PRODUÇÃO E CARACTERIZAÇÃO DE MATERIAIS COMPÓSITOS A PARTIR DE REJEITOS DA INDÚSTRIA PAPELEIRA E SUCROALCOOLEIRA
Autor(a) principal: | |
---|---|
Data de Publicação: | 2015 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações do UNICENTRO |
Texto Completo: | http://tede.unicentro.br:8080/jspui/handle/jspui/748 |
Resumo: | The Plastic wastes produced by paper industries in equipments called hidrapulper, cause financial losses to many businesses and can cause environmental impacts. The objective of this study was to characterize by physical, mechanical, thermal and morphological testing the hidrapulper plastic wastes (RPH, portuguese acronym) and then to use this material as polymer matrix at the composite materials manufacture. Specifically, it was used the RPH mixed with sugar cane bagasse fibers, like reinforcing fillers to obtain a kind of composite. Using a 22 factorial planning war analyzed the factors of the fibers proportion and the applied pressure on the composite samples made in quintuplicate. It was observed that this material supports efficiency high temperatures, can be used in the extrusion process without degradation of the polymeric chains, besides shows a low viscosity material and therefore with excellent fluidity. Analyzing the implemented factorial planning, the application of pressures more than 5 tons was not necessary because higher compaction decreased mechanical and physical strength of the composites at the most tests. Still showed that the incorporation of higher proportions of the composite fibers, make the material with a wood look, most significant results obtained, especially at the compression and impact tests. Due to hygroscopicity of natural fibers, a greater inclusion in composites, increased water absorption in the samples. With the realized work, it was found that the RPH, nowadays considered an environmental problem, can serve as polymer matrix for the formulation of composite materials, replacing thermoplastic resins. It was possible to observe that the material developed in this study can also solve one of the biggest problems facing the wood and its derivatives, the moisture. |
id |
UCEN_5f65db4e0610a04b7500a50220b462b7 |
---|---|
oai_identifier_str |
oai:localhost:jspui/748 |
network_acronym_str |
UCEN |
network_name_str |
Biblioteca Digital de Teses e Dissertações do UNICENTRO |
repository_id_str |
|
spelling |
Melquiades, Fábio Luizhttp://lattes.cnpq.br/8539939787669526Fábio Luiz MelquiadesMiyahara, Ricardo Yoshimitsuhttp://lattes.cnpq.br/4732577960462037013.483.180-23http://lattes.cnpq.br/7310435696180355LIGOWSKI, EZEQUIEL2017-06-30T18:29:38Z2015-03-27LIGOWSKI, EZEQUIEL. PRODUÇÃO E CARACTERIZAÇÃO DE MATERIAIS COMPÓSITOS A PARTIR DE REJEITOS DA INDÚSTRIA PAPELEIRA E SUCROALCOOLEIRA. 2015. 74 f. Dissertação (Programa de Pós-Graduação em Química - Mestrado) - Universidade Estadual do Centro-Oeste, Guarapuava - PR.http://tede.unicentro.br:8080/jspui/handle/jspui/748The Plastic wastes produced by paper industries in equipments called hidrapulper, cause financial losses to many businesses and can cause environmental impacts. The objective of this study was to characterize by physical, mechanical, thermal and morphological testing the hidrapulper plastic wastes (RPH, portuguese acronym) and then to use this material as polymer matrix at the composite materials manufacture. Specifically, it was used the RPH mixed with sugar cane bagasse fibers, like reinforcing fillers to obtain a kind of composite. Using a 22 factorial planning war analyzed the factors of the fibers proportion and the applied pressure on the composite samples made in quintuplicate. It was observed that this material supports efficiency high temperatures, can be used in the extrusion process without degradation of the polymeric chains, besides shows a low viscosity material and therefore with excellent fluidity. Analyzing the implemented factorial planning, the application of pressures more than 5 tons was not necessary because higher compaction decreased mechanical and physical strength of the composites at the most tests. Still showed that the incorporation of higher proportions of the composite fibers, make the material with a wood look, most significant results obtained, especially at the compression and impact tests. Due to hygroscopicity of natural fibers, a greater inclusion in composites, increased water absorption in the samples. With the realized work, it was found that the RPH, nowadays considered an environmental problem, can serve as polymer matrix for the formulation of composite materials, replacing thermoplastic resins. It was possible to observe that the material developed in this study can also solve one of the biggest problems facing the wood and its derivatives, the moisture.Os rejeitos plásticos produzidos pelas indústrias papeleiras, em equipamentos denominados Hidrapulper, acarretam prejuízos financeiros às empresas e causam impactos ambientais. O objetivo deste trabalho foi caracterizar por meio de ensaios físicos, mecânicos, térmicos e morfológicos o Rejeito Plástico de Hidrapulper (RPH) e em seguida utilizar este material como matriz polimérica na confecção de materiais compósitos. Especificamente, utilizou-se o RPH misturado a fibras de bagaço de cana de açúcar, inseridas como cargas reforçantes visando a obtenção de um compósito polimérico. Utilizando um planejamento fatorial 22 foram analisados os fatores da proporção de fibras e da pressão aplicada sobre as amostras compósitas confeccionadas em quintuplicata. Observou-se que este material suporta altas temperaturas com eficiência, podendo ser utilizado no processo de extrusão sem a degradação das cadeias poliméricas, além de se apresentar um material pouco viscoso e portanto com excelente fluidez. Analisando o planejamento fatorial implementado, foi observado não ser necessário a aplicação de pressões superiores a 5 toneladas, pois maiores compactações, diminuíram a resistência mecânica e física dos compósitos na maioria dos testes. Ainda apresentou que a incorporação de maiores proporções de fibras aos compósitos, além de deixar o material com um aspecto de madeira, obteve resultados mais significativos, principalmente nos testes de compressão e impacto. Devido a higroscopicidade das fibras naturais, uma maior inserção nos compósitos, aumentou a absorção de água nas amostras. Com o trabalho realizado, verificou-se que o RPH, considerado atualmente um problema ambiental, pode servir como matriz polimérica para formulação de materiais compósitos, substituindo resinas termoplásticas. Foi possível observar que o material desenvolvido neste estudo pode ainda resolver um dos maiores problemas enfrentados pela madeira e seus derivados, a umidade.Submitted by Fabiano Jucá (fjuca@unicentro.br) on 2017-06-30T18:29:38Z No. of bitstreams: 1 EZEQUIEL LIGOWSKI.pdf: 2638362 bytes, checksum: dd9ddc0065e77fe2bd8d3f5350f930cc (MD5)Made available in DSpace on 2017-06-30T18:29:38Z (GMT). No. of bitstreams: 1 EZEQUIEL LIGOWSKI.pdf: 2638362 bytes, checksum: dd9ddc0065e77fe2bd8d3f5350f930cc (MD5) Previous issue date: 2015-03-27Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://tede.unicentro.br:8080/jspui/retrieve/3648/EZEQUIEL%20LIGOWSKI.pdf.jpgporUniversidade Estadual do Centro-OestePrograma de Pós-Graduação em Química (Mestrado)UNICENTROBrasilUnicentro::Departamento de Químicarejeitos plásticosfibras de bagaço de cana-de-açúcarequipamento hidrapulper materiais compósitosindústria papeleiraplastic wastecane bagasse fibercomposite materialshidrapulper equipmentpaper industryCIENCIAS EXATAS E DA TERRA::QUIMICAPRODUÇÃO E CARACTERIZAÇÃO DE MATERIAIS COMPÓSITOS A PARTIR DE REJEITOS DA INDÚSTRIA PAPELEIRA E SUCROALCOOLEIRAinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-5600948132407545169600600600600-758308430858845636115717003253031171952075167498588264571info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações do UNICENTROinstname:Universidade Estadual do Centro-Oeste (UNICENTRO)instacron:UNICENTROTHUMBNAILEZEQUIEL LIGOWSKI.pdf.jpgEZEQUIEL LIGOWSKI.pdf.jpgimage/jpeg1952http://localhost:8080/tede/bitstream/jspui/748/4/EZEQUIEL+LIGOWSKI.pdf.jpg7216c0533e7f54c55f5c8c4bbfc68707MD54TEXTEZEQUIEL LIGOWSKI.pdf.txtEZEQUIEL LIGOWSKI.pdf.txttext/plain131123http://localhost:8080/tede/bitstream/jspui/748/3/EZEQUIEL+LIGOWSKI.pdf.txt3f2a44dacde1aa3c8fe1dae91ec00620MD53LICENSElicense.txtlicense.txttext/plain; charset=utf-82165http://localhost:8080/tede/bitstream/jspui/748/1/license.txtbd3efa91386c1718a7f26a329fdcb468MD51ORIGINALEZEQUIEL LIGOWSKI.pdfEZEQUIEL LIGOWSKI.pdfapplication/pdf2638362http://localhost:8080/tede/bitstream/jspui/748/2/EZEQUIEL+LIGOWSKI.pdfdd9ddc0065e77fe2bd8d3f5350f930ccMD52jspui/7482020-07-08 01:01:53.479oai:localhost: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede.unicentro.br:8080/jspui/PUBhttp://tede.unicentro.br/tde_oai/oai3.phprepositorio@unicentro.br||fabianoqueiroz@yahoo.com.bropendoar:2020-07-08T04:01:53Biblioteca Digital de Teses e Dissertações do UNICENTRO - Universidade Estadual do Centro-Oeste (UNICENTRO)false |
dc.title.por.fl_str_mv |
PRODUÇÃO E CARACTERIZAÇÃO DE MATERIAIS COMPÓSITOS A PARTIR DE REJEITOS DA INDÚSTRIA PAPELEIRA E SUCROALCOOLEIRA |
title |
PRODUÇÃO E CARACTERIZAÇÃO DE MATERIAIS COMPÓSITOS A PARTIR DE REJEITOS DA INDÚSTRIA PAPELEIRA E SUCROALCOOLEIRA |
spellingShingle |
PRODUÇÃO E CARACTERIZAÇÃO DE MATERIAIS COMPÓSITOS A PARTIR DE REJEITOS DA INDÚSTRIA PAPELEIRA E SUCROALCOOLEIRA LIGOWSKI, EZEQUIEL rejeitos plásticos fibras de bagaço de cana-de-açúcar equipamento hidrapulper materiais compósitos indústria papeleira plastic waste cane bagasse fiber composite materials hidrapulper equipment paper industry CIENCIAS EXATAS E DA TERRA::QUIMICA |
title_short |
PRODUÇÃO E CARACTERIZAÇÃO DE MATERIAIS COMPÓSITOS A PARTIR DE REJEITOS DA INDÚSTRIA PAPELEIRA E SUCROALCOOLEIRA |
title_full |
PRODUÇÃO E CARACTERIZAÇÃO DE MATERIAIS COMPÓSITOS A PARTIR DE REJEITOS DA INDÚSTRIA PAPELEIRA E SUCROALCOOLEIRA |
title_fullStr |
PRODUÇÃO E CARACTERIZAÇÃO DE MATERIAIS COMPÓSITOS A PARTIR DE REJEITOS DA INDÚSTRIA PAPELEIRA E SUCROALCOOLEIRA |
title_full_unstemmed |
PRODUÇÃO E CARACTERIZAÇÃO DE MATERIAIS COMPÓSITOS A PARTIR DE REJEITOS DA INDÚSTRIA PAPELEIRA E SUCROALCOOLEIRA |
title_sort |
PRODUÇÃO E CARACTERIZAÇÃO DE MATERIAIS COMPÓSITOS A PARTIR DE REJEITOS DA INDÚSTRIA PAPELEIRA E SUCROALCOOLEIRA |
author |
LIGOWSKI, EZEQUIEL |
author_facet |
LIGOWSKI, EZEQUIEL |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Melquiades, Fábio Luiz |
dc.contributor.advisor1ID.fl_str_mv |
http://lattes.cnpq.br/8539939787669526 |
dc.contributor.advisor1Lattes.fl_str_mv |
Fábio Luiz Melquiades |
dc.contributor.advisor-co1.fl_str_mv |
Miyahara, Ricardo Yoshimitsu |
dc.contributor.advisor-co1Lattes.fl_str_mv |
http://lattes.cnpq.br/4732577960462037 |
dc.contributor.authorID.fl_str_mv |
013.483.180-23 |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/7310435696180355 |
dc.contributor.author.fl_str_mv |
LIGOWSKI, EZEQUIEL |
contributor_str_mv |
Melquiades, Fábio Luiz Miyahara, Ricardo Yoshimitsu |
dc.subject.por.fl_str_mv |
rejeitos plásticos fibras de bagaço de cana-de-açúcar equipamento hidrapulper materiais compósitos indústria papeleira |
topic |
rejeitos plásticos fibras de bagaço de cana-de-açúcar equipamento hidrapulper materiais compósitos indústria papeleira plastic waste cane bagasse fiber composite materials hidrapulper equipment paper industry CIENCIAS EXATAS E DA TERRA::QUIMICA |
dc.subject.eng.fl_str_mv |
plastic waste cane bagasse fiber composite materials hidrapulper equipment paper industry |
dc.subject.cnpq.fl_str_mv |
CIENCIAS EXATAS E DA TERRA::QUIMICA |
description |
The Plastic wastes produced by paper industries in equipments called hidrapulper, cause financial losses to many businesses and can cause environmental impacts. The objective of this study was to characterize by physical, mechanical, thermal and morphological testing the hidrapulper plastic wastes (RPH, portuguese acronym) and then to use this material as polymer matrix at the composite materials manufacture. Specifically, it was used the RPH mixed with sugar cane bagasse fibers, like reinforcing fillers to obtain a kind of composite. Using a 22 factorial planning war analyzed the factors of the fibers proportion and the applied pressure on the composite samples made in quintuplicate. It was observed that this material supports efficiency high temperatures, can be used in the extrusion process without degradation of the polymeric chains, besides shows a low viscosity material and therefore with excellent fluidity. Analyzing the implemented factorial planning, the application of pressures more than 5 tons was not necessary because higher compaction decreased mechanical and physical strength of the composites at the most tests. Still showed that the incorporation of higher proportions of the composite fibers, make the material with a wood look, most significant results obtained, especially at the compression and impact tests. Due to hygroscopicity of natural fibers, a greater inclusion in composites, increased water absorption in the samples. With the realized work, it was found that the RPH, nowadays considered an environmental problem, can serve as polymer matrix for the formulation of composite materials, replacing thermoplastic resins. It was possible to observe that the material developed in this study can also solve one of the biggest problems facing the wood and its derivatives, the moisture. |
publishDate |
2015 |
dc.date.issued.fl_str_mv |
2015-03-27 |
dc.date.accessioned.fl_str_mv |
2017-06-30T18:29:38Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
LIGOWSKI, EZEQUIEL. PRODUÇÃO E CARACTERIZAÇÃO DE MATERIAIS COMPÓSITOS A PARTIR DE REJEITOS DA INDÚSTRIA PAPELEIRA E SUCROALCOOLEIRA. 2015. 74 f. Dissertação (Programa de Pós-Graduação em Química - Mestrado) - Universidade Estadual do Centro-Oeste, Guarapuava - PR. |
dc.identifier.uri.fl_str_mv |
http://tede.unicentro.br:8080/jspui/handle/jspui/748 |
identifier_str_mv |
LIGOWSKI, EZEQUIEL. PRODUÇÃO E CARACTERIZAÇÃO DE MATERIAIS COMPÓSITOS A PARTIR DE REJEITOS DA INDÚSTRIA PAPELEIRA E SUCROALCOOLEIRA. 2015. 74 f. Dissertação (Programa de Pós-Graduação em Química - Mestrado) - Universidade Estadual do Centro-Oeste, Guarapuava - PR. |
url |
http://tede.unicentro.br:8080/jspui/handle/jspui/748 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
-5600948132407545169 |
dc.relation.confidence.fl_str_mv |
600 600 600 600 |
dc.relation.department.fl_str_mv |
-7583084308588456361 |
dc.relation.cnpq.fl_str_mv |
1571700325303117195 |
dc.relation.sponsorship.fl_str_mv |
2075167498588264571 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Estadual do Centro-Oeste |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Química (Mestrado) |
dc.publisher.initials.fl_str_mv |
UNICENTRO |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Unicentro::Departamento de Química |
publisher.none.fl_str_mv |
Universidade Estadual do Centro-Oeste |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações do UNICENTRO instname:Universidade Estadual do Centro-Oeste (UNICENTRO) instacron:UNICENTRO |
instname_str |
Universidade Estadual do Centro-Oeste (UNICENTRO) |
instacron_str |
UNICENTRO |
institution |
UNICENTRO |
reponame_str |
Biblioteca Digital de Teses e Dissertações do UNICENTRO |
collection |
Biblioteca Digital de Teses e Dissertações do UNICENTRO |
bitstream.url.fl_str_mv |
http://localhost:8080/tede/bitstream/jspui/748/4/EZEQUIEL+LIGOWSKI.pdf.jpg http://localhost:8080/tede/bitstream/jspui/748/3/EZEQUIEL+LIGOWSKI.pdf.txt http://localhost:8080/tede/bitstream/jspui/748/1/license.txt http://localhost:8080/tede/bitstream/jspui/748/2/EZEQUIEL+LIGOWSKI.pdf |
bitstream.checksum.fl_str_mv |
7216c0533e7f54c55f5c8c4bbfc68707 3f2a44dacde1aa3c8fe1dae91ec00620 bd3efa91386c1718a7f26a329fdcb468 dd9ddc0065e77fe2bd8d3f5350f930cc |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações do UNICENTRO - Universidade Estadual do Centro-Oeste (UNICENTRO) |
repository.mail.fl_str_mv |
repositorio@unicentro.br||fabianoqueiroz@yahoo.com.br |
_version_ |
1811733812469563392 |