ESTUDO “IN LOCO” DA CONTRAÇÃO DE POLIMERIZAÇÃO E DO GRAU DE CONVERSÃO DE CIMENTOS RESINOSOS UTILIZADOS NA FIXAÇÃO DE PINOS INTRARRADICULARES

Detalhes bibliográficos
Autor(a) principal: Mora, Camilo Andrés Pulido
Data de Publicação: 2014
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da UEPG
Texto Completo: http://tede2.uepg.br/jspui/handle/prefix/1712
Resumo: The aim of this study was to investigate the shrinkage-strainand degree of conversion inside the rootcanal"in situ"of resin cements used to lute fiber posts (Whitepost DC, FG). Thirty maxillary canines with similar root length average were selected (14 mm ± 1 mm). Each root canal was treated with crown-down technique and filled with gutta-percha, leaving 4 mm of apical seal.One week later, the roots were prepared following fiber post system manufacturer’s instructions. For the cementation, teeth were randomly divided into 2 groups (n = 15) according to the resin cement used: Group 1: dual-cured resin cement RelyX™ ARC – Adper Scotchbond™ Multipurpose Plus Adhesive (3M/ESPE) and Group 2: dual-cured resin cement RelyX™ U200 (3M/ESPE). Two fiber optic sensors with recorded Bragg gratings were attached to the coronal section (not in contact with the root) of each post before inserting the resin cement inside the root canal. These sensors measured the deformations of the cement over the coronal and apical section of the root (μe). Once measured, the specimens were sectionated in order to obtain slides on its cervical and apical sections. The degree of conversion of the cements on each third was analyzed by μ-Raman micro-spectroscopy. The data were statitsticallyanalyzed by two-way ANOVA (p = 0.05). The dual-curedconventional resin cement tested in this study showed the highest values of shrinkage-strain and degree of conversion; cervical region showed higher values than apical region in both of resin cements.
id UEPG_568d76fb0906ac8397e818067652de3f
oai_identifier_str oai:tede2.uepg.br:prefix/1712
network_acronym_str UEPG
network_name_str Biblioteca Digital de Teses e Dissertações da UEPG
repository_id_str
spelling Gomes, Osnara Maria MongruelCPF:47308257991http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4773647J1Franco, Ana Paula GebertCPF:03851604962http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4730703E6Arrais, Cesar Augusto GalvãoCPF:20064607810http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4770689J6CPF:01220034975http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4373360J5Mora, Camilo Andrés Pulido2017-07-24T19:22:01Z2016-07-072017-07-24T19:22:01Z2014-02-17MORA, Camilo Andrés Pulido. Study “in situ” ofthe polymerization shrinkage-strain and degree of conversion of resin cements used for luting intracanal fiber posts. 2014. 66 f. Dissertação (Mestrado em Clinica Integrada, Dentística Restauradora e Periodontia) - UNIVERSIDADE ESTADUAL DE PONTA GROSSA, Ponta Grossa, 2014.http://tede2.uepg.br/jspui/handle/prefix/1712The aim of this study was to investigate the shrinkage-strainand degree of conversion inside the rootcanal"in situ"of resin cements used to lute fiber posts (Whitepost DC, FG). Thirty maxillary canines with similar root length average were selected (14 mm ± 1 mm). Each root canal was treated with crown-down technique and filled with gutta-percha, leaving 4 mm of apical seal.One week later, the roots were prepared following fiber post system manufacturer’s instructions. For the cementation, teeth were randomly divided into 2 groups (n = 15) according to the resin cement used: Group 1: dual-cured resin cement RelyX™ ARC – Adper Scotchbond™ Multipurpose Plus Adhesive (3M/ESPE) and Group 2: dual-cured resin cement RelyX™ U200 (3M/ESPE). Two fiber optic sensors with recorded Bragg gratings were attached to the coronal section (not in contact with the root) of each post before inserting the resin cement inside the root canal. These sensors measured the deformations of the cement over the coronal and apical section of the root (μe). Once measured, the specimens were sectionated in order to obtain slides on its cervical and apical sections. The degree of conversion of the cements on each third was analyzed by μ-Raman micro-spectroscopy. The data were statitsticallyanalyzed by two-way ANOVA (p = 0.05). The dual-curedconventional resin cement tested in this study showed the highest values of shrinkage-strain and degree of conversion; cervical region showed higher values than apical region in both of resin cements.O objetivo deste estudo foi conhecer o comportamento e a magnitude das deformações que ocorrem durante a polimerização “in loco” no interior do canal radicular, em cimentos resinosos durante a fixação de pinos de fibra de vidro Whitepost DC (FGM) e verificar o grau de conversão dos mesmos. Foram selecionados 30 caninos superiores (n=10) com comprimento radicular médio de 14 mm medidos da junção cemento-esmalte (JCE). Os canais foram tratados endodonticamente ea guta-percha foi removida deixando 4 mm do selamento apical. Após uma semana os canais foram preparados. Para a cimentação, os dentes foram divididos aleatoriamente em 2 grupos, segundo o cimento resinoso utilizado: Grupo ARC: cimento resinoso dual RelyX™ ARC – Adesivo Adper Scotchbond™ Multipurpose Plus (3M/ESPE) e Grupo U200: cimento resinoso dual RelyX™ U200 (3M/ESPE). Antes da inserção do cimento resinoso no interior do canal radicular foram posicionados no pino dois sensores de fibra óptica com redes de Bragg gravadas e colados na região que não entrou em contato com as paredes do canal; um na posição mais apical e outro na mais cervical do pino. Os sensores realizaram a mensuração das deformações do cimento em uma porção coronária e apical do canal radicular, para se obter valores em micro-strain (μe). Logo depois, os espécimes foram cortados em fatias para mensuração do grau de conversão dos cimentos, nos terços apical e cervical por meio da espectroscopia μ-Raman. Os dados obtidos foram analisados estatisticamente por meio do teste ANOVA de dois fatores (p=0,05).Os sensores de fibra óptica com redes de Bragg mostraram-se eficientes na mensuração de contração de polimerização de cimentos resinosos. O cimento resinoso convencional testado no estudoapresentou maiores valores de contração de polimerização e grau de conversão, quando comparado com o cimento resinoso autoadesivo. O terço cervical apresentou maiores valores de contração de polimerização e grau de conversão, quando comparado com o terço apical independentedo tipo de cimento.Made available in DSpace on 2017-07-24T19:22:01Z (GMT). No. of bitstreams: 1 Camilo Andres P Mora.pdf: 2179325 bytes, checksum: 956a5f1d8568fa3876b0879ad21942c4 (MD5) Previous issue date: 2014-02-17Coordenação de Aperfeiçoamento de Pessoal de Nível Superiorapplication/pdfporUNIVERSIDADE ESTADUAL DE PONTA GROSSAPrograma de Pós-Graduação em OdontologiaUEPGBRClinica Integrada, Dentística Restauradora e PeriodontiaFibras de Braggpolimerizaçãograu de conversão, cimentos resinososFiber Bragg Gratingspolymerizationdegree of conversionresinCNPQ::CIENCIAS DA SAUDE::ODONTOLOGIAESTUDO “IN LOCO” DA CONTRAÇÃO DE POLIMERIZAÇÃO E DO GRAU DE CONVERSÃO DE CIMENTOS RESINOSOS UTILIZADOS NA FIXAÇÃO DE PINOS INTRARRADICULARESStudy “in situ” ofthe polymerization shrinkage-strain and degree of conversion of resin cements used for luting intracanal fiber postsinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da UEPGinstname:Universidade Estadual de Ponta Grossa (UEPG)instacron:UEPGORIGINALCamilo Andres P Mora.pdfapplication/pdf2179325http://tede2.uepg.br/jspui/bitstream/prefix/1712/1/Camilo%20Andres%20P%20Mora.pdf956a5f1d8568fa3876b0879ad21942c4MD51prefix/17122017-07-24 16:22:01.66oai:tede2.uepg.br:prefix/1712Biblioteca Digital de Teses e Dissertaçõeshttps://tede2.uepg.br/jspui/PUBhttp://tede2.uepg.br/oai/requestbicen@uepg.br||mv_fidelis@yahoo.com.bropendoar:2017-07-24T19:22:01Biblioteca Digital de Teses e Dissertações da UEPG - Universidade Estadual de Ponta Grossa (UEPG)false
dc.title.por.fl_str_mv ESTUDO “IN LOCO” DA CONTRAÇÃO DE POLIMERIZAÇÃO E DO GRAU DE CONVERSÃO DE CIMENTOS RESINOSOS UTILIZADOS NA FIXAÇÃO DE PINOS INTRARRADICULARES
dc.title.alternative.eng.fl_str_mv Study “in situ” ofthe polymerization shrinkage-strain and degree of conversion of resin cements used for luting intracanal fiber posts
title ESTUDO “IN LOCO” DA CONTRAÇÃO DE POLIMERIZAÇÃO E DO GRAU DE CONVERSÃO DE CIMENTOS RESINOSOS UTILIZADOS NA FIXAÇÃO DE PINOS INTRARRADICULARES
spellingShingle ESTUDO “IN LOCO” DA CONTRAÇÃO DE POLIMERIZAÇÃO E DO GRAU DE CONVERSÃO DE CIMENTOS RESINOSOS UTILIZADOS NA FIXAÇÃO DE PINOS INTRARRADICULARES
Mora, Camilo Andrés Pulido
Fibras de Bragg
polimerização
grau de conversão, cimentos resinosos
Fiber Bragg Gratings
polymerization
degree of conversion
resin
CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA
title_short ESTUDO “IN LOCO” DA CONTRAÇÃO DE POLIMERIZAÇÃO E DO GRAU DE CONVERSÃO DE CIMENTOS RESINOSOS UTILIZADOS NA FIXAÇÃO DE PINOS INTRARRADICULARES
title_full ESTUDO “IN LOCO” DA CONTRAÇÃO DE POLIMERIZAÇÃO E DO GRAU DE CONVERSÃO DE CIMENTOS RESINOSOS UTILIZADOS NA FIXAÇÃO DE PINOS INTRARRADICULARES
title_fullStr ESTUDO “IN LOCO” DA CONTRAÇÃO DE POLIMERIZAÇÃO E DO GRAU DE CONVERSÃO DE CIMENTOS RESINOSOS UTILIZADOS NA FIXAÇÃO DE PINOS INTRARRADICULARES
title_full_unstemmed ESTUDO “IN LOCO” DA CONTRAÇÃO DE POLIMERIZAÇÃO E DO GRAU DE CONVERSÃO DE CIMENTOS RESINOSOS UTILIZADOS NA FIXAÇÃO DE PINOS INTRARRADICULARES
title_sort ESTUDO “IN LOCO” DA CONTRAÇÃO DE POLIMERIZAÇÃO E DO GRAU DE CONVERSÃO DE CIMENTOS RESINOSOS UTILIZADOS NA FIXAÇÃO DE PINOS INTRARRADICULARES
author Mora, Camilo Andrés Pulido
author_facet Mora, Camilo Andrés Pulido
author_role author
dc.contributor.advisor1.fl_str_mv Gomes, Osnara Maria Mongruel
dc.contributor.advisor1ID.fl_str_mv CPF:47308257991
dc.contributor.advisor1Lattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4773647J1
dc.contributor.referee1.fl_str_mv Franco, Ana Paula Gebert
dc.contributor.referee1ID.fl_str_mv CPF:03851604962
dc.contributor.referee1Lattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4730703E6
dc.contributor.referee2.fl_str_mv Arrais, Cesar Augusto Galvão
dc.contributor.referee2ID.fl_str_mv CPF:20064607810
dc.contributor.referee2Lattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4770689J6
dc.contributor.authorID.fl_str_mv CPF:01220034975
dc.contributor.authorLattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4373360J5
dc.contributor.author.fl_str_mv Mora, Camilo Andrés Pulido
contributor_str_mv Gomes, Osnara Maria Mongruel
Franco, Ana Paula Gebert
Arrais, Cesar Augusto Galvão
dc.subject.por.fl_str_mv Fibras de Bragg
polimerização
grau de conversão, cimentos resinosos
topic Fibras de Bragg
polimerização
grau de conversão, cimentos resinosos
Fiber Bragg Gratings
polymerization
degree of conversion
resin
CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA
dc.subject.eng.fl_str_mv Fiber Bragg Gratings
polymerization
degree of conversion
resin
dc.subject.cnpq.fl_str_mv CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA
description The aim of this study was to investigate the shrinkage-strainand degree of conversion inside the rootcanal"in situ"of resin cements used to lute fiber posts (Whitepost DC, FG). Thirty maxillary canines with similar root length average were selected (14 mm ± 1 mm). Each root canal was treated with crown-down technique and filled with gutta-percha, leaving 4 mm of apical seal.One week later, the roots were prepared following fiber post system manufacturer’s instructions. For the cementation, teeth were randomly divided into 2 groups (n = 15) according to the resin cement used: Group 1: dual-cured resin cement RelyX™ ARC – Adper Scotchbond™ Multipurpose Plus Adhesive (3M/ESPE) and Group 2: dual-cured resin cement RelyX™ U200 (3M/ESPE). Two fiber optic sensors with recorded Bragg gratings were attached to the coronal section (not in contact with the root) of each post before inserting the resin cement inside the root canal. These sensors measured the deformations of the cement over the coronal and apical section of the root (μe). Once measured, the specimens were sectionated in order to obtain slides on its cervical and apical sections. The degree of conversion of the cements on each third was analyzed by μ-Raman micro-spectroscopy. The data were statitsticallyanalyzed by two-way ANOVA (p = 0.05). The dual-curedconventional resin cement tested in this study showed the highest values of shrinkage-strain and degree of conversion; cervical region showed higher values than apical region in both of resin cements.
publishDate 2014
dc.date.issued.fl_str_mv 2014-02-17
dc.date.available.fl_str_mv 2016-07-07
2017-07-24T19:22:01Z
dc.date.accessioned.fl_str_mv 2017-07-24T19:22:01Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.citation.fl_str_mv MORA, Camilo Andrés Pulido. Study “in situ” ofthe polymerization shrinkage-strain and degree of conversion of resin cements used for luting intracanal fiber posts. 2014. 66 f. Dissertação (Mestrado em Clinica Integrada, Dentística Restauradora e Periodontia) - UNIVERSIDADE ESTADUAL DE PONTA GROSSA, Ponta Grossa, 2014.
dc.identifier.uri.fl_str_mv http://tede2.uepg.br/jspui/handle/prefix/1712
identifier_str_mv MORA, Camilo Andrés Pulido. Study “in situ” ofthe polymerization shrinkage-strain and degree of conversion of resin cements used for luting intracanal fiber posts. 2014. 66 f. Dissertação (Mestrado em Clinica Integrada, Dentística Restauradora e Periodontia) - UNIVERSIDADE ESTADUAL DE PONTA GROSSA, Ponta Grossa, 2014.
url http://tede2.uepg.br/jspui/handle/prefix/1712
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.publisher.none.fl_str_mv UNIVERSIDADE ESTADUAL DE PONTA GROSSA
dc.publisher.program.fl_str_mv Programa de Pós-Graduação em Odontologia
dc.publisher.initials.fl_str_mv UEPG
dc.publisher.country.fl_str_mv BR
dc.publisher.department.fl_str_mv Clinica Integrada, Dentística Restauradora e Periodontia
publisher.none.fl_str_mv UNIVERSIDADE ESTADUAL DE PONTA GROSSA
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da UEPG
instname:Universidade Estadual de Ponta Grossa (UEPG)
instacron:UEPG
instname_str Universidade Estadual de Ponta Grossa (UEPG)
instacron_str UEPG
institution UEPG
reponame_str Biblioteca Digital de Teses e Dissertações da UEPG
collection Biblioteca Digital de Teses e Dissertações da UEPG
bitstream.url.fl_str_mv http://tede2.uepg.br/jspui/bitstream/prefix/1712/1/Camilo%20Andres%20P%20Mora.pdf
bitstream.checksum.fl_str_mv 956a5f1d8568fa3876b0879ad21942c4
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Biblioteca Digital de Teses e Dissertações da UEPG - Universidade Estadual de Ponta Grossa (UEPG)
repository.mail.fl_str_mv bicen@uepg.br||mv_fidelis@yahoo.com.br
_version_ 1809460455239843840

Registros relacionados