Avaliação do efeito de resíduos galvânicos sobre a vulcanização e as propriedades da borracha natural (NR)

• Autor(a) principal: Santos, Alex Calcagno de Sales
• Data de Publicação: 2009
• Tipo de documento: Dissertação
• Idioma: por
• Título da fonte: Biblioteca Digital de Teses e Dissertações da UERJ
• Texto Completo: http://www.bdtd.uerj.br/handle/1/8024
• topic: Electroplating - Waste products; Electroplating - Waste reuse; Vulcanization; Rubber - Mechanical properties; Polymers - Mixtures; Waste; Reuse; Galvanoplastia Resíduos; Galvanoplastia Reaproveitamento (Sobras, refugos, etc.); Vulcanização; Borracha Propriedades mecânicas; Polímeros Misturas; Resíduos; Reaproveitamento; CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS

With the Industrial Revolution and the adoption of urban and industrial economic model, based on consumption, there was an increased in the generation of wastes, as a result of different human activities. Electroplating is a process that embellishes and mechanically protects metallic parts and it is present in the industries of metalmechanical segment of Nova Friburgo. In this process, two important wastes are generated: one from pre-treatment of metal parts, other from industrial sewage station. In this investigation, these wastes, named RGs, were incorporated in the natural rubber (NR) in partial or total replacement to zinc oxide (ZnO). A possible activator effect of RGs upon vulcanization and properties of natural rubber was investigated. Mixes are prepared in a two-roll mixer using a conventional system (CV). Vulcanization kinetics was studied at 150, 160 and 170°C through of rheometric tests and the determination of parameters such as: scorch time (ts1); optimum cure time (t90); minimum torque (Ml); maximum torque (Mh); constants rates (k); and, activation energies. In relation to mechanical properties, tensile and tear strength were determined. NR compositions with RGs presented a diminution in ts1 values, increase in the constants rates and diminution of activation energies. However, tear strength is maintained in a satisfactory level only in the compositions where ZnO was partially replaced in 25%.