Produção de concretos autoadensáveis com baixo consumo de cimento e sua influência na aderência aço-concreto
Autor(a) principal: | |
---|---|
Data de Publicação: | 2018 |
Tipo de documento: | Tese |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFSCAR |
Texto Completo: | https://repositorio.ufscar.br/handle/ufscar/10702 |
Resumo: | Self-compacting concrete (SCC) must simultaneously exhibit high fluidity, cohesion and absence of segregation. However, the maintenance of these properties in the fresh state requires a greater consumption of binders and additions, and consequently generating a cost increase in the manufacture of the concrete. In this context, the present work seeks to evaluate the feasibility of the production of Self-Adhesive Concretes with Low Cement Consumption (SCCLCC), determining their properties in the fresh and hardened state. Appropriate inputs for the CAABCC dosage were selected, characterized and the optimal voids index at the packaging step between the aggregates determined. Self-compacting concrete with reduced cement content, with high compressive strength and cement consumption indices of 4.50 to 5.45 kg / m³. MPa-1 at 28 days were reached, in which these values are below those obtained for this type of concrete. These results demonstrate that even under low cement content dosing conditions, the properties in the fresh and hardened state were maintained, thus not suffering significant losses in relation to the reference concrete. Therefore, the results indicate that SCCLCC production with the necessary flowability, satisfactory resistance and reduced cement consumption is feasible. This makes SCC more efficient, with significant cost reductions and environmental impact without compromising its properties. |
id |
SCAR_e317abb94c7b078d74b3ba013d50bfe7 |
---|---|
oai_identifier_str |
oai:repositorio.ufscar.br:ufscar/10702 |
network_acronym_str |
SCAR |
network_name_str |
Repositório Institucional da UFSCAR |
repository_id_str |
4322 |
spelling |
Barboza, Lucas da SilvaAlmeida Filho, Fernando Menezes dehttp://lattes.cnpq.br/0447825383222965http://lattes.cnpq.br/1159705362571916d38c321d-8c41-4aae-8186-3dd05d67778d2018-11-26T10:26:01Z2018-11-26T10:26:01Z2018-10-25BARBOZA, Lucas da Silva. Produção de concretos autoadensáveis com baixo consumo de cimento e sua influência na aderência aço-concreto. 2018. Tese (Doutorado em Engenharia Civil) – Universidade Federal de São Carlos, São Carlos, 2018. Disponível em: https://repositorio.ufscar.br/handle/ufscar/10702.https://repositorio.ufscar.br/handle/ufscar/10702Self-compacting concrete (SCC) must simultaneously exhibit high fluidity, cohesion and absence of segregation. However, the maintenance of these properties in the fresh state requires a greater consumption of binders and additions, and consequently generating a cost increase in the manufacture of the concrete. In this context, the present work seeks to evaluate the feasibility of the production of Self-Adhesive Concretes with Low Cement Consumption (SCCLCC), determining their properties in the fresh and hardened state. Appropriate inputs for the CAABCC dosage were selected, characterized and the optimal voids index at the packaging step between the aggregates determined. Self-compacting concrete with reduced cement content, with high compressive strength and cement consumption indices of 4.50 to 5.45 kg / m³. MPa-1 at 28 days were reached, in which these values are below those obtained for this type of concrete. These results demonstrate that even under low cement content dosing conditions, the properties in the fresh and hardened state were maintained, thus not suffering significant losses in relation to the reference concrete. Therefore, the results indicate that SCCLCC production with the necessary flowability, satisfactory resistance and reduced cement consumption is feasible. This makes SCC more efficient, with significant cost reductions and environmental impact without compromising its properties.O concreto autoadensável (CAA) deve apresentar simultaneamente alta fluidez, coesão e ausência de segregação. No entanto, o atendimento dessas propriedades no estado fresco requer um consumo maior de aglomerantes e adições, e por consequência gerando um aumento de custo na fabricação do concreto. Neste contexto, o presente trabalho busca avaliar a viabilidade da produção de Concretos Autoadensáveis com Baixo Consumo de Cimento (CAABCC), determinando suas propriedades no estado fresco e endurecido. Insumos adequados para a dosagem do CAABCC foram selecionados, caracterizados e o índice ótimo de vazios na etapa do empacotamento entre os agregados determinado. Concretos autoadensáveis com teores de cimento reduzidos, com elevada resistência à compressão e índices de consumo de cimento de 4,50 a 5,45 kg/m³.MPa-1 aos 28 dias foram atingidos, no qual esses valores estão abaixo dos obtidos para este tipo de concreto. Tais resultados, demonstram indícios de que mesmo nas circunstâncias de dosagens com teores de cimento reduzidos, as propriedades no estado fresco e endurecido foram mantidas, não sofrendo assim perdas significativas em relação ao concreto de referência. Portanto, os resultados obtidos indicam que é viável a produção do CAABCC com a fluidez necessária, resistência satisfatória e reduzido consumo de cimento. Isso torna o CAA mais eficiente, com importantes reduções de custos e impacto ambiental sem o comprometimento de suas propriedades.Não recebi financiamentoporUniversidade Federal de São CarlosCâmpus São CarlosPrograma de Pós-Graduação em Engenharia Civil - PPGECivUFSCarCAABCCBaixo consumo de cimentoArrancamentoDurabilidadeAderênciaSCCLCCLow cement consumptionPull-outDurabilityBond strengthENGENHARIAS::ENGENHARIA CIVIL::CONSTRUCAO CIVILENGENHARIAS::ENGENHARIA CIVIL::ESTRUTURASProdução de concretos autoadensáveis com baixo consumo de cimento e sua influência na aderência aço-concretoProduction of self-compacting concrete with low cement sonsumption and its influence on steel-concrete bondinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisOnline60060077f25346-bc48-49b3-a3e1-bf4b0e0fab52info:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINALTese - Lucas - R28-folha de aprovação.pdfTese - Lucas - R28-folha de aprovação.pdfTese - com folha de aprovaçãoapplication/pdf12273408https://repositorio.ufscar.br/bitstream/ufscar/10702/5/Tese%20-%20Lucas%20-%20R28-folha%20de%20aprova%c3%a7%c3%a3o.pdf12d57497a9d6946221840e201b67945dMD55LICENSElicense.txtlicense.txttext/plain; charset=utf-81957https://repositorio.ufscar.br/bitstream/ufscar/10702/6/license.txtae0398b6f8b235e40ad82cba6c50031dMD56TEXTTese - Lucas - R28-folha de aprovação.pdf.txtTese - Lucas - R28-folha de aprovação.pdf.txtExtracted texttext/plain462193https://repositorio.ufscar.br/bitstream/ufscar/10702/7/Tese%20-%20Lucas%20-%20R28-folha%20de%20aprova%c3%a7%c3%a3o.pdf.txtd8e11fe869527186c244da34f3f7470dMD57THUMBNAILTese - Lucas - R28-folha de aprovação.pdf.jpgTese - Lucas - R28-folha de aprovação.pdf.jpgIM Thumbnailimage/jpeg6977https://repositorio.ufscar.br/bitstream/ufscar/10702/8/Tese%20-%20Lucas%20-%20R28-folha%20de%20aprova%c3%a7%c3%a3o.pdf.jpg3f8053ecef6d0b43214d050040fdd165MD58ufscar/107022023-09-18 18:31:17.96oai:repositorio.ufscar.br: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Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222023-09-18T18:31:17Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.por.fl_str_mv |
Produção de concretos autoadensáveis com baixo consumo de cimento e sua influência na aderência aço-concreto |
dc.title.alternative.eng.fl_str_mv |
Production of self-compacting concrete with low cement sonsumption and its influence on steel-concrete bond |
title |
Produção de concretos autoadensáveis com baixo consumo de cimento e sua influência na aderência aço-concreto |
spellingShingle |
Produção de concretos autoadensáveis com baixo consumo de cimento e sua influência na aderência aço-concreto Barboza, Lucas da Silva CAABCC Baixo consumo de cimento Arrancamento Durabilidade Aderência SCCLCC Low cement consumption Pull-out Durability Bond strength ENGENHARIAS::ENGENHARIA CIVIL::CONSTRUCAO CIVIL ENGENHARIAS::ENGENHARIA CIVIL::ESTRUTURAS |
title_short |
Produção de concretos autoadensáveis com baixo consumo de cimento e sua influência na aderência aço-concreto |
title_full |
Produção de concretos autoadensáveis com baixo consumo de cimento e sua influência na aderência aço-concreto |
title_fullStr |
Produção de concretos autoadensáveis com baixo consumo de cimento e sua influência na aderência aço-concreto |
title_full_unstemmed |
Produção de concretos autoadensáveis com baixo consumo de cimento e sua influência na aderência aço-concreto |
title_sort |
Produção de concretos autoadensáveis com baixo consumo de cimento e sua influência na aderência aço-concreto |
author |
Barboza, Lucas da Silva |
author_facet |
Barboza, Lucas da Silva |
author_role |
author |
dc.contributor.authorlattes.por.fl_str_mv |
http://lattes.cnpq.br/1159705362571916 |
dc.contributor.author.fl_str_mv |
Barboza, Lucas da Silva |
dc.contributor.advisor1.fl_str_mv |
Almeida Filho, Fernando Menezes de |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/0447825383222965 |
dc.contributor.authorID.fl_str_mv |
d38c321d-8c41-4aae-8186-3dd05d67778d |
contributor_str_mv |
Almeida Filho, Fernando Menezes de |
dc.subject.por.fl_str_mv |
CAABCC Baixo consumo de cimento Arrancamento Durabilidade Aderência |
topic |
CAABCC Baixo consumo de cimento Arrancamento Durabilidade Aderência SCCLCC Low cement consumption Pull-out Durability Bond strength ENGENHARIAS::ENGENHARIA CIVIL::CONSTRUCAO CIVIL ENGENHARIAS::ENGENHARIA CIVIL::ESTRUTURAS |
dc.subject.eng.fl_str_mv |
SCCLCC Low cement consumption Pull-out Durability Bond strength |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS::ENGENHARIA CIVIL::CONSTRUCAO CIVIL ENGENHARIAS::ENGENHARIA CIVIL::ESTRUTURAS |
description |
Self-compacting concrete (SCC) must simultaneously exhibit high fluidity, cohesion and absence of segregation. However, the maintenance of these properties in the fresh state requires a greater consumption of binders and additions, and consequently generating a cost increase in the manufacture of the concrete. In this context, the present work seeks to evaluate the feasibility of the production of Self-Adhesive Concretes with Low Cement Consumption (SCCLCC), determining their properties in the fresh and hardened state. Appropriate inputs for the CAABCC dosage were selected, characterized and the optimal voids index at the packaging step between the aggregates determined. Self-compacting concrete with reduced cement content, with high compressive strength and cement consumption indices of 4.50 to 5.45 kg / m³. MPa-1 at 28 days were reached, in which these values are below those obtained for this type of concrete. These results demonstrate that even under low cement content dosing conditions, the properties in the fresh and hardened state were maintained, thus not suffering significant losses in relation to the reference concrete. Therefore, the results indicate that SCCLCC production with the necessary flowability, satisfactory resistance and reduced cement consumption is feasible. This makes SCC more efficient, with significant cost reductions and environmental impact without compromising its properties. |
publishDate |
2018 |
dc.date.accessioned.fl_str_mv |
2018-11-26T10:26:01Z |
dc.date.available.fl_str_mv |
2018-11-26T10:26:01Z |
dc.date.issued.fl_str_mv |
2018-10-25 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/doctoralThesis |
format |
doctoralThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
BARBOZA, Lucas da Silva. Produção de concretos autoadensáveis com baixo consumo de cimento e sua influência na aderência aço-concreto. 2018. Tese (Doutorado em Engenharia Civil) – Universidade Federal de São Carlos, São Carlos, 2018. Disponível em: https://repositorio.ufscar.br/handle/ufscar/10702. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufscar.br/handle/ufscar/10702 |
identifier_str_mv |
BARBOZA, Lucas da Silva. Produção de concretos autoadensáveis com baixo consumo de cimento e sua influência na aderência aço-concreto. 2018. Tese (Doutorado em Engenharia Civil) – Universidade Federal de São Carlos, São Carlos, 2018. Disponível em: https://repositorio.ufscar.br/handle/ufscar/10702. |
url |
https://repositorio.ufscar.br/handle/ufscar/10702 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.confidence.fl_str_mv |
600 600 |
dc.relation.authority.fl_str_mv |
77f25346-bc48-49b3-a3e1-bf4b0e0fab52 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.publisher.none.fl_str_mv |
Universidade Federal de São Carlos Câmpus São Carlos |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Engenharia Civil - PPGECiv |
dc.publisher.initials.fl_str_mv |
UFSCar |
publisher.none.fl_str_mv |
Universidade Federal de São Carlos Câmpus São Carlos |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFSCAR instname:Universidade Federal de São Carlos (UFSCAR) instacron:UFSCAR |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
UFSCAR |
institution |
UFSCAR |
reponame_str |
Repositório Institucional da UFSCAR |
collection |
Repositório Institucional da UFSCAR |
bitstream.url.fl_str_mv |
https://repositorio.ufscar.br/bitstream/ufscar/10702/5/Tese%20-%20Lucas%20-%20R28-folha%20de%20aprova%c3%a7%c3%a3o.pdf https://repositorio.ufscar.br/bitstream/ufscar/10702/6/license.txt https://repositorio.ufscar.br/bitstream/ufscar/10702/7/Tese%20-%20Lucas%20-%20R28-folha%20de%20aprova%c3%a7%c3%a3o.pdf.txt https://repositorio.ufscar.br/bitstream/ufscar/10702/8/Tese%20-%20Lucas%20-%20R28-folha%20de%20aprova%c3%a7%c3%a3o.pdf.jpg |
bitstream.checksum.fl_str_mv |
12d57497a9d6946221840e201b67945d ae0398b6f8b235e40ad82cba6c50031d d8e11fe869527186c244da34f3f7470d 3f8053ecef6d0b43214d050040fdd165 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
|
_version_ |
1813715597178961920 |