Efeito químico de aditivos em suspensões aquosas de magnésia para potenciais aplicações em concretos refratários
Autor(a) principal: | |
---|---|
Data de Publicação: | 2015 |
Tipo de documento: | Tese |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFSCAR |
Texto Completo: | https://repositorio.ufscar.br/handle/ufscar/743 |
Resumo: | Magnesium oxide is an important subject of investigation because of its physical and chemical properties, mainly for its application to refractory ceramics. However, magnesium oxide hydration generates its hydroxide, Mg(OH)2, which may cause a volumetric expansion, possibly tightening and damaging components made from this material. These factors are limiting for the use in refractory castables and, as a result, most studies regarding this application is focused on minimizing its harmful effects. In order to minimize the effects of hydration on refractory compositions, this work evaluated two types of magnesia presenting different reactivity, caustic and sinter magnesia, with additives (CaCl2, MgCl2, CaF2, MgF2, acetic acid, magnesium acetate, citric acid and EDTA). The results indicated that the soluble salts (CaCl2 and MgCl2) accelerated the hydration, diminishing the apparent volumetric expansion, increasing the mechanical strength and the hydration heat. Because the addition of insoluble salts (CaF2, MgF2) promoted a reduction in the hydration degree, however, samples showed cracks, became crispy, and presented low mechanical strength. In the case of adding acetic acid or magnesium acetate, it occurred a precipitation acceleration of brucite, Mg (OH)2, as a result of the acetate ion complexation power generated, being mechanical resistance of the acetate greater than the acetic acid. The chelating agents (citric acid and EDTA) had distinct behaviors: the citric acid caused hydration decrease because of the absorption effect; and EDTA caused hydration increase as a result of its Mg2+ ions complexation power. It may be concluded that additives, presented in the compositions studied herein, are promising materials for refractory application, assuming that the additives hydrating will improve refractories mechanical strength, and those decreasing the hydration must be incorporated to other materials to improve their performance. |
id |
SCAR_e258f779b37e8fa12eac8b207a2ec4f8 |
---|---|
oai_identifier_str |
oai:repositorio.ufscar.br:ufscar/743 |
network_acronym_str |
SCAR |
network_name_str |
Repositório Institucional da UFSCAR |
repository_id_str |
4322 |
spelling |
Santos, Ana Maria dosPandolfelli, Victor Carloshttp://lattes.cnpq.br/736937687398483933b2319f-8afa-49c3-b826-c425049717b72016-06-02T19:10:30Z2015-05-252016-06-02T19:10:30Z2015-02-05SANTOS, Ana Maria dos. Effect of chemical additives on aqueous suspension of magnesium for potential applications in refractory castables. 2015. 203 f. Tese (Doutorado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2015.https://repositorio.ufscar.br/handle/ufscar/743Magnesium oxide is an important subject of investigation because of its physical and chemical properties, mainly for its application to refractory ceramics. However, magnesium oxide hydration generates its hydroxide, Mg(OH)2, which may cause a volumetric expansion, possibly tightening and damaging components made from this material. These factors are limiting for the use in refractory castables and, as a result, most studies regarding this application is focused on minimizing its harmful effects. In order to minimize the effects of hydration on refractory compositions, this work evaluated two types of magnesia presenting different reactivity, caustic and sinter magnesia, with additives (CaCl2, MgCl2, CaF2, MgF2, acetic acid, magnesium acetate, citric acid and EDTA). The results indicated that the soluble salts (CaCl2 and MgCl2) accelerated the hydration, diminishing the apparent volumetric expansion, increasing the mechanical strength and the hydration heat. Because the addition of insoluble salts (CaF2, MgF2) promoted a reduction in the hydration degree, however, samples showed cracks, became crispy, and presented low mechanical strength. In the case of adding acetic acid or magnesium acetate, it occurred a precipitation acceleration of brucite, Mg (OH)2, as a result of the acetate ion complexation power generated, being mechanical resistance of the acetate greater than the acetic acid. The chelating agents (citric acid and EDTA) had distinct behaviors: the citric acid caused hydration decrease because of the absorption effect; and EDTA caused hydration increase as a result of its Mg2+ ions complexation power. It may be concluded that additives, presented in the compositions studied herein, are promising materials for refractory application, assuming that the additives hydrating will improve refractories mechanical strength, and those decreasing the hydration must be incorporated to other materials to improve their performance.O óxido de magnésio é objeto de investigação devido as suas notáveis propriedades físicas e químicas, principalmente para aplicações em cerâmicas refratárias. No entanto, a hidratação do óxido de magnésio gera o seu hidróxido, Mg(OH)2 e essa reação ainda pode causar uma significativa expansão volumétrica que pode tensionar e danificar um componente feito com esse material. Esses fatores são limitantes para uso em concretos refratários e, devido a isso, grande parte dos estudos para sua aplicação concentra-se em minimizar seus efeitos deletérios. Com o objetivo de minimizar os efeitos da hidratação em composições refratárias, neste trabalho foram avaliados dois tipos de magnésia com reatividades distintas, MgO cáustico e MgO sínter na presença de vários aditivos (CaCl2, MgCl2, CaF2, MgF2, ácido acético, acetato de magnésio, ácido cítrico e EDTA). Os resultados indicaram que os sais solúveis (CaCl2 e MgCl2) aceleram a hidratação, diminuem a expansão volumétrica aparente, aumentam a resistência mecânica e o calor de hidratação. Já a adição de sais insolúveis (CaF2 e MgF2) promoveram diminuição do grau de hidratação, no entanto, as amostras apresentaram trincas e se tornaram friáveis e com baixa resistência mecânica. No caso da adição de ácido acético ou acetato de magnésio ocorreu a aceleração da precipitação da brucita, Mg(OH)2, em decorrência do poder de complexação do íon acetato gerado, sendo a resistência mecânica do acetato superior ao do ácido acético. Os quelantes (ácido cítrico e EDTA) tiveram comportamentos distintos: o ácido cítrico causou a diminuição da hidratação, devido ao efeito de adsorção e o EDTA causou o aumento em consequência do seu poder de complexação dos íons Mg2+. Pode-se concluir que os aditivos, nas composições estudadas, são materiais promissores para aplicação em refratários, partindo do princípio dos que hidratam ocorre melhoria na sua resistência mecânica e os que diminuem a hidratação devem ser incorporados com outros materiais para melhorar o seu desempenho.Financiadora de Estudos e Projetosapplication/pdfporUniversidade Federal de São CarlosPrograma de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEMUFSCarBRMateriais refratáriosConcretos refratáriosÓxido de magnésioHidrataçãoAditivosENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICAEfeito químico de aditivos em suspensões aquosas de magnésia para potenciais aplicações em concretos refratáriosEffect of chemical additives on aqueous suspension of magnesium for potential applications in refractory castablesinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesis-1-1390bd4d1-c505-4015-b043-b075d197c61finfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINAL6795.pdfapplication/pdf7359081https://repositorio.ufscar.br/bitstream/ufscar/743/1/6795.pdfd0c54a98b409ddaf82c94716619e0ff9MD51TEXT6795.pdf.txt6795.pdf.txtExtracted texttext/plain0https://repositorio.ufscar.br/bitstream/ufscar/743/2/6795.pdf.txtd41d8cd98f00b204e9800998ecf8427eMD52THUMBNAIL6795.pdf.jpg6795.pdf.jpgIM Thumbnailimage/jpeg6436https://repositorio.ufscar.br/bitstream/ufscar/743/3/6795.pdf.jpg3e61bd08174bf99da76e06bd77b084a2MD53ufscar/7432023-09-18 18:31:28.005oai:repositorio.ufscar.br:ufscar/743Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222023-09-18T18:31:28Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.por.fl_str_mv |
Efeito químico de aditivos em suspensões aquosas de magnésia para potenciais aplicações em concretos refratários |
dc.title.alternative.eng.fl_str_mv |
Effect of chemical additives on aqueous suspension of magnesium for potential applications in refractory castables |
title |
Efeito químico de aditivos em suspensões aquosas de magnésia para potenciais aplicações em concretos refratários |
spellingShingle |
Efeito químico de aditivos em suspensões aquosas de magnésia para potenciais aplicações em concretos refratários Santos, Ana Maria dos Materiais refratários Concretos refratários Óxido de magnésio Hidratação Aditivos ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
title_short |
Efeito químico de aditivos em suspensões aquosas de magnésia para potenciais aplicações em concretos refratários |
title_full |
Efeito químico de aditivos em suspensões aquosas de magnésia para potenciais aplicações em concretos refratários |
title_fullStr |
Efeito químico de aditivos em suspensões aquosas de magnésia para potenciais aplicações em concretos refratários |
title_full_unstemmed |
Efeito químico de aditivos em suspensões aquosas de magnésia para potenciais aplicações em concretos refratários |
title_sort |
Efeito químico de aditivos em suspensões aquosas de magnésia para potenciais aplicações em concretos refratários |
author |
Santos, Ana Maria dos |
author_facet |
Santos, Ana Maria dos |
author_role |
author |
dc.contributor.author.fl_str_mv |
Santos, Ana Maria dos |
dc.contributor.advisor1.fl_str_mv |
Pandolfelli, Victor Carlos |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/7369376873984839 |
dc.contributor.authorID.fl_str_mv |
33b2319f-8afa-49c3-b826-c425049717b7 |
contributor_str_mv |
Pandolfelli, Victor Carlos |
dc.subject.por.fl_str_mv |
Materiais refratários Concretos refratários Óxido de magnésio Hidratação Aditivos |
topic |
Materiais refratários Concretos refratários Óxido de magnésio Hidratação Aditivos ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
description |
Magnesium oxide is an important subject of investigation because of its physical and chemical properties, mainly for its application to refractory ceramics. However, magnesium oxide hydration generates its hydroxide, Mg(OH)2, which may cause a volumetric expansion, possibly tightening and damaging components made from this material. These factors are limiting for the use in refractory castables and, as a result, most studies regarding this application is focused on minimizing its harmful effects. In order to minimize the effects of hydration on refractory compositions, this work evaluated two types of magnesia presenting different reactivity, caustic and sinter magnesia, with additives (CaCl2, MgCl2, CaF2, MgF2, acetic acid, magnesium acetate, citric acid and EDTA). The results indicated that the soluble salts (CaCl2 and MgCl2) accelerated the hydration, diminishing the apparent volumetric expansion, increasing the mechanical strength and the hydration heat. Because the addition of insoluble salts (CaF2, MgF2) promoted a reduction in the hydration degree, however, samples showed cracks, became crispy, and presented low mechanical strength. In the case of adding acetic acid or magnesium acetate, it occurred a precipitation acceleration of brucite, Mg (OH)2, as a result of the acetate ion complexation power generated, being mechanical resistance of the acetate greater than the acetic acid. The chelating agents (citric acid and EDTA) had distinct behaviors: the citric acid caused hydration decrease because of the absorption effect; and EDTA caused hydration increase as a result of its Mg2+ ions complexation power. It may be concluded that additives, presented in the compositions studied herein, are promising materials for refractory application, assuming that the additives hydrating will improve refractories mechanical strength, and those decreasing the hydration must be incorporated to other materials to improve their performance. |
publishDate |
2015 |
dc.date.available.fl_str_mv |
2015-05-25 2016-06-02T19:10:30Z |
dc.date.issued.fl_str_mv |
2015-02-05 |
dc.date.accessioned.fl_str_mv |
2016-06-02T19:10:30Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/doctoralThesis |
format |
doctoralThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
SANTOS, Ana Maria dos. Effect of chemical additives on aqueous suspension of magnesium for potential applications in refractory castables. 2015. 203 f. Tese (Doutorado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2015. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufscar.br/handle/ufscar/743 |
identifier_str_mv |
SANTOS, Ana Maria dos. Effect of chemical additives on aqueous suspension of magnesium for potential applications in refractory castables. 2015. 203 f. Tese (Doutorado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2015. |
url |
https://repositorio.ufscar.br/handle/ufscar/743 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.confidence.fl_str_mv |
-1 -1 |
dc.relation.authority.fl_str_mv |
390bd4d1-c505-4015-b043-b075d197c61f |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal de São Carlos |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEM |
dc.publisher.initials.fl_str_mv |
UFSCar |
dc.publisher.country.fl_str_mv |
BR |
publisher.none.fl_str_mv |
Universidade Federal de São Carlos |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFSCAR instname:Universidade Federal de São Carlos (UFSCAR) instacron:UFSCAR |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
UFSCAR |
institution |
UFSCAR |
reponame_str |
Repositório Institucional da UFSCAR |
collection |
Repositório Institucional da UFSCAR |
bitstream.url.fl_str_mv |
https://repositorio.ufscar.br/bitstream/ufscar/743/1/6795.pdf https://repositorio.ufscar.br/bitstream/ufscar/743/2/6795.pdf.txt https://repositorio.ufscar.br/bitstream/ufscar/743/3/6795.pdf.jpg |
bitstream.checksum.fl_str_mv |
d0c54a98b409ddaf82c94716619e0ff9 d41d8cd98f00b204e9800998ecf8427e 3e61bd08174bf99da76e06bd77b084a2 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
|
_version_ |
1802136246974152704 |