Avaliação dos agregados de resíduos da construção civil em matriz geopolimérica visando aplicação em pisos intertravados
Autor(a) principal: | |
---|---|
Data de Publicação: | 2022 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFSCAR |
Texto Completo: | https://repositorio.ufscar.br/handle/ufscar/16202 |
Resumo: | The production of Portland cement (PC) is seen as aggravating the environment, so scientists and engineers look for alternatives to replace this type of binder. Geopolymers have the potential to replace CP, as it aims to reduce CO2 emissions and contributes to high compressive strength. Therefore, this work aimed to prepare concrete from geopolymeric binder obtained with commercial metakaolin and sodium hydroxide (concentration of 12 mol) and pH above 12, respecting the Si/Al ratio equal to 2, which is appropriate for application in interlocking floors. Another point of interest was the evaluation of coarse aggregate from civil construction waste (RCC), especially those from red ceramics compared to conventional coarse aggregate (gravel). Application of civil construction waste in geopolymers is scarce in the literature, requiring a comparative analysis with CP concrete. The methodology consisted of preparing the concrete under the same conditions, that is, curing at room temperature and forming by sleeping pieces. Initially, the determinant characteristics analyzed for application were the compressive strength and water absorption, both at 28 days of curing. The results showed that only the composition of CP with crushed stone met the specifications for the application of interlocking pavements (39MPa), and that the geopolymer matrices are strongly dependent on the degree of crystallinity of the precursor and suitability of the activator, factors that were only confirmed by new compositions. with metakaolin of different Christianity and different activator of the same pH (composed of a mixture of silicate and sodium hydroxide). It was concluded that the previous characterization of the precursor raw material is important, especially regarding its chemical composition and crystallinity. For the development of geopolymer concrete for interlocking pavements, the produced and/or commercial metakaolin used in the matrix were exclusively contributors to the low compressive strength obtained. |
id |
SCAR_d625b796201c8b044330140f4f59b42c |
---|---|
oai_identifier_str |
oai:repositorio.ufscar.br:ufscar/16202 |
network_acronym_str |
SCAR |
network_name_str |
Repositório Institucional da UFSCAR |
repository_id_str |
4322 |
spelling |
Suave, LeonardoMorelli, Márcio Raymundohttp://lattes.cnpq.br/0172837599844991http://lattes.cnpq.br/7323183370981203a3dda68c-9f60-49a1-87dd-1721535d114b2022-05-27T15:41:34Z2022-05-27T15:41:34Z2022-04-14SUAVE, Leonardo. Avaliação dos agregados de resíduos da construção civil em matriz geopolimérica visando aplicação em pisos intertravados. 2022. Dissertação (Mestrado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2022. Disponível em: https://repositorio.ufscar.br/handle/ufscar/16202.https://repositorio.ufscar.br/handle/ufscar/16202The production of Portland cement (PC) is seen as aggravating the environment, so scientists and engineers look for alternatives to replace this type of binder. Geopolymers have the potential to replace CP, as it aims to reduce CO2 emissions and contributes to high compressive strength. Therefore, this work aimed to prepare concrete from geopolymeric binder obtained with commercial metakaolin and sodium hydroxide (concentration of 12 mol) and pH above 12, respecting the Si/Al ratio equal to 2, which is appropriate for application in interlocking floors. Another point of interest was the evaluation of coarse aggregate from civil construction waste (RCC), especially those from red ceramics compared to conventional coarse aggregate (gravel). Application of civil construction waste in geopolymers is scarce in the literature, requiring a comparative analysis with CP concrete. The methodology consisted of preparing the concrete under the same conditions, that is, curing at room temperature and forming by sleeping pieces. Initially, the determinant characteristics analyzed for application were the compressive strength and water absorption, both at 28 days of curing. The results showed that only the composition of CP with crushed stone met the specifications for the application of interlocking pavements (39MPa), and that the geopolymer matrices are strongly dependent on the degree of crystallinity of the precursor and suitability of the activator, factors that were only confirmed by new compositions. with metakaolin of different Christianity and different activator of the same pH (composed of a mixture of silicate and sodium hydroxide). It was concluded that the previous characterization of the precursor raw material is important, especially regarding its chemical composition and crystallinity. For the development of geopolymer concrete for interlocking pavements, the produced and/or commercial metakaolin used in the matrix were exclusively contributors to the low compressive strength obtained.A produção do cimento Portland (CP) é vista como agravante ao meio ambiente, assim cientistas e engenheiros buscam alternativas para substituir este tipo de ligante. Geopolímeros apresentam potencial de substituição do CP, pois visa redução da emissão de CO2 e contribui com elevada resistência à compressão. Portanto, este trabalho teve como objetivo o preparo de concretos a partir de ligante geopolimérico obtido com metacaulim comercial e hidróxido de sódio (concentração de 12 mols) e pH acima de 12, respeitando razão Si/Al igual a 2, a qual é apropriada para aplicação em pavimentos intertravados. Outro ponto de interesse foi a avaliação de agregado graúdo proveniente de resíduos da construção civil (RCC), especialmente os provenientes de cerâmicas vermelhas em comparação ao agregado graúdo convencional (brita). Aplicação de resíduos de construção civil em geopolímeros são escassos na literatura, sendo necessário a análise comparativa com concreto de CP. A metodologia consistiu no preparo dos concretos sob mesmas condições, ou seja, cura a temperatura ambiente e conformação por peças dormidas. Inicialmente as características analisadas determinantes para aplicação foram a resistência à compressão e absorção de água, ambas aos 28 dias de cura. Os resultados mostraram que apenas a composição de CP com brita atendeu as especificações para aplicação de pavimentos intertravados (39MPa), e que as matrizes geopoliméricas são fortemente dependentes do grau de cristalinidade do precursor e adequação do ativador, fatores que só foram confirmados por novas composições com metacaulim de diferentes cristanidades e diferente ativador de mesmo pH (compostos pela mistura de silicato e hidróxido de sódio). Concluiu-se que a caracterização prévia da matéria-prima precursora é importante, sobretudo quanto a sua composição química e cristalinidade. Para o desenvolvimento de concretos geopoliméricos destinado a pavimentos intertravados o metacaulim produzido e/ou comercial empregado na matriz foram exclusivamente contribuintes para baixa resistência à compressão obtida.Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)Processo: 88887.601932/2021-00porUniversidade Federal de São CarlosCâmpus São CarlosPrograma de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEMUFSCarAttribution-NonCommercial-NoDerivs 3.0 Brazilhttp://creativecommons.org/licenses/by-nc-nd/3.0/br/info:eu-repo/semantics/openAccessIntertravadosResíduosGeopolímerosMetacaulimInterlockedWasteGeopolymersMetakaolinENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOSENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS::CERAMICOSAvaliação dos agregados de resíduos da construção civil em matriz geopolimérica visando aplicação em pisos intertravadosEvaluation of construction waste aggregates in a geopolymeric matrix aiming for application in interlocked floorsinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis600600054faa10-e587-4736-bbba-5c3147983b48reponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINALLeonardo Suave - Dissertação.pdfLeonardo Suave - Dissertação.pdfDissertaçãoapplication/pdf4371827https://repositorio.ufscar.br/bitstream/ufscar/16202/1/Leonardo%20Suave%20-%20Disserta%c3%a7%c3%a3o.pdf7550091e6118e48c86fae18a9e2ed19aMD51BCO carta comprovante autoarquivamento (1).pdfBCO carta comprovante autoarquivamento (1).pdfCarta de versão final assinado pelo orientadorapplication/pdf163052https://repositorio.ufscar.br/bitstream/ufscar/16202/2/BCO%20carta%20comprovante%20autoarquivamento%20%281%29.pdf87c0b01d84ad7031ed7bd6c31166151dMD52CC-LICENSElicense_rdflicense_rdfapplication/rdf+xml; charset=utf-8811https://repositorio.ufscar.br/bitstream/ufscar/16202/3/license_rdfe39d27027a6cc9cb039ad269a5db8e34MD53TEXTLeonardo Suave - Dissertação.pdf.txtLeonardo Suave - Dissertação.pdf.txtExtracted texttext/plain183769https://repositorio.ufscar.br/bitstream/ufscar/16202/4/Leonardo%20Suave%20-%20Disserta%c3%a7%c3%a3o.pdf.txt17a16f45aaa8ea06efde22ecba0e4543MD54BCO carta comprovante autoarquivamento (1).pdf.txtBCO carta comprovante autoarquivamento (1).pdf.txtExtracted texttext/plain1292https://repositorio.ufscar.br/bitstream/ufscar/16202/6/BCO%20carta%20comprovante%20autoarquivamento%20%281%29.pdf.txt84ced82eee581c1d1845ae38b75c2204MD56THUMBNAILLeonardo Suave - Dissertação.pdf.jpgLeonardo Suave - Dissertação.pdf.jpgIM Thumbnailimage/jpeg6349https://repositorio.ufscar.br/bitstream/ufscar/16202/5/Leonardo%20Suave%20-%20Disserta%c3%a7%c3%a3o.pdf.jpgf18e59855b288db08a4f45f141fafdd7MD55BCO carta comprovante autoarquivamento (1).pdf.jpgBCO carta comprovante autoarquivamento (1).pdf.jpgIM Thumbnailimage/jpeg9745https://repositorio.ufscar.br/bitstream/ufscar/16202/7/BCO%20carta%20comprovante%20autoarquivamento%20%281%29.pdf.jpg4aa4548819c3a467fe7ec64d70a70425MD57ufscar/162022023-09-18 18:32:16.713oai:repositorio.ufscar.br:ufscar/16202Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222023-09-18T18:32:16Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.por.fl_str_mv |
Avaliação dos agregados de resíduos da construção civil em matriz geopolimérica visando aplicação em pisos intertravados |
dc.title.alternative.eng.fl_str_mv |
Evaluation of construction waste aggregates in a geopolymeric matrix aiming for application in interlocked floors |
title |
Avaliação dos agregados de resíduos da construção civil em matriz geopolimérica visando aplicação em pisos intertravados |
spellingShingle |
Avaliação dos agregados de resíduos da construção civil em matriz geopolimérica visando aplicação em pisos intertravados Suave, Leonardo Intertravados Resíduos Geopolímeros Metacaulim Interlocked Waste Geopolymers Metakaolin ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS::CERAMICOS |
title_short |
Avaliação dos agregados de resíduos da construção civil em matriz geopolimérica visando aplicação em pisos intertravados |
title_full |
Avaliação dos agregados de resíduos da construção civil em matriz geopolimérica visando aplicação em pisos intertravados |
title_fullStr |
Avaliação dos agregados de resíduos da construção civil em matriz geopolimérica visando aplicação em pisos intertravados |
title_full_unstemmed |
Avaliação dos agregados de resíduos da construção civil em matriz geopolimérica visando aplicação em pisos intertravados |
title_sort |
Avaliação dos agregados de resíduos da construção civil em matriz geopolimérica visando aplicação em pisos intertravados |
author |
Suave, Leonardo |
author_facet |
Suave, Leonardo |
author_role |
author |
dc.contributor.authorlattes.por.fl_str_mv |
http://lattes.cnpq.br/7323183370981203 |
dc.contributor.author.fl_str_mv |
Suave, Leonardo |
dc.contributor.advisor1.fl_str_mv |
Morelli, Márcio Raymundo |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/0172837599844991 |
dc.contributor.authorID.fl_str_mv |
a3dda68c-9f60-49a1-87dd-1721535d114b |
contributor_str_mv |
Morelli, Márcio Raymundo |
dc.subject.por.fl_str_mv |
Intertravados Resíduos Geopolímeros Metacaulim |
topic |
Intertravados Resíduos Geopolímeros Metacaulim Interlocked Waste Geopolymers Metakaolin ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS::CERAMICOS |
dc.subject.eng.fl_str_mv |
Interlocked Waste Geopolymers Metakaolin |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS::CERAMICOS |
description |
The production of Portland cement (PC) is seen as aggravating the environment, so scientists and engineers look for alternatives to replace this type of binder. Geopolymers have the potential to replace CP, as it aims to reduce CO2 emissions and contributes to high compressive strength. Therefore, this work aimed to prepare concrete from geopolymeric binder obtained with commercial metakaolin and sodium hydroxide (concentration of 12 mol) and pH above 12, respecting the Si/Al ratio equal to 2, which is appropriate for application in interlocking floors. Another point of interest was the evaluation of coarse aggregate from civil construction waste (RCC), especially those from red ceramics compared to conventional coarse aggregate (gravel). Application of civil construction waste in geopolymers is scarce in the literature, requiring a comparative analysis with CP concrete. The methodology consisted of preparing the concrete under the same conditions, that is, curing at room temperature and forming by sleeping pieces. Initially, the determinant characteristics analyzed for application were the compressive strength and water absorption, both at 28 days of curing. The results showed that only the composition of CP with crushed stone met the specifications for the application of interlocking pavements (39MPa), and that the geopolymer matrices are strongly dependent on the degree of crystallinity of the precursor and suitability of the activator, factors that were only confirmed by new compositions. with metakaolin of different Christianity and different activator of the same pH (composed of a mixture of silicate and sodium hydroxide). It was concluded that the previous characterization of the precursor raw material is important, especially regarding its chemical composition and crystallinity. For the development of geopolymer concrete for interlocking pavements, the produced and/or commercial metakaolin used in the matrix were exclusively contributors to the low compressive strength obtained. |
publishDate |
2022 |
dc.date.accessioned.fl_str_mv |
2022-05-27T15:41:34Z |
dc.date.available.fl_str_mv |
2022-05-27T15:41:34Z |
dc.date.issued.fl_str_mv |
2022-04-14 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
SUAVE, Leonardo. Avaliação dos agregados de resíduos da construção civil em matriz geopolimérica visando aplicação em pisos intertravados. 2022. Dissertação (Mestrado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2022. Disponível em: https://repositorio.ufscar.br/handle/ufscar/16202. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufscar.br/handle/ufscar/16202 |
identifier_str_mv |
SUAVE, Leonardo. Avaliação dos agregados de resíduos da construção civil em matriz geopolimérica visando aplicação em pisos intertravados. 2022. Dissertação (Mestrado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2022. Disponível em: https://repositorio.ufscar.br/handle/ufscar/16202. |
url |
https://repositorio.ufscar.br/handle/ufscar/16202 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.confidence.fl_str_mv |
600 600 |
dc.relation.authority.fl_str_mv |
054faa10-e587-4736-bbba-5c3147983b48 |
dc.rights.driver.fl_str_mv |
Attribution-NonCommercial-NoDerivs 3.0 Brazil http://creativecommons.org/licenses/by-nc-nd/3.0/br/ info:eu-repo/semantics/openAccess |
rights_invalid_str_mv |
Attribution-NonCommercial-NoDerivs 3.0 Brazil http://creativecommons.org/licenses/by-nc-nd/3.0/br/ |
eu_rights_str_mv |
openAccess |
dc.publisher.none.fl_str_mv |
Universidade Federal de São Carlos Câmpus São Carlos |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEM |
dc.publisher.initials.fl_str_mv |
UFSCar |
publisher.none.fl_str_mv |
Universidade Federal de São Carlos Câmpus São Carlos |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFSCAR instname:Universidade Federal de São Carlos (UFSCAR) instacron:UFSCAR |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
UFSCAR |
institution |
UFSCAR |
reponame_str |
Repositório Institucional da UFSCAR |
collection |
Repositório Institucional da UFSCAR |
bitstream.url.fl_str_mv |
https://repositorio.ufscar.br/bitstream/ufscar/16202/1/Leonardo%20Suave%20-%20Disserta%c3%a7%c3%a3o.pdf https://repositorio.ufscar.br/bitstream/ufscar/16202/2/BCO%20carta%20comprovante%20autoarquivamento%20%281%29.pdf https://repositorio.ufscar.br/bitstream/ufscar/16202/3/license_rdf https://repositorio.ufscar.br/bitstream/ufscar/16202/4/Leonardo%20Suave%20-%20Disserta%c3%a7%c3%a3o.pdf.txt https://repositorio.ufscar.br/bitstream/ufscar/16202/6/BCO%20carta%20comprovante%20autoarquivamento%20%281%29.pdf.txt https://repositorio.ufscar.br/bitstream/ufscar/16202/5/Leonardo%20Suave%20-%20Disserta%c3%a7%c3%a3o.pdf.jpg https://repositorio.ufscar.br/bitstream/ufscar/16202/7/BCO%20carta%20comprovante%20autoarquivamento%20%281%29.pdf.jpg |
bitstream.checksum.fl_str_mv |
7550091e6118e48c86fae18a9e2ed19a 87c0b01d84ad7031ed7bd6c31166151d e39d27027a6cc9cb039ad269a5db8e34 17a16f45aaa8ea06efde22ecba0e4543 84ced82eee581c1d1845ae38b75c2204 f18e59855b288db08a4f45f141fafdd7 4aa4548819c3a467fe7ec64d70a70425 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
|
_version_ |
1802136407418863616 |