Avaliação das propriedades de barreira a gases de membranas obtidas a partir de dispersões aquosas à base de poliuretanos e argila

• Autor(a) principal: Barboza, Elaine Moraes
• Data de Publicação: 2011
• Tipo de documento: Dissertação
• Idioma: por
• Título da fonte: Biblioteca Digital de Teses e Dissertações da UERJ
• Texto Completo: http://www.bdtd.uerj.br/handle/1/15669
• topic: polyurethanes; aqueous dispersions; nanocomposites; clay; montmorillonite; non-polluting formulations; membranes; gas permeability; barrier properties; poliuretanos; dispersões aquosas; nanocompósitos; argila; montmorilonita; formulações não poluentes; membranas; permeação de gases; propriedades de barreira; CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA::QUIMICA ORGANICA::POLIMEROS E COLOIDES

Nanostructured materials have been receiving increasing attention of scientific community, especially systems of nanocomposites based on polymer and clay. These materials can be obtained in aqueous state and the use of water, replacing organic solvents, is an important line of research due to environmental issues. In this work, dispersions based on waterbone polyurethanes and sodic hydrophilic clay montmorillonite (MMT) were synthesized, in order to evaluate the possible formation of nanocomposites (NWPU s). The monomers employed in the synthesis were: poly (propylene glycol) (PPG), block copolymer based on poly (ethylene glycol) and poly (propylene glycol) (EG-b-PG), containing 7% ethylene glycol; dimethylolpropionic acid (DMPA); isophorone diisocyanate (IPDI); and ethylenediamine (EDA) as chain extender. Aqueous dispersions with and without clay were synthesized by fixing the ratio between the equivalent-grams of diisocyanate and hydroxyl groups (NCO/OH ratio) in 1.5. The clay content also varied from 0.5% to 1% related to prepolymer initial mass. An additional stirring step with Turrax disperser was made in some formulations. The clay was previously delaminated in deionized water and incorporated at prepolymer dispersion in water-addition step. The dispersions were then evaluated in terms of solids content, particle size and apparent viscosity. The films cast from dispersions were characterized by infrared spectrometry (FTIR), thermogravimetry (TG) and permeability to CO2. Cast films were obtained and the gas barrier properties imparted by the clay were analyzed as well as the influence of poly (ethylene glycol) segments content. The insertion of clay imparted an improvement in thermal resistance properties and a decrease in membrane permeability. It was also observed an increase in permeability to CO2 of membranes obtained from formulations containing the higher amount of copolymer (EG-b-PG), independent of clay content.