Desenvolvimento de membranas de poli(éter imida) sultonada para a permeacão de gases

• Autor(a) principal: Chã, Michelle Silva Vila
• Data de Publicação: 2009
• Tipo de documento: Dissertação
• Idioma: por
• Título da fonte: Biblioteca Digital de Teses e Dissertações da UERJ
• Texto Completo: http://www.bdtd.uerj.br/handle/1/11932
• topic: Polyether imide; sulfonation of polymers; characterization of thick films; membrane permeation of gases; Poliéter imida; sulfonaçao de polImeros; caracterizaçao de filmes poliméricos densos; membrana para permeaçao de gases; CNPQ::ENGENHARIAS::ENGENHARIA QUIMICA::PROCESSOS INDUSTRIAIS DE ENGENHARIA QUIMICA

The search for membranes with suitable properties for gas separation in industrial scale has led to the modification and synthesis of engineering polymers with the purpose of obtaining membranes with superior properties. 0ne of the modifications that have been considered promising is the insertion of sulfonic groups in commercial polymers. Due to its structure more polar and flexible, it is expected that the sulfonated polymer present an increase in polar gas permeation in relation to nonpolar gases. In this context, the objective of this work is the synthesis and characterization of membranes of poly (ether imide) sulfonated for the permeation of gases. An experimental design was developed in different reaction conditions of temperature, time and an excess of one of the reagents (acetic acid), for the synthesis of poly (ether imide) sulfonated, SPEI. Through this planning, it was found that the variables that most influenced the degree of sulfonation are temperature and time. The polymer with the highest degree of sulfonation, by ion exchange capacity (IEC = 92 mEq H+ I g), was used to prepare SPEI membrane obtained by the technique of solvent evaporation, using chloroform. This film was characterized from the following analysis: infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA) and scanning electron microscopy (SEM) to evaluate the influence of insertion of the sulfonic group in the polymer matrix. The infrared spectrum showed bands of SPEI related to asymmetric vibrations at 1240cm- 1 (S = 0 = 0), in symmetric stretch at 1171 cm-1 (0 = S = 0) and S0 stretch between 1010-1024cm-1. This indicates the presence of sulfonic groups. The DSC analysis was carried out between 150-250ºC. In this range, there are no significant changes in glass transition temperature of the modified polymer (217ºC). It is believed that the decomposition of the sulfone group occurs before the temperature reaches the Tg of the polymer. This assumption is confirmed in the TGA analysis. The images of SEM showed that films were obtained free of pores and defects. The membrane SPEI obtained by the technique of solvent evaporation, was used for testing permeation of gases 02, N2 and C02 in order to determine the permeability and selectivity of the membrane. The permeabilities found for oxygen were 0.76 barrer for PEI and 0.46 barrer for SPEI. The selectivity of carbon dioxide relative to oxygen increased from 3.5 to 4.83. Regarding nitrogen, the permeability measurements were 0.064 barrer and 0.043 barrer for the PEI and the SPEI, respectively, while the selectivity relative to C02 increased from 41.1 to 55.5. These results indicate that the predominant effect of sorption due to increased molecular interactions, thus reducing the free volume, made the membrane sulfonated more compact with lower permeability and higher selectivity. These results agree with the premise that the sulfonation is a promising process for the development of more efficient membranes.