Influência das condições de eletrodeposição sobre a resistência a corrosão, susceptibilidade à fragilização por hidrogênio e à corrosão sob tensão do aço ABNT – 4340 revestido com liga Zn/Ni

Detalhes bibliográficos
Autor(a) principal: Calciolari, Fábio Luiz
Data de Publicação: 2011
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UFSCAR
Texto Completo: https://repositorio.ufscar.br/handle/ufscar/7433
Resumo: Zinc-nickel alloys were electrodeposited on ABNT 4340 high strength steel in chloride acid media. The effect of the electrolyte composition and electroplating conditions on cathodic efficiency, chemical composition, morphology and phase structure of the deposits was evaluated regarding their influence on the corrosion resistance of the coatings, resistance to corrosion fatigue cracking, susceptibility to stress corrosion cracking and hydrogen embrittlement of the coated part. The electrolyte composition, temperature and cathodic current density had influenced in a significantly manner the nickel content, phases structure, morphology and corrosion resistance of the coatings. In general, the amount of nickel and the fraction of phase in the alloys were promoted by decrease of current density, increase of temperature and nickel concentration in bath. The increase of the fraction, as well as the increase of the nickel content on monophasic alloys shifts the corrosion potential to more positive values and decreases corrosion current of the coatings. The results obtained allows to improve the knowledge about the relations between processing, structure and properties of electroplated Zn-Ni alloys in order to use these coatings on low alloy high strength steels components.
id SCAR_f6338df489145f90dffdd890d4df99c4
oai_identifier_str oai:repositorio.ufscar.br:ufscar/7433
network_acronym_str SCAR
network_name_str Repositório Institucional da UFSCAR
repository_id_str 4322
spelling Calciolari, Fábio LuizKuri, Sebastião Eliashttp://lattes.cnpq.br/6842072916153866http://lattes.cnpq.br/4416951586826865a825a6f2-f5ee-4854-a967-2c2ca1cfe56b2016-09-26T18:43:34Z2016-09-26T18:43:34Z2011-01-28CALCIOLARI, Fábio Luiz. Influência das condições de eletrodeposição sobre a resistência a corrosão, susceptibilidade à fragilização por hidrogênio e à corrosão sob tensão do aço ABNT – 4340 revestido com liga Zn/Ni. 2011. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2011. Disponível em: https://repositorio.ufscar.br/handle/ufscar/7433.https://repositorio.ufscar.br/handle/ufscar/7433Zinc-nickel alloys were electrodeposited on ABNT 4340 high strength steel in chloride acid media. The effect of the electrolyte composition and electroplating conditions on cathodic efficiency, chemical composition, morphology and phase structure of the deposits was evaluated regarding their influence on the corrosion resistance of the coatings, resistance to corrosion fatigue cracking, susceptibility to stress corrosion cracking and hydrogen embrittlement of the coated part. The electrolyte composition, temperature and cathodic current density had influenced in a significantly manner the nickel content, phases structure, morphology and corrosion resistance of the coatings. In general, the amount of nickel and the fraction of phase in the alloys were promoted by decrease of current density, increase of temperature and nickel concentration in bath. The increase of the fraction, as well as the increase of the nickel content on monophasic alloys shifts the corrosion potential to more positive values and decreases corrosion current of the coatings. The results obtained allows to improve the knowledge about the relations between processing, structure and properties of electroplated Zn-Ni alloys in order to use these coatings on low alloy high strength steels components.Ligas zinco-níquel foram eletrodepositadas sobre substratos de aço ABNT 4340 de alta resistência mecânica em meio ácido de cloretos. O efeito da composição do eletrólito e das condições operacionais de eletrodeposição sobre a eficiência de corrente do processo, composição química, morfologia e microestrutura de fases dos depósitos foi avaliada, assim como sua influência nas propriedades de resistência à corrosão dos revestimentos, resistência à corrosão-fadiga, suscetibilidade à corrosão sob tensão e fragilização por hidrogênio do conjunto depósito / substrato. A composição do eletrólito, temperatura e densidade de corrente catódica influenciaram significativamente o teor de níquel depositado, a distribuição de fases, morfologia e a resistência à corrosão dos revestimentos. De modo geral, a quantidade de níquel assim como a fração da fase na liga é favorecida pela diminuição da densidade de corrente, aumento da temperatura e da concentração de níquel no banho. O aumento da fração de na estrutura assim como o aumento de níquel nas ligas monofásicas deslocam o valor do potencial de corrosão para valores mais positivos e diminuem a corrente de corrosão dos revestimentos. Os resultados obtidos contribuíram para uma melhor compreensão das correlações existentes entre processamento, estrutura e propriedades de ligas Zn-Ni eletrodepositadas visando o revestimento de aços baixa liga de alta resistência mecânica.Não recebi financiamentoporUniversidade Federal de São CarlosCâmpus São CarlosPrograma de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEMUFSCarEletrodeposiçãoLigas zinco-níquelCorrosãoFragilização por hidrogênioENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::METALURGIA FISICAInfluência das condições de eletrodeposição sobre a resistência a corrosão, susceptibilidade à fragilização por hidrogênio e à corrosão sob tensão do aço ABNT – 4340 revestido com liga Zn/NiEffects of electrodeposition conditions on corrosion resistance, hydrogen embrittlement and stress corrosion cracking of abnt 4340 steel coated with zn-ni alloysinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisOnline600600dd65b32b-27ea-44dd-9f6f-c8b3b548e9bainfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINALTeseFLC.pdfTeseFLC.pdfapplication/pdf13129956https://repositorio.ufscar.br/bitstream/ufscar/7433/1/TeseFLC.pdf3158a0267e11eb05e0093c71858e435fMD51LICENSElicense.txtlicense.txttext/plain; charset=utf-81957https://repositorio.ufscar.br/bitstream/ufscar/7433/2/license.txtae0398b6f8b235e40ad82cba6c50031dMD52TEXTTeseFLC.pdf.txtTeseFLC.pdf.txtExtracted texttext/plain300755https://repositorio.ufscar.br/bitstream/ufscar/7433/3/TeseFLC.pdf.txt973d58846bafc8990d7e2c7c33dbefa0MD53THUMBNAILTeseFLC.pdf.jpgTeseFLC.pdf.jpgIM Thumbnailimage/jpeg7250https://repositorio.ufscar.br/bitstream/ufscar/7433/4/TeseFLC.pdf.jpgdd7b09e74a1790d9d528ae490b58c76eMD54ufscar/74332023-09-18 18:30:51.348oai:repositorio.ufscar.br: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Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222023-09-18T18:30:51Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false
dc.title.por.fl_str_mv Influência das condições de eletrodeposição sobre a resistência a corrosão, susceptibilidade à fragilização por hidrogênio e à corrosão sob tensão do aço ABNT – 4340 revestido com liga Zn/Ni
dc.title.alternative.eng.fl_str_mv Effects of electrodeposition conditions on corrosion resistance, hydrogen embrittlement and stress corrosion cracking of abnt 4340 steel coated with zn-ni alloys
title Influência das condições de eletrodeposição sobre a resistência a corrosão, susceptibilidade à fragilização por hidrogênio e à corrosão sob tensão do aço ABNT – 4340 revestido com liga Zn/Ni
spellingShingle Influência das condições de eletrodeposição sobre a resistência a corrosão, susceptibilidade à fragilização por hidrogênio e à corrosão sob tensão do aço ABNT – 4340 revestido com liga Zn/Ni
Calciolari, Fábio Luiz
Eletrodeposição
Ligas zinco-níquel
Corrosão
Fragilização por hidrogênio
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::METALURGIA FISICA
title_short Influência das condições de eletrodeposição sobre a resistência a corrosão, susceptibilidade à fragilização por hidrogênio e à corrosão sob tensão do aço ABNT – 4340 revestido com liga Zn/Ni
title_full Influência das condições de eletrodeposição sobre a resistência a corrosão, susceptibilidade à fragilização por hidrogênio e à corrosão sob tensão do aço ABNT – 4340 revestido com liga Zn/Ni
title_fullStr Influência das condições de eletrodeposição sobre a resistência a corrosão, susceptibilidade à fragilização por hidrogênio e à corrosão sob tensão do aço ABNT – 4340 revestido com liga Zn/Ni
title_full_unstemmed Influência das condições de eletrodeposição sobre a resistência a corrosão, susceptibilidade à fragilização por hidrogênio e à corrosão sob tensão do aço ABNT – 4340 revestido com liga Zn/Ni
title_sort Influência das condições de eletrodeposição sobre a resistência a corrosão, susceptibilidade à fragilização por hidrogênio e à corrosão sob tensão do aço ABNT – 4340 revestido com liga Zn/Ni
author Calciolari, Fábio Luiz
author_facet Calciolari, Fábio Luiz
author_role author
dc.contributor.authorlattes.por.fl_str_mv http://lattes.cnpq.br/4416951586826865
dc.contributor.author.fl_str_mv Calciolari, Fábio Luiz
dc.contributor.advisor1.fl_str_mv Kuri, Sebastião Elias
dc.contributor.advisor1Lattes.fl_str_mv http://lattes.cnpq.br/6842072916153866
dc.contributor.authorID.fl_str_mv a825a6f2-f5ee-4854-a967-2c2ca1cfe56b
contributor_str_mv Kuri, Sebastião Elias
dc.subject.por.fl_str_mv Eletrodeposição
Ligas zinco-níquel
Corrosão
Fragilização por hidrogênio
topic Eletrodeposição
Ligas zinco-níquel
Corrosão
Fragilização por hidrogênio
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::METALURGIA FISICA
dc.subject.cnpq.fl_str_mv ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::METALURGIA FISICA
description Zinc-nickel alloys were electrodeposited on ABNT 4340 high strength steel in chloride acid media. The effect of the electrolyte composition and electroplating conditions on cathodic efficiency, chemical composition, morphology and phase structure of the deposits was evaluated regarding their influence on the corrosion resistance of the coatings, resistance to corrosion fatigue cracking, susceptibility to stress corrosion cracking and hydrogen embrittlement of the coated part. The electrolyte composition, temperature and cathodic current density had influenced in a significantly manner the nickel content, phases structure, morphology and corrosion resistance of the coatings. In general, the amount of nickel and the fraction of phase in the alloys were promoted by decrease of current density, increase of temperature and nickel concentration in bath. The increase of the fraction, as well as the increase of the nickel content on monophasic alloys shifts the corrosion potential to more positive values and decreases corrosion current of the coatings. The results obtained allows to improve the knowledge about the relations between processing, structure and properties of electroplated Zn-Ni alloys in order to use these coatings on low alloy high strength steels components.
publishDate 2011
dc.date.issued.fl_str_mv 2011-01-28
dc.date.accessioned.fl_str_mv 2016-09-26T18:43:34Z
dc.date.available.fl_str_mv 2016-09-26T18:43:34Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.citation.fl_str_mv CALCIOLARI, Fábio Luiz. Influência das condições de eletrodeposição sobre a resistência a corrosão, susceptibilidade à fragilização por hidrogênio e à corrosão sob tensão do aço ABNT – 4340 revestido com liga Zn/Ni. 2011. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2011. Disponível em: https://repositorio.ufscar.br/handle/ufscar/7433.
dc.identifier.uri.fl_str_mv https://repositorio.ufscar.br/handle/ufscar/7433
identifier_str_mv CALCIOLARI, Fábio Luiz. Influência das condições de eletrodeposição sobre a resistência a corrosão, susceptibilidade à fragilização por hidrogênio e à corrosão sob tensão do aço ABNT – 4340 revestido com liga Zn/Ni. 2011. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2011. Disponível em: https://repositorio.ufscar.br/handle/ufscar/7433.
url https://repositorio.ufscar.br/handle/ufscar/7433
dc.language.iso.fl_str_mv por
language por
dc.relation.confidence.fl_str_mv 600
600
dc.relation.authority.fl_str_mv dd65b32b-27ea-44dd-9f6f-c8b3b548e9ba
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.publisher.none.fl_str_mv Universidade Federal de São Carlos
Câmpus São Carlos
dc.publisher.program.fl_str_mv Programa de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEM
dc.publisher.initials.fl_str_mv UFSCar
publisher.none.fl_str_mv Universidade Federal de São Carlos
Câmpus São Carlos
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSCAR
instname:Universidade Federal de São Carlos (UFSCAR)
instacron:UFSCAR
instname_str Universidade Federal de São Carlos (UFSCAR)
instacron_str UFSCAR
institution UFSCAR
reponame_str Repositório Institucional da UFSCAR
collection Repositório Institucional da UFSCAR
bitstream.url.fl_str_mv https://repositorio.ufscar.br/bitstream/ufscar/7433/1/TeseFLC.pdf
https://repositorio.ufscar.br/bitstream/ufscar/7433/2/license.txt
https://repositorio.ufscar.br/bitstream/ufscar/7433/3/TeseFLC.pdf.txt
https://repositorio.ufscar.br/bitstream/ufscar/7433/4/TeseFLC.pdf.jpg
bitstream.checksum.fl_str_mv 3158a0267e11eb05e0093c71858e435f
ae0398b6f8b235e40ad82cba6c50031d
973d58846bafc8990d7e2c7c33dbefa0
dd7b09e74a1790d9d528ae490b58c76e
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
MD5
MD5
repository.name.fl_str_mv Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)
repository.mail.fl_str_mv
_version_ 1813715561343877120

Registros relacionados