos sistemas (ZrO2)1-(x+y)(InO1,5)x(MOz)y com MOz = TaO2,5, NbO2,5, MoO3 ou WO3, como revestimento para barreira térmica Piva, Roger Honorato TBC Zircônia estabilizada Co-dopagem Estabilidade de fases stabilized zirconia co-doping phase stability ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
title_short |
Zircônia CO-dopada por compensação de cargas nos sistemas (ZrO2)1-(x+y)(InO1,5)x(MOz)y com MOz = TaO2,5, NbO2,5, MoO3 ou WO3, como revestimento para barreira térmica |
title_full |
Zircônia CO-dopada por compensação de cargas nos sistemas (ZrO2)1-(x+y)(InO1,5)x(MOz)y com MOz = TaO2,5, NbO2,5, MoO3 ou WO3, como revestimento para barreira térmica |
title_fullStr |
Zircônia CO-dopada por compensação de cargas nos sistemas (ZrO2)1-(x+y)(InO1,5)x(MOz)y com MOz = TaO2,5, NbO2,5, MoO3 ou WO3, como revestimento para barreira térmica |
title_full_unstemmed |
Zircônia CO-dopada por compensação de cargas nos sistemas (ZrO2)1-(x+y)(InO1,5)x(MOz)y com MOz = TaO2,5, NbO2,5, MoO3 ou WO3, como revestimento para barreira térmica |
title_sort |
Zircônia CO-dopada por compensação de cargas nos sistemas (ZrO2)1-(x+y)(InO1,5)x(MOz)y com MOz = TaO2,5, NbO2,5, MoO3 ou WO3, como revestimento para barreira térmica |
author |
Piva, Roger Honorato |
author_facet |
Piva, Roger Honorato |
author_role |
author |
dc.contributor.authorlattes.por.fl_str_mv |
http://lattes.cnpq.br/0515321727144523 |
dc.contributor.author.fl_str_mv |
Piva, Roger Honorato |
dc.contributor.advisor1.fl_str_mv |
Morelli, Márcio Raymundo |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/0172837599844991 |
dc.contributor.authorID.fl_str_mv |
9f374a6e-5dbb-4af9-86a3-872317c0ff8b |
contributor_str_mv |
Morelli, Márcio Raymundo |
dc.subject.por.fl_str_mv |
TBC Zircônia estabilizada Co-dopagem Estabilidade de fases |
topic |
TBC Zircônia estabilizada Co-dopagem Estabilidade de fases stabilized zirconia co-doping phase stability ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
dc.subject.eng.fl_str_mv |
stabilized zirconia co-doping phase stability |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
description |
InO1.5-stabilized zirconia (InSZ) is a potential hot corrosion resistant thermal barrier coating (TBC). However, the thermal instability prevents real applications of InSZ-based TBC. This thesis investigates the hypothesis of co-doping using the charge compensation to improve the phase stability of InSZ. Four co-doping systems were synthesized by coprecipitation and studied: (ZrO2)1-(x+y)(InO1.5)x(MOz)y with MOz = TaO2.5, NbO2.5, MoO3, or WO3. After synthesis, 9 mol% of InO1.5 plus the charge-compensating oxides was sufficient to stabilize the tetragonal phase. Specific surface area up to 106.1 m2.g-1 and crystallite size ~11 nm were achieved using ethanol washing followed by azeotropic distillation as dehydration technique in the precipitates. In these powders, initial thermal stability analysis indicated instability of the tetragonal phase, with extension of the t→m transformation less detrimental in the InMoSZ system. Further increase in the concentration of InO1.5:MoO3 results in monophasic samples with retention of cubic phase in the InMoSZ. Cubic InMoSZ exhibited hardness and thermal expansion coefficient of 13.5% and 9% higher than those of InSZ, respectively. However, thermal treatments at T ≥ 1200 °C showed that the InMoSZ is also passive to destabilization of the high temperature cubic polymorph. Although the cubic InMoSZ was the most promising system found in this thesis, the stability results do not support its application as TBC for temperatures ≥ 1000 ºC. A deep evaluation of the phase transformations between 1000 to 1200 °C indicated that the instability of the proposed systems is due to a progressive c→t→m destabilization of the polymorphs. This c→t→m transformation is directly associated with the reduction of the InO1.5 stabilizer in solid solution by volatilization as In2O during heat treatment. At temperatures ≤ 800 ºC, the c→t phase transformation do not occurs, then, InSZ-based TBC is stable in these conditions. |
publishDate |
2016 |
dc.date.accessioned.fl_str_mv |
2016-11-08T19:10:21Z |
dc.date.available.fl_str_mv |
2016-11-08T19:10:21Z |
dc.date.issued.fl_str_mv |
2016-09-30 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/doctoralThesis |
format |
doctoralThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
PIVA, Roger Honorato. Zircônia CO-dopada por compensação de cargas nos sistemas (ZrO2)1-(x+y)(InO1,5)x(MOz)y com MOz = TaO2,5, NbO2,5, MoO3 ou WO3, como revestimento para barreira térmica. 2016. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2016. Disponível em: https://repositorio.ufscar.br/handle/ufscar/8318. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufscar.br/handle/ufscar/8318 |
identifier_str_mv |
PIVA, Roger Honorato. Zircônia CO-dopada por compensação de cargas nos sistemas (ZrO2)1-(x+y)(InO1,5)x(MOz)y com MOz = TaO2,5, NbO2,5, MoO3 ou WO3, como revestimento para barreira térmica. 2016. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2016. Disponível em: https://repositorio.ufscar.br/handle/ufscar/8318. |
url |
https://repositorio.ufscar.br/handle/ufscar/8318 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.confidence.fl_str_mv |
600 600 |
dc.relation.authority.fl_str_mv |
054faa10-e587-4736-bbba-5c3147983b48 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.publisher.none.fl_str_mv |
Universidade Federal de São Carlos Câmpus São Carlos |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEM |
dc.publisher.initials.fl_str_mv |
UFSCar |
publisher.none.fl_str_mv |
Universidade Federal de São Carlos Câmpus São Carlos |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFSCAR instname:Universidade Federal de São Carlos (UFSCAR) instacron:UFSCAR |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
UFSCAR |
institution |
UFSCAR |
reponame_str |
Repositório Institucional da UFSCAR |
collection |
Repositório Institucional da UFSCAR |
bitstream.url.fl_str_mv |
https://repositorio.ufscar.br/bitstream/ufscar/8318/1/TeseRHP.pdf https://repositorio.ufscar.br/bitstream/ufscar/8318/2/license.txt https://repositorio.ufscar.br/bitstream/ufscar/8318/3/TeseRHP.pdf.txt https://repositorio.ufscar.br/bitstream/ufscar/8318/4/TeseRHP.pdf.jpg |
bitstream.checksum.fl_str_mv |
eb4553a13387041c0fd36d153b524c3c ae0398b6f8b235e40ad82cba6c50031d 95a940379a30671b6126cdf253e68eee 4973dc5cf503409b623c700b3a6c5112 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
|
_version_ |
1813715570109972480 |