Determinação da energia de fratura em materiais cerâmicos em altas temperaturas.
Autor(a) principal: | |
---|---|
Data de Publicação: | 2005 |
Tipo de documento: | Tese |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFSCAR |
Texto Completo: | https://repositorio.ufscar.br/handle/ufscar/745 |
Resumo: | In this work, the main objective was to determine the energy of fracture in ceramic materials, focused on refractories, at high temperatures and to inquire the interference of the creep on this measurement. Therefore, castable containing white fused and calcined aluminas, hydrated alumina as a binder, with and without, a glass of SiO2-CaO-Al2O3-B2O3-MgO was designed. This material can simulate the real situation of refractory castables that present possible glassy phase formation due to the presence of cement, silica fume and impurities of raw materials. In addition to this material two commercial refractories were also characterized. Physical characterizations, refractoriness under load, modulus of rupture, Young's modulus and coefficient of linear thermal expansion were evaluated. The energy of fracture was measured through stable crack propagation in three-point bending tests. The creep curves were obtained in three-point bending and compression tests. The concept of rate of energy of creep deformation was used to evaluate creep semiquantitatively as well as to consider a description for the energy of fracture at high temperatures. The results indicate that a maximum in the energy of fracture measured through stable crack propagation under three-point bending tests occurs as a function of temperature. For this case it will exist a range of temperature at which the material will suffer a transition from brittle to ductile behaviour due to the presence of glassy phase in the microstructure. In the transition, bridges of glassy phase contribute for the increase of the average energy for crack propagation. Consequently, these results have strong influence on the thermal shock damage resistance parameters. |
id |
SCAR_d423a620b0324d7e57618b210ab74475 |
---|---|
oai_identifier_str |
oai:repositorio.ufscar.br:ufscar/745 |
network_acronym_str |
SCAR |
network_name_str |
Repositório Institucional da UFSCAR |
repository_id_str |
4322 |
spelling |
Santos, Sérgio Francisco dosRodrigues, José de Anchietahttp://genos.cnpq.br:12010/dwlattes/owa/prc_imp_cv_int?f_cod=K4783623T3http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4728663Y6d7d16be4-4445-4362-9533-24b776114c012016-06-02T19:10:31Z2005-08-012016-06-02T19:10:31Z2005-03-11SANTOS, Sérgio Francisco dos. Evaluation of the energy of fracture in ceramic materials at high temperatures.. 2005. 226 f. Tese (Doutorado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2005.https://repositorio.ufscar.br/handle/ufscar/745In this work, the main objective was to determine the energy of fracture in ceramic materials, focused on refractories, at high temperatures and to inquire the interference of the creep on this measurement. Therefore, castable containing white fused and calcined aluminas, hydrated alumina as a binder, with and without, a glass of SiO2-CaO-Al2O3-B2O3-MgO was designed. This material can simulate the real situation of refractory castables that present possible glassy phase formation due to the presence of cement, silica fume and impurities of raw materials. In addition to this material two commercial refractories were also characterized. Physical characterizations, refractoriness under load, modulus of rupture, Young's modulus and coefficient of linear thermal expansion were evaluated. The energy of fracture was measured through stable crack propagation in three-point bending tests. The creep curves were obtained in three-point bending and compression tests. The concept of rate of energy of creep deformation was used to evaluate creep semiquantitatively as well as to consider a description for the energy of fracture at high temperatures. The results indicate that a maximum in the energy of fracture measured through stable crack propagation under three-point bending tests occurs as a function of temperature. For this case it will exist a range of temperature at which the material will suffer a transition from brittle to ductile behaviour due to the presence of glassy phase in the microstructure. In the transition, bridges of glassy phase contribute for the increase of the average energy for crack propagation. Consequently, these results have strong influence on the thermal shock damage resistance parameters.Neste trabalho, o objetivo principal foi determinar a energia de fratura em materiais cerâmicos, em particular refratários, em temperaturas elevadas e averiguar a interferência da fluência sobre esta medida. Para tanto, foram projetados e preparados compósitos contendo aluminas eletrofundidas e calcinadas, alumina hidratável como ligante e, com e sem, fibras moídas de um vidro de SiO2-CaO-Al2O3-B2O3-MgO. Com este material, colocando teores conhecidos de vidro, foi simulado um concreto refratário à base de alumina contendo fase vítrea que na prática são formulações contendo cimento de aluminato de cálcio, microssílica e impurezas típicas dessas matérias-primas. Além destes compósitos foram avaliados dois refratários comerciais. Foram realizadas caracterizações físicas e mecânicas, a saber, refratariedade-sobcarga, módulo de ruptura, módulo de Young e coeficiente de dilatação térmica linear. A energia de fratura foi obtida através de ensaios de flexão a três pontos com propagação estável de trinca. As curvas de fluência foram obtidas sob carregamento de compressão e de flexão a três pontos. Foi utilizado o conceito de taxa de energia de deformação de fluência tanto para avaliar semiquantitativamente a fluência quanto para propor uma descrição analítica para a energia de fratura em temperaturas elevadas. Os resultados indicam que a energia de fratura passa por um máximo na faixa de temperatura em que ocorre uma transição de comportamento mecânico frágil-dúctil de materiais cerâmicos que contêm fase vítrea na microestrutura. Nesta transição pontes de fase vítrea contribuem para o aumento da energia média dissipada para a propagação de uma trinca e a geração de duas superfícies de fratura. Por conseqüência, estes resultados influenciam fortemente os parâmetros de resistência ao dano por choque térmico.Universidade Federal de Sao Carlosapplication/pdfporUniversidade Federal de São CarlosPrograma de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEMUFSCarBRMateriais refratáriosCerâmicaChoque térmicoEnergia total de fraturaFluênciaENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOSDeterminação da energia de fratura em materiais cerâmicos em altas temperaturas.Evaluation of the energy of fracture in ceramic materials at high temperatures.info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesis-1-1eeac44e3-9996-464a-9f4c-724ff89d3f23info:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINALTeseSFS.pdfapplication/pdf10691709https://repositorio.ufscar.br/bitstream/ufscar/745/1/TeseSFS.pdf968fca4ee1f6c4fff2a9f8ed36b52c57MD51THUMBNAILTeseSFS.pdf.jpgTeseSFS.pdf.jpgIM Thumbnailimage/jpeg6098https://repositorio.ufscar.br/bitstream/ufscar/745/2/TeseSFS.pdf.jpge11431abd220018398df59bc8700e3efMD52ufscar/7452023-09-18 18:30:39.655oai:repositorio.ufscar.br:ufscar/745Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222023-09-18T18:30:39Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.por.fl_str_mv |
Determinação da energia de fratura em materiais cerâmicos em altas temperaturas. |
dc.title.alternative.eng.fl_str_mv |
Evaluation of the energy of fracture in ceramic materials at high temperatures. |
title |
Determinação da energia de fratura em materiais cerâmicos em altas temperaturas. |
spellingShingle |
Determinação da energia de fratura em materiais cerâmicos em altas temperaturas. Santos, Sérgio Francisco dos Materiais refratários Cerâmica Choque térmico Energia total de fratura Fluência ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS |
title_short |
Determinação da energia de fratura em materiais cerâmicos em altas temperaturas. |
title_full |
Determinação da energia de fratura em materiais cerâmicos em altas temperaturas. |
title_fullStr |
Determinação da energia de fratura em materiais cerâmicos em altas temperaturas. |
title_full_unstemmed |
Determinação da energia de fratura em materiais cerâmicos em altas temperaturas. |
title_sort |
Determinação da energia de fratura em materiais cerâmicos em altas temperaturas. |
author |
Santos, Sérgio Francisco dos |
author_facet |
Santos, Sérgio Francisco dos |
author_role |
author |
dc.contributor.authorlattes.por.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4728663Y6 |
dc.contributor.author.fl_str_mv |
Santos, Sérgio Francisco dos |
dc.contributor.advisor1.fl_str_mv |
Rodrigues, José de Anchieta |
dc.contributor.advisor1Lattes.fl_str_mv |
http://genos.cnpq.br:12010/dwlattes/owa/prc_imp_cv_int?f_cod=K4783623T3 |
dc.contributor.authorID.fl_str_mv |
d7d16be4-4445-4362-9533-24b776114c01 |
contributor_str_mv |
Rodrigues, José de Anchieta |
dc.subject.por.fl_str_mv |
Materiais refratários Cerâmica Choque térmico Energia total de fratura Fluência |
topic |
Materiais refratários Cerâmica Choque térmico Energia total de fratura Fluência ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS |
description |
In this work, the main objective was to determine the energy of fracture in ceramic materials, focused on refractories, at high temperatures and to inquire the interference of the creep on this measurement. Therefore, castable containing white fused and calcined aluminas, hydrated alumina as a binder, with and without, a glass of SiO2-CaO-Al2O3-B2O3-MgO was designed. This material can simulate the real situation of refractory castables that present possible glassy phase formation due to the presence of cement, silica fume and impurities of raw materials. In addition to this material two commercial refractories were also characterized. Physical characterizations, refractoriness under load, modulus of rupture, Young's modulus and coefficient of linear thermal expansion were evaluated. The energy of fracture was measured through stable crack propagation in three-point bending tests. The creep curves were obtained in three-point bending and compression tests. The concept of rate of energy of creep deformation was used to evaluate creep semiquantitatively as well as to consider a description for the energy of fracture at high temperatures. The results indicate that a maximum in the energy of fracture measured through stable crack propagation under three-point bending tests occurs as a function of temperature. For this case it will exist a range of temperature at which the material will suffer a transition from brittle to ductile behaviour due to the presence of glassy phase in the microstructure. In the transition, bridges of glassy phase contribute for the increase of the average energy for crack propagation. Consequently, these results have strong influence on the thermal shock damage resistance parameters. |
publishDate |
2005 |
dc.date.available.fl_str_mv |
2005-08-01 2016-06-02T19:10:31Z |
dc.date.issued.fl_str_mv |
2005-03-11 |
dc.date.accessioned.fl_str_mv |
2016-06-02T19:10:31Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/doctoralThesis |
format |
doctoralThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
SANTOS, Sérgio Francisco dos. Evaluation of the energy of fracture in ceramic materials at high temperatures.. 2005. 226 f. Tese (Doutorado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2005. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufscar.br/handle/ufscar/745 |
identifier_str_mv |
SANTOS, Sérgio Francisco dos. Evaluation of the energy of fracture in ceramic materials at high temperatures.. 2005. 226 f. Tese (Doutorado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2005. |
url |
https://repositorio.ufscar.br/handle/ufscar/745 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.confidence.fl_str_mv |
-1 -1 |
dc.relation.authority.fl_str_mv |
eeac44e3-9996-464a-9f4c-724ff89d3f23 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal de São Carlos |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEM |
dc.publisher.initials.fl_str_mv |
UFSCar |
dc.publisher.country.fl_str_mv |
BR |
publisher.none.fl_str_mv |
Universidade Federal de São Carlos |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFSCAR instname:Universidade Federal de São Carlos (UFSCAR) instacron:UFSCAR |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
UFSCAR |
institution |
UFSCAR |
reponame_str |
Repositório Institucional da UFSCAR |
collection |
Repositório Institucional da UFSCAR |
bitstream.url.fl_str_mv |
https://repositorio.ufscar.br/bitstream/ufscar/745/1/TeseSFS.pdf https://repositorio.ufscar.br/bitstream/ufscar/745/2/TeseSFS.pdf.jpg |
bitstream.checksum.fl_str_mv |
968fca4ee1f6c4fff2a9f8ed36b52c57 e11431abd220018398df59bc8700e3ef |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
|
_version_ |
1802136246981492736 |