Efeito da temperatura de secagem de dois tipos de silano e da supressão ou redução do tempo de condicionamento com ácido hidrofluorídrico na resistência de união entre uma cerâmica de dissilicato de lítio e um cimento resinoso

• Autor(a) principal: Peixoto, Leticia Monteiro
• Data de Publicação: 2012
• Tipo de documento: Tese
• Idioma: por
• Título da fonte: Biblioteca Digital de Teses e Dissertações da UERJ
• Texto Completo: http://www.bdtd.uerj.br/handle/1/14002
• topic: Dental ceramics; Microtensile strength; Scanning electron microscopy; Silane; Cerâmica odontológica; Microtração; Microscopia eletrônica de varredura; Resistência adesiva; Silano; Cerâmica odontológica; CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA

This study devaluated the effect of different types of silanization and hydrofluoric acid on the microtensile bond strength of a lithium dissilicate ceramic system. Forty IPS e.max Press /Ivoclar Vivadent blocks (5x5x6mm) were cemented to Z250/3M ESPE resin blocks (5x5x6mm) using RelyX ARC/3M ESPE resin-cement according to the following silanization methods: G1: 20s hydrofluoric acid (HF) + non-hydrolyzed silane Primer-Activactor/Dentsply (NHS) dried at room temperature; G2: 20sHF + pre-hydrolyzed silane RelyX Ceramic-Primer/3M ESPE (PHS) dried at room temperature; G3: 10sHF + NHS dried with hot air (50oC-2min); G4: 10sHF + PHS + hot air; G5: NHS + hot air; G6: PHS + hot air; G7: NHS dried at room temperature; G8: PHS dried at room temperature. Before each silanization method, all ceramic blocks were abraded with SiC grit papers (220-600) and cleaned with 37% phosphoric acid (1min). The cementation was made with vertical load of 01 kg for 10 min. After cementation procedure, all ceramic/ciment/resin blocks were stored in distilled water (37oC) for 24h before being cut to obtain stick-shapped specimens (n=45) of approximately 1mm2 cross-sectional area for microtensile test (v=0.5mm/min). Statistical analysis was performed using ANOVA/Dunnett (p-value = 0,000). The mean MPa(SD) values were: G1-21.5(8.9)BC; G2-30.5(7.2)A; G3-19.4(9.1)BC; G4-24.0(9.0)B; G5-8.1(3.2)D; G6-18.0(6.2)C; G7-7.8(2.6)D; G8-6.3(2.5)D. Groups 2, 3, 4 and 6 had no sticks premature fail against groups 1, 5, 7 and 8, that had 2.2, 44.4, 75.6 and 33.3% of sticks premature fails, respectively. As the correlation coefficient was statistically significant, -0.736 (p-value = 0.000), it could be argued that as the percentage of premature loss increased the MPa mean decreases. The failure mode was 44.97% of mixed failures, 51.70% of adhesive failures, 3.33% of cohesive failures of the cement. When the pretreatment is performed without HF conditioning of the IPS e.max Press ceramic surface, then PHS with hot air application should be the silanization method recommended, although higher bond strength values were obtained when HF conditioning for 20s was used with this type of silane. When the time of HF conditioning is reduced for 10 sec, the application of silane (SPH or SNH) must be always related to its heat treatment. NHS should only be used if IPS e.max Press ceramic surfaces are treated with HF.