Síntese e sinterização em micro-ondas, e caracterização da Perovskita BA 0,5Sr0,5Co0,8Fe0,2O 3-δ
Autor(a) principal: | |
---|---|
Data de Publicação: | 2014 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFSCAR |
Texto Completo: | https://repositorio.ufscar.br/handle/ufscar/926 |
Resumo: | Ba0,5Sr0,5Co0,8Fe0,2O3-δ (BSCF) perovskite-type oxide is currently one of the most promising materials for applications in oxygen separation membranes. BSCF powder synthesis has received considerable attention because the powder characteristics are extremely important in shaping and sintering process of these membranes. On the other hand, the sintering stage is crucial in consolidation and microstructure development. In this study, BSCF perovskite has been synthesized and sintered using microwave heating. BSCF powders were synthesized by combustion method using conventional and microwave heating. The resulting BSCF powders were characterized by DSC/TG, BET, XRD and SEM. The sintering stage of pellets obtained by uniaxial pressing was conducted in different time and temperature conditions, as well as, in conventional and microwave heating. Microstructural characterization of BSCF samples was performed by OM and SEM. Mechanical characterization was made by diametral compression and Vickers hardness test and electrical characterization was carried out in impedance spectroscopy equipment. The BSCF powder that was synthesized in microwave, presented phase homogeneity, high specific surface area (9.93 g/m2) and submicrometric particle size. The microstructural characterization of sintered samples showed that the microwave sintering can achieve a relative density as high as conventional sintering with only 10% of dwell time (continue...). |
id |
SCAR_dd8b1df89917edf5904318db9a9c0c7a |
---|---|
oai_identifier_str |
oai:repositorio.ufscar.br:ufscar/926 |
network_acronym_str |
SCAR |
network_name_str |
Repositório Institucional da UFSCAR |
repository_id_str |
|
spelling |
Nuernberg, Rafael BianchiniMorelli, Márcio Raymundohttp://genos.cnpq.br:12010/dwlattes/owa/prc_imp_cv_int?f_cod=K4780873E7http://lattes.cnpq.br/62612249242642202016-06-02T19:12:37Z2014-09-172016-06-02T19:12:37Z2014-02-27NUERNBERG, Rafael Bianchini. Microwave-assisted synthesis and sintering and characterization of Ba0,5Sr0,5Co0,8Fe0,2O3-Δ perovskite. 2014. 141 f. Dissertação (Mestrado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2014.https://repositorio.ufscar.br/handle/ufscar/926Ba0,5Sr0,5Co0,8Fe0,2O3-δ (BSCF) perovskite-type oxide is currently one of the most promising materials for applications in oxygen separation membranes. BSCF powder synthesis has received considerable attention because the powder characteristics are extremely important in shaping and sintering process of these membranes. On the other hand, the sintering stage is crucial in consolidation and microstructure development. In this study, BSCF perovskite has been synthesized and sintered using microwave heating. BSCF powders were synthesized by combustion method using conventional and microwave heating. The resulting BSCF powders were characterized by DSC/TG, BET, XRD and SEM. The sintering stage of pellets obtained by uniaxial pressing was conducted in different time and temperature conditions, as well as, in conventional and microwave heating. Microstructural characterization of BSCF samples was performed by OM and SEM. Mechanical characterization was made by diametral compression and Vickers hardness test and electrical characterization was carried out in impedance spectroscopy equipment. The BSCF powder that was synthesized in microwave, presented phase homogeneity, high specific surface area (9.93 g/m2) and submicrometric particle size. The microstructural characterization of sintered samples showed that the microwave sintering can achieve a relative density as high as conventional sintering with only 10% of dwell time (continue...).A perovskita Ba0,5Sr0,5Co0,8Fe0,2O3-δ (BSCF) é hoje um dos materiais mais promissores para aplicações em membranas de separação de oxigênio do ar. A síntese de pós BSCF tem recebido atenção, pois as características do pó são de extrema importância no processo de conformação e sinterização dessas membranas. Por outro lado, a etapa de sinterização é crucial na etapa de consolidação e desenvolvimento da microestrutura. Nesse estudo, a perovskita BSCF foi sintetizada e sinterizada utilizando aquecimento em micro-ondas. Pós da perovskita BSCF foram sintetizados pelo método de reação de combustão utilizando aquecimento em micro-ondas e convencional. Os pós obtidos foram caracterizados por DSC/TG, DRX, MEV e análise de área superficial específica pelo método BET. A sinterização de compactos obtidos por prensagem uniaxial foi conduzida em diferentes condições de tempo e temperatura, bem como, em aquecimento convencional e micro-ondas. A caracterização microestrutural das amostras BSCF foi realizada por MO e MEV. A caracterização mecânica foi realizada por meio de ensaio de compressão diametral e de dureza Vickers e a caracterização elétrica foi feita por espectroscopia de impedância. O pó BSCF sintetizado em micro-ondas apresentou homogeneidade de fase, alta área superficial específica (9.93 g/m2) e tamanho de partícula submicrométrico. A caracterização microestrutural das amostras sinterizadas demonstrou que a sinterização em micro-ondas pode alcançar a mesma densidade relativa que a sinterização convencional com apenas 10% do tempo de patamar da sinterização convencional (continua...).Universidade Federal de Sao Carlosapplication/pdfporUniversidade Federal de São CarlosPrograma de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEMUFSCarBRSinterizaçãoSínteseMicro-ondasPerovskitaENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICASíntese e sinterização em micro-ondas, e caracterização da Perovskita BA 0,5Sr0,5Co0,8Fe0,2O 3-δMicrowave-assisted synthesis and sintering and characterization of 0,5Sr0,5Co0,8Fe0,2O 3-δ ; Perovskiteinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINAL6141.pdfapplication/pdf4360236https://{{ getenv "DSPACE_HOST" "repositorio.ufscar.br" }}/bitstream/ufscar/926/1/6141.pdf27f139227439cfb9b96cf85faa894750MD51TEXT6141.pdf.txt6141.pdf.txtExtracted texttext/plain0https://{{ getenv "DSPACE_HOST" "repositorio.ufscar.br" }}/bitstream/ufscar/926/2/6141.pdf.txtd41d8cd98f00b204e9800998ecf8427eMD52THUMBNAIL6141.pdf.jpg6141.pdf.jpgIM Thumbnailimage/jpeg6845https://{{ getenv "DSPACE_HOST" "repositorio.ufscar.br" }}/bitstream/ufscar/926/3/6141.pdf.jpg6981d91292e6134a2de5879f1f2c095dMD53ufscar/9262019-09-11 03:28:10.788oai:repositorio.ufscar.br:ufscar/926Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222019-09-11T03:28:10Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.por.fl_str_mv |
Síntese e sinterização em micro-ondas, e caracterização da Perovskita BA 0,5Sr0,5Co0,8Fe0,2O 3-δ |
dc.title.alternative.eng.fl_str_mv |
Microwave-assisted synthesis and sintering and characterization of 0,5Sr0,5Co0,8Fe0,2O 3-δ ; Perovskite |
title |
Síntese e sinterização em micro-ondas, e caracterização da Perovskita BA 0,5Sr0,5Co0,8Fe0,2O 3-δ |
spellingShingle |
Síntese e sinterização em micro-ondas, e caracterização da Perovskita BA 0,5Sr0,5Co0,8Fe0,2O 3-δ Nuernberg, Rafael Bianchini Sinterização Síntese Micro-ondas Perovskita ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
title_short |
Síntese e sinterização em micro-ondas, e caracterização da Perovskita BA 0,5Sr0,5Co0,8Fe0,2O 3-δ |
title_full |
Síntese e sinterização em micro-ondas, e caracterização da Perovskita BA 0,5Sr0,5Co0,8Fe0,2O 3-δ |
title_fullStr |
Síntese e sinterização em micro-ondas, e caracterização da Perovskita BA 0,5Sr0,5Co0,8Fe0,2O 3-δ |
title_full_unstemmed |
Síntese e sinterização em micro-ondas, e caracterização da Perovskita BA 0,5Sr0,5Co0,8Fe0,2O 3-δ |
title_sort |
Síntese e sinterização em micro-ondas, e caracterização da Perovskita BA 0,5Sr0,5Co0,8Fe0,2O 3-δ |
author |
Nuernberg, Rafael Bianchini |
author_facet |
Nuernberg, Rafael Bianchini |
author_role |
author |
dc.contributor.authorlattes.por.fl_str_mv |
http://lattes.cnpq.br/6261224924264220 |
dc.contributor.author.fl_str_mv |
Nuernberg, Rafael Bianchini |
dc.contributor.advisor1.fl_str_mv |
Morelli, Márcio Raymundo |
dc.contributor.advisor1Lattes.fl_str_mv |
http://genos.cnpq.br:12010/dwlattes/owa/prc_imp_cv_int?f_cod=K4780873E7 |
contributor_str_mv |
Morelli, Márcio Raymundo |
dc.subject.por.fl_str_mv |
Sinterização Síntese Micro-ondas Perovskita |
topic |
Sinterização Síntese Micro-ondas Perovskita ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
description |
Ba0,5Sr0,5Co0,8Fe0,2O3-δ (BSCF) perovskite-type oxide is currently one of the most promising materials for applications in oxygen separation membranes. BSCF powder synthesis has received considerable attention because the powder characteristics are extremely important in shaping and sintering process of these membranes. On the other hand, the sintering stage is crucial in consolidation and microstructure development. In this study, BSCF perovskite has been synthesized and sintered using microwave heating. BSCF powders were synthesized by combustion method using conventional and microwave heating. The resulting BSCF powders were characterized by DSC/TG, BET, XRD and SEM. The sintering stage of pellets obtained by uniaxial pressing was conducted in different time and temperature conditions, as well as, in conventional and microwave heating. Microstructural characterization of BSCF samples was performed by OM and SEM. Mechanical characterization was made by diametral compression and Vickers hardness test and electrical characterization was carried out in impedance spectroscopy equipment. The BSCF powder that was synthesized in microwave, presented phase homogeneity, high specific surface area (9.93 g/m2) and submicrometric particle size. The microstructural characterization of sintered samples showed that the microwave sintering can achieve a relative density as high as conventional sintering with only 10% of dwell time (continue...). |
publishDate |
2014 |
dc.date.available.fl_str_mv |
2014-09-17 2016-06-02T19:12:37Z |
dc.date.issued.fl_str_mv |
2014-02-27 |
dc.date.accessioned.fl_str_mv |
2016-06-02T19:12:37Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
NUERNBERG, Rafael Bianchini. Microwave-assisted synthesis and sintering and characterization of Ba0,5Sr0,5Co0,8Fe0,2O3-Δ perovskite. 2014. 141 f. Dissertação (Mestrado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2014. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufscar.br/handle/ufscar/926 |
identifier_str_mv |
NUERNBERG, Rafael Bianchini. Microwave-assisted synthesis and sintering and characterization of Ba0,5Sr0,5Co0,8Fe0,2O3-Δ perovskite. 2014. 141 f. Dissertação (Mestrado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2014. |
url |
https://repositorio.ufscar.br/handle/ufscar/926 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal de São Carlos |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEM |
dc.publisher.initials.fl_str_mv |
UFSCar |
dc.publisher.country.fl_str_mv |
BR |
publisher.none.fl_str_mv |
Universidade Federal de São Carlos |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFSCAR instname:Universidade Federal de São Carlos (UFSCAR) instacron:UFSCAR |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
UFSCAR |
institution |
UFSCAR |
reponame_str |
Repositório Institucional da UFSCAR |
collection |
Repositório Institucional da UFSCAR |
bitstream.url.fl_str_mv |
https://{{ getenv "DSPACE_HOST" "repositorio.ufscar.br" }}/bitstream/ufscar/926/1/6141.pdf https://{{ getenv "DSPACE_HOST" "repositorio.ufscar.br" }}/bitstream/ufscar/926/2/6141.pdf.txt https://{{ getenv "DSPACE_HOST" "repositorio.ufscar.br" }}/bitstream/ufscar/926/3/6141.pdf.jpg |
bitstream.checksum.fl_str_mv |
27f139227439cfb9b96cf85faa894750 d41d8cd98f00b204e9800998ecf8427e 6981d91292e6134a2de5879f1f2c095d |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
|
_version_ |
1777472019406782464 |