Síntese, caracterização e aplicações na desidrogenação oxidativa de propano de materiais tipo hidrotalcita Ni-Mg-Al com diferentes ânions de compensação

• Autor(a) principal: Rodrigues, Renata Maria de Lima
• Data de Publicação: 2014
• Tipo de documento: Dissertação
• Idioma: por
• Título da fonte: Biblioteca Digital de Teses e Dissertações da UERJ
• Texto Completo: http://www.bdtd.uerj.br/handle/1/12024
• topic: HDL; terephthalate; heptamolybdate; decavanadato; oxidative dehydrogenation of propane; HDL; tereftalato; heptamolibdato; decavanadato; desidrogenação oxidativa de propano; CNPQ::ENGENHARIAS::ENGENHARIA QUIMICA::TECNOLOGIA QUIMICA

In the reaction of oxidative dehydrogenation of propane (ODHP), propane reacts with oxygen in the transition metal surface to produce propylene and water at temperatures of 300-700 ° C. However, the propylene can easily oxidize, forming CO and CO2. Thus, catalysts that promote the selectivity of propylene are being searched. Hydrotalcites type compounds are identified as potential major catalysts for the reaction. Therefore, the main objective of this work was to synthesize precursors hydrotalcites type (containing Ni2+, Mg 2+ and Al 3+ ions and terephthalate, heptamolybdate and decavanadate as compensation anions) to test in the reaction of oxidative dehydrogenation of propane.These precursors were synthesized with Al/(Ni+Mg+Al) = 0.5 for different ratios of Ni/Mg. In addition, there was the ion exchange terephthalate (TA) by heptamolybdate (Mo7O24) and decavanadate (V10O28). These compounds were calcined, to obtain NiMgAl, NiMgAlMo and NiMgAlV mixed oxides and tested as catalysts in the ODHP reaction.For determining the properties of the catalysts the following characterization techniques were used: XRD, TGA, N2 volumetry, TPR, ICP, FTIR and Raman spectroscopy. The results indicated that the hydrotalcite-like materials were successfully obtained. In the case of the precursors prepared by ion exchange crystallinity was lower than those of NiMgAl-TA series. These same precursors when calcined had very high areas. In three series, the calcined precursors are comprised by mixed oxides such as crystalline NiO, NiMoO4, Ni2V2O7 and Al an Mg species not detected by XRD. In ODHP catalytic test, it was observed that with increasing conversion the propylene selectivity decreased to the mixed oxides containing no molybdenum. The catalysts of molybdenum series were those who performed better with high selectivity even at high conversions and the terephthalate precursor series shows the highest conversions, but with lower selectivity than Mo series